CN115433536A - 一种透明的聚氨酯电子密封胶 - Google Patents
一种透明的聚氨酯电子密封胶 Download PDFInfo
- Publication number
- CN115433536A CN115433536A CN202211110141.XA CN202211110141A CN115433536A CN 115433536 A CN115433536 A CN 115433536A CN 202211110141 A CN202211110141 A CN 202211110141A CN 115433536 A CN115433536 A CN 115433536A
- Authority
- CN
- China
- Prior art keywords
- parts
- transparent polyurethane
- electronic sealant
- polyurethane electronic
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种透明的聚氨酯电子密封胶，包括如下质量份的各组分：第一原料组分40份至60份和第二原料组件40份至60份；所述第一原料组分包括如下质量份的各组分：异氰酸酯15份至30份、多元醇20份至30份、磷酸三脂8份‑15份、乙酸乙酯30份至40份、蓖麻油8份至15份以及氨基酸锌0.3份至0.7份；所述第二原料组分包括如下质量份的各组分：羟基封端聚二甲基硅氧烷40份至50份、四甲氧基硅烷4份‑8份、端羟二甲基硅油15份至25份、氨基硅油4份‑8份、乙醇4份‑8份、三甲基硅醇4份至8份、正硅酸乙酯10份至15份以及二丁基二月桂酸锡0.5份至0.8份。上述透明的聚氨酯电子密封胶，透明性良好、粘结性能强、稳定性强、耐候性良好，不易发黄变色。
Description
技术领域
本发明涉及电子密封胶领域，特别是涉及一种透明的聚氨酯电子密封胶。
背景技术
电子密封胶具有耐高温、耐低温、耐水煮、抗水浸泡的优异性能。电子密封胶粘结效果优越胶体呈弹性体，可以粘结金属及非金属材质，起到粘结、固定、密封、灌封、涂覆等作用。电子密封胶耐侯性佳、防潮、抗震、防紫外线、防水。电子密封胶不会因恶劣的天气环境而改变其性能优良的电气特性，电子密封胶的耐电晕、抗漏电、耐老化、电气绝缘性能佳、密封性强。
电子密封胶具有低挥发性，并且电子密封胶的强度高、粘接性好，对铝、铜、不锈钢等多种金属有优秀的粘接性。此外，电子密封胶中性固化，对金属无腐蚀性。传统的透明电子密封胶耐黄性能较差、稳定性较低。
发明内容
基于此，有必要提供一种透明的聚氨酯电子密封胶及其制作方法。
一种透明的聚氨酯电子密封胶，该透明的聚氨酯电子密封胶包括如下质量份的各组分：第一原料组分40份至60份和第二原料组件40份至60份；
所述第一原料组分包括如下质量份的各组分：异氰酸酯15份至30份、多元醇20份至30份、磷酸三脂8份-15份、乙酸乙酯30份至40份、蓖麻油8份至15份以及氨基酸锌0.3份至0.7份；
所述第二原料组分包括如下质量份的各组分：羟基封端聚二甲基硅氧烷40份至50份、四甲氧基硅烷4份-8份、端羟二甲基硅油15份至25份、氨基硅油4份-8份、乙醇4份-8份、三甲基硅醇4份至8份、正硅酸乙酯10份至15份以及二丁基二月桂酸锡0.5份至0.8份。
在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括增塑剂4份至8份。
在其中一个实施例中，所述多元醇包括如下质量份的各组分：聚醚多元醇40份至60份和聚酯多元醇40份至60份。
在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括阻燃剂2份至5份。
在其中一个实施例中，所述阻燃剂为三聚氰胺聚磷酸盐。
在其中一个实施例中，所述异氰酸酯包括如下质量份的各组分：HDI30份至40份、IPDI30份至40份、MDI30份至40份。
在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括消泡剂0.3份至0.5份。
在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括增粘剂1份至2份。
在其中一个实施例中，所述增粘机为液体环氧树脂。
在其中一个实施例中，所述消泡剂为有机硅消泡剂。
上述透明的聚氨酯电子密封胶，透明性良好、粘结性能强、稳定性强、耐候性良好，不易发黄变色。
附图说明
图1为一个实施例中透明的聚氨酯电子密封胶的组分图；
图2为一个实施例中第一原料组分的组分图；
图3为一个实施例中第二原料组分的组分图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
请参阅图1至图3，本发明提供了一种透明的聚氨酯电子密封胶，该透明的聚氨酯电子密封胶包括如下质量份的各组分：第一原料组分40份至60份和第二原料组件40份至60份；
所述第一原料组分包括如下质量份的各组分：异氰酸酯15份至30份、多元醇20份至30份、磷酸三脂8份-15份、乙酸乙酯30份至40份、蓖麻油8份至15份以及氨基酸锌0.3份至0.7份；
所述第二原料组分包括如下质量份的各组分：羟基封端聚二甲基硅氧烷40份至50份、四甲氧基硅烷4份-8份、端羟二甲基硅油15份至25份、氨基硅油4份-8份、乙醇4份-8份、三甲基硅醇4份至8份、正硅酸乙酯10份至15份以及二丁基二月桂酸锡0.5份至0.8份。
