CN116162855A - 一种600MPa级厚规格含磷热轧耐候钢板及其制造方法 - Google Patents
一种600MPa级厚规格含磷热轧耐候钢板及其制造方法 Download PDFInfo
- Publication number
- CN116162855A CN116162855A CN202310177330.7A CN202310177330A CN116162855A CN 116162855 A CN116162855 A CN 116162855A CN 202310177330 A CN202310177330 A CN 202310177330A CN 116162855 A CN116162855 A CN 116162855A
- Authority
- CN
- China
- Prior art keywords
- phosphorus
- mpa
- steel plate
- containing hot
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种600MPa级厚规格含磷热轧耐候钢板及其制造方法,成分:C:0.06%‑0.08%、Si:0.30%‑0.40%、Mn:0.56%‑0.70%、P:0.06%‑0.10%、S:≤0.002%、Cr:0.30%‑0.60%、Ni:0.10%‑0.20%、Cu:0.20%‑0.40%、Alt:0.020%‑0.040%、Nb:0.020%‑0.040%、V:0.030%‑0.060%、Ca:0.0010%‑0.0030%,其余为Fe及不可避免的杂质元素;与现有技术相比,本发明设计匹配的轧制、冷却工艺,实现优异的强韧性匹配,解决高强度厚规格含磷‑40℃低温韧性控制难题。
Description
技术领域
本发明属于钢铁材料领域,具体涉及一种基于传统热连轧板带流程生产的600MPa级厚规格含磷热轧耐候钢板及其制造方法。
背景技术
耐候钢广泛应用于集装箱、铁路车辆等行业,目前耐候钢高强度系列屈服强度最高已达800MPa以上,但大多集中在薄规格,厚度为6mm以下。且多为低P设计,这是因为P在晶界偏聚引起“冷脆”现象,直接影响低温韧性。但是P相对Cr/Ni/Cu等贵重耐蚀金属具有良好的经济性,可在Cu的配合下获得极其优良的耐蚀性,所以含P耐候钢在“双碳”的大环境和企业“降本增效”的大背景下,具有良好的应用前景。
如何实现厚规格含P耐候钢的高强化,其技术难度远大于薄规格低P钢。一方面是因为厚规格意味着较小的压缩比,无法通过大压下实现大量再结晶达到细晶强化的效果,另一方面耐候钢在塑韧性尤其是低温韧性要求远高于其他低合金钢,所以以相变强化为主的马氏体型耐候钢目前应用仍较少,主要是通过添加Nb、Ti等微合金,以析出强化和细晶强化方式为主。但是细晶强化的同时,伴随着P在晶界偏聚的加剧,限制了塑韧性的进一步提高。
目前国内外发明专利关于高强度、厚规格、含P耐候钢板的制造技术较少。2017年3月22日公开的公开号为CN106521352A的专利公开了一种含铌厚规格耐候钢及其轧制方法,采用低P单Nb设计,强度仅为450MPa级。
2022年6月24日公开的公开号为CN114657347A的专利公开了一种含铌高磷耐候钢及其制造方法,采用宽厚板轧机轧制,适用厚度规格8-130mm,进行20℃常温冲击,屈服强度仅为Q295级别。
2017年3月1日公开的公开号为CN104593695A的专利公开了热轧高强低镍铜比厚规格耐候钢及其生产方法,强度级别虽达700MPa,但是采用Nb、Ti微合金化低P设计,且厚度也仅限10-14mm。
