CN116262661A - 一种具有净化空气和除异味的负离子瓷砖及其生产工艺 - Google Patents
一种具有净化空气和除异味的负离子瓷砖及其生产工艺 Download PDFInfo
- Publication number
- CN116262661A CN116262661A CN202111514836.XA CN202111514836A CN116262661A CN 116262661 A CN116262661 A CN 116262661A CN 202111514836 A CN202111514836 A CN 202111514836A CN 116262661 A CN116262661 A CN 116262661A
- Authority
- CN
- China
- Prior art keywords
- oxide
- following components
- weight
- parts
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；所述底层包括以重量份计的如下组份：二氧化硅74％‑76％、三氧化二铝14％‑15％、三氧化二铁0.5％‑0.7％、二氧化钛0.05％‑0.1％、氧化钙0.11％‑0.2％、氧化镁0.24％‑0.37％、氧化钾5％‑8％和氧化钠3％‑5％；所述中层包括以重量份计的如下组份：二氧化硅80％‑85％、三氧化二铝14％‑20％、三氧化二铁0.5％‑0.7％、二氧化钛0.05％‑0.08％、氧化钙0.11％‑0.15％、氧化镁0.24％‑0.34％、氧化钾5％‑7％和氧化钠3％‑3.5％；所述面层包括以重量份计的如下组份：负离子素1％‑2％，其余为表层釉。本发明的瓷砖具有净化空气和除异味的能力，成为代替水泥和石材对路面硬化的优秀选择。
Description
技术领域
本发明涉及瓷砖领域，特别涉及一种具有净化空气和除异味的负离子瓷砖及其生产工艺。
背景技术
近年来，随着人们生活需求的不断提高，大量的电器产品、燃气用具进入家庭。这些产品在运转过程中排放的烟雾中含有大量的pm2.5微尘颗粒，并有大量的电磁辐射，是造成室内空气污染的罪魁祸首；另外，室内的墙壁装饰、涂料涂刷、皮革家具等也含有大量的甲醛、苯等有害物质，常年向外释放有害气体；由于人们常年生活在室内，一些长期使用的家具，日常用品还容易滋生致病细菌等，都是危害人们身体健康的杀手。
现有技术中的瓷砖不具备净化空气以及去除异味的能力，劣化了瓷砖的应用性能。
发明内容
本发明要解决的技术问题是提供一种能广泛应用在城市广场、人行道、高档小区、车站、步行街、停车场和机场等场所且具有净化空气和除异味能力的负离子瓷砖。
为了解决上述技术问题，本发明的技术方案为：
在第一方面，本发明提供一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅74％-76％、三氧化二铝14％-15％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.1％、氧化钙0.11％-0.2％、氧化镁0.24％-0.37％、氧化钾5％-8％和氧化钠3％-5％；
所述中层包括以重量份计的如下组份：二氧化硅80％-85％、三氧化二铝14％-20％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.08％、氧化钙0.11％-0.15％、氧化镁0.24％-0.34％、氧化钾5％-7％和氧化钠3％-3.5％；
所述面层包括以重量份计的如下组份：负离子素1％-2％，其余为表层釉。
优选的，所述底层包括以重量份计的如下组份：二氧化硅74％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述中层包括以重量份计的如下组份：二氧化硅80％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述面层包括以重量份计的如下组份：负离子素1％，其余为表层釉。
优选的，所述底层包括以重量份计的如下组份：二氧化硅76％、三氧化二铝15％、三氧化二铁0.7％、二氧化钛0.1％、氧化钙0.2％、氧化镁0.37％、氧化钾8％和氧化钠5％；
所述中层包括以重量份计的如下组份：二氧化硅85％、三氧化二铝20％、三氧化二铁0.7％、二氧化钛0.08％、氧化钙0.15％、氧化镁0.34％、氧化钾7％和氧化钠3.5％；
所述面层包括以重量份计的如下组份：负离子素2％，其余为表层釉。
优选的，所述底层包括以重量份计的如下组份：二氧化硅75％、三氧化二铝14.5％、三氧化二铁0.6％、二氧化钛0.08％、氧化钙0.17％、氧化镁0.3％、氧化钾7％和氧化钠4％；
