CN115141352B - 一种电疗肩托及其应用 - Google Patents

一种电疗肩托及其应用 Download PDF

Info

Publication number
CN115141352B
CN115141352B CN202110886554.6A CN202110886554A CN115141352B CN 115141352 B CN115141352 B CN 115141352B CN 202110886554 A CN202110886554 A CN 202110886554A CN 115141352 B CN115141352 B CN 115141352B
Authority
CN
China
Prior art keywords
parts
electrotherapy
shoulder rest
polyol
polyhydroxy compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110886554.6A
Other languages
English (en)
Other versions
CN115141352A (zh
Inventor
陈文�
林刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongkang Home Medical Technology Wuhan Co ltd
Original Assignee
Zhongkang Home Medical Technology Wuhan Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongkang Home Medical Technology Wuhan Co ltd filed Critical Zhongkang Home Medical Technology Wuhan Co ltd
Priority to CN202110886554.6A priority Critical patent/CN115141352B/zh
Publication of CN115141352A publication Critical patent/CN115141352A/zh
Application granted granted Critical
Publication of CN115141352B publication Critical patent/CN115141352B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及A61F5/042，具体涉及一种电疗肩托及其应用。包括肩托本体和电疗按摩器，所述肩托本体为记忆海绵，所述记忆海绵原料包括：按重量份计，多羟基化合物90‑120份，芳香族异氰酸酯45‑80份，催化剂0.2‑0.5份，壳聚糖2‑5份，表面活性剂2.5‑4份，小分子醇2‑5份，交联剂0.5‑2份，水3‑7份。本发明提供的一种电疗肩托及其应用力学性能优异，慢回弹性好，温度敏感度低。