具体的，该透明的聚氨酯电子密封胶在配制过程中，按照上述质量份的比例将多元醇、磷酸三脂、蓖麻油放入反应釜中加热至100摄氏度至120摄氏度，进行真空除水后冷却至20摄氏度至40设施度，然后加入异氰酸酯、氨基酸锌和乙酸乙酯充分混合搅拌均匀，充分反应后成为第一原料胶。
按照上述质量份的比例将羟基封端聚二甲基硅氧烷、四甲氧基硅烷、端羟二甲基硅油、氨基硅油、乙醇、三甲基硅醇放入反应釜混合搅拌均匀并在45摄氏度至55摄氏度的温度条件下充分反应后，减压浓缩后加入正硅酸乙酯和二丁基二月桂酸锡，混合搅拌均匀得到第二原料胶。
按照上述质量份的比例将第一原料胶和第二原料胶混合搅拌均匀得到上述透明的聚氨酯电子密封胶。
上述透明的聚氨酯电子密封胶，透明性良好、粘结性能强、稳定性强、耐候性良好，不易发黄变色。
为了增加透明的聚氨酯电子密封胶的可塑性，在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括增塑剂4份至8份。增塑剂增加了透明的聚氨酯电子密封胶中聚合物的可塑性，增加了透明的聚氨酯电子密封胶凝固后的柔软性，避免透明的聚氨酯电子密封胶凝固后质地过脆，容易崩裂。
为了改善聚合效果，在其中一个实施例中，所述多元醇包括如下质量份的各组分：聚醚多元醇40份至60份和聚酯多元醇40份至60份。进一步地，聚酯多元醇的分子量在1500至2500范围内。聚醚多元醇的分子量在500至800范围内。如此，可以改善聚合效果，从而增加透明的聚氨酯电子密封胶的稳定性。
为了增加透明的聚氨酯电子密封胶的阻燃性能，在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括阻燃剂2份至5份。进一步地，在本实施例中，所述阻燃剂为三聚氰胺聚磷酸盐。三聚氰胺聚磷酸盐为无卤氮系阻燃剂，具有优异的热稳定性和阻燃性能，可以极大地提高透明的聚氨酯电子密封胶的阻燃性能。
为了进一步地改善聚合效果，在其中一个实施例中，所述异氰酸酯包括如下质量份的各组分：HDI30份至40份、IPDI30份至40份、MDI30份至40份。多种类的异氰酸酯有利于与多元醇等其他组分充分进行聚合反应。从而进一步地增加透明的聚氨酯电子密封胶的稳定性。
为了避免在透明的聚氨酯电子密封胶制作过程中产生大量气泡，在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括消泡剂0.3份至0.5份。进一步地，在本实施例中，所述消泡剂为有机硅消泡剂。有机硅消泡剂具有良好的耐高温和耐低温效果，具有良好的化学稳定性和物理稳定性，在对透明的聚氨酯电子密封胶制作过程中产生的大量气泡进行有效地消除的同时，可以增加透明的聚氨酯电子密封胶的化学稳定性。
为了增加透明的聚氨酯电子密封胶的粘接力，在其中一个实施例中，所述透明的聚氨酯电子密封胶还包括增粘剂1份至2份。进一步地，在本实施例中，所述增粘机为液体环氧树脂。液体环氧树脂透明、粘性大。一方面可以增加透明的聚氨酯电子密封胶的粘接力，另一方面可以增加聚氨酯电子密封胶的稳定性和透光性。
对透明的聚氨酯电子密封胶进行测试结果如下：
根据上述测试结果可知，透明的聚氨酯电子密封胶的性能优异，耐候性强，强度稳定，不易变黄变质。
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种透明的聚氨酯电子密封胶，其特征在于，包括如下质量份的各组分：第一原料组分40份至60份和第二原料组件40份至60份；
所述第一原料组分包括如下质量份的各组分：异氰酸酯15份至30份、多元醇20份至30份、磷酸三脂8份-15份、乙酸乙酯30份至40份、蓖麻油8份至15份以及氨基酸锌0.3份至0.7份；
所述第二原料组分包括如下质量份的各组分：羟基封端聚二甲基硅氧烷40份至50份、四甲氧基硅烷4份-8份、端羟二甲基硅油15份至25份、氨基硅油4份-8份、乙醇4份-8份、三甲基硅醇4份至8份、正硅酸乙酯10份至15份以及二丁基二月桂酸锡0.5份至0.8份。
2.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述透明的聚氨酯电子密封胶还包括增塑剂4份至8份。
3.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述多元醇包括如下质量份的各组分：聚醚多元醇40份至60份和聚酯多元醇40份至60份。
4.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述透明的聚氨酯电子密封胶还包括阻燃剂2份至5份。
5.根据权利要求4所述的透明的聚氨酯电子密封胶，其特征在于，所述阻燃剂为三聚氰胺聚磷酸盐。
6.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述异氰酸酯包括如下质量份的各组分：HDI30份至40份、IPDI30份至40份、MDI30份至40份。
7.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述透明的聚氨酯电子密封胶还包括消泡剂0.3份至0.5份。
8.根据权利要求1所述的透明的聚氨酯电子密封胶，其特征在于，所述透明的聚氨酯电子密封胶还包括增粘剂1份至2份。
9.根据权利要求8所述的透明的聚氨酯电子密封胶，其特征在于，所述增粘机为液体环氧树脂。
10.根据权利要求7所述的透明的聚氨酯电子密封胶，其特征在于，所述消泡剂为有机硅消泡剂。