发明内容
本发明的目的在于提供一种600MPa级厚规格含磷热轧耐候钢板及其制造方法,在传统热连轧流程生产600MPa级厚规格含P耐候钢板,屈服强度≥600MPa,抗拉强度≥700MPa,-40℃冲击吸收功大于100J,延伸率≥22%,具有优异的低温韧性、强塑性和良好的耐大气腐蚀性能,本发明能解决高P钢-40℃低温韧性控制难题,大大提高厚规格高强度含P热轧耐候钢板的生产效率。
本发明具体技术方案如下:
本发明提供的一种600MPa级厚规格含磷热轧耐候钢板,包括以下质量百分比成分:
C:0.06%-0.08%、Si:0.30%-0.40%、Mn:0.56%-0.70%、P:0.06%-0.10%、S:≤0.002%、Cr:0.30%-0.60%、Ni:0.10%-0.20%、Cu:0.20%-0.40%、Alt:0.020%-0.040%、Nb:0.020%-0.040%、V:0.030%-0.060%、Ca:0.0010%-0.0030%,其余为Fe及不可避免的杂质元素。
所述600MPa级厚规格含磷热轧耐候钢板的成分满足:V/Nb=1-1.5。
所述600MPa级厚规格含磷热轧耐候钢板的耐大气腐蚀指数I≥7.0;耐大气腐蚀指数I根据ASTM G101-01中修正的Legault-Leckie公式计算,I=26.01(%Cu)+3.88(%Ni)+1.20(%Cr)+1.49(%Si)+17.28(%P)-7.29(%Cu)×(%Ni)-9.10(%Ni)×(%P)-33.39(%Cu)2。
所述600MPa级厚规格含磷热轧耐候钢板的厚度为12-25mm;
所述600MPa级厚规格含磷热轧耐候钢板的组织为铁素体+贝氏体组织,铁素体体积分数80-85%,铁素体平均晶粒尺寸11-12μm;心部无磷偏析带;贝氏体颗粒呈球状或者椭圆状,弥散分布在晶内或者晶界上,无块状珠光体组织和带状组织。
所述600MPa级厚规格含磷热轧耐候钢板的力学性能:ReL≥600MPa,Rm≥700MPa,A≥22%,-40℃夏比V型缺口冲击功>100J,具有高强度和优良的塑韧性;具有良好的耐大气腐蚀性能,相对于Q345B腐蚀率<50%。
所述600MPa级厚规格含磷热轧耐候钢板具有优良的冷弯成形性能:经180°冷弯(d=a)后,弯曲试样没有裂纹出现。
本发明提供的厚规格含P热轧耐候钢板合金元素及其质量百分比设计原理如下:
C(碳):经济性良好且强化效果显著的元素,通过间隙固溶强化提高强度,但是C含量过高会增加珠光体/贝氏体含量,降低钢材的低温韧性,本发明组织为铁素体+少量细贝氏体,所以碳含量不宜过高。本发明为提高耐候钢板的低温韧性,将C含量设计为0.06-0.08%。
Si(硅):Si有利于细化腐蚀产物,促进钢材表面形成致密的保护性锈层从而提高耐大气腐蚀性能,但是Si含量过高会降低钢材的焊接性能,同时也会在钢板表面形成条带,因此本发明将Si含量设计为0.30-0.40%。
Mn(锰):Mn是钢中重要的固溶强化元素之一,在高强钢中强度贡献效果显著。但是Mn含量过高会形成带状组织,非均匀分布的带状组织是引起低温韧性较差的原因之一;另一方面,较高的Mn含量会与S结合形成MnS夹杂,通常在铸态下呈骨架状或链状,对冲击韧性不利。因此,本发明采用中Mn设计,既保证了强度,又不出现带状组织,将其含量设计为0.56-0.70%。
