CN1161946A - Coating resisting molten-metal aluminium liquid corrosion and coating method thereof - Google Patents
Coating resisting molten-metal aluminium liquid corrosion and coating method thereof Download PDFInfo
- Publication number
- CN1161946A CN1161946A CN 97100841 CN97100841A CN1161946A CN 1161946 A CN1161946 A CN 1161946A CN 97100841 CN97100841 CN 97100841 CN 97100841 A CN97100841 A CN 97100841A CN 1161946 A CN1161946 A CN 1161946A
- Authority
- CN
- China
- Prior art keywords
- coating
- material surface
- aluminium liquid
- metal material
- coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invented paint is mainly used for resisting corrosion of molten metallic aluminium and its chemical composition (by wt.%) is corundum fines 40-60%, fire clay 15-30%, bentonite 9-10%, flux 8-12%, HB-type infiltration retardant 2-3%, binder 5-10% and liquid assistant 1-2%. The method for coating this paint on the metallic material surface includes the surface clearing, the paint coating and the drying treatment. The coat formed by using this invented paint to coat on th metal matrix is high in bond strength and compact so that the molten aluminium is not liable to intrude into the coat and no corrosion occurs. The coat has long service life.
Description
The invention belongs to paint field.Mainly be applicable to the metal material surface that needs resisting molten-metal aluminium liquid corrosion.
Resemble in the production unit of hot-dip aluminizing and so on, placing the metal of hot dip aluminum pot (or groove) to sink to part is one of key equipment, as the roller that sinks, support arm, stove nose etc. all are the vitals that sinks in the hot dip aluminum pot (or groove), no matter this base part is to adopt 05F, 08F, A3, No. 20 steel, soft steel, still adopt cast iron, all be subjected to high temperature aluminum liquid (680～720 ℃) etch, wash away, seriously corroded seriously influences the work-ing life of sinking to part in these hot dip aluminum pots (or groove).In the prior art; in order to prevent that molten metal aluminium liquid is to sinking to the corrosion of part; usually adopt heat resisting coating that metal is sunk to part and apply and protect that for example Japanese kokai publication sho 52-58736, spy open clear 46-37273 and Chinese patent application 96109105.3 all provides a kind of resistant to elevated temperatures coated coating, immerse but these coating are difficult to form the competent aluminium liquid that prevents in molten metal aluminium liquid.Molten metal aluminium liquid erosive ability is promptly resisted on the blocking layer of etch, and work-ing life is very short
The object of the present invention is to provide a kind of coating and coating method of resisting molten-metal aluminium liquid corrosion.This coating can have clinging power preferably with the matrix of the hardware that places high-temperature fusion aluminium liquid, formed the competent blocking layer that prevents the intrusion of aluminium liquid, etch, prevent the corrosion that aluminium liquid sinks to part to metal effectively, solve the returning of hardware seriously corroded that places the hot-dip aluminizing pot in the hot-dip aluminizing production line and inscribe
At above-mentioned purpose, the designing chemical composition of resisting molten-metal aluminium liquid coating of the present invention (weight %) is:
Lapis amiridis 40～60%, fireclay 15～30%, wilkinite 9～10%, fusing assistant 8～12%, HB type resistance penetration enhancer 2～3%, binding agent 5～10%, liquid flux 1～2%
Wherein, the chemical constitution of fusing assistant (weight %) is: sliding native powder 20～40%, mica 60～80%;
Liquid flux be in propyl carbinol, Pentyl alcohol or the tbp any
Binding agent is the liquid composite inorganic of TC type-organic adhesive profit
In the coating, the effect of lapis amiridis, fireclay, fusing assistant and binding agent is when coating is used under high temperature (600～800 ℃), these combination raw materials can at high temperature form fine and close enamel body barrier, stop of invasion or the etch of aluminium liquid to matrix, simultaneously, the existence of fusing assistant makes coating can expand and do not crack and peel off with matrix under 600～800 ℃ of high temperature.Resistance penetration enhancer in the coating can increase the surface tension of aluminium liquid and coating, makes aluminium liquid not soak into, not invade corrosion to coating, guarantees to sink to metalwork in the molten metal aluminium liquid not by the aluminium corrosion, makes metal sink to part and keeps the favorable mechanical performance; Liquid adjuvants is to prevent that coating from producing bubble owing to stirring, and influences coating quality.
