CN115124928A - 一种曲面屏用oca光学胶水、胶膜及其制备方法 - Google Patents
一种曲面屏用oca光学胶水、胶膜及其制备方法 Download PDFInfo
- Publication number
- CN115124928A CN115124928A CN202210842030.1A CN202210842030A CN115124928A CN 115124928 A CN115124928 A CN 115124928A CN 202210842030 A CN202210842030 A CN 202210842030A CN 115124928 A CN115124928 A CN 115124928A
- Authority
- CN
- China
- Prior art keywords
- parts
- photoinitiator
- bis
- oca
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂A 0.5份、光引发剂B 1份、流平剂0.1份、消泡剂0.2份、抗氧剂0.05份、偶联剂0.5份、交联剂1份、阻聚剂0.03份,所述光引发剂A为阳离子光引发剂。本发明制得的曲面屏用OCA光学胶水经过初次固化后,会保持在一个半固化的状态,具有很稳定的高蠕变性,这种半固化的状态既能对曲面位置对柔性屏和OLED进行有效的粘接,还能对不同的油墨段差进行有效填充,而且不会在常温和高温高湿等环境下出现气泡反弹等不良现象。
Description
【技术领域】
本发明涉及光学胶的技术领域,特别是OCA光学胶水的技术领域。
【背景技术】
受全球电子事业发展,全球触摸显示屏发展越来越快,触摸显示时代悄然改变和丰富了我们的日常生活,日常使用的智能手机和平板电脑都离不开触摸屏,特别是现在越来越流行的曲面屏技术大大提高了我们的视觉感受,曲面触屏的组装工艺中需要使用OCA光学胶膜对特殊柔性曲面屏和OLED之间进行粘接,曲面弧度大大增加了柔性屏和OLED之间的无缝粘接,现有的OCA光学胶膜不具备优异的力学拉伸性能和填充性能,很难满足对曲面位置的有效填充和油墨段差填充,容易出现气泡反弹等不良现象;且稳定性差,不耐储存。
【发明内容】
本发明的目的就是解决现有技术中的问题,提出一种曲面屏用OCA光学胶水及其制备方法,利用该OCA光学胶水制得的胶膜既可以满足曲面位置对柔性屏和OLED进行有效的粘接,又能满足对曲面位置的有效填充和油墨段差填充,且稳定性高,耐储存。
为实现上述目的,本发明提出了一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂A 0.3-1份、光引发剂B 0.5-3份、流平剂0.05-0.2份、消泡剂0.1-0.3份、抗氧剂0.03-0.06份、偶联剂0.3-1份、交联剂0.5-2份、阻聚剂0.01-0.05份。
作为优选,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂A 0.5份、光引发剂B1份、流平剂0.1份、消泡剂0.2份、抗氧剂0.05份、偶联剂0.5份、交联剂1份、阻聚剂0.03份,所述光引发剂A为阳离子光引发剂。
作为优选,所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯30-60份、丙烯酸羟乙酯10-25份、丙烯酸羟丁酯5-15份、甲基丙烯酸异冰片酯3-10份、丙烯酸异冰片酯3-10份、丙烯酸3-8份、丙烯酸丁酯5-20份、甲基丙烯酸缩水甘油酯1-5份、甲基丙烯酸葵酯1-6份、分子量调节剂0.5-2份、光引发剂C 0.3-0.7份。
作为优选,所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯40份、丙烯酸羟乙酯15份、丙烯酸羟丁酯10份、甲基丙烯酸异冰片酯5份、丙烯酸异冰片酯5份、丙烯酸5份、丙烯酸正丁酯15份、甲基丙烯酸缩水甘油酯3份、甲基丙烯酸葵酯2份、分子量调节剂1份、光引发剂C 0.5份。
作为优选,所述光引发剂A为光引发剂6992、9-(4一羟乙氧苯基)六氟磷酸酯、4-异丁基苯基-4'-甲基苯基碘六氟磷酸盐、二苯基-(4-苯基硫)苯基锍六氟锑酸盐、双(4-(二苯基锍)苯基)硫醚-双六氟磷酸盐、双(4-叔丁基苯基)碘对甲苯磺酸盐、硫鎓六氟锑酸盐、双(4-叔丁苯基)碘鎓六氟磷酸盐、二苯基碘鎓六氟砷酸盐、二苯基碘嗡三氟甲烷磺酸盐、2-(3,4-二甲氧基苯乙烯基)-4,6-双(三氯甲基)-1,3,5-三嗪、4-异丙基-4'-甲基二苯基碘鎓四(五氟苯基)硼酸盐、三苯基溴化锍、三对甲苯基锍六氟磷酸盐、三对甲苯基锍三氟甲烷磺酸盐中的一种或多种;所述光引发剂B为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、二苯甲酮、a,a-二甲氧基-a-苯基苯乙酮、二苯基-(2,4,6-三甲基苯甲酰)氧磷、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮中的一种或多种;所述流平剂为BYK-358N、BYK371、BYK370、BYK3700中的一种或多种;所述消泡剂为TEGO