P(磷):P是提高钢材耐大气腐蚀性能最经济的元素,配合Cu在添加少量Cr、Ni的基础上即可获得优良的耐腐蚀性能。另外P还具有较强的固溶强化作用。但是P含量较高,易在晶界偏聚急剧降低钢的韧性尤其是低温韧性,引起“冷脆”现象,且增加焊接裂纹敏感性。本发明添加P提高耐大气腐蚀性能,因此将P含量设计为0.06-0.10%;
S(硫):S是钢中的有害残余元素,易在钢中形成硫化物夹杂,恶化钢材的低温韧性和耐大气腐蚀性能。因此本发明采用超低S设计,S含量为≤0.002%。
Alt(铝):Al是钢中加入的主要脱氧元素。但过高的Al会导致钢中Al的氧化物夹杂增加,降低钢材的低温韧性和耐大气腐蚀性能。因此,将其含量设计为0.020-0.040%。
Cr(铬):Cr在锈层富集促进与基体结合致密的保护性锈层生成,促进阳极钝化,提高钢材耐大气腐蚀性能。Cr含量过高会恶化钢材的焊接性能,因此将Cr含量设计为0.30-0.60%。
Cu(铜):Cu能显著提高钢材耐大气腐蚀性能,与P复合添加时效果更佳;Cu还能在冷却过程中析出细小的第二相粒子提高钢材强度。但是Cu的熔点只有1083℃,含量过高容易导致钢坯在热轧过程中产生裂纹,因此将Cu含量设计为0.20-0.40%。
Ni(镍):Ni能提高材料的自腐蚀电位,降低腐蚀倾向,提高耐大气腐蚀性能;还能与Cu反应生成高熔点的Cu-Ni二元合金相,有效阻止Cu引起的铜脆;还能提高材料低温韧性。但是Ni是贵重金属元素,含量过高显著提高制造成本,因此将Ni含量设计为0.10-0.20%。
Nb(铌):Nb是强碳氮化物形成元素,抑制形变奥氏体再结晶,扩大未再结晶区,提高未再结晶区控制轧制细化晶粒作用;在冷却过程中析出纳米级第二相粒子,具有显著的细晶强化和析出强化作用,提高材料的强韧性。但是Nb含量过高会显著提高钢材制造成本,因此将其含量控制在0.020%-0.040%。
V(钒):V亦是强碳氮化物形成元素,V促进奥氏体再结晶细化和通过V(C,N)的析出促进相变铁素体晶粒细化,具有显著的细晶强化和析出强化效果,是实现高强高韧性匹配的关键合金元素,同时V能提高钢的腐蚀电位,对耐腐蚀性能有积极作用。但较高的V含量制造成本较高,且并不能充分发挥与C、N等元素的最佳匹配和有效结合,所以将V含量设计为0.030%-0.060%。
Ca(钙):Ca能促进非金属夹杂物球化,避免在非金属夹杂物的尖角处产生应力集中,导致裂纹萌生,成为裂纹扩展的快速通道,提高低温韧性。将其含量控制在0.0010%-0.0030%。
本发明提供的一种600MPa级厚规格含磷热轧耐候钢板的制造方法,包括以下工艺流程:
铁水预处理→转炉冶炼→精炼→连铸→板坯加热→控制轧制→控制冷却→卷取。
所述转炉冶炼,按照上述化学成分进行钢水冶炼;
所述精炼:LF终点加入钙线促进非金属夹杂物球化;将S含量控制在0.002%以下;
所述连铸:中包温度采用低过热度控制:液相线以上10-25℃,连铸采用动态轻压下和电磁搅拌,动态轻压下压下量范围为3.0-5.0mm。控制铸坯中心偏析为C类≤1.0级,提高铸坯内部质量。
连铸后板坯优先采用热装轧制,且铸坯入炉温度≥550℃。未能及时热装的铸坯,应及时入保温坑缓冷,待检查清理确认无裂纹后方可投轧。
所述板坯加热,为防止铸坯奥氏体晶粒粗化,严格控制一加热段末温度≤1050℃,铸坯出炉温度为1180℃-1220℃,保温时间120-180min,促进合金元素充分固溶和奥氏体均匀化。板坯出炉后采用高压水除鳞,去除加热过程中产生的一次氧化铁皮。
