CN116987310A - 一种双抗防静电离型膜及其制备工艺 - Google Patents
一种双抗防静电离型膜及其制备工艺 Download PDFInfo
- Publication number
- CN116987310A CN116987310A CN202310791925.1A CN202310791925A CN116987310A CN 116987310 A CN116987310 A CN 116987310A CN 202310791925 A CN202310791925 A CN 202310791925A CN 116987310 A CN116987310 A CN 116987310A
- Authority
- CN
- China
- Prior art keywords
- layer
- antistatic
- release
- agent
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及离型膜技术领域,具体是一种双抗防静电离型膜及其制备工艺,离型膜包括基膜、抗静电层与离型层,基膜1的两面分别设有抗静电层,抗静电层的表面设有耐磨层,至少其中一个耐磨层的表面设置离型层,在制备工艺中,耐磨层采用聚四氟乙烯制成,既可以提供耐磨特性,同时可以提高耐热特性;离型层的采用非硅离型剂,主要成分为丙烯酸酯、聚氨酯、相容剂、催化剂、稳定剂与锚固剂,本发明的离型膜通过丙烯酸酯与聚氨酯的共混反应生成,具备良好的断裂拉伸性能,并且具备良好的耐水性与耐溶剂性,避免了含硅离型膜存在的硅转移的问题,设有两层抗静电层,可以降低剥离电压,避免对物造成破坏。
Description
技术领域
本发明涉及离型膜技术领域,具体是一种双抗防静电离型膜及其制备工艺。
背景技术
现在离型膜广泛应用于电子行业,一般会作为手机、平板电脑等电子产品的生产过程的复合模切膜材、柔性电路板的压合或电子封装脱模等,传统的离型膜一般不具有抗静电性能,但是实际的使用过程中,电磁波会对未经屏蔽的敏感性电子元件、电路板、通信设备等产生不同程度的干扰,造成数据失真、通信紊乱,而电磁感应和摩擦产生的静电对各种敏感元件、仪器仪表、某些化工产品等,如因包装薄膜静电积累产生高压放电,造成电子元件的损坏,所以离型膜的抗静电性能也是至关重要的。
现有的增加离型膜抗静电效果的方式大多是在离型层外部喷涂一层抗静电保护层,技术发展使要求也逐渐提高,需要更高的抗静电能力以防止产生静电斑纹和空气中颗粒尘埃的吸附。
因此,需要设计一种双抗防静电离型膜。
发明内容
为了解决上述问题,本发明提供的双抗防静电离型膜,设有两个抗静电层,并且所使用的离型剂为非硅离型剂,避免了硅转移的问题。
为了达到上述目的,本发明采用以下技术方案:
一种双抗防静电离型膜,所述离型膜包括基膜、抗静电层与离型层,所述基膜的两面分别设有抗静电层,所述抗静电层的表面设有耐磨层,至少其中一个所述耐磨层的表面设有离型层。
可选的,在本发明一实施例中,所述离型层的采用非硅离型剂,所述非硅离型剂的成分包括丙烯酸酯乳液、聚氨酯、相容剂、催化剂、固化剂与锚固剂,各成分的比例为:丙烯酸酯乳液为80%-85%,聚氨酯4%-5%、相容剂5%-8%、催化剂0.5%-1%、稳定剂2%-3%、锚固剂3%-5%。
可选的,在本发明一实施例中,所述相容剂为乙酸乙酯。
可选的,在本发明一实施例中,所述抗静电层的厚度至少为5μm。
可选的,在本发明一实施例中,所述催化剂为异辛酸锌。
可选的,在本发明一实施例中,所述基膜为PET膜,所述PET膜的厚度至少为10μm。
可选的,在本发明一实施例中,所述抗静电层的成分包括聚噻吩导电液、异丙醇、抗氧化剂、分散剂、消泡剂与成膜助剂,各成分的比例为:聚噻吩导电液为30%-40%,异丙醇20%-30%,抗氧化剂10%-15%,分散剂5%-8%,消泡剂10%-15%,成膜助剂5%-10%。
可选的,在本发明一实施例中,所述耐磨层采用聚四氟乙烯制成,所述耐磨层的厚度至少为10μm。
可选的,在本发明一实施例中,所述离型层的厚度至少为5μm。
一种双抗防静电离型膜的制备工艺,包括以下步骤:
步骤S1,预先准备好基膜、抗静电剂、耐磨层材料以及制备丙烯酸酯乳液;
步骤S2,将丙烯酸酯乳液与聚氨酯共混反应,制备离型剂;
步骤S3,通过涂布机将抗静电剂在基膜表面进行涂布,固化后,形成抗静电层;
