CN1162242C - Technology for machining squeeze screw tap - Google Patents
Technology for machining squeeze screw tap Download PDFInfo
- Publication number
- CN1162242C CN1162242C CNB021141843A CN02114184A CN1162242C CN 1162242 C CN1162242 C CN 1162242C CN B021141843 A CNB021141843 A CN B021141843A CN 02114184 A CN02114184 A CN 02114184A CN 1162242 C CN1162242 C CN 1162242C
- Authority
- CN
- China
- Prior art keywords
- thread forming
- grinding
- processing method
- screw tap
- threaded portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for machining a squeeze screw tap, which comprises the following steps: (1), turn milling is carried out to rough; (2), heat processing is carried out; (3), thread grinding shaping is carried out, and indexing grinding is carried out during the grinding to make the cross section of a thread part form an n-side shape; (4), soft nitriding and transposition crystallization are carried out. The service life of the obtained squeeze screw tap is four to six times of that of the current product, or even more; the cost performance ratio of the squeeze screw tap is excellent. The present invention provides a non-chip manufacturing tool for internal threads of steel material.
Description
Technical field
The present invention relates to a kind of processing method of thread forming tap, belong to the processing method of the ELEMENTARY INTRODUCTION TO NON instrument of machining cutlery class, particularly axle head screw.
Background technology
The common employing of the cutlery removal material on the bottom outlet basis that is used for the processing of steel part screw in the market forms.This processing method disadvantage is a lot, and particularly iron filings are difficult to remove in blind hole, influence in enormous quantities or automated production degree and effect, and it is exactly owing to the cutlery that does not find does not reach optimum state that present heavy industry industry has the lathe of many autocratic screws.In order to change this present situation, have indivedual cutlery manufactory to produce some chipless throwing cutleries, but technology and technological level do not reach a standard yet, be difficult to produce good screw, in use repair rate is higher, causes labor strength to increase, and the cutlery life-span is also shorter.For example: being equivalent on the 50# steel part to make M22-6H is 40 internal thread deeply, the hole count of each screw tap processing between 24-250, average about 180.The crudy instability expends higherly, thereby is difficult to promote.
Technology contents
Main purpose of the present invention provides that a kind of material by high-wearing feature, high red hardness is made and the processing method of economical and practical thread forming tap, the thread forming tap that utilizes this method to process can solve the internal thread chipless manufacturing of present steel material preferably, mainly is a difficult problem that solves in enormous quantities or automated production.The chipless that can be applied to rail vehicles axle shaft end three screws is processed in enormous quantities, and the chipless of vehicle wheel shaft axle head 16 screws is processed in enormous quantities, also can be used for other axle head or position fixedly the screw chipless of steel part process in enormous quantities.
In order to reach above purpose, the processing method of this thread forming tap is as follows:
Step 1: with lathe and milling machine turnning and milling blank;
Step 2: the blank of step 1 gained heated in high temperature furnace heat-treat;
Step 3: will carry out heat treated blank and carry out sharpening thread forming of grinding;
When implementation step 3, allow grinding machine calibration and carry out the calibration grinding, make the cross section of threaded portion become positive n limit shape;
Step 4: the positive n limit shape threaded portion of step 3 gained is heated to 510-580 degree enforcement tufftride Celsius---transposition in ammonia or potassium cyanide liquation or Cymag liquation, penetrant crystalline thickness is greater than 0.05 millimeter, and the penetrant crystalline filler is the N atom.
Because metal belongs to the constraint body-crystal of weak interaction, atom in the crystal can spread with extraneous atom transposition under certain condition, tungsten can have red hardness, chromium has good antirust candle performance, vanadium is the element that forms carbide strongly, and tungsten carbide has very high hardness and red hardness, and nitrogen-atoms is diffused in and can forms in the crystal of body-centered cubic lattic than the strong much bigger binding force of original crystal, tungsten, chromium, vanadium all belong to the crystal of body-centered cubic lattic, existing homemade steel W
18Cr
4V just belongs to the crystal of this body-centered cubic lattic, and idea is diffused into nitrogen-atoms in this body-centered cubic lattic, is easy to reach goal of the invention.
The thread forming tap that utilizes this method to process carries out machine and uses, can produce good screw, the theoretical life-span is cutlery powerful friction in steel material advancing a 1000-1500 rice, only weares and teares 0.01 millimeter, that is to say that the life-span is four times to six times of present product, in addition more.The excellent ratio of performance to price is arranged.
The specific embodiment
Adopt the W of well-known steel mill
18Cr
4The V steel are made, and with reference to standard GB/T967-94, GB/T968-94, GB/T969-94, implement following steps:
Step 1: with lathe and milling machine turnning and milling blank, the screw thread of blank is partly refused car system;
Step 2: the blank of step 1 gained is heat-treated in the high temperature furnace heating, make shank hardness HRC45-52, blade reaches HRC64-66:
Step 3: will carry out heat treated blank and carry out grinding, a sharpening thread forming by single thread mill or accurate omnipotent mill; , stop ring logical in this step employing special use advised strict controlling dimension.
When carrying out step 3, allow grinding machine carry out the calibration grinding, make the cross section of threaded portion become regular hexagon;
Step 4: become orthohexagonal threaded portion in ammonia (or in potassium cyanide or Cymag liquation) gas, to be heated to 560 degree enforcement tufftrides Celsius more than 5 hours the cross section of step 3 gained, penetrant crystalline thickness is greater than 0.05 millimeter, and the penetrant crystalline filler is the N atom.
By implementing tufftride after the sharpening moulding, the penetrant crystalline filler is the N atom, and NH3 or NaCN (KCN) are heated to about 560 degree Celsius and decomposite N, and its case hardness reaches HV900-950 after the crystallization, and filling the crystallization diffusion thickness must be greater than 0.05 millimeter.
Threaded portion cross section of the present invention can be processed into positive n (n=3,4,5,6,7 ...) and limit shape, as regular hexagon, octagon.
Claims (4)
1, a kind of processing method of thread forming tap is characterized in that: step 1: with lathe and milling machine turnning and milling blank;
Step 2: the blank of step 1 gained heated in high temperature furnace heat-treat;
Step 3: will carry out heat treated blank and carry out grinding, a sharpening thread forming;
Cross section with threaded portion when grinding becomes the shape calibration grinding of positive n limit;
Step 4: the positive n limit shape threaded portion of step 3 gained is heated to 510-580 degree enforcement tufftride Celsius in ammonia or potassium cyanide liquation or Cymag liquation, makes penetrant crystalline thickness greater than 0.05 millimeter, the penetrant crystalline filler is the N atom.
2, the processing method of a kind of thread forming tap as claimed in claim 1 is characterized in that the threaded portion cross section of described step 3 is processed into regular hexagon.
3, the processing method of a kind of thread forming tap as claimed in claim 1 is characterized in that threaded portion tufftride in the described step 4 more than 5 hours.
4, the processing method of a kind of thread forming tap as claimed in claim 1 is characterized in that after the heat treatment of having carried out described step 2 hardness that makes the screw tap shank is HRC45-52, and the hardness of screw tap blade is HRC64-66.