CN115304268A - 光学玻璃及由其制成的玻璃预制件、光学元件和光学仪器 - Google Patents
光学玻璃及由其制成的玻璃预制件、光学元件和光学仪器 Download PDFInfo
- Publication number
- CN115304268A CN115304268A CN202210859321.1A CN202210859321A CN115304268A CN 115304268 A CN115304268 A CN 115304268A CN 202210859321 A CN202210859321 A CN 202210859321A CN 115304268 A CN115304268 A CN 115304268A
- Authority
- CN
- China
- Prior art keywords
- glass
- optical
- content
- chemical stability
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种光学玻璃及由该光学玻璃制成的玻璃预制件、光学元件和光学仪器。本发明的光学玻璃的组成按摩尔%表示,含有Si4+:1‑10%、B3+:25‑40%、La3+:20‑40%、Gd3+:0‑15%、Y3+:大于0小于或等于10%、Zr4+:1‑10%、Nb5+:1‑12%、Ti4+:8‑25%,其中(La3++Gd3+)/Y3+为40‑65。本发明设计科学,配方合理,具有优异的化学稳定性,其折射率高,生产成本低。
Description
本申请是针对申请号为201811128324.8,申请日为2018年09月27日,名称为“光学玻璃及由其制成的玻璃预制件、光学元件和光学仪器”的发明专利申请的分案申请。
技术领域
本发明属于玻璃技术领域,具体涉及光学玻璃及由该光学玻璃制成的玻璃预制件、光学元件和光学仪器。
背景技术
光学玻璃的化学稳定性是指光学零件抛光表面在加工、贮存和使用过程中对所接触的各种侵蚀性介质的抗蚀能力。光学玻璃的化学稳定性不佳,会导致光学零件的抗腐蚀能力降低,在光学零件上产生不规则的点状或片状斑痕,从而造成光学仪器的性能和功能不达标,严重影响光学仪器的使用寿命。现有技术中,主要通过调整玻璃中碱金属氧化物的含量以提高其化学稳定性。但采用这种方法所得的光学玻璃又存在折射率低、生产成本高的问题。
因此,提供一种光学玻璃,其具有优异的化学稳定性,且折射率高,生产成本低,成为了本领域技术人员亟待解决的问题。
发明内容
本发明的目的之一在于:提供一种光学玻璃,解决现有技术中光学玻璃化学稳定性不好、折射率低、生产成本高的问题。
本发明的目的之二在于:提供采用光该学玻璃制成的玻璃预制件。
本发明的目的之三在于:提供采用光该学玻璃制成的光学元件。
本发明的目的之四在于:提供包含该光学元件的光学仪器。
为实现上述目的,本发明采用的技术方案如下:
光学玻璃,其组成按摩尔%表示,含有:Si4+:1-10%、B3+:25-40%、La3+:20-40%、Gd3+:0-15%、Y3+:大于0但小于或等于10%、Zr4+:1-10%、Nb5+:1-12%、Ti4+:8-25%,其中(La3++Gd3+)/Y3+为39-65。
进一步地,还含有:Zn2+:0-8%、W6+:0-10%、R2+:0-10%、R+:0-10%,其中R2+为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
光学玻璃,其组成按摩尔%表示为Si4+:1-10%、B3+:25-40%、La3+:20-40%、Gd3+:0-15%、Y3+:大于0但小于或等于10%、Zr4+:1-10%、Nb5+:1-12%、Ti4+:8-25%、Zn2+:0-8%、W6+:0-10%、R2+:0-10%、R+:0-10%,其中(La3++Gd3+)/Y3+为39-65,R2+:为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
进一步地,各组分满足以下6种情形中的一种或一种以上:
