CN1176974A - Injection of bulk moulding compound - Google Patents
Injection of bulk moulding compound Download PDFInfo
- Publication number
- CN1176974A CN1176974A CN 97116801 CN97116801A CN1176974A CN 1176974 A CN1176974 A CN 1176974A CN 97116801 CN97116801 CN 97116801 CN 97116801 A CN97116801 A CN 97116801A CN 1176974 A CN1176974 A CN 1176974A
- Authority
- CN
- China
- Prior art keywords
- initiator
- weight
- stirrer
- stirred
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The injection bulk molding compound consists of polyester resin, vinyl resin, PVAC, nitrile rubber, initiator, stuffing, etc. and has long storage period, fast initiation, short curing period, high flowability and high injection manufacturability.
Description
The present invention relates to a kind of follow-on thermoset injecting lump like moulding plastic (international common name injecting BMC), this moulding compound is in order to automobile front reflection shields such as production cars, also applicable to all kinds of glass fiber reinforced plastics products that require A level surface, anti-high thermal distortion, high-impact requirement, as household electrical appliance and contemporary business automation equipments such as plastic packaging motor, electric iron shells.
The application of mold pressing BMC technology at existing in the world report of the initial stage eighties, has been arrived the application that the mid-80 starts injecting BMC technology again fast, has the goods on A level surface in order to production, is widely used in departments such as automobile and household electrical appliances.Its main ingredient of injecting BMC has caking agent, additive, initiator, stopper, thickening material, pigment paste, filler, glass fiber reinforced materials etc.Wherein the performance of each component is very big to the surface influence of goods A level, and particularly additive is to the flowability of moulding compound, very big to low contraction, the low ripple effect in A level surface of goods.Among this class research is being inquired in the world always.
The present invention seeks to improve the injecting BMC prescription, make it have better flowability and manufacturability, and also improve the products machinery performance, production efficiency height again, cost are also suitable.
Feature of the present invention is:
(1) formulation weight part ratio
Unsaturated polyester resin 60-80
Vinylite 25-50
PVAC 35-50
Contain carboxy nitrile rubber 0.3-0.4
Initiator 1 peroxidation-second-ethyl
The special butyl ester 0.3-0.4 of caproic acid
Two (the tertiary butyl peroxides of initiator 2 1.1-
Change)-3.3.5-trimethyl-cyclohexane 1.0-1.5
KH-550 1.8-2.4
MgO 0.4-0.6
Zinc Stearate 3.0-4.5
Filler treating compound BYK--980 0.8-1.2
Inorganic mixed fillers CaCO
3China clay Al (OH)
3190-250
Chopped glass fiber (1/4 ") 50-70
Pigment paste 0.4-1.0
(2) the selecting for use and mechanism of each component in this prescription:
A) selecting high reactivity metaphenylene vibrin for use is caking agent, and it has the heat-drawn wire height, and its resin-cast body heat texturing temperature is greater than 120 ℃, and over-all properties is superior; With Vinylite and to contain carboxy nitrile rubber toughness reinforcing, common reaction forms network structure, makes reflection shield surface flawless spots, and has higher toughness and resistance to impact shock again.
B) adopted the crosslinked fast initiator 1 of high reactivity and in the mixed initiator of active curing initiator 2, make product have period of storage long, cause characteristics such as fast, that set time is short.
C) adopt compounded mix and varigrained filler to mix, improved the rheological characteristics of admixtion, improved product surface quality.
D) in this prescription KH-550 and MgO are used, with the flowability of control injecting BMC.
3. the preparation technology of this prescription:
(1) earlier unsaturated polyester resin, Vinylite, PVAC, contain liquid such as carboxy nitrile rubber, initiator 1,2, by weight than after the weighing, pour in the stirrer, stirred 3 minutes.
(2) add Zinc Stearate, KH-550, MgO, stirred 3 minutes than adding in the stirrer after the weighing by weight.
(3) add again by weight than inorganic mixed fillers and filler treating compound in stirrer, stirred 3 minutes.
(4) adding chopped glass fiber at last kneads evenly.
(5) product packs and dispatches from the factory.
(6) use this formulation product with injection technique, make the Car headlamp reflection shield.
Advantage of the present invention;
1. used network structure in this injecting BMC prescription, the low shrinkage component of low ripple, the shock strength and the leakless of product have been improved, reach the requirement of " A " level surface quality, this moulding compound period of storage is long, can store below 30 ℃ more than 35 days, and initiation is fast again, set time is short, it gives the time of moulding in 5-10 second, and be 50-90 second set time.
2. this injecting BMC material has good flowability and operational characteristic, in injection technique, does not have material and is stained with sticking to mould tool and runner, and production efficiency height, cost are also suitable, can satisfy the requirement of producing the reflection shield later process, and goods have the overall characteristic on A level surface.
Embodiment:
This injecting BMC material has been used for charade car headlight reflection shield, and the characteristic of its goods is good, and it is as follows to detect data:
Shrinking percentage＜0.05%;
Surfaceness＜0.2 μ m;
Reach A level surface requirements;
Defectives such as the no bubble in surface, crackle, spots;
Heat-drawn wire 〉=250 ℃;
Notched Izod impact strength＞the 1.5J/cm of unit
2
Adopt the weathering test of normes Francaises, through 5 circulation thermocyclings, no abnormal variation, dimensional stabilizing satisfies the light type requirement of Car headlamp reflection shield.
Claims (1)
1. injecting lump like moulding plastic is characterized in that:
[1] formulation weight part ratio
Unsaturated polyester resin 60-80
Vinylite 25-50
PVAC 35-50
Contain carboxy nitrile rubber 0.3-0.4
Initiator 1 peroxidation-second-ethyl
The special butyl ester 0.3-0.4 of caproic acid
Two (the tertiary butyl peroxides of initiator 2 1.1-
Change)-3.3.5-trimethyl-cyclohexane 1.0-1.5
KH--550 1.8-2.4
MgO 0.4-0.6
Zinc Stearate 3.0-4.5
Filler treating compound BYK-980 0.8-1.2
Inorganic mixing is filled out and is produced material CaCO
3China clay Al (OH)
3190-250
Chopped glass fiber (1/4 ") 50-70
Pigment paste 0.4-1.0
[2] preparation technology of this prescription:
(1) earlier unsaturated polyester resin, Vinylite, PVAC, contain liquid such as carboxy nitrile rubber, initiator 1,2, by weight than after the weighing, pour in the stirrer, stirred 3 minutes.
(2) add Zinc Stearate, KH-550, MgO, stirred 3 minutes than adding in the stirrer after the weighing by weight.
(3) add again by weight than inorganic mixed fillers and filler treating compound in stirrer, stirred 3 minutes.
(4) adding chopped glass fiber at last kneads evenly.(5) product packs and dispatches from the factory.