CN117627213A - 一种内墙保温结构 - Google Patents
一种内墙保温结构 Download PDFInfo
- Publication number
- CN117627213A CN117627213A CN202311755713.4A CN202311755713A CN117627213A CN 117627213 A CN117627213 A CN 117627213A CN 202311755713 A CN202311755713 A CN 202311755713A CN 117627213 A CN117627213 A CN 117627213A
- Authority
- CN
- China
- Prior art keywords
- wall
- layer
- heat
- cement
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及内墙保温领域,特别涉及一种内墙保温结构，包括堆砌在承重墙外壁的砖墙，其特征在于，所述砖墙的侧边外壁均设有水泥面层、找平层一、挂网层、覆盖层、保温层、找平层二和漆层，且一种内墙保温结构施工步骤如下。本发明利用在水泥面层上的找平层一与保温板上的找平层二，使得保温板上墙后会保证整体连接的平整性，找平层二保证后续漆层的平整性，配件将保温板牢牢固定在砖墙上，避免后续保温板松动导致裂缝，降低墙面裂缝出现概率，保证墙体的平整性；找平层一上的玻璃纤维网配合保温板接缝处的网，在固定后对接缝和墙体进行一体化，进一步方式前面出现裂缝的几率。
Description
技术领域
本发明涉及内墙保温技术领域，特别涉及一种内墙保温结构。
背景技术
按墙体在建筑中的位置和走向分类：分为外墙和内墙两类。沿建筑四周边缘布置的墙体称为外墙，被外墙包围的墙体称为内墙。内墙是指在室内起分隔空间的作用，没有和室外空气直接接触的墙体；
保温层时建筑墙面的一部分，它多于墙面粘在一起，分为外墙保温层和内墙保温层两种，内墙保温层比较薄，而外墙保温层则要按照相关规定达到一定厚度才能合格，它是有优质的保温材料构成的，起着重要的保温隔热作用，是一种专业构造层；
目前的内墙保温施工时，由于水泥表面为进行找平，且保温板多数为粘接在墙面上的，导致后续的腻子层和乳胶漆会在保温板的接缝处出现裂缝问题。
发明内容
本发明目的是针对上述存在的问题和不足，提出一种内墙保温结构：利用在水泥面层上的找平层一与保温板上的找平层二，使得保温板上墙后会保证整体连接的平整性，找平层二保证后续漆层的平整性，配件将保温板牢牢固定在砖墙上，避免后续保温板松动导致裂缝，降低墙面裂缝出现概率，保证墙体的平整性，解决了墙体不平导致的开裂问题。
为了实现上述目的，本发明采用了如下技术方案：
一种内墙保温结构，包括堆砌在承重墙外壁的砖墙，所述砖墙的侧边外壁均设有水泥面层、找平层一、挂网层、覆盖层、保温层、找平层二和漆层，且一种内墙保温结构施工步骤如下：第一步：清理砖墙表面，对砖墙的表面进行洒水，并搅拌制作水泥面层的水泥砂浆；
第二步：将制作好的水泥砂浆涂抹在砖墙的表面，再使用刮杠对前面的砂浆进行刮平，待到水泥砂浆干燥后形成第一层水泥面层；
第三步：使用设备在砖墙上打出平行与砖墙一面的水平线，再次使用水泥砂浆对第一层水泥面层进行涂抹，根据水平线进行涂抹，保证干燥后的水泥面层较平整，形成找平层一；
第三步：将内墙使用的玻璃纤维网铺设在找平层一外壁，在使用白水泥与石膏混合物涂抹在找平层一中，白水泥与石膏混合五涂抹后将玻璃纤维网隐藏，形成挂网层和覆盖层；
第四步：将保温板等距离铺设在白水泥与石膏混合物的表面，使得白水泥和石膏混合物将保温板粘接在墙壁中；
第五步：待白水泥和石膏混合物体干燥后，使用钻孔设备在保温板和砖墙上开设有等距离分布的隐藏安装孔，使用膨胀配件固定在隐藏安装孔中，进一步将保温板固定在墙壁中；
第六步：对保温板的连接缝隙使用嵌缝膏进行填充，并在保温板的连接处表面铺设接缝网，嵌缝膏将接缝网粘接在保温板的表面；