1)(La3++Gd3+)/Y3+为40-60;
2)(Si4++B3+)/Y3+为36-69;
3)(Nb5++Ti4++W6+)/Y3+为26-46;
4)Si4+/(La3++Gd3++Y3+)为0.02-0.4;
5)(Si4++Zr4+)/(Nb5++Ti4+)为0.06-2;
6)La3+/(Si4++Zr4+)为1.5-15。
进一步地,其中Si4+:3-9%、和/或B3+:26-35%、和/或La3+:25-35%、和/或Gd3+:0-10%、和/或Y3+:0.1-5%、和/或Zr4+:1-8%、和/或Nb5+:2-10%、和/或Ti4+:10-20%、和/或Zn2+:0.1-5%、和/或W6+:0-5%、和/或R2+:0-5%、和/或R+:0-5%,其中R2+:为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
进一步地,各组分满足以下6种情形中的一种或一种以上:
1)(La3++Gd3+)/Y3+为42-55;
2)(Si4++B3+)/Y3+为40-65;
3)(Nb5++Ti4++W6+)/Y3+为26-40;
4)Si4+/(La3++Gd3++Y3+)为0.05-0.3;
5)(Si4++Zr4+)/(Nb5++Ti4+)为0.08-1;
6)La3+/(Si4++Zr4+)为2-10。
进一步地,其中Si4+:4-8%、和/或B3+:27-32%、和/或La3+:26-33%、和/或Gd3+:1-8%、和/或Y3+:0.3-3%、和/或Zr4+:2-6%、和/或Nb5+:3-8%、和/或Ti4+:14-20%、和/或Zn2 +:1-4%。
进一步地,各组分满足以下5种情形中的一种或一种以上:
1)(Si4++B3+)/Y3+为45-58;
2)(Nb5++Ti4++W6+)/Y3+为28-35;
3)Si4+/(La3++Gd3++Y3+)为0.08-0.21;
4)(Si4++Zr4+)/(Nb5++Ti4+)为0.1-0.52;
5)La3+/(Si4++Zr4+)为2.42-8。
进一步地,不含有W6+和/或R2+和/或R+。
进一步地,所述玻璃的折射率(nd)为1.99-2.01,阿贝数(vd)为28-31。
进一步地,所述玻璃的耐酸作用稳定性(DA)为2类以上,优选为1类;所述玻璃的耐水作用稳定性(DW)为2类以上,优选为1类。
玻璃预制件,由上述光学玻璃制成。
光学元件,由上述光学玻璃制成,或上述玻璃预制件制成。
光学仪器,包含上述的光学元件。
与现有技术相比,本发明具有以下有益效果:
本发明设计科学,配方合理,具有优异的化学稳定性,其折射率高,生产成本低。
本发明创造性地在降低碱金属的含量或不含碱金属的情况下,通过各个组份的优化,以及对(La3++Gd3+)/Y3+比值的优化,获得了化学稳定性优异,折射率为1.99-2.01,阿贝数为28-31的光学玻璃,满足了对光学玻璃化学稳定性以及折射率的高要求。
具体实施方式
在本说明书中,各成分的含量在没有特别说明的情况下,阳离子组分含量以该阳离子占全部阳离子总摩尔的百分比含量表示,阴离子组分含量以该阴离子占全部阴离子总摩尔的百分比含量表示。另外,在以下的说明中,提到规定值以下或规定值以上时也包括该规定值。
需要说明的是,各成分的离子价不过是为了方便而使用的代表值,与其他的离子价没有区别。光学玻璃中存在的各成分的离子价存在为代表值以外的可能性。例如,Si通常以离子价为4价的状态在玻璃中存在,因此在本说明书中以“Si4+”作为代表,但是存在以其他的离子价的状态存在的可能性,同时也在本发明的保护范围之内。
本发明中B3+的氧化物为玻璃网络形成体,是形成玻璃的必要成分,具有维持玻璃稳定性、熔融性、降低液相温度、以及低分散化的作用。本发明中,当B3+含量低于25%,玻璃的析晶稳定性不好;但当B3+含量大于40%时,玻璃的液相温度上升,化学稳定性变差。因此,本发明中其含量范围限制为25-40%,优选为26-35%,进一步优选为27-32%。