Description

一种电疗肩托及其应用
技术领域
本发明涉及A61F5/042，具体涉及一种电疗肩托及其应用。
背景技术
康复医疗一直是现代医学的重要组成部分，随着国外康复医疗发展经验的不断影响，国内政策的不断完善和开放，康复医疗的新模式、新技术层出不穷。康复医疗产业的市场价值和市场空间也在不断增长。为了更好的回归社会，重返工作，出来药物治疗外，医疗康复逐渐进入人们的视线。目前我国的康复医疗发展有限，医疗康复设备短缺，关于医疗康复设备研究较少。
尤其是近几年来社会内卷严重，人们的生活压力增大，长时间的伏案工作，驾车以及生活中一些不好的生活习惯等导致颈椎病，肩周炎等“中老年疾病低龄化”，发病率不断增加。
发明内容
为了解决上述技术问题，本发明的第一个方面提供了一种电疗肩托，包括肩托本体和电疗按摩器，所述肩托本体为记忆海绵，所述记忆海绵原料包括：按重量份计，多羟基化合物90-120份，芳香族异氰酸酯45-80份，催化剂0.2-0.5份，壳聚糖2-5份，表面活性剂2.5-4份，小分子醇2-5份，交联剂0.5-2份，水3-7份。
多羟基化合物
优选的，所述多羟基化合物包括第一多羟基化合物，第二多羟基化合物，第三多羟基化合物。所述第一多羟基化合物，第二多羟基化合物，第三多羟基化合物的质量比为(7-10)：(1-3)：(1-3)。
优选的，所述多羟基化合物的官能度为2-4。
优选的，所述多羟基化合物的聚醚多元醇和/或聚酯多元醇。
第一多羟基化合物
优选的，所述第一多羟基化合物平均分子量为2500-3500，羟基值为50-65。
进一步优选的，所述第一多羟基化合物的在25℃时的粘度为600-750mPa·s。
更进一步优选的，所述第一多羟基化合物为聚醚多元醇，官能度为2。
第二多羟基化合物
优选的，所述第二多羟基化合物平均分子量为400-500，羟基值为350-430。
通常情况下记忆海绵含有的多羟基化合物的平均分子量在1000-3500之间，本发明意外研究发现当平均分子量为400-500的第二多羟基化合物与体系内其他物质进行复配，能显著提高体系的交联密度，有利于延长回弹时间。同时促使电疗肩托在更宽的温度范围(0-40℃)内保持优异的使用性能。
进一步优选的，所述第二多羟基化合物在25℃时的粘度为300-400mPa·s。
更进一步优选的，所述第二多羟基化合物为聚醚多元醇，官能度为3。
第三多羟基化合物
优选的，所述第三多羟基化合物平均分子量为1500-2500，羟基值为50-60。
进一步优选的，所述第三多羟基化合物为聚酯多元醇，官能度为2。
本发明意外研究发现，壳聚糖的加入促使制备得到的电疗肩托具有更好的抗菌性能，并且能够降低泡沫孔径。但是壳聚糖会导致拉伸强度和断裂伸长率降低。通过多羟基化合物之间的相互配合，交联密度高，弹性模量好，有效改善了表观密度，孔隙之间相互贯通，形成稳定的三维网络结构。
芳香族异氰酸酯
优选的，所述芳香族异氰酸酯包括甲苯二异氰酸酯，二苯二甲烷二异氰酸酯，1,5-萘二异氰酸酯，多亚甲基多苯基多异氰酸酯的至少一种。
优选的，所述芳香族异氰酸酯中异氰酸酯含量为30-35％，在25℃下的粘度为10-15mPa·s。
优选的，所述二苯二甲烷二异氰酸酯包括4,4-MDI和2,4-MDI。
催化剂
优选的，所述催化剂包括三乙烯二胺，四甲基丁二胺，三亚乙基二胺，二月桂酸二丁基锡，辛酸亚锡的至少一种。
为了进一步提高压陷硬度和力学性能，进一步优选的，所述催化剂包括三乙烯二胺和辛酸亚锡。所述三乙烯二胺和辛酸亚锡的质量比为(2-4)：(1-2)。当三乙烯二胺用量过大时，发泡反应过于剧烈，形成的泡孔的泡壁强度不够，容易导致电疗肩托在使用过程中发生压陷。
壳聚糖
为了进一步提升电疗肩托的抗菌性能和回弹性，优选的，所述壳聚糖的平均粒径50-100目，脱乙酰度≥85％。壳聚糖本身具有一定的抗菌性，应用于本体系可以显著提高电疗肩托的抑菌能力，同时与体系的聚合物之间形成了氢键作用，改善了泡孔孔径和表观密度。
表面活性剂
优选的，所述表面活性剂包括第一表面活性剂和第二表面活性剂。所述第一表面活性剂和第二表面活性剂的重量比为(5-8)：(3-5)。
优选的，所述第一表面活性剂在25℃时的粘度为80-120cst。
优选的，所述第二表面活性剂在40℃时的粘度为650-800mPa·s。
本发明研究发现在此条件下，能显著降低发泡过程中的表面张力，改善泡沫密度，使得发泡均匀，还能促使泡孔破裂从而得到开孔结构，防止泡沫收缩。
小分子醇
优选的，所述小分子醇包括乙二醇，丁二醇，二乙二醇，己二醇的至少一种。
交联剂
优选的，所述交联剂为二甲硫基甲苯二胺。
一种记忆海绵的制备方法，包括以下步骤：按配方称取各原料，依次加入多羟基化合物，催化剂，表面活性剂，水，小分子醇，壳聚糖，交联剂，并在添加过程中不停搅拌，全部搅拌均匀后加入芳香族异氰酸酯，继续搅拌40-70s，倒入膜具，经发泡，固化，脱模干燥即得记忆海绵。
一种记忆海绵的制备方法，包括以下步骤：将多羟基化合物在100℃条件下真空脱水，冷却降温后，加入芳香族异氰酸酯，催化剂升温至80℃，反应2h，停止反应，然后迅速加入壳聚糖，表面活性剂，小分子醇，交联剂，水搅拌均匀，浇注于模具中，熟化12h，室温放置6h后即得记忆海绵。
