CN115503315A - 一种透气性好弹性间隔织物 - Google Patents
一种透气性好弹性间隔织物 Download PDFInfo
- Publication number
- CN115503315A CN115503315A CN202211234473.9A CN202211234473A CN115503315A CN 115503315 A CN115503315 A CN 115503315A CN 202211234473 A CN202211234473 A CN 202211234473A CN 115503315 A CN115503315 A CN 115503315A
- Authority
- CN
- China
- Prior art keywords
- warp knitting
- layer
- knitting layer
- spacer fabric
- air permeability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及纺织加工技术领域,公开了一种透气性好弹性间隔织物,所述间隔织物由上经编层、弹性纱线层和下经编层,上经编层和下经编层均采用粗纱的六根纱线,通过编织机进行上针道两道,下针道四道交叉编织,经编层和下经编层之间通过弹性纱线层完成上下的连接,同时其安装规律形成往复连接,经编层和下经编层之间通过间隔层完成填充,其通过超大隔距的上经编层和下经编层之间由2个***的表层纱线和1个***的间隔纱线编织而成。本发明有利于通过工艺方式使得间隔织物中空具有弹性,形成很好的填充效果,同时保证其结构性具有透气的效果,使得其在受压包覆的情况下,其仍然保持良好的透气性。
Description
技术领域
本发明涉及纺织加工技术领域,具体为一种透气性好弹性间隔织物。
背景技术
间隔织物的应用领域非常广泛,如应用于医用纺织品、家用纺织品、军用纺织品、汽车用纺织品、航空用纺织品及运动用纺织品,其由若干组纱线形成两层或两层以上的织物,并由另一组纱线将各层织物连接起来而形成的织物,而其连接各层织物的纱线一般比较稀疏,同时连接的浮线较长,相邻两层织物之间的间距比较大,可以较多地注入基体和填料。
现有中国专利(公告号:CN108437595A)及一种纬编间隔织物及其制备方法,以及包含该织物的聚氨酯泡沫复合材料,此专利的间隔织物的厚度变化与鞋底厚度变化相一致,在不同厚度部位都起到增强作用,此外能够根据鞋底不同部位的承载状况来改变间隔丝的排列密度,承受载荷大的部位增加间隔丝的排列密度,反之则减少间隔丝的密度,从而充分发挥纬编间隔织物在鞋底不同部位的不同增强效果,然而其应用于床垫以及沙发背垫以及座椅坐垫时,其弹性较低,且所能提供的支撑以及填充效果较低;
现有中国专利(公告号:CN206970818U)及双面贾卡间隔经编织物,此专利整个双面贾卡间隔经编织物通过贾卡经编机一次成型,效率高,无需再将花型通过缝制拼接,节约成本,并且双面贾卡间隔经编织物能够产生双色、三色或者多色效果,使得提花更加美观,当双面的提花镂空结构较多、较大或者镂空结构上下相通时,面料的透气性良好,尤其在双面的镂空结构正好相对时,透气性最佳,而且中间层具有良好的弹性和保温性,可以根据需要织造中间层的厚度,能够满足双面贾卡间隔经编织物整体的厚度变化需求,其所述面料的透气性良好,尤其在双面的镂空结构正好相对时,透气性最佳,然而纬编间隔织物使用过程中,其外部均需要包裹布料,对其进行装饰包覆,其中通过材料本身的透气性,对于床垫、沙发类进行透气其效果明显较低,且受到外部包覆的影响使得其弹性较低不够柔软。
因此,我们透气性好弹性间隔织物,有利于通过工艺方式使得间隔织物中空具有弹性,形成很好的填充效果,同时保证其结构性具有透气的效果,使得其在受压包覆的情况下,其仍然保持良好的透气性。
发明内容
本发明的目的在于提供一种透气性好弹性间隔织物,解决了背景技术中所提出的问题。
为实现上述目的,本发明提供如下技术方案:一种透气性好弹性间隔织物,所述间隔织物由上经编层、弹性纱线层和下经编层,上经编层和下经编层均采用粗纱的六根纱线,通过编织机进行上针道两道,下针道四道交叉编织,经编层和下经编层之间通过弹性纱线层完成上下的连接,同时其安装规律形成往复连接,经编层和下经编层之间通过间隔层完成填充,其通过超大隔距的上经编层和下经编层之间由2个***的表层纱线和1个***的间隔纱线编织而成。
作为本发明的一种优选实施方式,上经编层和下经编之间形成超大隔距经在200~500mm,其织物表层的厚度约1~2mm。
作为本发明的一种优选实施方式,上经编层和下经编层的间隔丝排列较为稀疏,且采用高强度长丝,间隔层的组织工艺中适当加入缺垫经编组织。