所述中层包括以重量份计的如下组份：二氧化硅82％、三氧化二铝18％、三氧化二铁0.6％、二氧化钛0.06％、氧化钙0.13％、氧化镁0.32％、氧化钾6％和氧化钠3.2％；
所述面层包括以重量份计的如下组份：负离子素1.2％，其余为表层釉。
在第二方面，本发明提供一种生产第一方面所述的具有净化空气和除异味负离子瓷砖的生产工艺，包括以下步骤：
原料粉碎：将制成底层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
将制成中层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
粉料混合：将底层的粉料混合均匀；
将中层的粉料混合均匀；
陈腐：分别将混合后的底层粉料以及中层粉料在存储器内陈腐不少于48小时；
压铸成型：在压铸机的模具里布设两层陈腐后的底层粉料以及布设一层陈腐后的中层粉料，然后采用压铸机成型制得砖坯；
烧成：将砖坯放置于炉中烧成，砖坯的底面温度控制在1179℃-1180℃，砖坯表面温度控制在1191℃-1198℃，保温40分钟-45分钟制成砖体；
淋釉：用清水清洗砖体并晾干后在砖体表面淋釉，其中，砖体表面每平方米淋釉112.8克至113克；
面层制作：将面层淋至淋釉后的砖体上，砖体每平方米淋面层114克至115克。
优选的，还包括印花：面层制作完毕后在面层印花。
优选的，还包括煅烧：在温度为1100℃的条件下对印花后的砖体煅烧60分钟-70分钟。
优选的，还包括抛光：煅烧完毕后采用200-1000目的磨头或磨块对煅烧后的砖体进行抛光。
优选的，还包括磨边：对煅烧完毕后的砖体进行磨边处理。
优选的，所述压铸成型中的压力为27500N-28500N。
本发明的有益效果：
第一方面，本发明通过在面层中加入以重量计1％-2％的负离子素，负离子素具有产生负离子的能力，可以有效地净化空气并且具有去除异味的能力。另外，负离子素与表层釉混合制成面层，负离子素易于掺入面层，负离子瓷砖易于生产。
第二方面，本发明通过选用陶瓷废砖和矿渣边角料为原材料，然后通过两次布料，自动液压机高压成型，全自动辊道窑炉高温烧成，提供了一种能广泛应用在城市广场、人行道、高档小区、车站、步行街、停车场和机场等等场所的具有净化空气和除异味的负离子瓷砖，成为代替水泥和石材对路面硬化的优秀选择。
附图说明
图1为本发明的生产工艺流程图。
具体实施方式
下面结合附图对本发明的具体实施方式作进一步说明。在此需要说明的是，对于这些实施方式的说明用于帮助理解本发明，但并不构成对本发明的限定。此外，下面所描述的本发明各个实施方式中所涉及的技术特征只要彼此之间未构成冲突就可以相互组合。
第一方面：一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅74％-76％、三氧化二铝14％-15％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.1％、氧化钙0.11％-0.2％、氧化镁0.24％-0.37％、氧化钾5％-8％和氧化钠3％-5％；
所述中层包括以重量份计的如下组份：二氧化硅80％-85％、三氧化二铝14％-20％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.08％、氧化钙0.11％-0.15％、氧化镁0.24％-0.34％、氧化钾5％-7％和氧化钠3％-3.5％；
所述面层包括以重量份计的如下组份：负离子素1％-2％，其余为表层釉。
实施例一：
一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅74％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述中层包括以重量份计的如下组份：二氧化硅80％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述面层包括以重量份计的如下组份：负离子素1％，其余为表层釉。
实施例二：
一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅76％、三氧化二铝15％、三氧化二铁0.7％、二氧化钛0.1％、氧化钙0.2％、氧化镁0.37％、氧化钾8％和氧化钠5％；
所述中层包括以重量份计的如下组份：二氧化硅85％、三氧化二铝20％、三氧化二铁0.7％、二氧化钛0.08％、氧化钙0.15％、氧化镁0.34％、氧化钾7％和氧化钠3.5％；
所述面层包括以重量份计的如下组份：负离子素2％，其余为表层釉。
实施例三：
