CN116377268B - 一种高强韧反珍珠母结构B4C/Al复合材料的制备方法 - Google Patents
一种高强韧反珍珠母结构B4C/Al复合材料的制备方法 Download PDFInfo
- Publication number
- CN116377268B CN116377268B CN202310242296.7A CN202310242296A CN116377268B CN 116377268 B CN116377268 B CN 116377268B CN 202310242296 A CN202310242296 A CN 202310242296A CN 116377268 B CN116377268 B CN 116377268B
- Authority
- CN
- China
- Prior art keywords
- powder
- mother
- composite material
- composite
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种高强韧反珍珠母结构B4C/Al复合材料的制备方法。本发明涉及高强韧金属基复合材料领域，具体涉及一种高强韧反珍珠母结构B4C/Al复合材料及其制备方法。本发明是要解决现有反珍珠母结构金属基复合材料制备困难，微观结构难以调控的问题。方法：一、一、“核‑壳”结构复合B4C/Al粉末制备；二、“核‑壳”结构复合B4C/Al粉末浸渗铝液；三、三、B4C/Al复合材料热挤压。通过本发明可以简便地实现反珍珠母结构“砖”和“泥”厚度以及“泥”强度的调控，从而制备出不同强塑性组合的反珍珠母结构B4C/Al复合材料。
Description
技术领域
本发明涉及高强韧金属基复合材料领域，具体涉及一种高强韧反珍珠母结构B4C/Al复合材料及其制备方法。
背景技术
碳化硼增强铝基复合材料比强度高、耐磨性好、耐腐蚀性强，且中子吸收截面大，吸收中子后不产生二次辐射，能够应用于飞机蒙皮、直升机螺旋桨、汽车车壳、火车车身、乏燃料储存容器等，对国防军事、交通运输等领域的发展有重要意义，是代替铝合金的理想材料。但是碳化硼增强铝基复合材料在强度获得大幅提升的同时，韧性发生急剧下降，导致材料在服役过程中发生突然失效，大大限制了碳化硼增强铝基复合材料的实际应用。随着科技的进步与发展，对碳化硼增强铝基复合材料的性能提出了更高的要求。
相比于传统均匀分布的碳化硼增强铝基复合材料，反珍珠母结构复合材料能够在保持强度基本不变，甚至获得更高的强度情况下提高材料韧性。但目前反珍珠母结构复合材料的制备方法复杂，制备周期长，成本高昂且只能小规模制备。同时，由于反珍珠母结构复合材料微观上呈复杂的“砖-泥”式排列，在微观尺度上实现精确结构调控具有较高难度。因此，需要一种新的简单的反珍珠母结构复合材料制备方法，实现反珍珠母结构复合材料的大规模制备和微观结构调控。
发明内容
本发明是要解决现有反珍珠母结构金属基复合材料制备困难，微观结构难以调控的问题。而提供一种高强韧反珍珠母结构B4C/Al复合材料的制备方法。
一种高强韧反珍珠母结构B4C/Al复合材料的制备方法具体按以下步骤进行：
一、“核-壳”结构复合B4C/Al粉末制备：
将纳米B4C粉末、微米Al粉和过程控制剂混合进行高能球磨；然后在氩气气氛下保温除去球磨后粉末中的过程控制剂，得到“核-壳”结构的复合B4C/Al粉末；
二、“核-壳”结构复合B4C/Al粉末浸渗铝液：
将“核-壳”结构的复合B4C/Al粉末装入钢模具中，然后施加压力压制成型，得到预制体；将铝液浇入装有预制体的钢模具中，施加压力进行浸渗，浸渗完成后自然冷却至室温，脱模得到B4C/Al复合材料铸锭；
三、B4C/Al复合材料热挤压：
将B4C/Al复合材料铸锭置于热挤压机中进行热挤压，得到反珍珠母结构B4C/Al复合材料。
本发明的有益效果：
本发明以Al基体为软质的“砖”，B4C/Al复合材料为硬质的“泥”，原材料廉价易得，制得的反珍珠母结构B4C/Al复合材料具有优异的强塑性结合且性能稳定。本发明通过高能球磨法制备“核-壳”结构复合粉末，通过压力浸渗铝液获得相互连通的硬质区，通过热挤压实现硬质区、软质区的片层化和定向排列，制备流程少，工艺简单，成本低廉，易于大规模制备。
