CN1207989A - Producing process of antique large vase - Google Patents
Producing process of antique large vase Download PDFInfo
- Publication number
- CN1207989A CN1207989A CN 97115716 CN97115716A CN1207989A CN 1207989 A CN1207989 A CN 1207989A CN 97115716 CN97115716 CN 97115716 CN 97115716 A CN97115716 A CN 97115716A CN 1207989 A CN1207989 A CN 1207989A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- product
- silica gel
- glue
- type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The production uses No.182 glue, No.895 glue, No.196 glue and calcium powder as main material, and after production of gypsum frame, inner gypsum carved mold and soft silica gel mold, the above said material is deposited to produce initial product, which is further processed through trimming, adhering, polishing and painting to result in finished product. The product is moistureproof, acid resistant, mothproof, collisionproof and long-lifed and is high grade handicrafts.
Description
The present invention relates to the processing technology of antique large technology vase.
In the prior art, general large-scale vase is two kinds of pottery or redwood, during the ceramic vase production costs, effort,
Can not make the large-scale art bottle that surpasses 4 meters, product easily splits, and transport difficulty is big.The making raw material costliness of redwood bottle,
Artificial engraving cost height not can manufacture.
The purpose of this invention is to provide a kind of technology of making antique large technology vase of composite.
Purpose of the present invention realizes by following measure:
A kind of manufacture craft of antique large technology vase may further comprise the steps:
A. make the gypsum framework: the basic configuration that large-scale technology vase is carved out with clay by elder generation, type in clay
(1) skin is coated with gypsic horizon and forms gypsum external form (3), and framework of steel reinforcement (2) is arranged in the gypsum external form (3), promptly forms Fig. 1 institute
The gypsum framework that shows;
B. make type in the gypsum engraving: earlier type in the clay is taken out, then pouring gypsum in the gypsum framework
After the moulding, carve, promptly form type (4) in the gypsum engraving shown in Figure 2;
C. make the silica gel soft mode: type (4) surface brush silica gel in the gypsum engraving, the silica gel upper glue cloth repeats to glue
With brush, form silica gel soft mode (5) shown in Figure 3;
D. the preparation of raw material (weight is kilogram):
Be equipped with following raw material: 182 glue 10-20,196 glue 10-20,895 glue 1-1.5
JD96 glue 1-1.5 calcium powder 40-80
It is even to pour above-mentioned raw materials into container for stirring, standby.
E. pour into a mould product: as Fig. 4, silica gel soft mode (5) is put into the gypsum framework, in the silica gel soft mode, put into again
Press required size and make interior type lining mould, raw material is injected in the silica gel soft mode, depanning after the moulding is head product.
F. product post-processed: after the head product depanning, through shaping, bonding, scrape, spray paint, be product.
Above-mentioned manufacturing process can be selected the half module cast for use, is bonded as product then.
The height of product is 5cm-15cm.In the above-mentioned cast product technology, add netted reinforcement material in the raw material, form the intensity enhancement Layer.
The large-scale technology vase of this explained hereafter has fire prevention, protection against the tide, acidproofly, anti-damages by worms, is not afraid of characteristics such as bump, product can manufacture, life of product is long, attractive in appearance, can be according to the product of user's needs, making different shaping, and this technology also can be produced products such as case clock.
Narrate below in conjunction with drawings and Examples.
Fig. 1 is for making the art shapes figure of gypsum framework.
Fig. 2 is for making the art shapes figure of type in the gypsum engraving.
Fig. 3 is for making the art shapes figure of silica gel soft mode.
Fig. 4 is for making the art shapes figure of head product.
With reference to accompanying drawing is an embodiment of this technology, and this product is 10 meters high big bottles modelled after an antique, adopts the half module pouring technology.
The manufacture craft of antique large technology vase may further comprise the steps:
A. make the gypsum framework: the basic configuration that large-scale technology vase is carved out with clay by elder generation, the skin of type in clay (1) are coated with gypsic horizon and form gypsum external form (3), and framework of steel reinforcement (2) is arranged in the gypsum external form (3), promptly form gypsum framework shown in Figure 1;
B. make type in the gypsum engraving: earlier type in the clay is taken out, pouring gypsum in the gypsum framework after the moulding, is carved by the sculptor then, promptly forms type (4) in the gypsum engraving shown in Figure 2;
C. make the silica gel soft mode: type (4) surface brush silica gel in the gypsum engraving, the silica gel upper glue cloth repeats sticking and brush, forms silica gel soft mode (5) shown in Figure 3;
D. the preparation of raw material (weight is kilogram):
Be equipped with following raw material: 182 glue, 15 196 glue, 15 895 glue 1
JD96 glue 1 calcium powder 60
It is even to pour above-mentioned raw materials into container for stirring, standby.
E. pour into a mould product: as Fig. 4. silica gel soft mode (5) is put into the gypsum framework, put in the silica gel soft mode by required size again and make type lining mould, raw material is injected in the silica gel soft mode, depanning after the moulding is head product.
F. product post-processed: after the head product depanning, through shaping, bonding, scrape, spray paint, be product.
Claims (4)
1. the manufacture craft of an antique large technology vase, its feature may further comprise the steps:
A. make the gypsum framework: the basic configuration that large-scale technology vase is carved out with clay by elder generation, the skin of type in clay (1) are coated with gypsic horizon and form gypsum external form (3), and framework of steel reinforcement (2) is arranged in the gypsum external form (3), promptly form the gypsum framework;
B. make type in the gypsum engraving: earlier type in the clay is taken out, pouring gypsum in the gypsum framework after the moulding, is carved by the sculptor then, promptly forms type (4) in the gypsum engraving;
C. make the silica gel soft mode: type (4) surface brush silica gel in the gypsum engraving, the silica gel upper glue cloth repeats sticking and brush, forms silica gel soft mode (5);
D. the preparation of raw material (weight is kilogram):
Be equipped with following raw material: 182 glue 10-20,196 glue 10-20,895 glue 1-1.5
JD96 glue 1-1.5 calcium powder 40-80
It is even to pour above-mentioned raw materials into container for stirring, standby:
E. pour into a mould product: silica gel soft mode (5) is put into the gypsum framework, put in the silica gel soft mode by required size again and make type lining mould, raw material is injected in the silica gel soft mode, depanning after the moulding is head product.
F. product post-processed: after the head product depanning, through shaping, bonding, scrape, spray paint, be product.
2. manufacture craft according to claim 1 is characterized in that described manufacturing process is the half module cast, is bonded as product then.
3. manufacture craft according to claim 1, the height that it is characterized in that product is 5cm-15cm.
4. manufacture craft according to claim 1 and 2 is characterized in that in the described cast product technology, adds netted reinforcement material in the raw material, forms the intensity enhancement Layer.