一种具有净化空气和除异味的负离子瓷砖，包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅75％、三氧化二铝14.5％、三氧化二铁0.6％、二氧化钛0.08％、氧化钙0.17％、氧化镁0.3％、氧化钾7％和氧化钠4％；
所述中层包括以重量份计的如下组份：二氧化硅82％、三氧化二铝18％、三氧化二铁0.6％、二氧化钛0.06％、氧化钙0.13％、氧化镁0.32％、氧化钾6％和氧化钠3.2％；
所述面层包括以重量份计的如下组份：负离子素1.2％，其余为表层釉。
第二方面：一种生产第一方面所述的具有净化空气和除异味负离子瓷砖的生产工艺，包括以下步骤：
参阅图1所示，原料粉碎：将制成底层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
将制成中层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
粉料混合：将底层的粉料混合均匀；
将中层的粉料混合均匀；
陈腐：分别将混合后的底层粉料以及中层粉料在存储器内陈腐不少于48小时；
压铸成型：在压铸机的模具里布设两层陈腐后的底层粉料以及布设一层陈腐后的中层粉料，然后采用压铸机成型制得砖坯；所述压铸成型中的压力为27500N-28500N。
烧成：将砖坯放置于炉中烧成，砖坯的底面温度控制在1179℃-1180℃，砖坯表面温度控制在1191℃-1198℃，保温40分钟-45分钟制成砖体；
淋釉：用清水清洗砖体并晾干后在砖体表面淋釉，其中，砖体表面每平方米淋釉112.8克至113克；施釉采用钟罩淋釉的方法，钟罩淋釉通过溢流的方法使釉浆形成釉浆膜，使砖体从釉膜下通过，在砖体表面黏附上一层釉；
面层制作：将面层淋至淋釉后的砖体上，砖体每平方米淋面层114克至115克。
还包括印花：面层制作完毕后在面层印花。采用数码喷墨机的印花技术，把图案调好颜色，然后输入到数码喷墨机的控制器内，即可像打印机一样把图案打印在砖面上，所述数码喷墨机墨水的颜色有蓝色、棕色、黄色、包裹红、黑色和白色等，功能墨水有亮光墨水、哑光墨水、精雕墨水、下陷墨水等，所述颜色墨水用来表现丰富的图案颜色，所述功能墨水可以结合图案增加釉面的光泽变化和表面的凹凸效果，使产品变得丰富和自然。
还包括煅烧：在温度为1100℃的条件下对印花后的砖体煅烧60分钟-70分钟。
还包括抛光：煅烧完毕后采用200-1000目的磨头或磨块对煅烧后的砖体进行抛光。
还包括磨边：对煅烧完毕后的砖体进行磨边处理。按照标准要求通过磨边机进行磨削，配备的设备包括自动上砖、下砖机、轨道式智能储坯***和干式磨边机等。
其中，原料粉碎中，先将大块的陶瓷废砖和矿渣边角料挑出来，然后对这些大块的陶瓷废砖和矿渣边角料进行鄂***理，鄂***理后将小块的陶瓷废砖和矿渣边角料挑出来，然后将这些小块的陶瓷废砖和矿渣边角料进行反击***理，反击***理后将这些小块的陶瓷废砖和矿渣边角料进行三层筛网的平筛，平筛分三层，每层目数分别为：3目、4目、5目或6目。
平筛后3目以上的碎料可以再进行一次粉碎，然后再经过一次平筛，这时平筛后3-6目的碎料再经过一次粉碎，然后收纳到中转仓去，剩余6目以上的碎料去经过20目滚轮筛，20目以下的回收到料仓，然后过筛后20目以上的碎料再经过8目滚轮筛，这时筛后8目以下的碎料回收到料仓，8-20目的碎料回收到半成品仓面料泥料仓，然后对这些8-20的碎料经过水分检测和外观成色判断后经过喂料机，经过16目的滚轮筛，这时8-16目的碎料进面料仓或底料大颗粒仓，16-20目的碎料进面料仓或底料小颗粒仓。
负离子瓷砖的断裂模数应在38mpa以上。
由于在面层里面混合有负离子素，当用户使用本发明的瓷砖贴铺于城市广场、人行道、高档小区、车站、步行街、停车场和机场等等场所进行使用时，负离子粉是人类利用自然界产生负离子的原理，人工合成或者配比的一种复合矿物，负离子在医学界被确认是具有杀灭病菌及净化空气的有效手段，其机理主要在于负离子与细菌结合后，使细菌产生结构的改变或能量的转移，导致细菌死亡，最终降沉于地面。
医学研究表明，空气中带负电的微粒使血中含氧量增加，有利于血氧输送、吸收和利用，具有促进人体新陈代谢，提高人体免疫能力，增强人体肌能，调节肌体功能平衡的作用。据考证，负离子对人体7个***，近30多种疾病具有抑制、缓解和辅助治疗作用，尤其对人体的保健作用更为明显，为此能对对空气中的细菌和异味等进行有效净化，并且能对人体进行保健。
本发明通过选用陶瓷废砖和矿渣边角料为原材料，然后通过两次布料，自动液压机高压成型，全自动辊道窑炉高温烧成，提供了一种能广泛应用在城市广场、人行道、高档小区、车站、步行街、停车场和机场等等场所的具有净化空气和除异味的负离子瓷砖，成为代替水泥和石材对路面硬化的优秀选择。
以上结合附图对本发明的实施方式作了详细说明，但本发明不限于所描述的实施方式。对于本领域的技术人员而言，在不脱离本发明原理和精神的情况下，对这些实施方式进行多种变化、修改、替换和变型，仍落入本发明的保护范围内。