本发明中Si4+的氧化物为玻璃网络形成体,适当的引入可提高玻璃的抗析晶性能和高温粘度;当其含量大于10%时,会使玻璃的转变温度升高,并使玻璃的熔融性降低,玻璃的化学稳定性有变差的趋势。因此,本发明中其含量范围限制为1-10%,优选为3-9%,进一步优选为4-8%。
本发明中稀土离子的氧化物作为玻璃的网络外体氧化物,主要填充于玻璃的网络空隙中,使得玻璃的结构更加紧密。本发明中的稀土离子为La3+、Gd3+和Y3+。
本发明中La3+能提高玻璃的化学稳定性、机械强度和折射率,并可降低玻璃的相对部分色散,但当其含量超过40%时,玻璃的抗析晶性能会出现明显恶化,其含量低于20%时,玻璃的化学稳定性下降。因此,本发明中其含量范围限制为20-40%,优选为25-35%,进一步优选为26-33%。
本发明中Gd3+能提高玻璃的折射率,且具有提高玻璃抗析晶性能及化学稳定性的作用。但其原料价格昂贵,且当其含量超过15%时,玻璃耐失透性降低且玻璃的密度呈上升趋势。本发明中Gd3+的含量范围限制为0-15%,优选为0-10%,进一步优选为1-8%。
本发明中Y3+能改善玻璃的熔融性,并提高玻璃的抗析晶性能及化学稳定性。但当其含量超过10%,玻璃的化学稳定性和抗析晶性能下降。因此,本发明中Y3+的含量范围上限为10%,优选为8%,更优选为5%,进一步优选为3%,更进一步优选为1%;Y3+下限含量优选为大于0,更优选为0.1%,进一步优选为0.3%,更进一步优选为0.5%。
本发明人经过大量研究发现,La3+、Gd3+和Y3+共同存在时,具有改善玻璃的抗析晶性能和化学稳定性的作用。尤其是当(La3++Gd3+)/Y3+的值为39-65时,玻璃具有优异的化学稳定性,优选为40-60,更优选当(La3++Gd3+)/Y3+为42-55时,玻璃的耐酸作用稳定性和耐水作用稳定性均可达到2类以上,优选1类。
本发明人研究发现,Si4++B3+的总量与Y3+存在一定比例关系时,有利于获得抗析晶性能优异的玻璃,尤其是当(Si4++B3+)/Y3+的值范围为36-69时,可在获得所需的光学性能的同时,具有优异的抗析晶性能,优选为40-65,进一步优选为45-58,可保证玻璃在生产和压型过程中不易析晶。
本发明同时还发现,Si4+与稀土离子的总量存在一比例关系时,能获得抗析晶性能优异的玻璃。当Si4+/(La3++Gd3++Y3+)的值大于0.4时,其抗析晶性能恶化;当其值小于0.02时,化学稳定性变差。因此,Si4+/(La3++Gd3++Y3+)的比值范围限定为0.02-0.4,优选为0.05-0.3,进一步优选为0.08-0.21。
本发明中,Zn2+具有改善玻璃的熔融性和化学稳定性,抗析晶性能,以及降低玻璃的转变温度的作用。本发明中Zn2+的含量大于8%时,其析晶性能恶化,色散增大,不能满足对折射率的要求。本发明中Zn2+的含量范围限制为0-8%,优选为0.1-5%,进一步优选为1-4%。
本发明中,Zr4+可以起到提高玻璃化学稳定性的作用。当Zr4+的含量为1-10%时,具有适宜的折射率、热膨胀系数,良好的化学稳定性和抗析晶性能。当其含量大于10%时,玻璃的液相温度上升,玻璃透过率下降;当其含量小于1%时,抗析晶性能恶化,不能满足折射率的要求。本发明中Zr4+的含量范围限制为1-10%,优选为1-8%,进一步优选为2-6%。
本发明人经大量研究发现,Si4+、Zr4+的总量与La3+存在一定比例关系时,能明显提升玻璃的化学稳定性。当La3+/(Si4++Zr4+)的值低于1.5时,玻璃的化学稳定性变差;当其值高于15时,抗析晶性能恶化,不能满足折射率的要求。本发明中,La3+/(Si4++Zr4+)的值优选为2-10,更优选为2.42-8。
本发明中Nb5+具有提高玻璃折射率、增加色散的作用,同时还具有提高玻璃化学稳定性的作用。当其含量高于12%时,玻璃可见光区域的短波部分的透射率降低,玻璃着色明显;其含量小于1%时,不能满足对折射率的要求,其化学稳定性能也下降。本发明中Nb5+的含量范围限制为1-12%,优选含量范围为2-10%,再优选范围为3-8%。
