CN116454524B - Explosion-proof valve and preparation method and application thereof - Google Patents
Explosion-proof valve and preparation method and application thereof Download PDFInfo
- Publication number
- CN116454524B CN116454524B CN202310637337.2A CN202310637337A CN116454524B CN 116454524 B CN116454524 B CN 116454524B CN 202310637337 A CN202310637337 A CN 202310637337A CN 116454524 B CN116454524 B CN 116454524B
- Authority
- CN
- China
- Prior art keywords
- explosion
- coating
- proof valve
- valve body
- valve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the technical field of battery preparation, and particularly relates to an explosion-proof valve and a preparation method and application thereof. The explosion-proof valve comprises a valve body, wherein a coating is arranged on the inner surface of the valve body, and the coating comprises a first coating and a second coating; the second coating comprises a component that can react to produce a third coating; the third coating is an anti-corrosion film. The explosion-proof valve provided by the invention is not easy to be corroded by HF acid in the use process, especially the notch is not easy to be corroded, the valve opening time of the explosion-proof valve is delayed, and the service life of a battery can be prolonged when the explosion-proof valve is applied to the battery.
Description
Technical Field
The invention belongs to the technical field of battery preparation, and particularly relates to an explosion-proof valve and a preparation method and application thereof.
Background
The explosion-proof valve is a safety accessory in the battery, is installed on the cover plate or the shell, and can quickly relieve pressure in time under the conditions of overcharging and the like of the battery, so that the explosion of the battery core is avoided.
Because the electrolyte contains LiPOF 6 and additives, HF can be generated when LiPOF 6 encounters water (including water in air), so that an HF acid solution is formed, and the electrolyte is prevented from contacting the explosion-proof valve by increasing the distance between the liquid injection hole on the cover plate and the explosion-proof valve, or adding a convex rib between the liquid injection hole and the explosion-proof valve, or increasing the height of the edge of the explosion-proof valve hole, or adding a groove at the edge of the explosion-proof valve hole, and the like because the electrolyte has corrosiveness to the explosion-proof valve (aluminum and steel). The outside of the explosion-proof valve is contacted with electrolyte, so that the explosion-proof valve is easy to observe and clean, and the outside of the explosion-proof valve is usually protected in the prior art, for example, a protective film is arranged, but in the use process, the explosion-proof valve still has the problems of corrosion and the like.
As the thinnest notch of the explosion-proof valve is as low as 0.1mm, the explosion-proof valve is easy to be corroded by HF acid, electrolyte is corroded by HF acid solution generated by a small amount of water contained in a pole piece, a diaphragm or the electrolyte, and in the use process of a battery, the HF acid solution contacts the explosion-proof valve due to vibration of the battery, so that the explosion-proof valve is corroded, the explosion-proof valve is opened too early, and the service life of the battery is shortened.
Disclosure of Invention
Therefore, the invention aims to overcome the defects that an explosion-proof valve, particularly a notch position in the prior art is easy to be corroded by HF acid, the valve is opened prematurely, the service life of a battery is shortened and the like, and further provides the explosion-proof valve, a preparation method and application thereof.
For this purpose, the invention provides the following technical scheme.
The invention provides an explosion-proof valve, which comprises a valve body;
the inner surface of the valve body is provided with a coating;
the second coating comprises a component that can react to produce a third coating;
the third coating is an anti-corrosion film.
The inner surface of the valve body is the surface close to the inner side of the battery cell.
The outer surface of the explosion-proof valve is provided with a notch;
Preferably, the coating is positioned at the projection position of the notch on the inner surface of the valve body; and/or the number of the groups of groups,
The coating is arranged in the welding area of the explosion-proof valve and the cover plate.
The thickness of the coating is 10nm-20 mu m;
preferably, the porosity of the coating is less than or equal to 5%;
preferably, the thickness of the first coating is 2nm-5 μm;
Preferably, the thickness of the second coating layer is 8nm-15 μm.