一种电疗肩托的制备方法，包括以下步骤：将电疗按摩器放入肩托本体内即得。
本发明的第二个方面提供了一种电疗肩托在医疗康复技术领域的应用。
有益效果：
1)本发明提供的一种电疗肩托及其应用抗菌性能好，力学性能优异，慢回弹性好。
2)本发明提供的一种电疗肩托及其应用温度敏感度低，在0-40℃内都能保持较好使用性能，适用范围广。
3)本发明提供的一种电疗肩托及其应用热稳定性好，抗疲劳性能好，耐久性好，制备简单，价格低廉，适合大规模生产。
具体实施方式
下面通过实施例对本发明进行具体描述。有必要在此指出的是，以下实施例只用于对本发明作进一步说明，不能理解为对本发明保护范围的限制，该领域的专业技术人员根据上述本发明的内容做出的一些非本质的改进和调整，仍属于本发明的保护范围。
另外，如果没有其它说明，所用原料都是市售得到的。
实施例
实施例1
一种电疗肩托，包括肩托本体和电疗按摩器，所述肩托本体为记忆海绵，所述记忆海绵原料包括：按重量份计，多羟基化合物105份，芳香族异氰酸酯65份，催化剂0.45份，壳聚糖3份，表面活性剂3份，小分子醇3份，交联剂1份，水5份。
所述多羟基化合物包括第一多羟基化合物，第二多羟基化合物，第三多羟基化合物。所述第一多羟基化合物，第二多羟基化合物，第三多羟基化合物的质量比为9：2：2。
所述第一多羟基化合物为聚醚多元醇，官能度为2，平均分子量为3000，羟基值为37，在25℃时水的粘度为674mPa·s，牌号：VORANOL 3000LM。所述第二多羟基化合物为聚醚多元醇，官能度为3，平均分子量为450，羟基值为383，在25℃时水的粘度为330mPa·s，牌号：VORANOL CP450。所述第一多羟基化合物和第二多羟基化合物均购自凯茵化工。所述第三多羟基化合物为聚酯多元醇，官能度为2，平均分子量为2000，羟基值为54-58，牌号：P-2420TL。购自日胜化工股份有限公司。
所述芳香族异氰酸酯为二苯二甲烷二异氰酸酯。所述二苯二甲烷二异氰酸酯中包括4,4-MDI和2,4-MDI，异氰酸酯含量为33.5％，在25℃下的粘度为12mPa·s，牌号：Lupranate MI，购自凯茵化工。
所述催化剂包括三乙烯二胺和辛酸亚锡。所述三乙烯二胺和辛酸亚锡的质量比为3.5：1.5。
所述壳聚糖的平均粒径80目，脱乙酰度90％，购自山东奥康生物科技有限公司。
所述表面活性剂包括第一表面活性剂和第二表面活性剂。所述第一表面活性剂和第二表面活性剂的重量比为7：4。所述第一表面活性剂在25℃时的粘度为100cst。所述第一表面活性剂为有机硅表面活性剂，牌号：L-580，购自凯茵化工。所述第二表面活性剂在40℃时的粘度为650-800mPa·s。所述第二表面活性剂为聚醚多元醇表面活性剂，牌号：YUKOL1900。购自上海晔兴实业有限公司。
所述小分子醇为乙二醇。
所述交联剂为二甲硫基甲苯二胺，牌号：Ethacure300，购自张家港雅瑞化工有限公司。
一种记忆海绵的制备方法，包括以下步骤：将多羟基化合物在100℃条件下真空脱水，冷却降温后，加入芳香族异氰酸酯，催化剂升温至80℃，反应2h，停止反应，然后迅速加入壳聚糖，表面活性剂，小分子醇，交联剂，水搅拌均匀，浇注于模具中，熟化12h，室温放置6h后即得记忆海绵。
一种电疗肩托的制备方法，包括以下步骤：将电疗按摩器放入肩托本体内即得。
实施例2
一种电疗肩托具体实施方式同实施例1不同之处在于所述三乙烯二胺和辛酸亚锡的质量比为2：1。
实施例3
一种电疗肩托具体实施方式同实施例1不同之处在于所述记忆海绵原料包括：按重量份计，多羟基化合物90份，芳香族异氰酸酯45份，催化剂0.2份，壳聚糖2份，表面活性剂2.5份，小分子醇2份，交联剂0.5份，水3份。
实施例4
一种电疗肩托具体实施方式同实施例1不同之处在于所述第一表面活性剂和第二表面活性剂的重量比为7：1。
对比例1
一种电疗肩托具体实施方式同实施例1不同之处在于所述第一多羟基化合物，第二多羟基化合物，第三多羟基化合物的质量比为5：2：2。
对比例2
一种电疗肩托具体实施方式同实施例1不同之处在于所述第二多羟基化合物为聚醚多元醇，官能度为3，平均分子量为1000，羟基值为156，在25℃时水的粘度为220mPa·s，牌号：VORANOL SD301，购自凯茵化工。
性能测试
1.力学性能测试：按照GB/T 6344进行拉伸强度和拉断伸长率测试。
2.回弹率时间测试：采用100mm*100mm*100mm的试样，用电子万能试验机将记忆海绵压缩至原厚度的95％，力值清零，设为起始点。用500mm/min的速度压缩至原厚度的50％，然后压头迅速返回起点(1000mm/min)，根据测量的负荷时间曲线计算回弹时间。
表1 性能测试结果
以上所述，仅是本发明的较佳实施例而已，并非是对发明作其他形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或更改为等同变化的等效实施例，但是凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改，等同变化与改型，仍属于本发明技术方案的保护范围。