Foamex 842、tegofoamex 840、BYK-054中的一种或者多种;所述抗氧剂为抗氧化剂1076、抗氧化剂703、抗氧化剂1010中的一种或多种;所述偶联剂为KH550、KH560、KH570中的一种或多种;交联剂为1,4-丁二醇二丙烯酸酯、1,6-己二醇二丙烯酸酯、双-三羟甲基丙烷四丙烯酸酯、三羟甲基丙烷三丙烯酸酯中的一种或多种;所述阻聚剂为对苯二酚、对羟基苯甲醚、甲基氢醌、2-叔丁基对苯二酚、2,5-二叔丁基对苯二酚中的一种或多种;所述分子量调节剂为正十二烷基硫醇、巯基乙酸异辛酯、叔十二烷基硫醇中的一种或多种;所述光引发剂C为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、苯基双(2,4,6-三甲基苯甲酰基)氧化膦中的一种或多种。
作为优选,所述光引发剂A为光引发剂6992;所述光引发剂B为二苯基-(2,4,6-三甲基苯甲酰)氧磷;所述流平剂为BYK370;所述消泡剂为TEGO foamex840;所述抗氧剂为抗氧化剂703;所述偶联剂为KH550和KH560的一比一混合物;交联剂为1,6-己二醇二丙烯酸酯;所述阻聚剂为对苯二酚;所述分子量调节剂为正十二烷基硫醇;所述光引发剂C为1-羟基环己基苯基甲酮。
本发明还提出了一种曲面屏用OCA光学胶水制备方法,包括以下步骤:
a、制备丙烯酸酯预聚物:按照配比称取预聚物的原料;将原料依次加入到玻璃反应釜中,在氮气氛围保护下,一定时间搅拌均匀后,进行UV紫外光照射发生自由基聚合反应,控制反应的预聚物粘度为3000-30000mpa﹒s,重均分子量在60-300万之间,玻璃化转变温度在-40℃-20℃之间;
b、按照配比依次将步骤a得到的丙烯酸酯预聚物、光引发剂A、光引发剂B、流平剂、消泡剂、抗氧剂、偶联剂、交联剂、阻聚剂加入到玻璃反应釜中,常温下搅拌1-3小时,得到OCA胶水。
本发明还提出了一种曲面屏用OCA光学胶膜,包括重离型膜和轻离型膜,所述重离型膜和轻离型膜层之间设有光学胶层,所述光学胶层由上述的曲面屏用OCA光学胶水涂布制得。
作为优选,胶膜厚度为50-200um,重离型膜和轻离型膜的抗静电值为106-109Ω,厚度在50-150um之间。
作为优选,重离型膜和轻离型膜均为透光率大于90%的光学级离型膜,所述胶膜的厚度为125um,光学重离型膜的厚度为100um,光学轻离型膜层的厚度为75um。
作为优选,所述轻离型膜离型力为5-10gf/in,所述重离型膜离型力为15-35gf/in。
本发明还提出了一种曲面屏用OCA光学胶膜的制备方法,包括以下步骤:步骤b制得的OCA胶水在常温下静置消泡,将OCA胶水涂布于光学PET重离型膜和光学PET轻离型膜之间,通过紫外光照射一定的时间进行一次固化得到半固化的曲面屏OCA光学胶膜,紫外光的波长为330-420nm,OCA胶膜对屏幕进行初步粘接后,通过紫外光照射一定的时间进行二次固化,紫外光的波长为200-310nm。
本发明的有益效果:
(1)本发明制得的曲面屏用OCA光学胶膜经过固化后,会保持在一个半固化的状态,具有很好的蠕变性,这种半固化的状态既能对曲面位置对柔性屏和OLED进行有效的粘接,还能对不同的油墨段差进行有效填充,而且不会在常温和高温高湿等环境下出现气泡反弹等不良现象。
(2)固化后的OCA光学胶膜先对屏幕进行一个初步的粘接,进行加压脱泡后,再进行二次固化实现真正的固化粘接,这样的二次固化粘接胶膜技术可以很好的应用到曲面屏用OCA胶膜的技术领域,对以后的曲面屏手机发展具有重要意义。
(3)OCA光学胶膜里面由于添加阻聚剂使得OCA胶膜中未反应的活性双键得到有效阻聚,所以蠕变稳定性较好,这样就很好的保证了OCA胶膜产品的有效储存性,可以在运输过程中和下游触控模组厂保证产品的稳定性能。
(4)通过在光学胶水的配方中添加光引发剂A和光引发剂B,光引发剂B作为一次固化的引发剂;光引发剂A为阳离子光引发剂,作为二次固化的引发剂,用于实现真正的固化粘接。
(5)首先由光引发剂C引发光学胶体系的单体进行自由基聚合反应,得到丙烯酸酯预聚物,接着在丙烯酸酯预聚物内加入光引发剂A、光引发剂B和其他添加剂,得到光学胶水;将光学胶水制成光学胶膜后先通过中波紫外线进行照射,只激活光引发剂B,使光学胶进行一次固化,得到半固化的光学胶软胶膜;光学胶进行粘接后,再通过短波紫外线进行照射,激活光引发剂A,进行二次固化,实现真正的固化粘接;具有含阳杂环烷烃结构的(甲基)丙烯酸酯(如甲基丙烯酸缩水甘油酯)和阳离子光引发剂在短波长辐射光照时进行进一步交联固化,从而增加了胶膜的拉伸强度和粘结力,这种二次固化的方式方便了光学胶的运输使用,且粘接效果好。