The components in the second coating layer comprise metal;
preferably, the second coating is a nickel layer;
preferably, the explosion-proof valve is an aluminum alloy;
preferably, the first coating is a nickel aluminum layer.
In addition, the invention provides a preparation method of the explosion-proof valve, which comprises the following steps:
And spraying by adopting a plasma spraying technology or a magnetron sputtering technology, and forming the first coating and the second coating on the inner surface of the valve body.
The technological parameters of the plasma spraying technology comprise: the powder feeding speed is 10-25g/min; the speed of the spray gun is 500-600mm/s. Preferably, the powder feeding speed is 10-20g/min, and the spray gun speed is 500-560mm/s; more preferably, the powder feed rate is 13g/min and the spray gun speed is 550mm/s.
The technological parameters of the plasma spraying technology further comprise: the spraying current is 500-600A; the spraying voltage is 70-90V; the nitrogen flow is 10-15L/min; argon flow is 10-25L/min; the spraying distance is 100-110mm. Preferably, the spray current is 510-580A; the spraying voltage is 70-85V; more preferably, the spray current 550A; the spraying voltage was 75V.
The technological parameters of the magnetron sputtering are as follows: sputtering power is 2-5w/cm 2; sputtering air pressure is 0.2-1Pa; argon flow is 40-60sccm. Preferably, the sputtering power is 3-4w/cm 2; sputtering air pressure is 0.2-0.5Pa; more preferably, the sputtering power is 3.5w/cm 2; the sputtering air pressure was 0.3Pa.
The sprayed material is nickel powder and/or nickel alloy powder.
Further, the invention also provides a battery comprising the explosion-proof valve or the explosion-proof valve manufactured by the manufacturing method.
The technical scheme of the invention has the following advantages:
1. the invention provides an explosion-proof valve, which comprises a valve body, wherein the inner surface of the valve body is provided with a coating, and the coating comprises a first coating and a second coating; the second coating comprises a component that can react to produce a third coating; the third coating is an anti-corrosion film. The explosion-proof valve provided by the invention is not easy to be corroded by HF acid in the use process, especially the notch is not easy to be corroded, the valve opening time of the explosion-proof valve is delayed, and the service life of a battery can be prolonged when the explosion-proof valve is applied to the battery. The inventor finds that in the application process of the explosion-proof valve, the corrosion phenomenon still occurs after the protective film is arranged on the outer surface of the explosion-proof valve in the prior art, because electrolyte splashes to the inner surface of the explosion-proof valve in the use process, and the explosion-proof valve is easy to corrode due to thinner nick positions, so that the explosion-proof valve is opened prematurely. The invention is provided with the coating on the inner surface of the explosion-proof valve, and part of components in the second coating, such as metallic nickel and the like, can react with HF to generate a third coating, and the third coating is a compact anti-corrosion protective film and is attached to the surface of the second coating, so that the inner surface of the valve body is prevented from being corroded, the content of HF acid in a battery cell can be reduced, and the service performance of the cell can be improved.
When the explosion-proof valve is stamped, the thickness of the notch area is reduced from 0.5mm to 0.1mm, the deformation is large, a large number of crystal defects appear, the internal energy of the crystal is increased along with the deformation, and the temperature is transferred to the notch part when the explosion-proof valve is welded, so that the grain size is further increased, and the pressure resistance value of the explosion-proof valve is reduced. The invention is provided with the coating on the inner surface of the valve body, and the coating and the valve body can form firm self-bonding in a micro metallurgical bonding mode or a physical bonding method, so that the reduction of the pressure resistance value is compensated, and the service life of the battery is prolonged.