所述控制轧制:热连轧分为粗轧和精轧两个阶段进行;粗轧阶段采用两架四辊可逆式粗轧机各轧制3个道次,轧制温度≥1050℃,总变形量≥70%。在奥氏体再结晶区进行往返轧制,采用道次大变形,促进奥氏体晶粒回复再结晶从而细化奥氏体晶粒尺寸。精轧阶段采用7架四辊轧机进行连轧,该阶段在奥氏体未再结晶区轧制,开轧温度≤1030℃,中间坯厚度55-60mm,轧制16mm以上厚度时,中间坯厚度60mm。通过累计大变形,增加奥氏体晶粒内形变带和位错密度,从而增加相变形核点细化铁素体晶粒。另外,如果温度较低,钒析出不彻底,析出强化效果会大幅降低,直接影响高强度的实现。所述精轧终轧温度为860-910℃。
所述控制冷却,具体为:轧制结束后对钢板进行双段冷却,前一段冷却速率为30-50℃/s,快速冷却至700-750℃,间隔时间5-8s后进行后一段冷却,冷却速率10-30℃/s,冷却至460-520后进行卷取;卷取温度高于520℃使得铁素体晶粒尺寸粗化,材料强度不足;卷取温度低于460℃,生成马氏体或者板条状贝氏体组织,降低钢材塑韧性。
本发明为提高600MPa级厚规格含磷热轧耐候钢板的低温韧性,获得高强度、优异的塑韧性匹配和良好的耐大气腐蚀性能,采取了以下方法:
1)采用低C-中Mn-Nb-V复合微合金化成分和两段冷却工艺匹配设计:①低C-中Mn配合两段冷却可得到铁素体+贝氏体组织,其中塑性更好的铁素体占比约80-85%,铁素体平均晶粒尺寸11-12μm,细贝氏体颗粒呈球状或者椭圆状,弥散且均匀的分布在晶内或者晶界上,无块状珠光体组织和带状组织出现,相对于低强度级别的铁素体+珠光体型耐候钢,通过相变强化显著提高了强度和韧性。②Nb-V复合微合金化成分既发挥Nb在未再结晶区良好的细晶强化效果,又发挥V在奥氏体区析出V(C,N)促进晶内铁素体形核进一步细化铁素体晶粒,同时严格控制V/Nb=1~1.5,可有效减少厚规格Nb钢混晶缺陷的发生。以上成分设计及控制控冷工艺,在多种强化方式的协同作用下,即使针对厚规格,也可实现600MPa高强度和高韧性的良好匹配。
2)采用P-Si-Cr-Cu-Ni协同设计,在提高Si、P含量的基础上,适当减少Cu、Cr、Ni含量,降低合金成本,且保证耐候指数I值≥7.0;
3)高洁净度钢水冶炼及铸坯内部质量控制:非金属夹杂物是点蚀诱发源和裂纹萌生源,本发明采用LF精炼提高钢水结净度,将S含量控制在0.002%以下。喂钙线促进非金属夹杂物球化,降低非金属夹杂对耐蚀性能和低温韧性的不利影响。连铸工艺过程中中包实行低过热度(液相线以上10-25℃)、采用动态轻压下(压下量范围为3.0-5.0mm)和电磁搅拌,通过在凝固末端糊状区给予额外压力,打碎晶界搭桥,使富含P的液相回流、补缩。以上冶炼和连铸工艺,控制铸坯中心偏析为C类≤1.0级,抑制了心部磷偏析带的形成,提高低温韧性。
与现有技术相比,本发明采用热连轧板带流程制造,通过P-Si-Cr-Cu-Ni协同设计,耐候指数I值≥7.0,提高Si、P含量,减少Cu、Cr、Ni含量,具有良好的耐大气腐蚀性能,相对于Q345B腐蚀率<50%。本发明采用Nb-V复合微合金化设计,在小压缩比条件限制下仍能充分实现厚规格含P钢的析出强化和细晶强化作用,同时在双段冷却工艺下以铁素体+贝氏体组织通过相变强化作用进一步实现高强化。本发明钢板适用厚度12-25mm,力学性能:Rel≥600MPa,抗拉强度≥700MPa,A≥22%,-40℃夏比V型缺口冲击功>100J,具有高强度和优良的塑韧性。且钢板还具有优良的冷弯成形性能:经180°冷弯(d=a)后,弯曲试样没有裂纹出现。本发明钢板生产可热装轧制,节约加热炉能耗,免除铸坯角部清理,进一步降低制造成本。
附图说明
图1为本发明钢板不同厚度处的金相组织,图中可见通过化学成分和轧制、冷却工艺控制,使得钢板显微组织为铁素体+贝氏体组织,铁素体体积分数约82%,铁素体平均晶粒尺寸约12μm;心部未见磷偏析带;