步骤S4,通过涂布机将耐磨层材料在抗静电层表面进行涂布,固化后,形成耐磨层;
步骤S5,通过涂布机将离型剂在耐磨层表面进行涂布,固化后,形成离型层,获得双抗防静电离型膜。
本发明有益效果
本发明的一种双抗防静电离型膜,与现有的离型膜相比具备以下优点:
离型膜设有双抗静电层,抗静电层为永久性抗静电剂制成,可起到永久性的抗静电,因此,离型膜的有效使用寿命更长,离型层为非硅离型层,避免了含硅离型层会出现硅转移的问题,离型层所采用的材料为丙烯酸酯与聚氨酯共混反应生成,实现两者性能上的互补,具备高剥离强度、耐磨性与环境适应性。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案,下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍。
图1为本发明的实施例1的双抗防静电离型膜结构示意图;
图2为本发明的实施例1的双抗防静电离型膜制备工艺流程图;
附图标记:基膜1、抗静电层2、耐磨层3、离型层4。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂,下面结合附图对本发明的具体实施方式做详细的说明。在下面的描述中阐述了很多具体细节以便于充分理解本发明。但是本发明能够以很多不同于在此描述的其它方式来实施,本领域技术人员可以在不违背本发明内涵的情况下做类似改进,因此本发明不受下面公开的具体实施例的限制。
在本发明的描述中,需要理解的是,术语“中心”、“纵向”、“横向”、“长度”、“宽度”、“厚度”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”、“内”、“外”、“顺时针”、“逆时针”、“轴向”、“径向”、“周向”等指示的方位或位置关系为基于附图所示的方位或位置关系,仅是为了便于描述本发明和简化描述,而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作,因此不能理解为对本发明的限制。
此外,术语“第一”、“第二”仅用于描述目的,而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此,限定有“第一”、“第二”的特征可以明示或者隐含地包括至少一个该特征。在本发明的描述中,“多个”的含义是至少两个,例如两个,三个等,除非另有明确具体的限定。
在本发明中,除非另有明确的规定和限定,术语“安装”、“相连”、“连接”、“固定”等术语应做广义理解,例如,可以是固定连接,也可以是可拆卸连接,或成一体;可以是机械连接,也可以是电连接;可以是直接相连,也可以通过中间媒介间接相连,可以是两个元件内部的连通或两个元件的相互作用关系,除非另有明确的限定。对于本领域的普通技术人员而言,可以根据具体情况理解上述术语在本发明中的具体含义。
在本发明中,除非另有明确的规定和限定,第一特征在第二特征“上”或“下”可以是第一和第二特征直接接触,或第一和第二特征通过中间媒介间接接触。而且,第一特征在第二特征“之上”、“上方”和“上面”可是第一特征在第二特征正上方或斜上方,或仅仅表示第一特征水平高度高于第二特征。第一特征在第二特征“之下”、“下方”和“下面”可以是第一特征在第二特征正下方或斜下方,或仅仅表示第一特征水平高度小于第二特征。
需要说明的是,当元件被称为“固定于”或“设置于”另一个元件,它可以直接在另一个元件上或者也可以存在居中的元件。当一个元件被认为是“连接”另一个元件,它可以是直接连接到另一个元件或者可能同时存在居中元件。本文所使用的术语“垂直的”、“水平的”、“上”、“下”、“左”、“右”以及类似的表述只是为了说明的目的,并不表示是唯一的实施方式。
为更进一步阐述本发明为实现预定发明目的所采取的技术手段及功效,以下结合附图及较佳实施例,对依据本发明的具体实施方式、结构、特征及其功效,详细说明如后。
实施例1
为提高现有的离型膜的抗静电性能以及解决含硅离型膜出现硅转移的问题,设计了一种多层结构的防静电离型膜及其制备工艺,具体方案如下:
如图1所示,一种双抗防静电离型膜,所述离型膜包括基膜1、抗静电层2与离型层4,基膜1的两面分别设有抗静电层2,抗静电层2的表面设有耐磨层3,至少其中一个耐磨层3的表面设有离型层4。