本发明中Ti4+能参与玻璃网络形成,并具有提高玻璃折射率以及化学稳定性的作用。本发明中,Ti4+含量为8-25%时,玻璃具有良好的化学稳定性,并能提升折射率。当其含量大于25%时,玻璃可见光区域的短波部分的透射率降低,玻璃着色明显;其含量小于8%时,不能满足对折射率的要求,其化学稳定性能也下降。本发明中Ti4+的含量范围限制为8-25%,优选含量范围为10-20%,再优选范围为14-20%。
本发明人经大量研究发现,Si4+、Zr4+的总量与Nb5+、Ti4+的总量存在一定比例关系时,会影响玻璃的成玻稳定性和抗析晶性能。通过进一步研究发现,当(Si4++Zr4+)/(Nb5++Ti4+)的比值范围限定为0.06-2时,玻璃的成玻稳定性和抗析晶性能优异,优选(Si4++Zr4+)/(Nb5++Ti4+)为0.08-1,进一步优选为0.1-0.52。
本发明中,W6+具有提高玻璃折射率的作用,但当其含量大于10%时,玻璃的化学稳定性、透过率和抗析晶性能均变差。因此,其含量范围限制为0-10%,优选为0-5%,进一步优选为不含有。
本发明人经大量实验研究发现,Nb5+、Ti4+及W6+的总量与Y3+存在一定比例关系时,玻璃具有优异的抗析晶性能。当(Nb5++Ti4++W6+)/Y3+的值小于26时,其抗析晶性能恶化,当其值大于46时,其化学稳定性恶化。因此,其比值范围限制为26-46,优选为26-40,进一步优选为28-35。
本发明中,Li+能增加玻璃熔融性,降低转变温度,当其含量超过10%时,玻璃的折射率达不到设计要求,故将其上限控制在10%。
本发明中Na+、K+都具有提高玻璃的熔融性的作用。本发明中,Na+、K+的含量大于10%时,玻璃的折射率达不到要求,因此Na+、K+的含量分别限定为10%以下。
本发明中的Li+、Na+、K+均为碱金属离子,可以调整玻璃的光学数据,提高玻璃的熔融效果,使玻璃具有较低的转变温度。当其总量Li++Na++K+的值小于10%时,玻璃具有良好的化学稳定性,并能满足折射率的要求。当其值大于10%时,玻璃的抗析晶性能恶化。因此,Li++Na++K+的值的范围限定为0-10%,优选为0-5%,进一步优选为不含有。
本发明中,Ba2+具有提高玻璃折射率,改善玻璃透过率的作用,但当其含量大于10%时,玻璃的化学稳定性和抗析晶性能均变差。因此,其含量范围限制为0-10%,优选为0-5%,进一步优选为不含有。
本发明中,Sr2+能有效调节玻璃的折射率和阿贝数,但其原料成本较高,且当其含量大于于10%时,玻璃的化学稳定性和抗析晶性能均变差。因此,其含量范围限制为0-10%,优选为0-5%,进一步优选为不含有。
本发明中,Ca2+能降低玻璃的阿贝数和比重,但当其含量大于10%时,玻璃的抗析晶性能变差。因此,其含量范围限制为0-10%,优选为0-5%,进一步优选为不含有。
本发明中,Mg2+能提升玻璃的化学稳定性,但当其含量过大时,玻璃的折射率不能满足要求,且析晶性能及化学稳定性会下降。因此,其含量范围限制为0-10%,优选为0-5%,进一步优选为不含有。
本发明中,Ba2+、Sr2+、Ca2+、Mg2+均为碱土金属离子,能调整玻璃的折射率,降低玻璃的高温粘度。当Ba2+、Sr2+、Ca2+、Mg2+的总量,即(Ba2++Sr2++Ca2++Mg2+)的值大于10%时,玻璃的化学稳定性和抗性晶性能明显变差。因此,将(Ba2++Sr2++Ca2++Mg2+)的值限定为0-10%,优选为0-5%,进一步优选为不含有。
本发明中所含主要阴离子为O2-,在不影响本发明光学玻璃的性能的情况下,可在一定程度上含有如F-、Cl-等其他阴离子,本发明光学玻璃中O2-含量为95%以上,优选为98%以上,更优选为100%。
本发明的光学玻璃折射率(nd)的范围为1.99-2.01;本发明玻璃的阿贝数(vd)的范围为28-31,优选范围为28-30。
本发明中玻璃的抗析晶性能测试方法为:将样品玻璃切割为20×20×10mm规格,放入温度为Tg+230℃温度的马弗炉中保温预设30分钟,取出后放入保温棉中徐冷,冷却后观察表面析晶情况。
本发明中玻璃的化学稳定性通过耐水作用稳定性Dw和耐酸作用稳定性DA表示。本发明中玻璃的耐水作用稳定性Dw为2类以上,优选为1类;耐酸作用稳定性DA为2类以上,优选为1类。