图2为实施例1的铸坯低倍宏观形貌;
图3为对比例1的铸坯低倍宏观形貌;
图4为对比例3的显微组织;
图5为对比例4的显微组织。
具体实施方式
实施例1-实施例4
一种600MPa级厚规格含磷热轧耐候钢板,包括以下质量百分比成分:如表1所示,表1没有显示的余量为Fe和不可避免的杂质。
对比例1-对比例4
一种600MPa级厚规格含磷热轧耐候钢板,包括以下质量百分比成分:如表1所示,表1没有显示的余量为Fe和不可避免的杂质。
表1本发明各实施例和对比例化学成分
以上各实施例和对比例600MPa级厚规格含磷热轧耐候钢板的制造方法,包括以下工艺流程:
铁水预处理→转炉冶炼→精炼→连铸→板坯加热→控制轧制→控制冷却→卷取。
具体如下:
按照上述化学成分进行钢水冶炼,LF终点加入钙线促进非金属夹杂物球化,将S含量控制在0.002%以下;中包温度控制在液相线以上10-25℃,连铸采用动态轻压下和电磁搅拌,动态轻压下压下量范围为3.0~5.0mm,控制铸坯中心偏析为C类≤1.0级。连铸后板坯优先热装轧制,铸坯入炉温度≥550℃。未能及时热装的铸坯,应及时入保温坑缓冷,待检查清理确认无裂纹后方可投轧。
采用步进式加热炉对板坯进行加热,严格控制一加热段末温度≤1050℃,出炉温度为1180℃-1220℃,保温时间120-180min,板坯出炉后采用高压水除鳞,去除加热过程中产生的一次氧化铁皮。热连轧分为粗轧和精轧两个阶段进行。粗轧阶段采用两架四辊可逆式粗轧机各轧制3个道次,轧制温度≥1050℃,总变形量≥70%。精轧阶段采用7架四辊轧机进行连轧,开轧温度≤1030℃。中间坯厚度55-60mm,轧制16mm以上厚度时,中间坯厚度60mm。精轧终轧温度为860-910℃。轧制结束后采用两段冷却对钢板进行快速冷却,前一段冷却速率为30-50℃/s,快速冷却至700-750℃,间隔时间5-8s后进行后一段冷却,冷却速率10-30℃/s,冷却至460-520℃后进行卷取。各实施例和对比例的主要生产工艺参数如表2所示。
表2各实施例和对比例主要工艺参数及性能
以上各实施例和对比例生产的600MPa级厚规格含磷热轧耐候钢板进行性能测试,拉伸性能测试根据GB/T 228.1《金属材料拉伸试验第1部分:室温试验方法》进行,冷弯性能测试根据GB/T 232《金属材料弯曲试验方法》进行。冲击性能测试根据GB-T 229《金属材料夏比摆锤冲击试验方法》。本发明各实施例及对比例的主要生产工艺参数。本发明各实施例及对比例的性能如表3所示。
表3各实施例和对比例主要工艺参数及组织、性能
按照TB/T 2375《铁路用耐候钢周期浸润腐蚀试验方法》进行72h周期浸润腐蚀试验评价各实施例的耐大气腐蚀性能,腐蚀式样尺寸40mm×60mm×4mm,以Q345B低合金钢作为对比腐蚀试样,试验结果如表4所示。各实施例相对于Q345B低合金钢耐大气腐蚀性能提高了1倍以上,具有优良的耐大气腐蚀性能。
表4各实施例及对比例的耐大气腐蚀性能
综上所述,对比例1的C、Mn、P和S含量偏高,铸坯中心偏析B1.0(见图3),显微组织中出现了6%珠光体,产品延伸率和低温韧性较低;对比例2中C、Mn、Ni、V含量较低,即使按照本发明工艺生产,强度亦未能达到600MPa级;对比例3中的Nb、V含量较低,且未按V/Nb=1~1.5分配,即使按照本发明工艺生产,也难以发挥细晶强化和析出强化的作用,显微组织粗大,平均晶粒尺寸达13.6μm,并出现混晶现象(图4所示),导致产品的强度和韧性显著降低;对比例4中各成分皆在合适范围内,但终轧和卷取温度较低,显微组织为F+B+M,出现了马氏体条带(图5所示),产品的强度较高,但延伸率和低温韧性都较低。实施例均按本发明钢种化学成分、冶炼、连铸和控轧控冷工艺控制技术所得耐候钢板屈服强度≥600MP,抗拉强度≥700MPa,延伸率≥22%,-40℃KV2≥100J,具有高强度和优异的塑韧性匹配,相对于Q345B腐蚀率<50%,可应用于铁道车辆、桥梁等长期在严寒环境中服役的承重结构件。
