CN115305136B - 一种粘附性能优异的高温链条油及其制备方法 - Google Patents

一种粘附性能优异的高温链条油及其制备方法 Download PDF

Info

Publication number
CN115305136B
CN115305136B CN202210920787.8A CN202210920787A CN115305136B CN 115305136 B CN115305136 B CN 115305136B CN 202210920787 A CN202210920787 A CN 202210920787A CN 115305136 B CN115305136 B CN 115305136B
Authority
CN
China
Prior art keywords
oil
mdi
temperature chain
chain oil
diphenylamine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202210920787.8A
Other languages
English (en)
Other versions
CN115305136A (zh
Inventor
乔志
张利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lubemater Qingdao Material Technology Co ltd
Original Assignee
Lubemater Qingdao Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lubemater Qingdao Material Technology Co ltd filed Critical Lubemater Qingdao Material Technology Co ltd
Priority to CN202210920787.8A priority Critical patent/CN115305136B/zh
Publication of CN115305136A publication Critical patent/CN115305136A/zh
Application granted granted Critical
Publication of CN115305136B publication Critical patent/CN115305136B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种粘附性能优异的高温链条油及其制备方法，涉及链条油技术领域。本发明的高温链条油是由合成酯类基础油、MDI功能化的二苯胺类环氧大豆油添加剂、硫代酚酯型抗氧剂、抗磨剂以及分散剂为原料制备而成，其中MDI功能化的二苯胺类环氧大豆油添加剂是将4‑氨基二苯胺与环氧大豆油进行反应，然后再与MDI进行反应制备而成。本发明高温链条油不仅抗氧化性能优异，而且可增强其粘附性能，显著改善链条油粘附性差的问题。