2. Compared with polymer material coatings such as PP and PE in the prior art, the explosion-proof valve provided by the invention has the advantages that the second coating is a nickel layer, nickel can react with HF acid in electrolyte to generate a NiF 2 compact protective layer, namely a third coating, so that the weakest notch of the explosion-proof valve can be prevented from being corroded to open the valve prematurely, and the content of HF acid in the electrolyte is reduced; in addition, the adhesion between the coating of the high polymer materials such as PP, PE and the like and the aluminum alloy is poor, and the coating is easy to fall off when the battery works normally, so that the corrosion resistance is invalid.
The specific coating thickness of the invention does not influence the function of the explosion-proof valve, can protect the explosion-proof valve from being corroded to fail in advance, and controls the variation of the explosion-proof valve within 0.4 MPa.
3. The preparation method of the explosion-proof valve provided by the invention can control the thickness of the coating to be 5-20 mu m by controlling the technological parameters of the plasma spraying technology, the porosity is not higher than 5%, and the plasma spraying can enable the coating and the valve body to form firm self-bonding in a micro metallurgical bonding mode. The spraying current, voltage, gas flow and spraying distance mainly influence the ability of melting powder, and the speed of a spray gun and the speed of powder feeding have great influence on the thickness and the porosity of a coating.
The preparation method can control the thickness of the coating to be 10-300nm by controlling the technological parameters of magnetron sputtering, the porosity is not higher than 2%, the magnetron sputtering can enable the coating and the valve body to form firm self-bonding in a physical bonding mode, the sputtering power and the sputtering air pressure mainly influence the coating efficiency, the coating adhesion, the coating thickness and the porosity, and the argon flow mainly prevents oxidation and influences the coating thickness and the porosity.
Drawings
In order to more clearly illustrate the embodiments of the present invention or the technical solutions in the prior art, the drawings that are needed in the description of the embodiments or the prior art will be briefly described, and it is obvious that the drawings in the description below are some embodiments of the present invention, and other drawings can be obtained according to the drawings without inventive effort for a person skilled in the art.
FIGS. 1-3 are schematic structural views of an explosion-proof valve in an embodiment of the present invention;
FIG. 4 is a schematic diagram of the structure of the explosion-proof valve according to the embodiment of the present invention after the valve is applied to HF liquid;
1-a valve body; 101-scoring; a 2-nickel layer; 201-nickel aluminum layer; 202-a nickel layer; 203-a third coating; and a welding area of the 3-explosion-proof valve and the cover plate.
Detailed Description
The following examples are provided for a better understanding of the present invention and are not limited to the preferred embodiments described herein, but are not intended to limit the scope of the invention, any product which is the same or similar to the present invention, whether in light of the present teachings or in combination with other prior art features, falls within the scope of the present invention.
The specific experimental procedures or conditions are not noted in the examples and may be followed by the operations or conditions of conventional experimental procedures described in the literature in this field. The reagents or apparatus used were conventional reagent products commercially available without the manufacturer's knowledge.
It can be understood that the point value data of the present invention is a test reference value, and may have a certain measurement error or instrument error in the actual operation or detection process, so that a certain amplitude of fluctuation may occur. For example, in the practical experimental process, the gas flow is a floating value, which meets the requirements of the invention.
Example 1
The embodiment provides an explosion-proof valve, as shown in fig. 1-3, the explosion-proof valve comprises a valve body 1, a notch 101 is arranged on the outer surface of the valve body, a coating 2 is arranged on the inner surface of the valve body, fig. 1 is the outer surface of the valve body, fig. 2 is the inner surface of the valve body, 3 in fig. 2 is a welding area of the explosion-proof valve and a cover plate, the welding area is an edge of the lower surface of the valve body, and the width of the welding area is not larger than the welding melting width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 3.3%, the thickness of the nickel layer is 13.8 mu m, the thickness of the nickel aluminum layer is 3.4 mu m, and the coating is positioned at the projection position of the notch on the inner surface of the valve body; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting a plasma spraying technology to form a coating; wherein, the technological parameters of the plasma spraying technology are as follows: the spraying current is 600A, the spraying voltage is 70V, the nitrogen flow is 10-15L/min, the argon flow is 10-15L/min, the powder feeding speed is 20g/min, the spraying gun speed is 580mm/s, and the spraying distance is 110mm. And nickel sprayed on the inner surface of the valve body reacts with aluminum in the valve body to generate nickel-aluminum alloy, and the nickel-aluminum layer is connected with the inner surface of the valve body.
