CN115869216A - 一种耐汗粉底液及其制备方法 - Google Patents
一种耐汗粉底液及其制备方法 Download PDFInfo
- Publication number
- CN115869216A CN115869216A CN202211649203.4A CN202211649203A CN115869216A CN 115869216 A CN115869216 A CN 115869216A CN 202211649203 A CN202211649203 A CN 202211649203A CN 115869216 A CN115869216 A CN 115869216A
- Authority
- CN
- China
- Prior art keywords
- percent
- sweat
- stabilizer
- extract
- polydimethylsiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种耐汗粉底液及其制备方法,该粉底液包含如下重量百分比的原料:成膜剂:3~10%;润肤剂:8.5~42%;保湿剂:3.5~15%;填充剂:0.5~5%;乳化剂:1~10%;皮肤调理剂:0.7~21%;粘度调节剂:0.1~2%;稳定剂:0.2~6%;螯合剂:0.001~0.5%;着色剂:0~40%;防腐剂:0~1%;所述成膜剂采用质量比为1~3:2~5的丙烯酸酯类/聚二甲基硅氧烷共聚物和环五聚二甲基硅氧烷。本申请的粉底液具有优异的防水耐汗性能,且具有良好的美容护肤效果。
Description
技术领域
本申请涉及化妆品领域,尤其是涉及一种耐汗粉底液及其制备方法。
背景技术
粉底液是一种添加有粉料的乳液型化妆品,一方面可用于面部美容修饰,能够在皮肤表面形成平滑的覆盖层,有效遮盖面部的瑕疵;另一方面可结合皮肤护理成分,起到美容护肤的效果。
市面上的粉底液大多采用亲水性的原料,尤其是亲水性的成膜材料,使粉液质地轻薄不油腻,易于在皮肤表面铺展。但粉底液的亲水性导致其防水耐汗性能较差,遇水容易脱妆。
发明内容
为提高粉底液的防水耐汗性能,减少脱妆现象,本申请提供了一种耐汗粉底液及其制备方法。
第一方面,本申请提供一种耐汗粉底液,其包含如下重量百分比的原料:
成膜剂:3~10%;
润肤剂:8.5~42%;
保湿剂:3.5~15%;
填充剂:0.5~5%;
乳化剂:1~10%;
皮肤调理剂:0.7~21%;
粘度调节剂:0.1~2%;
稳定剂:0.2~6%;
螯合剂:0.001~0.5%;
着色剂:0~40%;
防腐剂:0~1%;
所述成膜剂采用质量比为1~3:2~5的丙烯酸酯类/聚二甲基硅氧烷共聚物和环五聚二甲基硅氧烷。
常规粉底液通常以黄原胶、卡波姆、纤维素等亲水性物质为成膜剂,致使粉底液成膜后的性能较差。为此,本申请的粉底液采用了丙烯酸酯类/聚二甲基硅氧烷共聚物为基础的成膜剂,该共聚物中既含有亲水性的丙烯酸酯类链段,又含有疏水性的有机硅链段,能够有效改善粉底液的性,在皮肤表面成膜后不易因汗液出现脱妆现象。
上述丙烯酸酯类/聚二甲基硅氧烷共聚物粘度较大,极大的降低了粉底液的流动性,不利于分散涂膜。为此,本申请采用了环五聚二甲基硅氧烷进行复配,有效补偿了其流动性,提高了粉底液成膜的均匀性。
本申请对着色剂无特殊要求,根据需要选用适宜颜料或颜料溶液即可。
优选的,所述乳化剂采用质量比为0.5~5:0.5~5的鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷和PEG-10聚二甲基硅氧烷。
成膜剂中疏水链段的引入在改善性能的同时,也一定程度上阻隔了亲水性的皮肤调理剂、润肤剂渗透并作用至肌肤,影响粉底液的护肤效果。本申请采用的乳化剂,其含有疏水性聚硅氧烷链段和亲水性聚醚链段的乳化剂,可促进皮肤调理剂、润肤剂和水从疏水性膜层中释放、渗透至肌肤表面,且随着亲水性物质的释放,能够在膜层上形成通道,进一步促进皮肤调理剂、水分的释放,保障良好的护肤作用。