Description

一种粘附性能优异的高温链条油及其制备方法
技术领域
本发明属于链条油技术领域，具体涉及一种粘附性能优异的高温链条油及其制备方法。
背景技术
合成酯类高温链条油广泛应用于高温环境下的链条传动，其应用领域主要有高温烤箱、汽车涂装生成线、人造板板材生成线、聚氯乙烯手套生成线等。
目前随着机械设备的大型化、快速化、高温化，对高温链条油在更高温度、更快速度下是否能够提供充足润滑提出了很高的要求。高温下的抗氧化性能直接关乎油品的劣化趋势，如果油品抗氧化性能差，那么在苛刻的高温环境下油品极易挥发产生油烟。挥发的油烟不仅会影响车间环境而且会带来一定的环境污染。
同时，润滑油的粘度会随环境温度的升高逐渐降低。尤其是在高温条件下，润滑油的粘度普遍偏很小，无法提供足够的粘附性能，进而不能保证润滑油膜的稳定性。因此开发一款在高温使用环境下仍具有优异的粘附性能的链条油是目前研究的热点。
发明内容
针对现有技术的不足，本发明提供了一种粘附性能优异的高温链条油及其制备方法。
为实现上述目的，本发明提供了如下技术方案来实现的：
本发明粘附性能优异的高温链条油是由以下质量百分数的原料构成：
82-98％的合成酯类基础油
0.1-10％的MDI功能化的二苯胺类环氧大豆油添加剂
0.1-3％的硫代酚酯型抗氧剂
0.1-3％的抗磨剂
0.1-2％的分散剂；
所述MDI功能化的二苯胺类环氧大豆油添加剂是将4-氨基二苯胺与环氧大豆油进行反应，然后再与MDI进行反应制备而成。
优选的，所述合成酯类基础油为偏苯三酸酯。
优选的，所述MDI为二苯基甲烷二异氰酸酯MDI-100。
进一步优选的，所述MDI功能化的二苯胺类环氧大豆油添加剂的制备方法如下：
将10g环氧大豆油与1.84g 4-氨基二苯胺在80-90℃保温下进行开环反应 3-6h，然后在80-90℃保温下,加入4-氨基二苯胺等摩尔比的MDI进行搅拌反应 2-3h。
优选的，所述硫代酚酯型抗氧剂为硫代二丙酸双十二醇酯、硫代二丙酸双十八酯、2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]中的至少一种。
优选的，所述抗磨剂为磷酸三甲酚酯T306和苯***脂肪酸胺盐T406构成的混合物。
优选的，所述分散剂为聚异丁烯丁二酰亚胺T154。
本发明还提供了所述粘附性能优异的高温链条油的制备方法，具有步骤是按比例将合成酯类基础油、MDI功能化的二苯胺类环氧大豆油添加剂、硫代酚酯型抗氧剂、抗磨剂以及分散剂混合，在75-85℃下搅拌均匀制成所述高温链条油。优选的搅拌温度为80℃。
与现有技术相比，本发明具有以下有益效果：
本发明是利用MDI功能化的二苯胺类环氧大豆油添加剂为原料配制链条油，其结构中含有-NH-的二苯胺结构可提供抗氧化性能，与硫酚型抗氧剂复配抗氧化性能更优，同时含有异氰酸酯和羟基反应后的-N-COO-基团可增强与金属表面的粘附力。因此，本发明的高温链条油不仅抗氧化性能优异，而且可增强其粘附性能，显著改善链条油粘附性差的问题。
具体实施方式
为使本发明的目的、特征和优点能够更加明显易懂，下面结合本发明的具体实施方式做详细的说明。给出了本发明的若干实施例。但是，本发明可以以许多不同的形式来实现，并不限于本文所描述的实施例。相反地，提供这些实施例的目的是使对本发明的公开内容更加透彻全面。
实施例1
一种粘附性能优异的高温链条油，制备方法如下：
(1)、将10g环氧大豆油和1.84g 4-氨基二苯胺混合，85℃搅拌反应4h，然后加入2.51g的MDI，85℃搅拌反应2h，得到MDI功能化的二苯胺类环氧大豆油添加剂。
(2)、将96g的偏苯三酸异癸异十三醇酯、1g的MDI功能化的二苯胺类环氧大豆油添加剂、1g的抗氧剂2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154，80℃混合搅拌60min。
实施例2
一种粘附性能优异的高温链条油，制备方法如下：
(1)、将10g环氧大豆油和1.84g 4-氨基二苯胺混合，85℃搅拌反应4h，然后加入2.51g的MDI，85℃搅拌反应2h，得到MDI功能化的二苯胺类环氧大豆油添加剂。
(2)、将95g的偏苯三酸异癸异十三醇酯、2g的MDI功能化的二苯胺类环氧大豆油添加剂、1g的抗氧剂2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154，80℃混合搅拌60min。
实施例3
一种粘附性能优异的高温链条油，制备方法如下：
(1)、将10g环氧大豆油和1.84g 4-氨基二苯胺混合，85℃搅拌反应4h，然后加入2.51g的MDI，85℃搅拌反应2h，得到MDI功能化的二苯胺类环氧大豆油添加剂。
(2)、将91g的偏苯三酸异癸异十三醇酯、5g的MDI功能化的二苯胺类环氧大豆油添加剂、2g的抗氧剂2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154，80℃混合搅拌60min。
实施例4
一种粘附性能优异的高温链条油，制备方法如下：
(1)、将10g环氧大豆油和1.84g 4-氨基二苯胺混合，85℃搅拌反应4h，然后加入2.51g的MDI，85℃搅拌反应2h，得到MDI功能化的二苯胺类环氧大豆油添加剂。
(2)、将88g的偏苯三酸异癸异十三醇酯、8g的MDI功能化的二苯胺类环氧大豆油添加剂、2g的抗氧剂2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154，80℃混合搅拌60min。
对比例1
一种链条油，制备方法如下：
(1)、将97g的偏苯三酸异癸异十三醇酯、1g的抗氧剂2,2'-硫代双[3-(3,5- 二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154，80℃混合搅拌60min。
对比例2
一种链条油，制备方法如下：
将96g的偏苯三酸异癸异十三醇酯、2g的抗氧剂2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]、1g的抗磨剂T306和0.5g的T406、0.5g的分散剂T154， 80℃混合搅拌60min。
表1实施例1-4与对比例1-2的数据
Figure SMS_1
其中各性能指标的测试方法如下：
运动粘度：GB/T 265石油产品运动粘度测定法
开口闪点：GB/T 3536石油产品闪点和燃点的测定(克利夫兰开口杯法)
抗氧化性能：SH/T 0719润滑油氧化诱导期测定法(压力差示扫描量热法)， (温度，220℃；氮气压力35bar；氧气流量100ml/min)
抗磨性能：SH/T 0189润滑油抗磨性能测定法(四球法)
蒸发损失：烘箱烘烤，(260℃，50g油，2h)
试验结果分析：在220℃温度下，添加MDI功能化的二苯胺类环氧大豆油添加剂的实施例1-4的链条油，PDSC时间明显比对比例1-2的时间长，而且260℃高温蒸发损失明显小于对比例1-2，说明该添加剂与硫酚酯型抗氧剂起到协同作用，增强了链条油组合物的抗氧化性能，延长了使用寿命同时减少了油烟挥发。
另外，实施例1-4随着MDI功能化的二苯胺类环氧大豆油添加剂的增加，抗氧化性能也略有提高，这说明该添加剂本身能够提供一定的抗氧化性能。实施例1-4和对比例1-2的四球磨斑直径均小于0.5mm，表现出非常优异的抗磨性能。
实施例1-4制备的链条油在40℃运输粘度和开口闪点指标性能优异，尤其是对链条的粘附力有所增强，适合于高温环境下链条的润滑。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。