Example 2
The embodiment provides an explosion-proof valve, as shown in fig. 1-3, the explosion-proof valve comprises a valve body 1, a notch 101 is arranged on the outer surface of the valve body, a coating 2 is arranged on the inner surface of the valve body, fig. 1 is the outer surface of the valve body, fig. 2 is the inner surface of the valve body, 3 is a welding area of the explosion-proof valve and a cover plate, the welding area is an edge of the lower surface of the valve body, and the width of the welding area is not larger than the welding melting width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 2.2%, the thickness of the nickel layer is 12.7 mu m, the thickness of the nickel aluminum layer is 3.2 mu m, and the coating is arranged in a welding area of the valve body and the cover plate and in a projection position of the notch on the inner surface of the valve body; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting a plasma spraying technology to form a nickel coating; wherein, the technological parameters of the plasma spraying technology are as follows: spraying current 580A, spraying voltage 70V, nitrogen flow 10-15L/min, argon flow 15-20L/min, powder feeding rate 16g/min, spray gun speed 570mm/s and spraying distance 110mm.
Example 3
The embodiment provides an explosion-proof valve, as shown in fig. 1-3, the explosion-proof valve comprises a valve body 1, a notch 101 is arranged on the outer surface of the valve body, a coating 2 is arranged on the inner surface of the valve body, fig. 1 is the outer surface of the valve body, fig. 2 is the inner surface of the valve body, 3 is a welding area of the explosion-proof valve and a cover plate, the welding area is an edge of the lower surface of the valve body, and the width of the welding area is not larger than the welding melting width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 1.7%, the thickness of the nickel layer is 110nm, the thickness of the nickel aluminum layer is 9nm, and the coating is positioned at the projection position of the notch corresponding to the inner surface; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting magnetron sputtering to form a nickel coating; wherein, the technological parameters of the magnetron sputtering are as follows: the sputtering power was 3.5w/cm 2, the sputtering pressure was 0.2Pa, and the argon flow was 50sccm.
Example 4
The embodiment provides an explosion-proof valve, as shown in fig. 1-3, the explosion-proof valve comprises a valve body 1, a notch 101 is arranged on the outer surface of the valve body, a coating 2 is arranged on the inner surface of the valve body, fig. 1 is the outer surface of the valve body, fig. 2 is the inner surface of the valve body, 3 is a welding area of the explosion-proof valve and a cover plate, the welding area is an edge of the lower surface of the valve body, and the width of the welding area is not larger than the welding melting width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity is 1.1%, the thickness of the nickel layer is 155nm, the thickness of the nickel aluminum layer is 13nm, and the coating is arranged on the whole inner surface of the valve body and comprises a welding area and a projection position of a notch corresponding to the inner surface; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting magnetron sputtering to form a nickel coating; wherein, the technological parameters of the magnetron sputtering are as follows: the sputtering power was 5w/cm 2, the sputtering pressure was 0.3Pa, and the argon flow was 50sccm.
Example 5
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 in figure 2 are explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 2.1 percent, the thickness of the nickel layer is 8.1 mu m, the thickness of the nickel aluminum layer is 2.4 mu m, and the coating is arranged in a welding area of the valve body and the cover plate and the projection position of the notch on the inner surface of the valve body; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting a plasma spraying technology to form a coating; wherein, the technological parameters of the plasma spraying technology are as follows: the spraying current is 550A, the spraying voltage is 75V, the nitrogen flow is 10-15L/min, the argon flow is 15-20L/min, the powder feeding speed is 13g/min, the spraying gun speed is 550mm/s, and the spraying distance is 110mm. And nickel sprayed on the inner surface of the valve body reacts with aluminum in the valve body to generate nickel-aluminum alloy, and the nickel-aluminum layer is connected with the inner surface of the valve body.