另外,上述鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷和PEG-10聚二甲基硅氧烷具有协同配合作用,PEG-10聚二甲基硅氧烷怼膜层的渗透性较好,有利于通道的形成,而鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷空间位阻作用较强,有利于通常的扩展,促进皮肤调理剂、润肤剂和水分向皮肤表面的的渗透。
优选的,所述水相稳定剂选自琼脂糖、黄原胶、羟乙基纤维素、卡波姆中的一种或几种的组合物;所述油相稳定剂选自季铵盐-18水辉石、季铵盐-18膨润土中的一种或几种的组合物。更优选的,所述水相稳定剂采用琼脂糖,所述油相稳定剂采用季铵盐-18水辉石。
上述稳定剂的作用在体系中能够形成网络结构,起到增稠作用,减少沉淀和分层现象,提高产品的稳定性。
优选的,所述稳定剂采用质量比为0.1~3:0.1~3的水相稳定剂和油相稳定剂,所述水相稳定剂和油相稳定剂分别为琼脂糖和季铵盐-18水辉石。
季铵盐-18水辉石具有亲油性,能够在油相溶液中起到良好的稳定作用,而琼脂糖含有大量羟基基团,能够在水相溶液中溶胀成胶体,起到稳定作用。油相和水相混合后,琼脂糖中的羟基能够和丙烯酸酯类/聚二甲基硅氧烷共聚物的羰基或硅羟基形成氢键,起到稳定作用,并有效降低环五聚二甲基硅氧烷等硅油离析的可能,保障粉底液的成膜稳定性。
优选的,所述保湿剂采用质量比为0.5~5:3~10的丁二醇和甘油。
上述保湿剂均为小分子化合物,渗透性能突出,能够快速穿过粉底液膜层并作用于肌肤,起到保水保湿作用。同时,能够促进前述亲水性通道的形成,提高粉底液的美容护肤效果。
优选的,所述填充剂选自高岭土、膨润土、滑石粉、氢氧化铝中的一种或几种的组合物;更优选采用云母或其悬浮液。
优选的,所述皮肤调理剂选自掌状海带提取物、具距石枝藻提取物、齿缘墨角藻提取物、海带提取物、伸长海条藻提取物、石莼提取物、皱波角叉菜提取物中的一种或几种的组合物。
上述植物提取物中含有天然色素、抗氧化物,能够抑制皮肤过氧化,调理修复皮肤缺陷,起到延缓衰老、防皱抗衰的效果。
优选的,所述粘度调节剂采用氯化钠、氯化铵等无机盐,更优选采用氯化钠。
第二方面,本申请提供一种耐汗粉底液的制备方法,包括如下步骤:
油相制备:加热条件下,取成膜剂、润肤剂、防腐剂、乳化剂和10~90wt%的稳定剂混合均匀,得到乳化液;取部分乳化液和填充剂、着色剂混合均匀,研磨后得到油相溶液,保温备用;
水相制备:加热条件下,取保湿剂、粘度调节剂、螯合剂加入水中,溶解并混合均匀,得水相溶液;
成品制备:将水相溶液与油相溶液混合经过均质乳化、抽真空后制得耐汗粉底液;
优选的,所述加热温度均为70-85℃;
优选的,所述均质乳化的转速为2500-3000rpm,所述均质乳化的时间为5-10分钟。
通过上述制备工艺,可获得均质稳定的粉底液,具有良好的和美容护肤效果。同时,该乳液易于涂抹推开,有效保障妆面的均匀性。
综上所述,本申请具有如下有益效果:
1、本申请通过采用丙烯酸酯类/聚二甲基硅氧烷共聚物和环五聚二甲基硅氧烷的复合物作为粉底液的成膜剂,能够在保障粉底液涂抹推开性能的前提下,显著提高其性能。
2、本申请的乳化剂采用鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷和PEG-10聚二甲基硅氧烷进行协同配合,在起到乳化均质作用的同时,能够在粉底液膜层上形成通道结构,补偿膜层亲水物质的通过率,促进皮肤调理剂、润肤剂等亲水性物质的向肌肤表面的渗透,保障其美容护肤作用。
3、本申请稳定剂采用琼脂糖和季铵盐-18水辉石进行协同配合,能够起到良好的抗沉淀分层和看硅油离析的作用,保障粉底液成膜和储存的稳定性。
具体实施方式
实施例