找平层一上的玻璃纤维网配合保温板接缝处的网，在固定后对接缝和墙体进行一体化，进一步方式前面出现裂缝的几率；
第六步：干燥后，对保温板的表面进行刮涂腻子，第一遍腻子将保温板进行隐藏，干燥后刮涂第二遍腻子，第二遍腻子对砖墙整体进行找平，形成找平层二；
利用在水泥面层上的找平层一与保温板上的找平层二，使得保温板上墙后会保证整体连接的平整性，找平层二保证后续漆层的平整性，配件将保温板牢牢固定在砖墙上，避免后续保温板松动导致裂缝，降低墙面裂缝出现概率，保证墙体的平整性；
第七步：对干燥后的找平层二进行滚涂或喷涂色漆，干燥后形成漆层。
优选的，所述保温板的连接处均为倒角处理，且膨胀配件低于保温板的平面。
优选的，所述第二遍腻子干燥后，需要对其表面进行打磨处理，进一步保证找平层二的平整性，便于后续漆层附着。
优选的，所述砖墙由砖块交错砌成，承重墙位于砖块的顶部处均开设加强槽，加强槽中插有钢筋，砖块与水泥的砌合将钢筋固定在砖墙中。
优选的，所述第一遍腻子：将白水泥与大白粉按7：3的比例，同时加入少量的纤维素，用108建筑胶水搅匀，然后用铁皮刮板将墙面，厚度约为0.6mm；第二遍刮腻子：将大白、滑石粉、聚醋酸乙烯乳液、纤维素按50：25：1：0.5的比例搅拌均匀，用铁皮刮板满刮。
优选的，找平层二中头遍腻子干燥后用1号砂纸磨，将浮腻子及斑迹磨平磨光，再将墙面清扫干净，二遍腻子干燥后用0号砂纸磨平磨光。
本发明的有益效果为：
利用在水泥面层上的找平层一与保温板上的找平层二，使得保温板上墙后会保证整体连接的平整性，找平层二保证后续漆层的平整性，配件将保温板牢牢固定在砖墙上，避免后续保温板松动导致裂缝，降低墙面裂缝出现概率，保证墙体的平整性；
找平层一上的玻璃纤维网配合保温板接缝处的网，在固定后对接缝和墙体进行一体化，进一步方式前面出现裂缝的几率。
附图说明
图1为本发明提出的一种内墙保温结构的整体展开结构示意图；
图2为本发明提出的一种内墙保温结构的砖墙展开结构示意图；
图3为本发明提出的一种内墙保温结构的结构示意图保温板截面。
实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例
参照图1-3所示，一种内墙保温结构，包括堆砌在承重墙外壁的砖墙，所述砖墙的侧边外壁均设有水泥面层、找平层一、挂网层、覆盖层、保温层、找平层二和漆层，所述砖墙由砖块交错砌成，承重墙位于砖块的顶部处均开设加强槽，加强槽中插有钢筋，砖块与水泥的砌合将钢筋固定在砖墙中，且一种内墙保温结构施工步骤如下：第一步：清理砖墙表面，对砖墙的表面进行洒水，并搅拌制作水泥面层的水泥砂浆；
第二步：将制作好的水泥砂浆涂抹在砖墙的表面，再使用刮杠对前面的砂浆进行刮平，待到水泥砂浆干燥后形成第一层水泥面层；
第三步：使用设备在砖墙上打出平行与砖墙一面的水平线，再次使用水泥砂浆对第一层水泥面层进行涂抹，根据水平线进行涂抹，保证干燥后的水泥面层较平整，形成找平层一；
第三步：将内墙使用的玻璃纤维网铺设在找平层一外壁，在使用白水泥与石膏混合物涂抹在找平层一中，白水泥与石膏混合五涂抹后将玻璃纤维网隐藏，形成挂网层和覆盖层；
第四步：将保温板等距离铺设在白水泥与石膏混合物的表面，使得白水泥和石膏混合物将保温板粘接在墙壁中，所述保温板的连接处均为倒角处理，且膨胀配件低于保温板的平面；
第五步：待白水泥和石膏混合物体干燥后，使用钻孔设备在保温板和砖墙上开设有等距离分布的隐藏安装孔，使用膨胀配件固定在隐藏安装孔中，进一步将保温板固定在墙壁中；
第六步：对保温板的连接缝隙使用嵌缝膏进行填充，并在保温板的连接处表面铺设接缝网，嵌缝膏将接缝网粘接在保温板的表面；
第六步：干燥后，对保温板的表面进行刮涂腻子，第一遍腻子将保温板进行隐藏，干燥后刮涂第二遍腻子，第二遍腻子对砖墙整体进行找平，形成找平层二，所述第二遍腻子干燥后，需要对其表面进行打磨处理，进一步保证找平层二的平整性，便于后续漆层附着，所述第一遍腻子：将白水泥与大白粉按7：3的比例，同时加入少量的纤维素，用108建筑胶水搅匀，然后用铁皮刮板将墙面，厚度约为0.6mm；第二遍刮腻子：将大白、滑石粉、聚醋酸乙烯乳液、纤维素按50：25：1：0.5的比例搅拌均匀，用铁皮刮板满刮，找平层二中头遍腻子干燥后用1号砂纸磨，将浮腻子及斑迹磨平磨光，再将墙面清扫干净，二遍腻子干燥后用0号砂纸磨平磨光，操作时一刮板紧接着一刮板，接头不留槎，每一刮板收头时，干净利落。第一遍腻子不宜过厚，这样可以使腻子层和基层良好的结合；腻子打磨时应随时打磨随时采用碘钨灯照射检；