在本实施例中,两个耐磨层3的表面均设有离型层4。
离型层4的采用非硅离型剂,非硅离型剂的成分包括丙烯酸酯乳液、聚氨酯、相容剂、催化剂、固化剂与锚固剂,在本实施例中,各成分的比例为:丙烯酸酯乳液为80%,聚氨酯4%、相容剂5%、催化剂0.5%、稳定剂2%、锚固剂3%。
相容剂为乙酸乙酯,可通过乙酸乙酯将丙烯酸酯和聚氨酯溶解,使二者进行聚合反应。
在本实施例中,抗静电层2的厚度为5μm。
催化剂为异辛酸锌。
基膜1为PET膜,在本实施例中,PET膜的厚度为20μm,基膜及各层间结构的厚度可以根据离型膜的轻薄需求或性能要求进行厚度上的调整。
在其它实施例中,PET膜在生产时,可以加入其它物质,以提高PET膜某方面的性能,进而提高离型膜的性能。
抗静电层2的成分包括聚噻吩导电液、异丙醇、抗氧化剂、分散剂、消泡剂与成膜助剂,在本实施例中,各成分的比例为:聚噻吩导电液为40%,异丙醇40%,抗氧化剂10%,分散剂5%,消泡剂10%,成膜助剂5%。
耐磨层3采用聚四氟乙烯制成,耐磨层3的厚度至少为10μm,在本寿司护理中,耐磨层3的厚度为15μm。
离型层4的厚度至少为5μm,在本实施例中,离型层4的厚度为5μm。
一种双抗防静电离型膜的制备工艺,包括以下步骤:
步骤S1,预先准备好基膜1、抗静电剂、耐磨层3材料以及制备丙烯酸酯乳液;
步骤S2,将丙烯酸酯乳液与聚氨酯共混反应,制备离型剂;
步骤S3,通过涂布机将抗静电剂在基膜1表面进行涂布,固化后,形成抗静电层2;
步骤S4,通过涂布机将耐磨层3材料在抗静电层2表面进行涂布,固化后,形成耐磨层3;
步骤S5,通过涂布机将离型剂在耐磨层3表面进行涂布,固化后,形成离型层4,获得双抗防静电离型膜。
其中,在步骤S1中,制备丙烯酸酯乳液具体为:按比例将水、乳化剂、十二烷基硫酸钠、焦磷酸钠溶液、单体混合物进行升温混合,单体混合物中加入有双丙酮丙烯酰胺,升温中加入过硫酸钾溶液,恒温控制1h后降温,并用氨水中和,即制得丙烯酸酯乳液。
单体混合物为钡、苯乙烯、丙烯酸和二甲氨基苯甲酸异辛酯按比例混合成。
丙烯酸酯与聚氨酯混合生成聚氨酯丙烯酸酯,聚氨酯丙烯酸酯的分子中含有丙烯酸官能团和氨基甲酸酯键,固化后的胶黏剂具有聚氨酯的高耐磨性、粘附力、柔韧性、高剥离强度和优良的耐低温性能以及聚丙烯酸酯卓越的光学性能和耐候性。
在对各层结构进行涂布后,需要等先前进行涂布的层结构稳定后再进行下一步的涂布。
本发明的抗静电膜,通过丙烯酸酯与聚氨酯共混制作离型层,使离型膜的适用性更广,并且避免了硅油离型剂存在的硅转移的问题,离型膜内还设有耐磨层,进一步地提高离型膜的耐磨性能,基膜的两面均设有抗静电层,抗静电层采用永久性抗静电剂,可起到永久性地抗静电。
实施例2
一种双抗防静电离型膜,所述离型膜包括基膜1、抗静电层2与离型层4,基膜1的两面分别设有抗静电层2,抗静电层2的表面设有耐磨层3,至少其中一个耐磨层3的表面设有离型层4。
在本实施例中,其中一个耐磨层3的表面均设有离型层4。
离型层4的采用非硅离型剂,非硅离型剂的成分包括丙烯酸酯乳液、聚氨酯、相容剂、催化剂、固化剂与锚固剂,在本实施例中,各成分的比例为:丙烯酸酯乳液为85%,聚氨酯10%、相容剂8%、催化剂1%、稳定剂3%、锚固剂5%。
相容剂为乙酸乙酯,可通过乙酸乙酯将丙烯酸酯和聚氨酯溶解,使二者进行聚合反应。
在本实施例中,抗静电层2的厚度为10μm。
催化剂为异辛酸锌。
基膜1为PET膜,在本实施例中,PET膜的厚度为50μm。
在其它实施例中,PET膜在生产时,可以加入其它物质,以提高PET膜某方面的性能,进而提高离型膜的性能。
抗静电层2的成分包括聚噻吩导电液、异丙醇、抗氧化剂、分散剂、消泡剂与成膜助剂,在本实施例中,各成分的比例为:聚噻吩导电液为30%,异丙醇30%,抗氧化剂15%,分散剂8%,消泡剂15%,成膜助剂10%。
耐磨层3采用聚四氟乙烯制成,耐磨层3的厚度至少为10μm,在本实施例中,耐磨层3的厚度为25μm。
离型层4的厚度至少为5μm,在本实施例中,离型层4的厚度为15μm。
一种双抗防静电离型膜的制备工艺,包括以下步骤:
步骤S1,预先准备好基膜1、抗静电剂、耐磨层3材料以及制备丙烯酸酯乳液;
步骤S2,将丙烯酸酯乳液与聚氨酯共混反应,制备离型剂;
步骤S3,通过涂布机将抗静电剂在基膜1表面进行涂布,固化后,形成抗静电层2;