实施例1,一种耐汗粉底液,按照如下方法制备得到:
油相制备:加热条件下,取丙烯酸(酯)类/聚二甲基硅氧烷共聚物、环五聚二甲基硅氧烷成膜剂、润肤剂、防腐剂、乳化剂和季铵盐-18水辉石投入乳化锅中,搅拌升温至80±2℃,搅拌均匀,得到乳化液;取40wt%的乳化液和填充剂、着色剂混合均匀,研磨后与剩余乳化液在乳化锅中混合均匀,得到油相溶液,78±2℃保温备用;
水相制备:取保湿剂、粘度调节剂、螯合剂与水投入水相锅中,搅拌升温至70~85℃,溶解并搅拌均匀,得水相溶液;
成品制备:将水相溶液加入乳化锅中与油相溶液混合,在2500rpm下均质乳化8min,再抽真空出料制得耐汗粉底液。
实施例3,一种耐汗粉底液,按照如下方法制备得到:
油相制备:加热条件下,取丙烯酸(酯)类/聚二甲基硅氧烷共聚物、环五聚二甲基硅氧烷成膜剂、润肤剂、防腐剂、乳化剂和季铵盐-18水辉石投入乳化锅中,搅拌升温至82±2℃,搅拌均匀,得到乳化液;取30wt%的乳化液和填充剂、着色剂混合均匀,研磨后与剩余乳化液在乳化锅中混合均匀,得到油相溶液,78±2℃保温备用;
水相制备:取保湿剂、粘度调节剂、螯合剂与水投入水相锅中,搅拌升温至70~85℃,溶解并搅拌均匀,得水相溶液;
成品制备:将水相溶液加入乳化锅中与油相溶液混合,在2500rpm下均质乳化10min,再抽真空出料制得耐汗粉底液。
实施例3,一种耐汗粉底液,按照如下方法制备得到:
油相制备:加热条件下,取丙烯酸(酯)类/聚二甲基硅氧烷共聚物、环五聚二甲基硅氧烷成膜剂、润肤剂、防腐剂、乳化剂和季铵盐-18水辉石投入乳化锅中,搅拌升温至75±2℃,搅拌均匀,得到乳化液;取50wt%的乳化液和填充剂、着色剂混合均匀,研磨后与剩余乳化液在乳化锅中混合均匀,得到油相溶液78±2℃保温备用;
水相制备:取保湿剂、粘度调节剂、螯合剂与水投入水相锅中,搅拌升温至70~85℃,溶解并搅拌均匀,得水相溶液;
成品制备:将水相溶液加入乳化锅中与油相溶液混合,在3000rpm下均质乳化5min,再抽真空出料制得耐汗粉底液。
表1、实施例1-3原料配比
实施例4,一种耐汗粉底液,与实施例1的区别在于,乳化剂中,采用等量鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷替换PEG-10聚二甲基硅氧烷。
实施例5,一种耐汗粉底液,与实施例1的区别在于,乳化剂中,采用等量PEG-10聚二甲基硅氧烷替换鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷。
实施例6,一种耐汗粉底液,与实施例1的区别在于,乳化剂中采用等量PEG/PPG-8/3月桂酸酯替换PEG-10聚二甲基硅氧烷与鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷。
实施例7,一种耐汗粉底液,与实施例1的区别在于,乳化剂中采用等量鲸蜡基聚二甲基硅氧烷替换PEG-10聚二甲基硅氧烷与鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷。
实施例8,一种耐汗粉底液,与实施例1的区别在于,稳定剂中采用等量卡波姆替换琼脂糖。
实施例9,一种耐汗粉底液,与实施例1的区别在于,稳定剂中采用等量季铵盐-18膨润土替换季铵盐-18水辉石。
实施例10,一种耐汗粉底液,与实施例1的区别在于,保湿剂中采用等量甘油替换丁二醇。
实施例11,一种耐汗粉底液,与实施例1的区别在于,保湿剂中采用等量丁二醇替换甘油。
实施例12,一种耐汗粉底液,与实施例1的区别在于,保湿剂中采用等量聚乙二醇-4替换丁二醇和甘油。
对比例
对比例1,一种耐汗粉底液,与实施例1的区别在于,成膜剂中采用等量丙烯酸酯类/聚二甲基硅氧烷替代环五聚二甲基硅氧烷。
对比例2,一种耐汗粉底液,与实施例1的区别在于,成膜剂中采用等量环五聚二甲基硅氧烷替代丙烯酸酯类/聚二甲基硅氧烷。