下面结合实施例对本发明作进一步说明,本发明的方式包括但不仅限于以下实施例。
实施例1
本实施例提供了本发明的光学玻璃的制备方法。使用碳酸盐、硝酸盐、氢氧化物、氧化物、硼酸等作为原料,将光学玻璃成分所对应的原料按比例称量各原料,充分混合后成为调合原料,将该调合原料放入到铂制坩埚内,加热至1250~1450℃,并澄清搅拌3~5小时后成为均匀的熔融玻璃,再将该熔融玻璃浇注到预热的模中并在600~700℃保持2~4小时之后进行缓冷,得到玻璃No.1~33的各光学玻璃。
实施例2
本实施例提供了本发明的光学玻璃的性能测试方法,具体为:
折射率(nd)参照GB/T7962.1-2010规定的方法进行测试;
阿贝数(vd)参照GB/T7962.1-2010规定的方法进行测试;
玻璃的抗析晶性能测试方法为:将样品玻璃切割为20×20×10mm规格,放入温度为Tg+230℃温度的马弗炉中保温预设30分钟,取出后放入保温棉中徐冷,冷却后观察表面析晶情况。无明显析晶记做“A”,有明显析晶记为“B”。
耐水作用稳定性Dw的测试方法参照GB/T17129规定的方法进行测试;
耐酸作用稳定性DA的测试方法参照GB/T17129规定的方法进行测试。
实施例3
本实施例提供了本发明的光学玻璃的组成及性能,具体见下表:
表1.
表2.
表3.
组分(mol%) | 17 | 18 | 19 | 20 | 21 | 22 | 23 | 24 |
Si<sup>4+</sup> | 9.77 | 9.66 | 9.61 | 9.44 | 9.16 | 3.89 | 4.00 | 1.00 |
B<sup>3+</sup> | 22.0 | 22.14 | 21.94 | 20.85 | 23.44 | 30.24 | 25.90 | 27.00 |
La<sup>3+</sup> | 29.55 | 28.95 | 29.15 | 29.85 | 34.89 | 32.11 | 25.00 | 21.34 |
Gd<sup>3+</sup> | 1.01 | 1.22 | 1.22 | 1.75 | 0.78 | 5.11 | 0.00 | 5.96 |
Y<sup>3+</sup> | 0.70 | 0.70 | 0.75 | 0.67 | 0.65 | 0.94 | 0.46 | 0.42 |
Zn<sup>2+</sup> | 8.0 | 7.94 | 7.94 | 8.0 | 5.39 | 0.0 | 1.00 | 8.00 |
Zr<sup>4+</sup> | 10.0 | 9.67 | 9.67 | 9.87 | 7.44 | 1.26 | 8.00 | 1.00 |
Nb<sup>5+</sup> | 7.91 | 7.69 | 7.72 | 6.99 | 6.48 | 8.53 | 1.00 | 2.00 |
Ti<sup>4+</sup> | 11.06 | 12.03 | 12.0 | 12.58 | 11.77 | 17.92 | 20.00 | 14.00 |
W<sup>6+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Ba<sup>2+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 10 | 0 |
Sr<sup>2+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Ca<sup>2+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
Mg<sup>2+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 9.28 |
Li<sup>+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 2.01 | 10 |
