CN1186091A - Preparation of mixed polyaniline aqueous solution and dispersant liquid - Google Patents
Preparation of mixed polyaniline aqueous solution and dispersant liquid Download PDFInfo
- Publication number
- CN1186091A CN1186091A CN96122196A CN96122196A CN1186091A CN 1186091 A CN1186091 A CN 1186091A CN 96122196 A CN96122196 A CN 96122196A CN 96122196 A CN96122196 A CN 96122196A CN 1186091 A CN1186091 A CN 1186091A
- Authority
- CN
- China
- Prior art keywords
- water
- polyaniline
- aqueous solution
- hour
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for preparing doped polyphenylamine's aqueous solution and water disperser features that water is used as solvent or dispersing medium, and the proton acid with hydrophilic functional groups is used as doping agent. A solution or sol whose solid content is 1-70 g/100 ml can be prepared by mixng them with water-soluble polymer or oligomer, which can be used to prepare non-toxic electrically conducting water paint with electric conductivity of ten to the power from-9 to 0 s/cm. Said paint can be used in antistatic, electromagnetic shelding and anticorrosion.
Description
The invention belongs to the preparation method of the doped polyaniline aqueous solution and aqueous dispersion.
Processing of doped polyaniline is the target that the various countries scholar pursues always.People such as Y.Cao are at Synth.Met., disclose a kind of preparation method who dissolves in the doped polyaniline of ordinary organic solvents in 48 (1992) 91, and its core is to make doping agent with the specific functional groups organic acid.But need to use poisonous organic solvents such as dimethylbenzene, chloroform, meta-cresol.People such as A.J.Epstein, S.A.Chen is at J.Am.Chem.Soc., 112 (1990) 2800,118 (1996) 2545 and Macromoleculars, reported the preparation method of self-doped polyaniline in 29 (1996) 3950 respectively, they adopt technology such as sulfonation, on the polyaniline main chain, insert hydrophilic functional groups-sulfonate radical, realized the dissolving of polyaniline in water.But the preparation of self-doped polyaniline and purifying are very complicated, and cost is very high.Therefore, these two kinds of methods all are unfavorable for the suitability for industrialized production and the large-scale application of solubility doped polyaniline.
The objective of the invention is to adopt water is solvent or dispersion medium, with the protonic acid common polyaniline that directly mixes of band hydrophilic functional groups, prepares the aqueous solution or the aqueous dispersion of doped polyaniline, and Zhi Bei conductive coating specific conductivity is between 10 thus
-9~10
0S/cm.
Polyaniline solutions of the present invention or aqueous dispersion are made up of following component:
R wherein
1, R
2, R
1', R
2'=C
nH
2n+1Or OC (n=0-18),
nH
2n+1(n=0-18);
Solvent or dispersion medium: water;
Water soluble polymer: polyvinyl alcohol (PVAc), polyethylene oxide (PEO), polyvinyl methyl ether, polyoxymethylene etc.;
Water-soluble oligopolymer: resol, trimeric cyanamide etc.;
Defrother: lipid acid C
6~C
10Alkyl ester, oxygen ethylene low polymer or multipolymer contain silicon defoaming agent; Dopant acid has the structure in general formula (1)-(3):
R=R
1(OCH
2CH
2)
nO or R
1(OCH
2)
nO (n=1-100),
R wherein
1=C
mH
2m+1(m=0-12), C
mH
2m+1C
6H
4(m=0-12), CH
2=CH (CH
2)
m(m=0-12) or CH
2=CH (CH
2)
mC
6H
4(m=0-12);
Doping agent can be the mixture of above a kind of acid or several acid;
With above-mentioned component thorough mixing by a certain percentage, mixture is processed with following method, the preparation doped polyaniline aqueous solution or aqueous dispersion:
1) magnetic stirrer fully stirred 2-48 hour;
2) processing of ball mill or colloidal mill is 1-24 hour;
3) in the container of granulated glass sphere or porcelain ball, with vibrator vibration 2-48 hour;
4) use ultrasonication 0.5-48 hour;
Mol ratio N/H wherein
+=0.3-1.0, defrother 0.1-5wt%, total solid content 1-70wt%, each component can be regulated as required.
In addition, water soluble polymer also can use poly(propylene oxide), Polyvinylpyrolidone (PVP), polyvinylpyridine, the plain ester of polyvinyl acetate fibers etc.
Method of the present invention can be prepared the aqueous solution or the aqueous dispersion of doped polyaniline easily.By regulating content, the structure of polymkeric substance, oligopolymer or micromolecule additive in each component ratio and the system, under the prerequisite that does not need complicated technology and equipment, can prepare solid content 1-70wt%, the coating specific conductivity is between 10
-9~10
0The electrically conducting coating that has good adhesion with various base materials of S/cm.Method of the present invention can have the coating of different specific conductivity through the preparation of simple means such as spray, brush.Because with water is solvent or dispersion medium, can be used for preparing non-harmful electrically conducting coating.
Embodiment provided by the invention is as follows:
Embodiment 1:
With 0.4g polyaniline, 2.0g (CH
3(OCH
2CH
2)
7O)
2PO (OH) and 0.05g glycerol fatty acid ester grind in mortar evenly, and this mixture is added in the 100ml there-necked flask, with three washings of 50ml secondary moisture mortar, and add in the there-necked flask.Said mixture is used ultrasonication 48 hours, promptly obtain the aqueous solution of doped polyaniline, the electrodeposited coating film conductance is 1.2 * 10
-1S/cm.