作为本发明的一种优选实施方式,上经编层和下经编层采用带有4把梳栉和E32的双针床经编机上编织的,其门幅为425CM,机器速度为900rpm。
作为本发明的一种优选实施方式,上经编层16%,45dtex/32f涤纶长丝,消光;68%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光。
作为本发明的一种优选实施方式,间隔层原料采用混纺纤维,其中包含有聚酯、阻燃纤维、100%芳纶加捻纱以及尼龙材料。
作为本发明的一种优选实施方式,下经编层料采用16%,45dtex/32f涤纶长丝,消光;58%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光;以及10%的莱卡纤维。
与现有技术相比,本发明的有益效果如下:
本发明通过复合结构的方式,通过上经编层和下经编层之间上经编层和下经编之间形成连接弹性纱线层,使得内部结构更多孔体,在通过填充层采用2个***的表层纱线和1个***的间隔纱线编织而成,使得上经编层和下经编层之间的超大隔距复合组织有另一内部结构,增加填充效果,同时弹性更加,孔体更多,同时上经编层和下经编层采用不同材料,使上经编层具有良好的透气性和耐磨性,而下经编层更为柔软适,有利于通过工艺方式使得间隔织物中空具有弹性,形成很好的填充效果,同时保证其结构性具有透气的效果,使得其在受压包覆的情况下,其仍然保持良好的透气性。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述,本发明的其它特征、目的和优点将会变得更明显:
图1为本发明一种透气性好弹性间隔织物的整体外层结构示意图;
图2为本发明一种透气性好弹性间隔织物的整体内部结构示意图。
图中:1、上经编层;2、弹性纱线层;3、下经编层。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
请参阅图1-2,本发明提供一种技术方案:一种透气性好弹性间隔织物,所述间隔织物由上经编层1、弹性纱线层2和下经编层3,上经编层1和下经编层3均采用粗纱的六根纱线,通过编织机进行上针道两道,下针道四道交叉编织,经编层和下经编层3之间通过弹性纱线层完成上下的连接,同时其安装规律形成往复连接,经编层和下经编层3之间通过间隔层完成填充,其通过超大隔距的上经编层1和下经编层3之间由2个***的表层纱线和1个***的间隔纱线编织而成;
采用复合结构的方式,通过上经编层1和下经编层3之间上经编层1和下经编之间形成连接弹性纱线层,使得内部结构更多孔体,在通过填充层采用2个***的表层纱线和1个***的间隔纱线编织而成,使得上经编层1和下经编层3之间的超大隔距复合组织有另一内部结构,增加填充效果,同时弹性更加,孔体更多,同时上经编层1和下经编层3采用不同材料,使上经编层1具有良好的透气性和耐磨性,而下经编层3更为柔软适,有利于通过工艺方式使得间隔织物中空具有弹性,形成很好的填充效果,同时保证其结构性具有透气的效果,使得其在受压包覆的情况下,其仍然保持良好的透气性;
作为床垫的内衬来说,本间隔织物其孔隙更为微小,其利用众多的纱线支撑出大空间,以上所列举出的特性对于生产高档的床垫来说非常重要,其意味着更好的透气性,和填充效果更高,同时其也可用来做汽车坐垫和沙发垫;
间隔织物的间隙为10-15mm,具有很高的抗压性;
间隔织物通过上述设置使其具有特殊的网孔结构,使其干燥速度较快,从而防止了霉菌和细菌的生长,同时其重量更为轻便。
本实施例中,上经编层1和下经编之间形成超大隔距经在200~500mm,其织物表层的厚度约1~2mm;
超大隔距经编间隔织物的间隔距离很大,通常在100~300mm左右,最高达到650mm,其距离也可以根据不同结构性能的要求进行生产,而本间隔织物的在200~500mm,织物表面层的厚度约1~2mm。
本实施例中,上经编层1和下经编层3的间隔丝排列较为稀疏,且采用高强度长丝,间隔层的组织工艺中适当加入缺垫经编组织;
间隔丝密度太大则会导致产品的压缩厚度变大而不易收纳存放,并且也会造成多余间隔丝的浪费,若间隔丝密度过小则不能保证间隔层的强度,所以要根据织物的具体应用设计间隔丝密度,缺垫经编组织为部分梳栉按组织结构要求在某些横列垫纱成圈,在另一些横列不垫纱成圈,在织物反面相应横列产生缺垫纱段的经编针织物花色组织,通过增加缺垫经编组织以达到符合要求的间隔丝密度的目的。
本实施例中,上经编层1和下经编层3采用带有4把梳栉和E32的双针床经编机上编织的,其门幅为425CM,机器速度为900rpm;
采用在双针床拉舍尔经编机上生产,其带有四把梳栉和EL型电子梳栉横移机构,使得织物的一面带有花纹,借助于花梳的编织,间隔织物工艺反面的外观得到了改进,目前采用白色纱线,使得编织的花型柔和美观,可以更换纱线颜色,使得花型效果将更为突出;