对比例3,一种粉底液,以100kg为总重量,包括的组分及对应的质量如下:
分散剂:包括鲸蜡基聚二甲基硅氧烷3.8㎏、聚乙烯1.3㎏;季铵盐-18膨润土0.3㎏;着色剂6㎏;氢氧化铋2.2㎏;润肤剂4㎏;增稠剂:包括卡波姆(2%水溶液)5㎏、黄原胶(2%水溶液)5㎏;调理剂:包括鸡蛋果提取物0.2㎏、糖鞘脂类3.6㎏、芍药根提取物0.22㎏、甘油3㎏、1,3-丁二醇3㎏;防腐剂包括辛甘醇1㎏;水59.38㎏。
且该粉底液由以下步骤制得:
S1:称量并将季铵盐-18膨润土、润肤剂以及鲸蜡基聚二甲基硅氧烷混合,在6000r/min的搅拌速度下均质5min;加入着色剂,在6000r/min的搅拌速度下均质5min;再加入聚乙烯和氯氧化铋,加热至80℃并保温,得到混合物A;
S2:称量并将增稠剂、调理剂、防腐剂和水混合,并加热至80℃,在搅拌速度为800r/min的条件下搅拌2h,得到混合物B;
S3:将混合物A加入混合物B中,在搅拌速度为800r/min的条件下搅拌10s,得到粉底液。
性能检测试验
1、粉底液防水抗汗性能与涂抹分散性能测试
选取18-35岁健康且无过敏史的女性受试者,用同一温和型洗面奶洗净脸部并擦干,再涂抹同一爽肤水,拍打吸收完全,最后进行粉底上妆。每组试样受试者各3名,分别由3名3-5年执业年限的化妆师进行上妆。
防水抗汗性能:上妆完成后,受试者需在30℃、50RH%的室内环境下使用跑步机进行运动,跑步机速度为6-8㎞/h,单次跑步时间为5-10min;跑完后休息20-30min,休息期间用喷壶往脸部均匀喷水将妆容打湿,每次喷水量为10-20ml,自然晾干。重复上述跑步和喷水操作5次,观察粉底液是否脱妆并记录出现脱妆时实验进行的次数,以3个试样平均值为测试结果,记作防水耐汗测试次数(次)。
涂抹分散性能:上妆完成后,化妆师需对粉底液的涂抹分散性能(爽滑度)以及状面均匀度进行评分,以1-5分记分,1分最差,5分最佳,以3个试样平均值为测试结果。
2、粉底液美容护肤性能测试
选取30-45岁无过敏史的女性受试者,使用上述各组粉底液试样进行上妆,每组试样受试者各3名,使用时间为1个月。每次用同种温和型洗面奶洗净脸部并擦干,再涂抹同种爽肤水,拍打吸收完全,最后进行粉底上妆,试验周期内不使用其他护肤品。试验结束前后,用同一相机和相同光线、镜头参数情况下拍下脸部照片,由专业美容师对脸部皱纹使用前后皱纹变化情况并进行评分,以1-5分记分,分数越高,表示脸部皱纹减少或皮肤修复效果越明显。
3、粉底液稳定性测试
从刚配制完成的各组粉底液中取75ml试样放入透明玻璃瓶中,然后置于45℃的烘箱中静置1h,取出观察是否有沉淀和油水分层现象。
表2、实验结果
实验结果分析:
(1)结合实施例1~12和对比例3并结合表2可以看出,相比采用常规亲水性成膜剂或增稠剂,本申请通过采用丙烯酸酯类/聚二甲基硅氧烷共聚物和环五聚二甲基硅氧烷,能够显著提高粉底液的防水耐汗性能,提高其持妆性能。再结合实施例1和对比例1~2并结合表2可以看出,环五聚二甲基硅氧烷能够有效补偿因丙烯酸酯类/聚二甲基硅氧烷共聚物使用导致的流动性下降,进而提高耐汗粉底液的爽滑度和妆面均匀度。
(2)结合实施例1和实施例4~7并结合表2可以看出,本申请通过采用鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷和PEG-10聚二甲基硅氧烷一同作为乳化剂,能够显著改善因成膜剂中有机硅疏水链段引入造成的亲水物质通过率下降问题,促进皮肤调理剂、润肤剂、保湿剂等护肤成分的渗透率,保障粉底液的美容护肤效果。且两者配合更有助于扩展亲水通道,促进有效护肤成分通过膜层并作用于肌肤。