Na<sup>+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 2.63 | 0 |
K<sup>+</sup> | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
合计 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 | 100.00 |
(La<sup>3+</sup>+Gd<sup>3+</sup>)/Y<sup>3+</sup> | 43.66 | 43.10 | 40.49 | 47.16 | 54.88 | 39.60 | 54.35 | 65.00 |
(Si<sup>4+</sup>+B<sup>3+</sup>)/Y<sup>3+</sup> | 45.39 | 45.43 | 42.07 | 45.21 | 50.15 | 36.31 | 65.00 | 66.67 |
(Nb<sup>5+</sup>+Ti<sup>4+</sup>+W<sup>6+</sup>)/Y<sup>3+</sup> | 27.10 | 28.17 | 26.29 | 29.21 | 28.08 | 28.14 | 45.65 | 38.10 |
Si<sup>4+</sup>/(La<sup>3+</sup>+Gd<sup>3+</sup>+Y<sup>3+</sup>) | 0.31 | 0.31 | 0.31 | 0.29 | 0.25 | 0.10 | 0.16 | 0.04 |
(Si<sup>4+</sup>+Zr<sup>4+</sup>)/(Nb<sup>5+</sup>+Ti<sup>4+</sup>) | 1.04 | 0.98 | 0.98 | 0.99 | 0.91 | 0.19 | 0.57 | 0.13 |
La<sup>3+</sup>/(Si<sup>4+</sup>+Zr<sup>4+</sup>) | 1.49 | 1.50 | 1.51 | 1.55 | 2.10 | 6.23 | 2.08 | 10.67 |
n<sub>d</sub> | 2.0044 | 2.0035 | 2.0007 | 2.0033 | 2.0015 | 2.0001 | 1.9965 | 1.9971 |
v<sub>d</sub> | 29.18 | 29.23 | 29.28 | 29.41 | 29.22 | 28.33 | 29.26 | 30.53 |
抗析晶性能 | A | A | A | A | A | A | A | A |
耐水稳定性(D<sub>W</sub>) | 1类 | 1类 | 2类 | 1类 | 1类 | 1类 | 1类 | 2类 |
耐酸稳定性(D<sub>A</sub>) | 1类 | 1类 | 2类 | 1类 | 1类 | 2类 | 1类 | 1类 |
表4.
实施例4
本实施例提供了采用本发明的光学玻璃制备玻璃预制件的方法。将表1-4中所得到的光学玻璃切割成预定大小,再在表面上均匀地涂布由氮化硼粉末构成的脱模剂,然后将其加热、软化,进行加压成型,制作凹弯月形透镜、凸弯月形透镜、双凸透镜、双凹透镜、平凸透镜、平凹透镜等各种透镜、棱镜的预制件。
实施例5
本实施例提供了采用本发明的玻璃预制件制备光学元件的方法。
将按实施例4方法制得的玻璃预制件退火,在降低玻璃内部的变形的同时进行微调,使得折射率等光学特性达到所需值。接着,对各预制件进行磨削、研磨,制作凹弯月形透镜、凸弯月形透镜、双凸透镜、双凹透镜、平凸透镜、平凹透镜等各种透镜、棱镜。所得光学元件的表面上还可涂布防反射膜。
实施例6
光学仪器实施例
将上述光学元件实施例制得的光学元件通过光学设计,通过使用一个或多个光学元件形成光学部件或光学组件,可用于例如成像设备、传感器、显微镜、医药技术、数字投影、通信、光学通信技术/信息传输、汽车领域中的光学/照明、光刻技术、准分子激光器、晶片、计算机芯片以及包括这样的电路及芯片的集成电路和电子器件。