The compound method of coating of the present invention is as follows: according to chemical composition proportioning is got the raw materials ready earlier, afterwards, powder raw material fitted over together mix, to be mixed evenly after, add liquid composite inorganic-organic binder bond of TC type and liquid flux, stir once more, carry out ball milling after evenly, and to control its density be 3.2～3.6g/cm
3, can apply subsequently.
The applying coating of resisting molten-metal aluminium liquid corrosion of the present invention comprises metal material surface cleaning, applying coating and 3 operations of drying treatment at the coating method of metal material surface, and existing division is as follows:
(1), needs the cleaning of metallizing material surface
With the surface that needs sink to metallic substance in the molten metal aluminium liquid or metallic element deoil, rust cleaning and shot peening, make its no greasy dirt in surface and rusty scale, the matrix of cleaning is exposed on the surface, and has certain roughness.
(2), applying coating
Can adopt craft or mechanical means, paint brush is coated in through clearing up the clean metallic substance or the surface of metallic element.Coat-thickness is 0.3～0.8mm.
(3), drying treatment
The metallic substance or the metallic element that are coated with application layer are put into heat treatment furnace, coating is carried out drying treatment, treatment temp is 100～200 ℃, in 0.2～2.5 hour treatment time, requires heat-up rate＜100 ℃/hour simultaneously.
Metallic substance after drying is handled and metallic element can sink in the molten metal aluminium liquid and use.
Compared with prior art, the present invention has following advantage:
(1) because coating forms fine and close enamel body blocking layer at matrix surface, so aluminium liquid is difficult for invading or the etch matrix, it is strong to make it solidity to corrosion, the component long service life sank in the aluminium liquid after 60 days, and coating is still intact, prior art immerses two days later, then begins corrosion.
(2) because coating and basal body binding force are strong, do not peel off, strengthened the work-ing life of coating yet.
(3) compound method is simple.
(4) starting material of coating source is sufficient, and price is low, and promptly cost is low.
When (5) metalwork of applying coatings used the back to take out from aluminium liquid, coating was peeled off automatically, can apply once more, continued to use.
Embodiment
According to coatings chemistry composition of the present invention, prepared 5 batches of coating, the concrete chemical ingredients of 5 batches of coating is shown in table 1, table 2.Then 5 batches of coating are coated in five kinds of metal material surfaces respectively, the material and the size of five kinds of metallic substance are as shown in table 3, and the processing parameter of coating method is as shown in table 4.With 5 kinds the metalwork of applying coatings to put into temperature be 710 ℃ molten metal aluminium liquid, and immerse different time (fate) back respectively and take out, the check metalwork situation that is corroded, assay is as shown in table 5.
In order to contrast, adopted in the prior art commercially available TP type heat resisting coating on the metal base surface of four kinds of materials, also to carry out the coating test.Basic material and specification, coating method and corrosion test result also list in the corresponding table.
Table 1 embodiment chemical ingredients (weight %)
Annotate: binding agent is the liquid composite inorganic-organic binder bond of TC type
The chemical constitution (weight %) of fusing assistant in the table 2 embodiment coatings chemistry composition
Appended body material material of table 3 embodiment coating and dimensions
Table 4 embodiment applying coating processing parameter
Table 5 embodiment and the anti-aluminium corrosion of Comparative Examples coating assay
Claims (3)
1, a kind of coating of refractory erosion metal aluminium liquid corrosion is characterized in that the chemical ingredients (weight %) of coating is:
Lapis amiridis 40～60%, fireclay 15～30%, wilkinite 9～10%, fusing assistant 8～12%, HB type resistance penetration enhancer 2～3%, the liquid composite inorganic-organic binder bond 5～10% of TC type, liquid flux 1～2%;
Wherein, the chemical constitution of fusing assistant (weight %) is: sliding scholar's powder 20～40%, mica 60～80%;
Liquid flux is a propyl carbinol, in Pentyl alcohol or the tbp any.
2, a kind of with the coating method of the described applying coating of claim 1 at metal material surface, comprise that at first employing is deoiled, processing of rust removing is cleared up metal material surface, adopt craft or mechanical means afterwards, paint brush is coated in through clearing up clean metal material surface, carry out drying treatment at last, it is characterized in that:
(1), metal material surface deoil the rust cleaning after, also must carry out shot peening;
(2), coat-thickness is 0.3～0.8mm;
(3), the drying treatment parameter is: treatment temp is 100～200 ℃, and the treatment time is 0.2～2.5 hour, heat-up rate≤100 ℃/hour.
3, coating according to claim 1, the density that it is characterized in that coating is 3.2～3.6g/cm
3