Claims (10)
1.一种具有净化空气和除异味的负离子瓷砖，其特征在于：包括从上到下依次设置的面层、中层和底层；
所述底层包括以重量份计的如下组份：二氧化硅74％-76％、三氧化二铝14％-15％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.1％、氧化钙0.11％-0.2％、氧化镁0.24％-0.37％、氧化钾5％-8％和氧化钠3％-5％；
所述中层包括以重量份计的如下组份：二氧化硅80％-85％、三氧化二铝14％-20％、三氧化二铁0.5％-0.7％、二氧化钛0.05％-0.08％、氧化钙0.11％-0.15％、氧化镁0.24％-0.34％、氧化钾5％-7％和氧化钠3％-3.5％；
所述面层包括以重量份计的如下组份：负离子素1％-2％，其余为表层釉。
2.根据权利要求1所述的一种具有净化空气和除异味的负离子瓷砖，其特征在于：
所述底层包括以重量份计的如下组份：二氧化硅74％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述中层包括以重量份计的如下组份：二氧化硅80％、三氧化二铝14％、三氧化二铁0.5％、二氧化钛0.05％、氧化钙0.11％、氧化镁0.24％、氧化钾5％和氧化钠3％；
所述面层包括以重量份计的如下组份：负离子素1％，其余为表层釉。
3.根据权利要求1所述的一种具有净化空气和除异味的负离子瓷砖，其特征在于：
所述底层包括以重量份计的如下组份：二氧化硅76％、三氧化二铝15％、三氧化二铁0.7％、二氧化钛0.1％、氧化钙0.2％、氧化镁0.37％、氧化钾8％和氧化钠5％；
所述中层包括以重量份计的如下组份：二氧化硅85％、三氧化二铝20％、三氧化二铁0.7％、二氧化钛0.08％、氧化钙0.15％、氧化镁0.34％、氧化钾7％和氧化钠3.5％；
所述面层包括以重量份计的如下组份：负离子素2％，其余为表层釉。
4.根据权利要求1所述的一种具有净化空气和除异味的负离子瓷砖，其特征在于：
所述底层包括以重量份计的如下组份：二氧化硅75％、三氧化二铝14.5％、三氧化二铁0.6％、二氧化钛0.08％、氧化钙0.17％、氧化镁0.3％、氧化钾7％和氧化钠4％；
所述中层包括以重量份计的如下组份：二氧化硅82％、三氧化二铝18％、三氧化二铁0.6％、二氧化钛0.06％、氧化钙0.13％、氧化镁0.32％、氧化钾6％和氧化钠3.2％；
所述面层包括以重量份计的如下组份：负离子素1.2％，其余为表层釉。
5.一种生产权利要求1具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于：包括以下步骤：
原料粉碎：将制成底层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
将制成中层的原料粉碎为两种粒度的粉料，其中，粉料的粒度分别为：8目-16目和16目-20目；
粉料混合：将底层的粉料混合均匀；
将中层的粉料混合均匀；
陈腐：分别将混合后的底层粉料以及中层粉料在存储器内陈腐不少于48小时；
压铸成型：在压铸机的模具里布设两层陈腐后的底层粉料以及布设一层陈腐后的中层粉料，然后采用压铸机成型制得砖坯；
烧成：将砖坯放置于炉中烧成，砖坯的底面温度控制在1179℃-1180℃，砖坯表面温度控制在1191℃-1198℃，保温40分钟-45分钟制成砖体；
淋釉：用清水清洗砖体并晾干后在砖体表面淋釉，其中，砖体表面每平方米淋釉112.8克至113克；
面层制作：将面层淋至淋釉后的砖体上，砖体每平方米淋面层114克至115克。
6.根据权利要求5所述的一种具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于，还包括印花：面层制作完毕后在面层印花。
7.根据权利要求6所述的一种具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于，还包括煅烧：在温度为1100℃的条件下对印花后的砖体煅烧60分钟-70分钟。
8.根据权利要求7所述的一种具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于，还包括抛光：煅烧完毕后采用200-1000目的磨头或磨块对煅烧后的砖体进行抛光。
9.根据权利要求8所述的一种具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于，还包括磨边：对煅烧完毕后的砖体进行磨边处理。
10.根据权利要求5所述的一种具有净化空气和除异味负离子瓷砖的生产工艺，其特征在于，所述压铸成型中的压力为27500N-28500N。