CN115232941B - 一种减少高碳线材低温脆断及马氏体的方法 - Google Patents
一种减少高碳线材低温脆断及马氏体的方法 Download PDFInfo
- Publication number
- CN115232941B CN115232941B CN202210876324.6A CN202210876324A CN115232941B CN 115232941 B CN115232941 B CN 115232941B CN 202210876324 A CN202210876324 A CN 202210876324A CN 115232941 B CN115232941 B CN 115232941B
- Authority
- CN
- China
- Prior art keywords
- cooling line
- air cooling
- martensite
- sections
- outlet end
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种减少高碳线材低温脆断及马氏体的方法，当10℃＜环境温度≤15℃时，关闭风冷线出口端的两段的保温罩；当5℃＜环境温度≤10℃时，关闭风冷线出口端的两段的保温罩，将风冷线出口端的5台风机风量降低至设定风量的95%；当环境温度≤5℃时，关闭风冷线出口端的两段的保温罩，将风冷线出口端的5台风机风量降低至设定风量的90%。本发明通过监测实时环境温度变化、在***中维护风冷线工艺和设定风量，将风冷线工艺与实时环境温度匹配，避免冬季高碳线材在风冷线冷却过快，减少产生马氏体、脆断现象，以82B系列为例，2级以上马氏体检出率从10%减少到2%以下，脆断现象从0.1%减少到0.01%以下。
Description
技术领域
本发明属于高线生产技术领域，具体涉及一种减少高碳线材低温脆断及马氏体的方法。
背景技术
冬季等环境温度较低的情况下，高碳线材发生马氏体增加、脆断是较为普遍的现象，尤其是大规格77B/82B高碳加Mn加Cr盘条，在冬季气温低于10℃、气温波动大的情况下，为保证盘条的冷却，风冷线风机风量开启较大，但冬季气温较低时，容易产生马氏体并增加盘条内部应力，产生脆断。
由于现有的生产工艺采用固定参数，难以与环境温度的实时变化匹配，因此需要一种能够针对低温环境减少脆断和马氏体的方法。
发明内容
解决的技术问题：针对上述技术问题，本发明提供了一种减少高碳线材低温脆断及马氏体的方法，通过将环境温度与风冷线的风机风量、保温罩开合等工艺参数连锁，可以有效避免高碳线材冷却过快，减少脆断和马氏体现象的产生。
技术方案：一种减少高碳线材低温脆断及马氏体的方法，包括步骤如下：当10℃＜环境温度≤15℃时，关闭风冷线出口端的两段的保温罩；当5℃＜环境温度≤10℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的95%；当环境温度≤5℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的90%。
优选的，所述风冷线依次设有入口段、1-10段、出口段共12段辊道。
优选的，所述风冷线的1-7段每段设有2台风机。
优选的，所述风冷线的1-9段每段设有2只保温罩。
优选的，所述风机的设定风量为19.5万m3/h。
有益效果：本发明通过将环境温度与高碳线材风冷线风机风量、保温罩开合等关键工艺参数联锁，根据环境温度的实时变化，调整高碳线材的风冷线风机风量、保温罩的关闭，确保风冷线工艺与实时环境温度匹配，避免冬季高碳线材在风冷线冷却过快，减少产生马氏体、脆断现象，以82B系列为例，2级以上马氏体检出率从10%减少到2%以下，脆断现象从0.1%减少到0.01%以下。
具体实施方式
下面结合具体实施例对本发明作进一步描述。
实施例1
一种减少高碳线材低温脆断及马氏体的方法，包括步骤如下：当10℃＜环境温度≤15℃时，关闭风冷线出口端的两段的保温罩；当5℃＜环境温度≤10℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的95%；当环境温度≤5℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的90%。
其中，所述风冷线设有12段辊道，依次为入口端的入口段辊道、1-10段辊道和出口端的出口段辊道；第1-7段每段设有2台风机，第1-9段每段设有2只保温罩。风机的设定风量为26万或19.5万m3/h。
本发明通过***监测环境温度变化，维护不同环境温度对应的最佳风冷线风机风量和保温罩开关状态，实现了环境温度与风冷线工艺连锁，可以根据环境温度自动切换工艺。利用本发明所述方法以来，以82B系列为例，2级以上马氏体检出率从10%减少到2%以下，脆断现象从0.1%减少到0.01%以下，极大地减少了高碳线材的低温脆断和马氏体现象，提高了产品质量。
Claims (5)
1.一种减少高碳线材低温脆断及马氏体的方法，其特征在于，包括步骤如下：当10℃＜环境温度≤15℃时，关闭风冷线出口端的两段的保温罩；当5℃＜环境温度≤10℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的95%；当环境温度≤5℃时，关闭风冷线出口端的两段的保温罩，并将风冷线出口端的5台风机风量降低至设定风量的90%。
2.根据权利要求1所述的一种减少高碳线材低温脆断及马氏体的方法，其特征在于，所述风冷线依次设有入口段、1-10段、出口段共12段辊道。
3.根据权利要求2所述的一种减少高碳线材低温脆断及马氏体的方法，其特征在于，所述风冷线的1-7段每段设有2台风机。
4.根据权利要求2所述的一种减少高碳线材低温脆断及马氏体的方法，其特征在于，所述风冷线的1-9段每段设有2只保温罩。
5.根据权利要求1所述的一种减少高碳线材低温脆断及马氏体的方法，其特征在于，所述风机的设定风量为19.5万m3/h。