通过改变纳米B4C粉和微米Al粉的粒径，可以改变复合粉末“核”区和“壳”区的尺寸以及复合粉末间隙浸渗区的尺寸，从而调控反珍珠母结构B4C/Al复合材料软质区和硬质区的厚度；通过改变纳米B4C粉和微米Al粉的比例，可以改变复合粉末“壳”区和复合粉末间隙浸渗区的纳米B4C体积分数，从而调控反珍珠母结构B4C/Al复合材料硬质区的体积分数。通过本发明可以简便地实现反珍珠母结构“砖”和“泥”厚度以及“泥”强度的调控，从而制备出不同强塑性组合的反珍珠母结构B4C/Al复合材料。
附图说明
图1为实施例1得到的反珍珠母结构B4C/Al复合材料的显微组织照片；
图2为实施例1得到的反珍珠母结构B4C/Al复合材料的拉伸曲线；
图3为实施例2得到的反珍珠母结构B4C/Al复合材料的显微组织照片；
图4为实施例2得到的反珍珠母结构B4C/Al复合材料的拉伸曲线。
具体实施方式
具体实施方式一：本实施方式一种高强韧反珍珠母结构B4C/Al复合材料的制备方法具体按以下步骤进行：
一、“核-壳”结构复合B4C/Al粉末制备：
将纳米B4C粉末、微米Al粉和过程控制剂混合进行高能球磨；然后在氩气气氛下保温除去球磨后粉末中的过程控制剂，得到“核-壳”结构的复合B4C/Al粉末；
二、“核-壳”结构复合B4C/Al粉末浸渗铝液：
将“核-壳”结构的复合B4C/Al粉末装入钢模具中，然后施加压力压制成型，得到预制体；将铝液浇入装有预制体的钢模具中，施加压力进行浸渗，浸渗完成后自然冷却至室温，脱模得到B4C/Al复合材料铸锭；
三、B4C/Al复合材料热挤压：
将B4C/Al复合材料铸锭置于热挤压机中进行热挤压，得到反珍珠母结构B4C/Al复合材料。
本实施方式中过程控制剂的质量分数为1～2％。
具体实施方式二：本实施方式与具体实施方式一不同的是：步骤一中所述纳米B4C粉末粒径为50～200nm；所述微米Al粉粒径为1～100μm。其它与具体实施方式一相同。
具体实施方式三：本实施方式与具体实施方式二不同的是：步骤一中所述纳米B4C的体积分数为1～5％，所述微米Al粉的体积分数为95～99％。其它与具体实施方式二相同。
具体实施方式四：本实施方式与具体实施方式一不同的是：步骤一中所述过程控制剂为硬脂酸、油酸、硅油、聚乙烯醇或甘油。其它与具体实施方式一相同。
具体实施方式五：本实施方式与具体实施方式一不同的是：步骤一中所述高能球磨的工艺参数为：球料比大于5:1，球磨转速大于200rpm，球磨时间大于5h，保护气氛为氩气。其它与具体实施方式一相同。
具体实施方式六：本实施方式与具体实施方式一不同的是：步骤一中在氩气气氛下400℃保温0.5h除去球磨后粉末中的过程控制剂。其它与具体实施方式一相同。
具体实施方式七：本实施方式与具体实施方式一不同的是：步骤二中所述压制成型的工艺参数为：压强为50～100MPa，保压时间为15～20min。其它与具体实施方式一相同。
具体实施方式八：本实施方式与具体实施方式一不同的是：步骤二中所述铝液为纯铝、铝硅合金、2xxx铝合金、5xxx铝合金、6xxx铝合金、7xxx铝合金中的一种。其它与具体实施方式一相同。
具体实施方式九：本实施方式与具体实施方式一不同的是：步骤二中所述浸渗的工艺参数为：压强为150～250MPa，保压时间为5～10min。其它与具体实施方式一相同。
具体实施方式十：本实施方式与具体实施方式一不同的是：步骤三中所述热挤压的工艺参数为：挤压比为8:1、10:1或13:1，挤压温度为450～500℃，挤出速率为0.25～0.3m/min。其它与具体实施方式一相同。
通过以下试验验证本发明的效果：
实施例1：一种高强韧反珍珠母结构B4C/Al复合材料的制备方法具体按以下步骤进行：
一、“核-壳”结构复合B4C/Al粉末制备：
将1.57g粒径为200nm的B4C粉末、31.98g粒径为10μm的Al粉和硬脂酸混合进行高能球磨；然后在氩气气氛下400℃保温0.5h除去球磨后粉末中的硬脂酸，得到“核-壳”结构的复合B4C/Al粉末；高能球磨的工艺参数为：球料比10:1，球磨转速300rpm，球磨时间为20h，过程控制剂为硬脂酸，保护气氛为氩气；
二、“核-壳”结构复合B4C/Al粉末浸渗铝液：
将“核-壳”结构的复合B4C/Al粉末装入钢模具中，然后施加100MPa的压力，保压20min压制成型，得到预制体；将铝液浇入装有预制体的钢模具中，施加250MPa压力，保压10min进行浸渗，浸渗完成后自然冷却至室温，脱模得到B4C/Al复合材料铸锭；
三、B4C/Al复合材料热挤压：