其加工工艺参数可参考
例1
其门幅为425CM,机器速度为900rpm;间隔距离:3.5mm
组织、送经与送经量:
GB1:满穿A,1400mm
GB2:满穿A,1630mm
GB3:满穿B,4870mm
GB4:满穿A,1840mm
织物参数
纵密:20.8cpc(机上:20.4cpc);横密:33wpi;克重:210.3g/m2;横向缩率:97%;产量:11.3m/h。
例2
其门幅为415CM,机器速度为800rpm;间隔距离:3.2mm
组织、送经与送经量
GB1:满穿A 1200mm/
JB2.1/JB2.2满穿B 1680mm/Rack
GB3:满穿C 6870mm/Rack
GB4:满穿D 2840mm/Rack
织物参数
纵密:25cpc(机上24cpc);横密:36wpi;克重:295g/m2;横向缩率:97%;产量;:11.3m/h;
本实施例中,上经编层116%,45dtex/32f涤纶长丝,消光;68%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光。
本实施例中,间隔层原料采用混纺纤维,其中包含有聚酯、阻燃纤维、100%芳纶加捻纱以及尼龙材料;
间隔层原料在编制完成后,使得内部填充更高,其复位弹性更佳,同时增加了透气效果,同时隔热效果更好。
本实施例中,下经编层3料采用16%,45dtex/32f涤纶长丝,消光;58%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光;以及10%的莱卡纤维;
下经编层3料相较于上经编层1其降低22dtex/1f涤纶长丝,并增加了10%的莱卡纤维,由于下编制层靠近人体皮肤,其需要更好的柔软度和舒适度。
需要注意上经编层1和下经编层3料均需要经过开松机对布料进行松弛,通过撕扯使大块的纤维开松变成小块或束状小块纤维,同时在开松过程中进行混合、除杂,材料成型有需要通过洗布机进行水洗、通过高压水流对布料进行冲洗及浸泡处理后达到去污的效果,通过布料预缩机对布料完成预定型,在一定的温度条件下,利用机械物理方法预先调整织带的缩率并进行整烫定型,使织带的密度预先收缩从而减小或避免织带在浸水或使用过程中发生收,气候不再引起径向长度缩短,明显降低成品缩水率的效果,布料经过漂白剂完成漂白,通过漂白剂使得布料本身的颜色进行漂白,在通过荧光剂增白,最后将布料送入拉幅机中,通过加热和向两边绷紧张力的作用,将布料伸展平挺、并使其纬向的门幅尺寸宽窄一致。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种透气性好弹性间隔织物,所述间隔织物由上经编层(1)、弹性纱线层(2)和下经编层(3),其特征在于:上经编层(1)和下经编层(3)均采用粗纱的六根纱线,通过编织机进行上针道两道,下针道四道交叉编织,经编层和下经编层(3)之间通过弹性纱线层完成上下的连接,同时其安装规律形成往复连接,经编层和下经编层(3)之间通过间隔层完成填充,其通过超大隔距的上经编层(1)和下经编层(3)之间由2个***的表层纱线和1个***的间隔纱线编织而成。
2.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:上经编层(1)和下经编之间形成超大隔距经在200~500mm,其织物表层的厚度约1~2mm。
3.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:上经编层(1)和下经编层(3)的间隔丝排列较为稀疏,且采用高强度长丝,间隔层的组织工艺中适当加入缺垫经编组织。
4.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:上经编层(1)和下经编层(3)采用带有4把梳栉和E32的双针床经编机上编织的,其门幅为425CM,机器速度为900rpm。
5.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:上经编层(1)16%,45dtex/32f涤纶长丝,消光;68%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光。
6.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:间隔层原料采用混纺纤维,其中包含有聚酯、阻燃纤维、100%芳纶加捻纱以及尼龙材料。
7.根据权利要求1所述的一种透气性好弹性间隔织物,其特征在于:下经编层(3)料采用16%,45dtex/32f涤纶长丝,消光;58%,22dtex/1f涤纶长丝,单丝;16%,45dtex/32f涤纶长丝,消光;以及10%的莱卡纤维。