CN115806404A - 抗泥型聚羧酸减水剂 - Google Patents
抗泥型聚羧酸减水剂 Download PDFInfo
- Publication number
- CN115806404A CN115806404A CN202111070522.5A CN202111070522A CN115806404A CN 115806404 A CN115806404 A CN 115806404A CN 202111070522 A CN202111070522 A CN 202111070522A CN 115806404 A CN115806404 A CN 115806404A
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- agent
- acid
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗泥型聚羧酸减水剂，制备步骤如下：S1：在配有电动搅拌器、温度计、滴液装置、以及回流冷凝管的圆底烧瓶中，将200份的软水投入圆底烧瓶作为底水；S2：将60份聚合单体、3份聚合引发剂、5份分子量调节剂、20份小分子抗泥剂、10份过氧化氢和6份链转移剂倒入圆底烧瓶内，得到抗泥型聚羧酸减水剂母液；S3：在抗泥型聚羧酸减水剂母液内加入25份引气剂和15份缓凝剂，加入适量的氢氧化钠，使整体装置内溶液PH值为7；S4：加入10份牺牲剂，使其充分反应，水浴降温，析出晶体，出料。本发明能适应泥含量不超过10％的砂石骨料，在适当掺量下具有良好的分散减水效果，使混凝土具有良好的和易性。
Description
技术领域
本发明涉及减水剂技术领域，尤其涉及抗泥型聚羧酸减水剂。
背景技术
随着我国基础建设行业的迅猛发展，国内预拌混凝土的产量也是逐年提高，其中所用到的砂石料中含有的粘土矿物主要有高岭土 (Al2O3·2SiO2·2H2O)、膨润土(主要成份是蒙脱石，(Al2， Mg3)Si4O10OH2·nH2O)和伊利石(K0.75(Al1.75R)[Si3.5Al0.5O10](OH)2)，在砂石料和聚羧酸系减水剂混合过程中，膨润土对聚羧酸系减水剂会产生负面影响，降低聚羧酸系减水剂减水效果，降低混凝土的和易性。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的抗泥型聚羧酸减水剂。
为了实现上述目的，本发明采用了如下技术方案：
抗泥型聚羧酸减水剂，制备原料包括：软水、聚合单体、聚合引发剂、分子量调节剂、链转移剂、缓凝剂、引气剂、牺牲剂、过氧化氢和氢氧化钠。
作为本发明再进一步的方案：所述制备步骤如下：
S1：在配有电动搅拌器、温度计、滴液装置、以及回流冷凝管的圆底烧瓶中，将200份的软水投入圆底烧瓶作为底水；
S2：将60份聚合单体、3份聚合引发剂、5份分子量调节剂，10 份过氧化氢和6份链转移剂倒入圆底烧瓶内，使其进行自由基共聚反应，得到抗泥型聚羧酸减水剂母液；
S3：在抗泥型聚羧酸减水剂母液内加入25份引气剂和15份缓凝剂，加入适量的氢氧化钠，使整体装置内溶液PH值为7；
S4：加入10份牺牲剂，使其充分反应，水浴降温，析出晶体，出料。
作为本发明再进一步的方案：所述聚合单体选自甲基丙烯酸、丙烯酸，丙烯酸乙酯、丙烯酸羟乙酯、烯丙基磺酸钠、甲基丙烯酸甲酯、 2-丙烯酰胺基-2-甲基丙烯酸、甲氧基聚氧乙烯醚甲基丙烯酸酯中的一种或多种。
作为本发明再进一步的方案：所述聚合引发剂选自过硫酸盐、过氧化苯甲酰、偶氮中一种或多种。
作为本发明再进一步的方案：所述分子量调节剂选自3-疏基丙酸、疏基乙酸、疏基乙醇、异丙醇中一种或多种。
作为本发明再进一步的方案：所述缓凝剂选自糖蜜、木钙、木钠、羟基羧酸、柠檬酸、硼酸盐中一种或多种。
作为本发明再进一步的方案：所述引气剂选自松香树脂类、烷基、烷基芳烃磺酸类、脂肪醇磺酸盐类、皂苷类、蛋白质盐、石油磺盐酸中一种或多种。
作为本发明再进一步的方案：所述牺牲剂选自聚乙二醇类、陶瓷分散剂类、有机膦酸类、小分子羧酸类和阳离子型聚合物中一种或多种。
本发明的有益效果为：
1.能适应泥含量不超过10％的砂石骨料，在适当掺量下具有良好的分散减水效果，混凝土具有良好的和易性，添加小分子抗泥剂与抗泥型聚羧酸系减水剂两方面相结合，充分降低粘土对聚羧酸系减水剂的吸附能力，抗泥效果好。
