CN1215706A - Compound additive for increase of blending amount and performance of cement mixed material - Google Patents
Compound additive for increase of blending amount and performance of cement mixed material Download PDFInfo
- Publication number
- CN1215706A CN1215706A CN 98110360 CN98110360A CN1215706A CN 1215706 A CN1215706 A CN 1215706A CN 98110360 CN98110360 CN 98110360 CN 98110360 A CN98110360 A CN 98110360A CN 1215706 A CN1215706 A CN 1215706A
- Authority
- CN
- China
- Prior art keywords
- cement
- qualified
- gypsum
- performance
- alunite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
The content sequence number | Grog % | Slag % | Gypsum % | Admixture % | Fineness % | Denseness % | Stability | SO 3% | Initial set t | Final set t | 3 days | 7 days | 28 days | |||
Anti-folding MPa | Resistance to compression MPa | Anti-folding MPa | Resistance to compression MPa | Anti-folding MPa | Resistance to compression MPa | |||||||||||
?1# | 95.0 | ?0.0 | ?4.5 | ?0.0 | ?5.2 | ?25.5 | Qualified | 2.0 | ?1∶20 | ?2∶25 | ?4.3 | ?25.3 | ?5.5 | ?34.6 | ?7.8 | ?50.8 |
?2# | 69.2 | ?20.0 | ?9.0 | ?0.8 | ?5.7 | ?26.0 | Qualified | 3.4 | ?1∶00 | ?2∶10 | ?4.4 | ?25.3 | ?5.5 | ?33.4 | ?7.6 | ?49.8 |
?3# | 64.2 | ?25.0 | ?9.0 | ?0.8 | ?5.4 | ?26.0 | Qualified | 3.3 | ?1∶45 | ?2∶30 | ?4.2 | ?24.0 | ?5.4 | ?32 | ?7.6 | ?48.3 |
?4# | 59.2 | ?30.0 | ?9.0 | ?0.8 | ?5.8 | ?26.0 | Qualified | 3.2 | ?2∶00 | ?3∶00 | ?4.1 | ?23.5 | ?5.2 | ?31 | ?7.4 | ?47.8 |
?5# | 54.2 | ?35.0 | ?9.0 | ?0.8 | ?5.1 | ?26.0 | Qualified | 3.1 | ?2∶20 | ?3∶30 | ?4.0 | ?23.0 | ?5.0 | ?30.5 | ?7.2 | ?45.2 |
?7# | 95.0 | ?0.0 | ?5.0 | ?0.0 | ?5.0 | ?25.5 | Qualified | 2.1 | 1∶40 | ?2∶30 | ?4.0 | ?23.9 | ?5.5 | ?32.8 | ?7.3 | ?48.0 |
?8# | 59.5 | ?30.0 | ?10.0 | ?0.5 | ?5.4 | ?25.5 | Qualified | 3.8 | ?1∶45 | ?2∶55 | ?4.3 | ?25.5 | ?6.5 | ?38.1 | ?8.3 | ?54.8 |
?9# | 49.5 | ?40.0 | ?10.0 | ?0.5 | ?5.6 | ?26.0 | Qualified | 3.6 | ?2∶00 | ?2∶40 | ?4.3 | ?25.0 | ?6.6 | ?41.0 | ?8.5 | ?56.5 |
?10# | 39.5 | ?50.0 | ?10.0 | ?0.5 | ?5.2 | ?26.0 | Qualified | 3.5 | ?2∶00 | ?3∶25 | ?5.0 | ?25.7 | ?7.5 | ?37.0 | ?9.3 | ?53.3 |
?11# | 29.5 | ?60.0 | ?10.0 | ?0.5 | ?5.6 | ?26.0 | Qualified | 3.4 | ?2∶40 | ?3∶45 | ?4.9 | ?24.0 | ?7.4 | ?35.3 | ?8.7 | ?48.5 |
?12# | 19.5 | ??70.0 | ?10.0 | ?0.5 | ?4.9 | ?26.0 | Qualified | 3.2 | ?2∶50 | ?4∶10 | ?5.3 | ?23.2 | ?6.5 | ?31.0 | ?8.2 | ?45.4 |