步骤S4,通过涂布机将耐磨层3材料在抗静电层2表面进行涂布,固化后,形成耐磨层3;
步骤S5,通过涂布机将离型剂在耐磨层3表面进行涂布,固化后,形成离型层4,获得双抗防静电离型膜。
其中,在步骤S1中,制备丙烯酸酯乳液具体为:按比例将水、乳化剂、十二烷基硫酸钠、焦磷酸钠溶液、单体混合物进行升温混合,单体混合物中加入有双丙酮丙烯酰胺,升温中加入过硫酸钾溶液,恒温控制1h后降温,并用氨水中和,即制得丙烯酸酯乳液。
单体混合物为钡、苯乙烯、丙烯酸和二甲氨基苯甲酸异辛酯按比例混合成。
丙烯酸酯与聚氨酯混合生成聚氨酯丙烯酸酯,聚氨酯丙烯酸酯的分子中含有丙烯酸官能团和氨基甲酸酯键,固化后的胶黏剂具有聚氨酯的高耐磨性、粘附力、柔韧性、高剥离强度和优良的耐低温性能以及聚丙烯酸酯卓越的光学性能和耐候性。
在对各层结构进行涂布后,需要等先前进行涂布的层结构稳定后再进行下一步的涂布,为确保涂布的效果,对单一层面进行涂布时,可以从分别前后不同方向对层面进行多次涂布,以确保涂布的效果。
实施例3
在本实施例中,离型膜的结构与实施例1的离型膜的结构基本相同,区别在于,其中一个耐磨层的表面设有离型层,另一耐磨层未设置离型层。
术语“中心”、“纵向”、“横向”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系,仅是为便于描述本发明的简化描述,而不是指示或暗指所指的装置或元件必须具有特定的方位、为特定的方位构造和操作,因而不能理解为对本发明保护内容的限制。
以上,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例揭示如上,然而并非用以限定本发明,任何本领域技术人员,在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简介修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (10)
1.一种双抗防静电离型膜,其特征在于,所述离型膜包括基膜、抗静电层与离型层,所述基膜的两面分别设有抗静电层,所述抗静电层的表面设有耐磨层,至少其中一个所述耐磨层的表面设有离型层。
2.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述离型层的采用非硅离型剂,所述非硅离型剂的成分包括丙烯酸酯乳液、聚氨酯、相容剂、催化剂、固化剂与锚固剂,各成分的比例为:丙烯酸酯乳液为80%-85%,聚氨酯4%-15%、相容剂5%-8%、催化剂0.5%-1%、稳定剂2%-3%、锚固剂3%-5%。
3.根据权利要求2所述的一种双抗防静电离型膜,其特征在于,所述相容剂为乙酸乙酯。
4.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述抗静电层的厚度至少为5μm。
5.根据权利要求2所述的一种双抗防静电离型膜,其特征在于,所述催化剂为异辛酸锌。
6.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述基膜为PET膜,所述PET膜的厚度至少为10μm。
7.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述抗静电层的成分包括聚噻吩导电液、异丙醇、抗氧化剂、分散剂、消泡剂与成膜助剂,各成分的比例为:聚噻吩导电液为30%-40%,异丙醇30%-40%,抗氧化剂10%-15%,分散剂5%-8%,消泡剂10%-15%,成膜助剂5%-10%。
8.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述耐磨层采用聚四氟乙烯制成,所述耐磨层的厚度至少为10μm。
9.根据权利要求1所述的一种双抗防静电离型膜,其特征在于,所述离型层的厚度至少为5μm。
10.一种双抗防静电离型膜的制备工艺,其特征在于,包括以下步骤:
步骤S1,预先准备好基膜、抗静电剂、耐磨层材料以及制备丙烯酸酯乳液;
步骤S2,将丙烯酸酯乳液与聚氨酯共混反应,制备离型剂;
步骤S3,通过涂布机将抗静电剂在基膜表面进行涂布,固化后,形成抗静电层;
步骤S4,通过涂布机将耐磨层材料在抗静电层表面进行涂布,固化后,形成耐磨层;
步骤S5,通过涂布机将离型剂在耐磨层表面进行涂布,固化后,形成离型层,获得双抗防静电离型膜。