Claims (5)

1.一种电疗肩托，其特征在于，包括肩托本体和电疗按摩器，其特征在于，所述肩托本体为记忆海绵，所述记忆海绵原料包括：按重量份计，多羟基化合物90-120份，芳香族异氰酸酯45-80份，催化剂0.2-0.5份，壳聚糖2-5份，表面活性剂2.5-4份，小分子醇2-5份，交联剂0.5-2份，水3-7份；
所述多羟基化合物包括第一多羟基化合物，第二多羟基化合物，第三多羟基化合物；所述第一多羟基化合物，第二多羟基化合物，第三多羟基化合物的质量比为(7-10)：(1-3)：(1-3)；
所述第一多羟基化合物为聚醚多元醇，官能度为2，平均分子量为3000，羟基值为37，在25℃时水的粘度为674mPa•s；
所述第二多羟基化合物为聚醚多元醇，官能度为3，平均分子量为450，羟基值为383；
所述第三多羟基化合物为聚酯多元醇，官能度为2，平均分子量为2000，羟基值为54-58。
2.根据权利要求1所述的一种电疗肩托，其特征在于，所述芳香族异氰酸酯包括甲苯二异氰酸酯，二苯二甲烷二异氰酸酯，1,5-萘二异氰酸酯，多亚甲基多苯基多异氰酸酯的至少一种。
3.根据权利要求2所述的一种电疗肩托，其特征在于，所述芳香族异氰酸酯中异氰酸酯含量为30-35%，在25℃下的粘度为10-15mPa•s。
4.根据权利要求1所述的一种电疗肩托，其特征在于，所述催化剂包括三乙烯二胺，四甲基丁二胺，三亚乙基二胺，二月桂酸二丁基锡，辛酸亚锡的至少一种。
5.根据权利要求1所述的一种电疗肩托，其特征在于，所述小分子醇包括乙二醇，丁二醇，二乙二醇，己二醇的至少一种。
CN202110886554.6A 2021-08-03 2021-08-03 一种电疗肩托及其应用 Active CN115141352B (zh)