The content sequence number | Grog % | Gypsum % | Zeolite % | Slag % | Slag % | Flyash % | Wingdale % | Admixture % | Stability | SO 3% | Initial set t | Final set t | 3 days | 7 days | 28 days | |||
Anti-folding MPa | Resistance to compression MPa | Anti-folding MPa | Resistance to compression MPa | Anti-folding MPa | Resistance to compression MPa | |||||||||||||
?1# | 95.5 | ?4.5 | ?0.0 | Qualified | 1.9 | ?1∶45 | ?2∶30 | ?5.4 | ?33.4 | ?6.7 | ?42.1 | ?8.0 | ?56.4 | |||||
?2# | 71.0 | ?9.0 | ?20.0 | ?1.0 | Qualified | 3.3 | ?2∶40 | ?3∶10 | ?5.4 | ?32.8 | ?6.8 | ?41.5 | ?8.2 | ?55.8 | ||||
?3# | 61.0 | ?9.0 | ?30.0 | ?1.0 | Qualified | 3.2 | ?2∶30 | ?3∶20 | ?5.2 | ?29.4 | ?6.2 | ?38.0 | ?8.0 | ?53.2 | ||||
?4# | 51.0 | ?9.0 | ?40.0 | ?1.0 | Qualified | 3.0 | ?2∶50 | ?4∶00 | ?4.6 | ?26.2 | ?6.0 | ?33.0 | ?7.4 | ?46.2 | ||||
?5# | 95.0 | ?5.0 | Qualified | 2.6 | ?2∶25 | ?3∶30 | ?5.7 | ?33.0 | ?6.8 | ?44.2 | ?8.0 | ?55.4 | ||||||
?6# | 63.5 | ?6.0 | ?20.0 | ?4.0 | ?1.0 | Qualified | 2.4 | ?2∶31 | ?3∶10 | ?4.9 | ?27.0 | ?5.9 | ?37.5 | ?8.2 | ?49.6 | |||
?7# | 63.5 | ?6.0 | ?20.0 | ?4.0 | ?1.0 | ?4.0 | ?1.0 | Qualified | 2.4 | 2∶11 | ?3∶10 | ?5.9 | ?33.5 | ?7.1 | ?40.9 | ?8.4 | ?53.6 | |
?8# | 61.5 | ?6.0 | ?20.0 | ?2.0 | ?5.0 | ?4.0 | ?1.0 | Qualified | 2.3 | ?2∶10 | ?2∶51 | ?5.6 | ?34.0 | ?7.2 | ?42.3 | ?8.9 | ?54.2 | |
?9# | 59.5 | ?6.0 | ?25.0 | ?2.0 | ?2.0 | ?4.0 | ?1.0 | Qualified | 2.2 | ?2∶30 | ?4∶20 | ?4.7 | ?21.9 | ?5.7 | ?35.4 | ?7.8 | ?44.4 | |
?10# | 53.5 | ?6.0 | ?33.0 | ?2.0 | ?4.0 | ?1.0 | Qualified | 2.1 | ?1∶55 | ?3∶27 | ?4.4 | ?21.7 | ?5.4 | ?32.3 | ?7.6 | ?43.1 | ||
?11# | 47.5 | ?6.0 | ?10.0 | ?30.0 | ?5.0 | ?1.0 | Qualified | 2.5 | ?2∶45 | ?4∶15 | ?5.9 | ?28.5 | ?7.9 | ?38.0 | ?8.8 | ?55.1 | ||
?12# | 57.5 | ?6.0 | ?15.0 | ?15.0 | ?5.0 | ?1.0 | Qualified | 2.4 | ?2∶00 | ?3∶40 | ?5.8 | ?34.0 | ?7.9 | ?43.3 | ?9.0 | ?56.2 | ||
?13# | 52.5 | ?6.0 | ?20.0 | ?15.0 | ?5.0 | ?1.0 | Qualified | 2.5 | ?2∶30 | ?4∶10 | ?5.3 | ?27.6 | ?6.8 | ?38.5 | ?8.4 | ?49.2 | ||
?14# | 57.5 | ?6.0 | ?20.0 | ?15.0 | ?1.0 | Qualified | 2.6 | ?2∶40 | ?4∶10 | ?5.9 | ?29.6 | ?7.0 | ?37.0 | ?8.2 | ?50.8 | |||
?15# | 57.5 | ?6.0 | ?15.0 | ?20.0 | ?1.0 | Qualified | 2.6 | ?2∶45 | ?4∶10 | ?5.7 | ?28.4 | ?6.8 | ?34.2 | ?8.0 | ?49.9 |
Claims (3)