Example 6
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 in figure 2 are explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 3.1 percent, the thickness of the nickel layer is 10.1 mu m, the thickness of the nickel aluminum layer is 3.0 mu m, and the coating is positioned at the projection position of the notch on the inner surface of the valve body; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
spraying nickel powder on the inner surface of the valve body by adopting a plasma spraying technology to form a coating; wherein, the technological parameters of the plasma spraying technology are as follows: spraying current 560A, spraying voltage 80V, nitrogen flow 10-15L/min, argon flow 20-25L/min, powder feeding speed 10g/min, spray gun speed 530mm/s and spraying distance 100mm. And nickel sprayed on the inner surface of the valve body reacts with aluminum in the valve body to generate nickel-aluminum alloy, and the nickel-aluminum layer is connected with the inner surface of the valve body.
Example 7
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 in figure 2 are explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 2.7%, the thickness of the nickel layer is 14.8 mu m, the thickness of the nickel aluminum layer is 4.5 mu m, and the coating is arranged on the whole inner surface of the valve body and comprises a welding area and a projection position of a notch corresponding to the inner surface; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting a plasma spraying technology to form a coating; wherein, the technological parameters of the plasma spraying technology are as follows: the spraying current is 600A, the spraying voltage is 85V, the nitrogen flow is 10-15L/min, the argon flow is 20-25L/min, the powder feeding rate is 25g/min, the spraying gun speed is 600mm/s, and the spraying distance is 105mm. And nickel sprayed on the inner surface of the valve body reacts with aluminum in the valve body to generate nickel-aluminum alloy, and the nickel-aluminum layer is connected with the inner surface of the valve body.
Example 8
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 is explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 1.9%, the thickness of the nickel layer is 118nm, the thickness of the nickel aluminum layer is 16nm, and the coating is arranged in a welding area of the valve body and the cover plate and in a projection position of the notch on the inner surface of the valve body; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting magnetron sputtering to form a nickel coating; wherein, the technological parameters of the magnetron sputtering are as follows: the sputtering power was 3.5w/cm 2, the sputtering pressure was 0.3Pa, and the argon flow was 50sccm.
Example 9
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 is explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 1.5%, the thickness of the nickel layer is 131nm, the thickness of the nickel aluminum layer is 19nm, and the coating is positioned at the projection position of the notch corresponding to the inner surface; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting magnetron sputtering to form a nickel coating; wherein, the technological parameters of the magnetron sputtering are as follows: the sputtering power was 4w/cm 2, the sputtering pressure was 0.5Pa, and the argon flow was 60sccm.
Example 10
The embodiment provides an explosion-proof valve, the explosion-proof valve includes valve body 1, and the valve body surface is provided with nick 101, and the valve body internal surface is provided with coating 2, and figure 1 is the surface of valve body, and figure 2 is the internal surface of valve body, and 3 is explosion-proof valve and apron welded area, and this welded area is the edge of valve body lower surface, and welded area's width is not greater than the welding width. In this example, the score had a thickness of 0.1mm; the coating comprises a nickel layer 202 and a nickel aluminum layer 201, the porosity of the coating is 1.2%, the thickness of the nickel layer is 83nm, the thickness of the nickel aluminum layer is 14nm, and the coating is arranged on the whole inner surface of the valve body and comprises a welding area and a projection position of a notch corresponding to the inner surface; the explosion-proof valve is 1 series aluminum.