Embodiment 2:
With 0.4g polyaniline, 0.1g molecular weight 1000 polyethylene oxide and 0.8g (CH
3(OCH
2CH
2)
7O)
2PO (OH) and 0.4gCH
3(OCH
2CH
2)
7OPO (OH)
2Press the method for embodiment 1 and mix, and on vibrator vibration 24 hours or ultrasonication 1 hour, the doped polyaniline aqueous dispersion electrodeposited coating film conductance that obtains is 1.05 * 10
-1S/cm, and have good electrochemical.
Embodiment 3:
With 0.4g polyaniline and 0.6g (CH
3(OCH
2CH
2)
2O)
2PO (OH) presses the method for embodiment 1 and handles, and adds the 2.0g molecular weight then and be 100,000 polyethylene oxide in mixed solution, continues vibration 24 hours, obtains heavy-gravity polyaniline aqueous dispersion, and the coating specific conductivity is 2.1 * 10
-4S/cm, and have the chemical property similar with doped polyaniline in 2 with example 1.
Embodiment 4:
Get the solution 5ml of embodiment 1, adding is dissolved with in the 50ml aqueous solution of 2.0g polyvinyl alcohol and 0.5g lipid acid n-Octanol ester, stirs 24 hours.Mixing solutions coating specific conductivity is about 4.0 * 10
-6S/cm.And have with example 1,2,3 in the similar chemical property of doped polyaniline.
Embodiment 5:
Get the solution 5ml of embodiment 1, add be dissolved with the 2.0g polyoxymethylene and the 50ml aqueous solution in, stirred 24 hours.Mixing solutions coating specific conductivity is 4.0 * 10
-6S/cm.
Embodiment 6:
To grind uniform polyaniline/dopant acid mixture 2.5g and 2.5g molecular weight with method among the embodiment 1 is that 500 polyethylene oxide adds in the Resins, epoxy of 50ml solid content 60wt%, vibration is 24 hours on vibrator, obtains the electrically conducting coating that solid content is about 70wt%.This solution is coated on the sheet glass, and room temperature was placed 24 hours, and then placed 24 hours in 50 ℃ of vacuum, can prepare surface conductivity about 10
-7The coating of S/cm.
Embodiment 7:
With 0.4g polyaniline, 0.52g (CH
2=CHCH
2(OCH
2)
3O)
2The method processing that PO (OH) and 0.2gFoamaster-111 press embodiment 1 with 20ml water, the polyaniline film specific conductivity of doped polyaniline formulations prepared from solutions is 5 * 10 thus
-1S/cm, and have excellent electrochemical reversibility.
Embodiment 8:
1.0g polyvinyl methyl ether is dissolved in the 20ml water, under induction stirring, adds the doped polyaniline solution of 5ml embodiment 7 preparations, continue to stir 1 hour.5ml solution is poured on the clean sheet glass of 7 * 7cm room temperature nature film forming.Film forming specific conductivity is 1.3 * 10
-5S/cm.
Embodiment 9:
With 0.4g polyaniline and 4.0g (CH
3(OCH
2CH
2)
20O)
2PO (OH) mixes and 50ml water adds in the 100ml Erlenmeyer flask together, and induction stirring is after 24 hours, and adding 4.0g molecular weight is 1000 ultrapas and 0.4g lipid acid n-hexyl alcohol ester, continues to stir 2 hours.This solution can prepare the coating of the about 10-7S/cm of specific conductivity.
Embodiment 10:
With 0.2g polyaniline, 0.1g glycerol fatty acid ester and 1.8gH (OCH
2CH
2)
40OSO
3H presses the method processing of embodiment 1, can prepare the aqueous solution of doped polyaniline, and the film of formulations prepared from solutions has excellent electrochemical reversibility, specific conductivity about 10 in propylene carbonate (PC) electrolytic solution of 1mol/L LiClO4 thus
-3S/cm.
Claims (1)
1. the preparation method of the doped polyaniline aqueous solution or aqueous dispersion is characterized in that polyaniline solutions or aqueous dispersion be made up of following component:
R wherein
1, R
2, R
1', R
2'=C
nH
2n+1Or OC (n=0-18),
nH
2n+1(n=0-18);
Solvent or dispersion medium: water;
Water soluble polymer: polyvinyl alcohol (PVAc), polyethylene oxide (PEO), polyvinyl methyl ether, polyoxymethylene etc.;
Water-soluble oligopolymer: resol, trimeric cyanamide etc.;
Defrother: lipid acid C
6~C
10Alkyl ester, oxygen ethylene low polymer or multipolymer contain silicon defoaming agent;
R=R
1(OCH
2CH
2)
nO or R
1(OCH
2)
nO (n=1-100),
R wherein
1=C
mH
2m+1(m=0-12), C
mH
2m+1C
6H
4(m=0-12), CH
2=CH (CH
2)
m(m=0-12) or CH
2=CH (CH
2)
mC
6H
4(m=0-12);
Doping agent can be the mixture of above a kind of acid or several acid;
With above-mentioned component thorough mixing by a certain percentage, mixture is processed with following method, the preparation doped polyaniline aqueous solution or aqueous dispersion:
1) magnetic stirrer fully stirred 2-48 hour;
2) processing of ball mill or colloidal mill is 1-24 hour;
3) in the container of granulated glass sphere or porcelain ball, with vibrator vibration 2-48 hour;
4) use ultrasonication 0.5-48 hour;
Mol ratio N/H wherein
+=0.3-1.0, defrother 0.1-5wt%, total solid content 1-70wt%, each component can be regulated as required.