CN1219561A - Antiseptic coating for wine pot and its production method - Google Patents
Antiseptic coating for wine pot and its production method Download PDFInfo
- Publication number
- CN1219561A CN1219561A CN 98111555 CN98111555A CN1219561A CN 1219561 A CN1219561 A CN 1219561A CN 98111555 CN98111555 CN 98111555 CN 98111555 A CN98111555 A CN 98111555A CN 1219561 A CN1219561 A CN 1219561A
- Authority
- CN
- China
- Prior art keywords
- production method
- cupric oxide
- pot
- antiseptic coating
- wine pot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An anticorrosion paint for wine tank is prepared from epoxy resin and copper oxide in weight ratio of 2 to 1 through mixing epoxy resin with copper oxide, heating to 230-240 deg.C, holding the temp. for 4-5 min, cooling to 200 deg.C, and thickening. Its advantages include high adhesion, high anticorrosion nature, long service life and no air pocket after the painted layer is dried.
Description
The present invention relates to a kind of protective system and production method thereof, especially store up protective system and production method thereof that the wine jar uses.
It mainly is made of iron being used at present storing up the big wine jar that wine uses in the brewery, after iron wine jar must be coated protective system and handles, can be used to store up wine.The protective system of iron wine jar use now mainly is " urushiol varnish ", is produced by Shanghai state lacquer factory, is commonly called as 101 states lacquer.The sticking power of urushiol varnish is relatively poor, just occurs paint film after the coating drying and plays bulging phenomenon.The alcoholic intolerance corrosion, use was just found the liquor variable color less than one month, and the suspended substance of a large amount of grey star samples is arranged in the liquor, the paint film big area plays drum.
The objective of the invention is to provide a kind of antiseptic coating for wine pot, and this paint adhesion is strong, can not occur paint film after the coating drying and play bulging phenomenon, corrosion-resistant, but life-time service; The present invention also will provide the production method of described antiseptic coating for wine pot for this reason.
The object of the present invention is achieved like this:
Formulation for coating material is that Resins, epoxy adds cupric oxide, its weight ratio=2: 1;
Its production method is mixed in the container for earlier Resins, epoxy and cupric oxide being placed on, and then is put into and is heated to 230 ℃~240 ℃ on the stove fire, be incubated 4~5 minutes, is cooled to 200 ℃ again, refines and sends out thick, take the dish out of the pot afterwards, product is a semi-cured state.
Described cupric oxide is that fine copper is placed in 450 ℃ the anthracite stove fire, keeps 16~24 hours, takes out then, regrinds into 4700~4900 purpose copper powders.
Strong adhesion of the present invention paint film can not occur and play bulging phenomenon after the coating drying, corrosion-resistant, but life-time service.The storage wine jar that is applicable to brewery uses, and also can be used for the rotproofing of other containers.Its technology is simple, but large-scale industrial production.
Elaborate below in conjunction with embodiment.
Embodiment:
Fine copper is placed in 450 ℃ the anthracite stove fire, kept 20 hours, take out then, regrind into 4900 purpose copper powders, promptly make cupric oxide;
50 kilograms of Resins, epoxy and 25 kilograms of cupric oxide are placed in the container mix, and then be put into and be heated to 230 ℃ on the stove fire, be incubated 5 minutes, be cooled to 200 ℃ again, refine and send out thick, the back that takes the dish out of the pot, product is a semi-cured state.
Reheat curing gets final product during use.
Claims (3)
1, a kind of antiseptic coating for wine pot is characterized in that Resins, epoxy adds cupric oxide, its weight ratio=2: 1.
2, the production method that is used for the described antiseptic coating for wine pot of claim 1, it is characterized in that earlier Resins, epoxy and cupric oxide be placed in the container and mix, and then be put into and be heated to 230 ℃~240 ℃ on the stove fire, be incubated 4~5 minutes, be cooled to 200 ℃ again, refine and send out thick, the back that takes the dish out of the pot, product is a semi-cured state.
3, production method according to claim 2 is characterized in that described cupric oxide is that fine copper is placed in 450 ℃ the anthracite stove fire, keeps 16~24 hours, takes out then, regrinds into 4700~4900 purpose copper powders.