The preparation method of the explosion-proof valve comprises the following steps:
Spraying nickel powder on the inner surface of the valve body by adopting magnetron sputtering to form a nickel coating; wherein, the technological parameters of the magnetron sputtering are as follows: the sputtering power was 2w/cm 2, the sputtering pressure was 0.2Pa, and the argon flow was 40sccm.
Comparative example 1
The present comparative example provides an explosion-proof valve, which is different from example 1 in that the explosion-proof valve in the present comparative example is not provided with a coating layer.
Comparative example 2
This comparative example provides an explosion-proof valve differing from example 1 in that PP is used as a coating. 10 parts by weight of PP (trade name: 4150), 60 parts by weight of methyl isobutyl ketone and 30 parts by weight of benzoyl peroxide were mixed to form a mixed solution, which was coated on the inner surface of the valve body of the explosion-proof valve to form a coating layer having a thickness of 62. Mu.m.
Test examples
The test example provides performance tests of the explosion-proof valves prepared in each example and comparative example, and the performance test is specifically as follows:
the explosion-proof valve was placed in a cell of about 100ppm HF acid solution electrolyte, 1C charged at 45C, 2C discharged, and cycled 200-2000 times or capacity decayed to 20% soh, and the results are shown in table 1.
The explosion pressure detection method of the explosion-proof valve comprises the following steps: disassembling a cover plate assembly in a battery, arranging an explosion-proof valve in the cover plate assembly, testing the explosion pressure of the explosion-proof valve, putting the cover plate assembly into an explosion-proof tester, clamping by a clamp in the tester, starting the test, filling 0.2Mpa air pressure into the tester, keeping 30s free of air leakage, and then raising the air pressure until the explosion-proof valve is exploded, and checking the maximum explosion pressure value. Wherein, the closer the burst pressure value is to the standard value of 0.6+/-0.2 MPa, the better the performance of the explosion-proof valve is.
Table 1 test results of the explosion-proof valves of examples and comparative examples
When the explosion-proof valve is placed in an HF acid solution electrolyte, part of nickel in the second coating on the inner surface of the valve body of the explosion-proof valve in the embodiment reacts with HF acid to generate NiF 2, namely a third coating 203, which is attached to the surface of the second coating, and as shown in fig. 4, the third coating is a compact protective film, so that corrosion of a notch can be prevented, and development time of the explosion-proof valve is delayed.
The results show that the coating is arranged on the surface of the valve body of the explosion-proof valve, so that the explosion-proof valve can be prevented from being abnormal, and the explosion-proof valve cannot be broken, and the battery core cannot bulge. The explosion-proof valve of comparative example 1 was broken during the test; comparative example 2 the explosion-proof valve was coated with PP, and the explosion-proof valve was broken during the test, and the coating was peeled off. None of comparative examples 1-2 was able to test the burst pressure value of the explosion proof valve.
The porosity, the nickel layer thickness and the nickel aluminum layer thickness of the coating are determined by the process parameters of plasma spraying and magnetron sputtering, and after the process parameters of plasma spraying and magnetron sputtering are determined, the porosity, the nickel layer thickness and the nickel aluminum layer thickness of the coating are determined, and as can be seen from the table 1, the performance of the explosion-proof valve adopting the magnetron sputtering is superior to that of the explosion-proof valve adopting the plasma treatment, and the explosion pressure of the explosion-proof valve adopting the magnetron sputtering is closer to the standard value.
Further, by comparing the plasma spraying process parameters, it was found that in example 5, when the powder feeding rate was 13g/min, the spray gun speed was 550mm/s, the spraying current was 550A, and the spraying voltage was 75V, the burst pressure of the explosion-proof valve was closer to the standard value, which indicates that the valve opening time of the explosion-proof valve obtained under the specific condition was delayed, and the specific condition was the optimum process of plasma spraying.