Claims (7)

1.一种粘附性能优异的高温链条油，其特征在于，由以下质量百分数的原料构成：
82-98％的合成酯类基础油
0.1-10％的MDI功能化的二苯胺类环氧大豆油添加剂
0.1-3％的硫代酚酯型抗氧剂
0.1-3％的抗磨剂
0.1-2％的分散剂；
所述MDI功能化的二苯胺类环氧大豆油添加剂是将4-氨基二苯胺与环氧大豆油进行反应，然后再与MDI进行反应制备而成；
所述粘附性能优异的高温链条油的制备方法包括以下步骤：按比例将合成酯类基础油、MDI功能化的二苯胺类环氧大豆油添加剂、硫代酚酯型抗氧剂、抗磨剂以及分散剂混合，在75-85℃下搅拌均匀制成所述高温链条油。
2.根据权利要求1所述粘附性能优异的高温链条油，其特征在于，所述合成酯类基础油为偏苯三酸酯。
3.根据权利要求1所述粘附性能优异的高温链条油，其特征在于，所述MDI为二苯基甲烷二异氰酸酯MDI-100。
4.根据权利要求3所述粘附性能优异的高温链条油，其特征在于，所述MDI功能化的二苯胺类环氧大豆油添加剂的制备方法如下：
将10g 环氧大豆油与1.84g 4-氨基二苯胺在80-90℃保温下进行开环反应3-6h，然后在80-90℃保温下,加入4-氨基二苯胺等摩尔比的MDI进行搅拌反应2-3h。
5.根据权利要求1所述粘附性能优异的高温链条油，其特征在于，所述硫代酚酯型抗氧剂为2,2'-硫代双[3-(3,5-二叔丁基-4-羟基苯基)丙酸乙酯]。
6.根据权利要求1所述粘附性能优异的高温链条油，其特征在于，所述抗磨剂为磷酸三甲酚酯T306和苯***脂肪酸胺盐T406构成的混合物。
7.根据权利要求1所述粘附性能优异的高温链条油，其特征在于，所述分散剂为聚异丁烯丁二酰亚胺T154。
CN202210920787.8A 2022-08-02 2022-08-02 一种粘附性能优异的高温链条油及其制备方法 Active CN115305136B (zh)