Claims (10)
1.一种600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板包括以下质量百分比成分:
C:0.06%-0.08%、Si:0.30%-0.40%、Mn:0.56%-0.70%、P:0.06%-0.10%、S:≤0.002%、Cr:0.30%-0.60%、Ni:0.10%-0.20%、Cu:0.20%-0.40%、Alt:0.020%-0.040%、Nb:0.020%-0.040%、V:0.030%-0.060%、Ca:0.0010%-0.0030%,其余为Fe及不可避免的杂质元素。
2.根据权利要求1或2所述的600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板的耐大气腐蚀指数I≥7.0。
3.根据权利要求1或2所述的600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板的成分满足:V/Nb=1-1.5。
4.根据权利要求1或2所述的600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板的厚度为12-25mm。
5.根据权利要求1或2所述的600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板的组织为铁素体+贝氏体组织,铁素体体积分数80-85%,铁素体平均晶粒尺寸11-12μm;心部无磷偏析带;贝氏体颗粒呈球状或者椭圆状,弥散分布在晶内或者晶界上,无块状珠光体组织和带状组织。
6.根据权利要求1或2所述的600MPa级厚规格含磷热轧耐候钢板,其特征在于,所述600MPa级厚规格含磷热轧耐候钢板的力学性能:ReL≥600MPa,Rm≥700MPa,A≥22%,-40℃夏比V型缺口冲击功>100J,相对于Q345B腐蚀率<50%。
7.一种权利要求1-6任一项所述600MPa级厚规格含磷热轧耐候钢板的制造方法,其特征在于,所述制造方法包括连铸:中包温度控制在液相线以上10-25℃,连铸采用动态轻压下和电磁搅拌,动态轻压下压下量范围为3.0-5.0mm,控制铸坯中心偏析为C类≤1.0级。
8.根据权利要求7所述的制造方法,其特征在于,所述板坯加热:用步进式加热炉对板坯进行加热,控制一加热段末温度≤1050℃,铸坯出炉温度为1180℃-1220℃,保温时间120-180min。
9.根据权利要求7所述的制造方法,其特征在于,所述控制轧制:热连轧分为粗轧和精轧两个阶段进行;粗轧阶段轧制温度≥1050℃,总变形量≥70%;精轧阶段开轧温度≤1030℃,中间坯厚度55-60mm,精轧终轧温度为860-910℃。
10.根据权利要求7所述的制造方法,其特征在于,所述控制冷却,具体为:轧制结束后采用双段冷却,前一段冷却速率为30-50℃/s,快速冷却至700-750℃,间隔时间5-8s后进行后一段冷却,冷却速率10-30℃/s,冷却至460-520进行卷取。