By comparing magnetron sputtering process parameters, the burst pressure values of the explosion-proof valves obtained in the examples 8 and 9 are found to be closest to standard values, the delay of the valve opening time of the two explosion-proof valves is the best, but the coating in the example 10 is positioned on the whole inner surface of the valve body, and the cost is higher than that in the example 8, so that the sputtering power is 3.5w/cm 2 in the example 8; the sputtering air pressure of 0.3Pa is the optimal process of magnetron sputtering.
In summary, the coating is arranged on the inner surface of the valve body, the second coating comprises components capable of generating the third coating by reaction, and the third coating is an anti-corrosion film, for example, the second coating is a nickel layer, so that the anti-explosion valve is not easy to be corroded by HF acid in the use process, particularly the notch is not easy to be corroded, the valve opening time of the anti-explosion valve is delayed, and the service life of the battery can be prolonged when the anti-explosion valve is applied to the battery; preferably a magnetron sputtering process, especially when the sputtering power is 3.5w/cm 2; when the sputtering air pressure is 0.3Pa, the performance of the explosion-proof valve is optimal and the cost is lowest.
It is apparent that the above examples are given by way of illustration only and are not limiting of the embodiments. Other variations or modifications of the above teachings will be apparent to those of ordinary skill in the art. It is not necessary here nor is it exhaustive of all embodiments. And obvious variations or modifications thereof are contemplated as falling within the scope of the present invention.
Claims (14)
1. An explosion-proof valve, characterized in that the explosion-proof valve comprises a valve body;
the inner surface of the valve body is provided with a coating;
the coating comprises a first coating and a second coating;
the second coating comprises a component that can react to produce a third coating;
the third coating is an anti-corrosion film; reacting the second coating with HF to produce the third coating;
The second coating is a nickel layer;
the preparation method of the explosion-proof valve comprises the following steps: spraying by adopting a plasma spraying technology or a magnetron sputtering technology, and forming the first coating and the second coating on the inner surface of the valve body;
the porosity of the coating obtained by the plasma spraying technology is less than or equal to 5 percent;
the porosity of the coating obtained by the magnetron sputtering technology is less than or equal to 2 percent.
2. The explosion proof valve of claim 1, wherein an outer surface of the explosion proof valve is provided with scores.
3. The explosion proof valve of claim 2, wherein said coating is located at a projected location of said score on an inner surface of the valve body; and/or the number of the groups of groups,
The coating is arranged in the welding area of the explosion-proof valve and the cover plate.
4. The explosion-proof valve according to claim 1 or 2, wherein the thickness of the coating is 10nm-20 μm.
5. The explosion-proof valve according to claim 1 or 2, wherein the thickness of the first coating layer is 2nm-5 μm.
6. The explosion-proof valve according to claim 1 or 2, wherein the thickness of the second coating layer is 8nm-15 μm.
7. The explosion protection valve according to claim 1 or 2, wherein the composition in the second coating comprises a metal.
8. The explosion-proof valve according to claim 1 or 2, wherein the explosion-proof valve is an aluminum-based alloy.
9. The explosion protection valve according to claim 1 or 2, wherein the first coating is a nickel aluminium layer.
10. The explosion protection valve of claim 1, wherein the process parameters of the plasma spray technique include: the powder feeding speed is 10-25g/min, and the spray gun speed is 500-600mm/s.
11. The explosion proof valve of claim 10, wherein the process parameters of the plasma spray technique further comprise: the spraying current is 500-600A; the spraying voltage is 70-90V; the nitrogen flow is 10-15L/min; argon flow is 10-25L/min; the spraying distance is 100-110mm.
12. The explosion-proof valve according to claim 1, wherein the process parameters of the magnetron sputtering are: sputtering power is 2-5w/cm 2; sputtering air pressure is 0.2-1Pa; argon flow is 40-60sccm.
13. The explosion-proof valve according to claim 1 or 2, wherein the sprayed material is nickel powder and/or nickel alloy powder when the spraying step is performed.
14. A battery comprising an explosion-proof valve as claimed in any one of claims 1 to 13.