2.通过牺牲剂与聚羧酸系减水剂进行复配，也可以起到一定的抗泥效果，保坍性能好：1h坍落度损失不超过30mm，且不离析泌水。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1为本发明的配置步骤图。
具体实施方式
下面结合具体实施方式对本专利的技术方案作进一步详细地说明。
一种抗泥型聚羧酸减水剂，制备原料包括：软水、聚合单体、聚合引发剂、分子量调节剂、链转移剂、缓凝剂、引气剂、牺牲剂、小分子抗泥剂、过氧化氢和氢氧化钠。
S1：在配有电动搅拌器、温度计、滴液装置、以及回流冷凝管的圆底烧瓶中，将200份的软水投入圆底烧瓶作为底水；
S2：将60份聚合单体、3份聚合引发剂、5份分子量调节剂、20 份小分子抗泥剂、10份过氧化氢和6份链转移剂倒入圆底烧瓶内，使其进行自由基共聚反应，得到抗泥型聚羧酸减水剂母液；
S3：在抗泥型聚羧酸减水剂母液内加入25份引气剂和15份缓凝剂，加入适量的氢氧化钠，使整体装置内溶液PH值为7；
S4：加入10份牺牲剂，使其充分反应，水浴降温，析出晶体，出料。
所述聚合单体选自甲基丙烯酸、丙烯酸，丙烯酸乙酯、丙烯酸羟乙酯、烯丙基磺酸钠、甲基丙烯酸甲酯、2-丙烯酰胺基-2-甲基丙烯酸、甲氧基聚氧乙烯醚甲基丙烯酸酯中的一种或多种。
所述聚合引发剂选自过硫酸盐、过氧化苯甲酰、偶氮中一种或多种。
所述分子量调节剂选自3-疏基丙酸、疏基乙酸、疏基乙醇、异丙醇中一种或多种。
所述缓凝剂选自糖蜜、木钙、木钠、羟基羧酸、柠檬酸、硼酸盐中一种或多种。
所述引气剂选自松香树脂类、烷基、烷基芳烃磺酸类、脂肪醇磺酸盐类、皂苷类、蛋白质盐、石油磺盐酸中一种或多种。
所述牺牲剂选自聚乙二醇类、陶瓷分散剂类、有机膦酸类、小分子羧酸类和阳离子型聚合物中一种或多种。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.抗泥型聚羧酸减水剂，其特征在于，制备原料包括：软水、聚合单体、聚合引发剂、分子量调节剂、链转移剂、缓凝剂、引气剂、牺牲剂、小分子抗泥剂、过氧化氢和氢氧化钠。
2.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述制备步骤如下：
S1：在配有电动搅拌器、温度计、滴液装置、以及回流冷凝管的圆底烧瓶中，将200份的软水投入圆底烧瓶作为底水；
S2：将60份聚合单体、3份聚合引发剂、5份分子量调节剂、20份小分子抗泥剂、10份过氧化氢和6份链转移剂倒入圆底烧瓶内，使其进行自由基共聚反应，得到抗泥型聚羧酸减水剂母液；
S3：在抗泥型聚羧酸减水剂母液内加入25份引气剂和15份缓凝剂，加入适量的氢氧化钠，使整体装置内溶液PH值为7；
S4：加入10份牺牲剂，使其充分反应，水浴降温，析出晶体，出料。
3.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述聚合单体选自甲基丙烯酸、丙烯酸，丙烯酸乙酯、丙烯酸羟乙酯、烯丙基磺酸钠、甲基丙烯酸甲酯、2-丙烯酰胺基-2-甲基丙烯酸、甲氧基聚氧乙烯醚甲基丙烯酸酯中的一种或多种。
4.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述聚合引发剂选自过硫酸盐、过氧化苯甲酰、偶氮中一种或多种。
5.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述分子量调节剂选自3-疏基丙酸、疏基乙酸、疏基乙醇、异丙醇中一种或多种。
6.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述缓凝剂选自糖蜜、木钙、木钠、羟基羧酸、柠檬酸、硼酸盐中一种或多种。
7.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述引气剂选自松香树脂类、烷基、烷基芳烃磺酸类、脂肪醇磺酸盐类、皂苷类、蛋白质盐、石油磺盐酸中一种或多种。
8.根据权利要求1所述的抗泥型聚羧酸减水剂，其特征在于，所述牺牲剂选自聚乙二醇类、陶瓷分散剂类、有机膦酸类、小分子羧酸类和阳离子型聚合物中一种或多种。