第七步：对干燥后的找平层二进行滚涂或喷涂色漆，干燥后形成漆层，上漆前用砂纸打磨，完毕后彻底清扫一遍墙面，以免粉尘太多，影响漆的附着力，凹凸差不超过3毫米；
刮腻子前将墙面等基层起皮、松动及鼓包等清除剔平，在墙面光滑的部位，用带钢丝轮的手提砂轮打磨面层，将残留在基层表面上的灰尘、污垢、溅沫和砂浆流痕等杂物清除干净。
文中参照实施例详细描述了本发明的示范性实施方式，然而本领域技术人员可理解的是，在不背离本发明理念的前提下，可以对上述具体实施例做出多种变型和改型，且可以对本发明提出的各技术特征、结构进行多种组合，而不超出本发明的保护范围，本发明的保护范围由所附的权利要求确定。前述对本发明的具体示例性实施方案的描述并非想将本发明限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本发明的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本发明的各种不同的示例性实施方案以及各种不同的选择和改变。本发明的范围意在由权利要求书及其等同形式所限定。
Claims (6)
1.一种内墙保温结构，包括堆砌在承重墙外壁的砖墙，其特征在于，所述砖墙的侧边外壁均设有水泥面层、找平层一、挂网层、覆盖层、保温层、找平层二和漆层，且一种内墙保温结构施工步骤如下：第一步：清理砖墙表面，对砖墙的表面进行洒水，并搅拌制作水泥面层的水泥砂浆；
第二步：将制作好的水泥砂浆涂抹在砖墙的表面，再使用刮杠对前面的砂浆进行刮平，待到水泥砂浆干燥后形成第一层水泥面层；
第三步：使用设备在砖墙上打出平行与砖墙一面的水平线，再次使用水泥砂浆对第一层水泥面层进行涂抹，根据水平线进行涂抹，保证干燥后的水泥面层较平整，形成找平层一；
第三步：将内墙使用的玻璃纤维网铺设在找平层一外壁，在使用白水泥与石膏混合物涂抹在找平层一中，白水泥与石膏混合五涂抹后将玻璃纤维网隐藏，形成挂网层和覆盖层；
第四步：将保温板等距离铺设在白水泥与石膏混合物的表面，使得白水泥和石膏混合物将保温板粘接在墙壁中；
第五步：待白水泥和石膏混合物体干燥后，使用钻孔设备在保温板和砖墙上开设有等距离分布的隐藏安装孔，使用膨胀配件固定在隐藏安装孔中，进一步将保温板固定在墙壁中；
第六步：对保温板的连接缝隙使用嵌缝膏进行填充，并在保温板的连接处表面铺设接缝网，嵌缝膏将接缝网粘接在保温板的表面；
第六步：干燥后，对保温板的表面进行刮涂腻子，第一遍腻子将保温板进行隐藏，干燥后刮涂第二遍腻子，第二遍腻子对砖墙整体进行找平，形成找平层二；
第七步：对干燥后的找平层二进行滚涂或喷涂色漆，干燥后形成漆层。
2.根据权利要求1所述的一种内墙保温结构，其特征在于，所述保温板的连接处均为倒角处理，且膨胀配件低于保温板的平面。
3.根据权利要求1所述的一种内墙保温结构，其特征在于，所述第二遍腻子干燥后，需要对其表面进行打磨处理，进一步保证找平层二的平整性，便于后续漆层附着。
4.根据权利要求1所述的一种内墙保温结构，其特征在于，所述砖墙由砖块交错砌成，承重墙位于砖块的顶部处均开设加强槽，加强槽中插有钢筋，砖块与水泥的砌合将钢筋固定在砖墙中。
5.根据权利要求1所述的一种内墙保温结构，其特征在于，所述第一遍腻子：将白水泥与大白粉按7：3的比例，同时加入少量的纤维素，用108建筑胶水搅匀，然后用铁皮刮板将墙面，厚度约为0.6mm；第二遍刮腻子：将大白、滑石粉、聚醋酸乙烯乳液、纤维素按50：25：1：0.5的比例搅拌均匀，用铁皮刮板满刮。
6.根据权利要求1所述的一种内墙保温结构，其特征在于，找平层二中头遍腻子干燥后用1号砂纸磨，将浮腻子及斑迹磨平磨光，再将墙面清扫干净，二遍腻子干燥后用0号砂纸磨平磨光。