上述实施例仅为本发明的优选实施方式之一,不应当用于限制本发明的保护范围,但凡在本发明的主体设计思想和精神上作出的毫无实质意义的改动或润色,其所解决的技术问题仍然与本发明一致的,均应当包含在本发明的保护范围之内。
Claims (10)
1.光学玻璃,其特征在于,其组成按摩尔%表示,含有:Si4+:1-10%、B3+:25-40%、La3+:20-40%、Gd3+:0-15%、Y3+:大于0但小于或等于10%、Zr4+:1-10%、Nb5+:1-12%、Ti4+:8-25%,其中(La3++Gd3+)/Y3+为40-65。
2.根据权利要求1所述的光学玻璃,其特征在于,还含有:Zn2+:0-8%、W6+:0-10%、R2+:0-10%、R+:0-10%,其中R2+为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
3.光学玻璃,其特征在于,其组成按摩尔%表示为Si4+:1-10%、B3+:25-40%、La3+:20-40%、Gd3+:0-15%、Y3+:大于0但小于或等于10%、Zr4+:1-10%、Nb5+:1-12%、Ti4+:8-25%、Zn2+:0-8%、W6+:0-10%、R2+:0-10%、R+:0-10%,其中(La3++Gd3+)/Y3+为40-65,R2+:为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
4.根据权利要求1-3任一所述的光学玻璃,其特征在于,各组分满足以下6种情形中的一种以上:
1)(La3++Gd3+)/Y3+为40-60,优选(La3++Gd3+)/Y3+为42-55;
2)(Si4++B3+)/Y3+为36-69,优选(Si4++B3+)/Y3+为40-65,更优选(Si4++B3+)/Y3+为45-58;
3)(Nb5++Ti4++W6+)/Y3+为26-46,优选(Nb5++Ti4++W6+)/Y3+为26-40,更优选(Nb5++Ti4++W6 +)/Y3+为28-35;
4)Si4+/(La3++Gd3++Y3+)为0.02-0.4,优选Si4+/(La3++Gd3++Y3+)为0.05-0.3,更优选Si4+/(La3++Gd3++Y3+)为0.08-0.21;
5)(Si4++Zr4+)/(Nb5++Ti4+)为0.06-2,优选(Si4++Zr4+)/(Nb5++Ti4+)为0.08-1,更优选(Si4++Zr4+)/(Nb5++Ti4+)为0.1-0.52;
6)La3+/(Si4++Zr4+)为1.5-15,优选La3+/(Si4++Zr4+)为2-10,更优选La3+/(Si4++Zr4+)为2.42-8。
5.根据权利要求1-3任一所述的光学玻璃,其特征在于,其中Si4+:3-9%,优选Si4+:4-8%、和/或B3+:26-35%,优选B3+:27-32%、和/或La3+:25-35%,优选La3+:26-33%、和/或Gd3 +:0-10%,优选Gd3+:1-8%、和/或Y3+:0.1-5%,优选Y3+:0.3-3%、和/或Zr4+:1-8%,优选Zr4 +:2-6%、和/或Nb5+:2-10%,优选Nb5+:3-8%、和/或Ti4+:10-20%,优选Ti4+:14-20%、和/或Zn2+:0.1-5%,优选Zn2+:1-4%、和/或W6+:0-5%,优选不含有W6+、和/或R2+:0-5%,优选不含有R2+、和/或R+:0-5%,优选不含有R+,其中R2+:为Ba2+、Sr2+、Ca2+、Mg2+中的一种或多种,R+为Li+、Na+、K+中的一种或多种。
6.根据权利要求1-3任一所述的光学玻璃,其特征在于,所述玻璃的折射率nd为1.99-2.01,阿贝数vd为28-31。
7.根据权利要求1-3任一所述的光学玻璃,其特征在于,所述玻璃的耐酸作用稳定性DA为2类以上,优选为1类;所述玻璃的耐水作用稳定性DW为2类以上,优选为1类。
8.玻璃预制件,其特征在于,由权利要求1-7任意一项所述的光学玻璃制成。
9.光学元件,其特征在于,由权利要求1-7任意一项所述的光学玻璃制成,或权利要求8所述的玻璃预制件制成。
10.光学仪器,其特征在于,包含权利要求9所述的光学元件。