(3)结合实施例1和实施例8~9并结合表2可以看出,本申请通过采用琼脂糖与季铵盐-18水辉石分别作为水相、油相稳定剂,能够抑制粉底液中的乳液沉淀或环五聚二甲基硅氧烷等硅油成分离析分层的现象。其原因可能在于,上述两种稳定剂在具有常规增稠增粘等稳定效用的同时,其中季铵盐-18水辉石还具有硅氧硅链段,与硅油具有较好的亲和性。而琼脂糖中的羟基能够和丙烯酸酯类/聚二甲基硅氧烷共聚物的羰基或硅羟基形成氢键,起到稳定作用,进而有效降低环五聚二甲基硅氧烷等硅油离析的可能,保障粉底液的成膜稳定性。
(4)结合实施例1和实施例10~12并结合表2可以看出,相比聚乙二醇-4,本申请通过采用甘油和丁二醇作为保湿剂,有助于保障粉底液的美容护肤效果。因甘油和丁二醇等具有突出的渗透性,在粉底液膜层中通过性较好,能够有效促进皮肤调理剂等物质的扩散。而聚乙二醇-4或透明质酸钠等大分子保湿剂的作用效果较差。
本具体实施例仅仅是对本申请的解释,其并不是对本申请的限制,本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改,但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (10)
1.一种耐汗粉底液,其特征在于,包含如下重量百分比的原料:
成膜剂:3~10%;
润肤剂:8.5~42%;
保湿剂:3.5~15%;
填充剂:0.5~5%;
乳化剂:1~10%;
皮肤调理剂:0.7~21%;
粘度调节剂:0.1~2%;
稳定剂:0.2~6%;
螯合剂:0.001~0.5%;
着色剂:0~40%;
防腐剂:0~1%;
所述成膜剂采用质量比为1~3:2~5的丙烯酸酯类/聚二甲基硅氧烷共聚物和环五聚二甲基硅氧烷。
2.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述乳化剂采用质量比为0.5~5:0.5~5的鲸蜡基PEG/PPG-10/1聚二甲基硅氧烷和PEG-10聚二甲基硅氧烷。
3.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述稳定剂选自琼脂糖、季铵盐-18水辉石、季铵盐-18膨润土中的一种或几种的组合物。
4.根据权利要求3所述的一种耐汗粉底液,其特征在于,所述稳定剂采用质量比为0.1~3:0.1~3的水相稳定剂和油相稳定剂,所述水相稳定剂和油相稳定剂分别为琼脂糖和季铵盐-18水辉石。
5.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述保湿剂采用质量比为0.5~5:3~10的丁二醇和甘油。
6.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述填充剂采用云母或其悬浮液。
7.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述皮肤调理剂选自掌状海带提取物、具距石枝藻提取物、齿缘墨角藻提取物、海带提取物、伸长海条藻提取物、石莼提取物、皱波角叉菜提取物中的一种或几种的组合物。
8.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述润肤液选自辛酸/癸酸甘油三酯、碳酸二辛酯、异十二烷、聚二甲基硅氧烷、氢化聚癸烯、鲸蜡醇乙基己酸酯中的一种或几种的组合物。
9.根据权利要求1所述的一种耐汗粉底液,其特征在于,所述粘度调节剂为氯化钠。
10.根据权利要求1~9中任一项所述的耐汗粉底液的制备方法,其特征在于,包括如下步骤:
油相制备:加热条件下,取成膜剂、润肤剂、防腐剂、乳化剂和10~90wt%的稳定剂混合均匀,得到乳化液;取部分乳化液和填充剂、着色剂混合研磨,研磨好后与剩余的乳化液混合后均匀,得到油相溶液,保温备用;
水相制备:加热条件下,取保湿剂、粘度调节剂、螯合剂加入水中,溶解并混合均匀,得水相溶液;
成品制备:将水相溶液与油相溶液混合经过均质乳化、抽真空后制得耐汗粉底液;
优选的,所述加热温度均为70~85℃;
优选的,所述均质乳化的转速为2500~3000rpm,所述均质乳化的时间为5~10分钟。