将B4C/Al复合材料铸锭置于热挤压机中进行热挤压，得到反珍珠母结构B4C/Al复合材料；热挤压的工艺参数为：挤压比为10:1，挤压温度为500℃，挤出速率为0.25m/min。
图1为实施例1得到的反珍珠母结构B4C/Al复合材料的显微组织照片，能够看出硬质区中纳米碳化硼颗粒分布均匀，且与基体结合良好。硬质区和软质区界面明显但结合良好，无分层等缺陷。硬质区平均厚度为5.37μm，软质区平均厚度为6.55μm。
图2为实施例1得到的反珍珠母结构B4C/Al复合材料的拉伸曲线，可以得到弹性模量为75.5GPa，屈服强度为272.7MPa，抗拉强度为428.0MPa，延伸率为4.1％。
实施例2：一种高强韧反珍珠母结构B4C/Al复合材料的制备方法具体按以下步骤进行：
一、“核-壳”结构复合B4C/Al粉末制备：
将1.57g粒径为200nm的B4C粉末、31.98g粒径为80μm的Al粉和硬脂酸混合进行高能球磨；然后在氩气气氛下400℃保温0.5h除去球磨后粉末中的硬脂酸，得到“核-壳”结构的复合B4C/Al粉末；高能球磨的工艺参数为：球料比10:1，球磨转速300rpm，球磨时间为20h，过程控制剂为硬脂酸，保护气氛为氩气；
二、“核-壳”结构复合B4C/Al粉末浸渗铝液：
将“核-壳”结构的复合B4C/Al粉末装入钢模具中，然后施加100MPa的压力，保压20min压制成型，得到预制体；将铝液浇入装有预制体的钢模具中，施加250MPa压力，保压10min进行浸渗，浸渗完成后自然冷却至室温，脱模得到B4C/Al复合材料铸锭；
三、B4C/Al复合材料热挤压：
将B4C/Al复合材料铸锭置于热挤压机中进行热挤压，得到反珍珠母结构B4C/Al复合材料；热挤压的工艺参数为：挤压比为10:1，挤压温度为500℃，挤出速率为0.25m/min。
图3为实施例2得到的反珍珠母结构B4C/Al复合材料的显微组织照片，能够看出硬质区中纳米碳化硼颗粒分布均匀，且与基体结合良好。硬质区和软质区界面明显但结合良好，无分层等缺陷。硬质区平均厚度为2.12μm，软质区平均厚度为12.27μm。
图4为实施例2得到的反珍珠母结构B4C/Al复合材料的拉伸曲线，可以得到弹性模量为75.9GPa，屈服强度为379.1MPa，抗拉强度为416.9MPa，延伸率为8.6％。
Claims (5)
1.一种高强韧反珍珠母结构B4C/Al复合材料的制备方法，其特征在于高强韧反珍珠母结构B4C/Al复合材料的制备方法具体按以下步骤进行：
一、“核-壳”结构复合B4C/Al粉末制备：
将纳米B4C粉末、微米Al粉和过程控制剂混合进行高能球磨；然后在氩气气氛下保温除去球磨后粉末中的过程控制剂，得到“核-壳”结构的复合B4C/Al粉末；所述纳米B4C粉末粒径为50～200nm；所述微米Al粉粒径为1～100μm；所述纳米B4C的体积分数为1～5％，所述微米Al粉的体积分数为95～99％；
二、“核-壳”结构复合B4C/Al粉末浸渗铝液：
将“核-壳”结构的复合B4C/Al粉末装入钢模具中，然后施加压力压制成型，得到预制体；将铝液浇入装有预制体的钢模具中，施加压力进行浸渗，浸渗完成后自然冷却至室温，脱模得到B4C/Al复合材料铸锭；所述压制成型的工艺参数为：压强为50～100MPa，保压时间为15～20min；所述浸渗的工艺参数为：压强为150～250MPa，保压时间为5～10min；
三、B4C/Al复合材料热挤压：
将B4C/Al复合材料铸锭置于热挤压机中进行热挤压，得到反珍珠母结构B4C/Al复合材料；所述热挤压的工艺参数为：挤压比为8:1、10:1或13:1，挤压温度为450～500℃，挤出速率为0.25～0.3m/min。
2.根据权利要求1所述的一种高强韧反珍珠母结构B4C/Al复合材料的制备方法，其特征在于步骤一中所述过程控制剂为硬脂酸、油酸、硅油、聚乙烯醇或甘油。
3.根据权利要求1所述的一种高强韧反珍珠母结构B4C/Al复合材料的制备方法，其特征在于步骤一中所述高能球磨的工艺参数为：球料比大于5:1，球磨转速大于200rpm，球磨时间大于5h，保护气氛为氩气。
4.根据权利要求1所述的一种高强韧反珍珠母结构B4C/Al复合材料的制备方法，其特征在于步骤一中在氩气气氛下400℃保温0.5h除去球磨后粉末中的过程控制剂。
5.根据权利要求1所述的一种高强韧反珍珠母结构B4C/Al复合材料的制备方法，其特征在于步骤二中所述铝液为纯铝、铝硅合金、2xxx铝合金、5xxx铝合金、6xxx铝合金、7xxx铝合金中的一种。