本发明的特征及优点将通过实施例结合附图进行详细说明。
【附图说明】
图1是本发明一种曲面屏用OCA光学胶膜的结构示意图。
图中:1-重离型膜、2-轻离型膜层、3-光学胶层。
【具体实施方式】
实施例1:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGOfoamex 840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份、对苯二酚0.01份。
所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯40份、丙烯酸羟乙酯15份、丙烯酸羟丁酯10份、甲基丙烯酸异冰片酯5份、丙烯酸异冰片酯5份、丙烯酸5份、丙烯酸正丁酯15份、甲基丙烯酸缩水甘油酯3份、甲基丙烯酸葵酯2份、正十二烷基硫醇1份、光引发剂184(1-羟基环己基苯基甲酮)0.5份。
制备方法:
a、将制备丙烯酸酯预聚物的原料按照配比依次加入到玻璃反应釜中,在氮气氛围保护下搅拌均匀,进行UV紫外光照射发生自由基聚合反应,紫外光的波长为246-350nm,控制反应的预聚物粘度为3000-30000mpa﹒s,重均分子量在60-300万之间,玻璃化转变温度在-40℃-20℃之间;
b、将上述制得的丙烯酸酯预聚物与其他制备光学胶的原料依次加入到加入到玻璃反应釜中,常温下搅拌1-3小时,得到曲面屏用OCA光学胶水产品;
c、将上述制得的OCA光学胶水在常温下静置2H消泡,然后将OCA胶涂布于光学PET重离型膜和光学PET轻离型膜之间,通过紫外光照射一定的时间进行固化,所用紫外光能量为6000mj/cm2,紫外光的波长为365nm,固化时间为400s,控制胶膜厚度为125um,照射完毕后得到到半固化的曲面屏OCA光学胶膜产品,结构如图1所示。
OCA光学胶膜在完成模组和曲面盖板的初步粘接后,常温加压排出气泡,,再在288nm的紫外光波长下进行二次固化,所用紫外光能量为3500mj/cm2,固化时间40s,完成模组和曲面盖板的粘接。
实施例2:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGOfoamex 840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份、对苯二酚0.02份。
所述丙烯酸酯预聚物的配比与实施例1相同。
制备方法与实施例1相同。
实施例3:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGOfoamex 840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份、对苯二酚0.03份。
所述丙烯酸酯预聚物的配比与实施例1相同。
制备方法与实施例1相同。
实施例4:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGOfoamex 840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份、对苯二酚0.04份。
所述丙烯酸酯预聚物的配比与实施例1相同。
制备方法与实施例1相同。
实施例5:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGOfoamex 840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份、对苯二酚0.05份。
所述丙烯酸酯预聚物的配比与实施例1相同。
制备方法与实施例1相同。
实施例6:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂69921份、光引发剂TPO 3份、流平剂BYK3700.2份、消泡剂TEGO foamex840 0.3份、抗氧剂703 0.06份、KH550 1份、1,6-己二醇二丙烯酸酯2份、对苯二酚0.03份。
所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯30份、丙烯酸羟乙酯10份、丙烯酸羟丁酯5份、甲基丙烯酸异冰片酯3份、丙烯酸异冰片酯3份、丙烯酸3份、丙烯酸正丁酯5份、甲基丙烯酸缩水甘油酯1份、甲基丙烯酸葵酯1份、正十二烷基硫醇0.5份、光引发剂184(1-羟基环己基苯基甲酮)0.3份。
制备方法与实施例1相同。
实施例7:
本实施例提供一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.3份、光引发剂TPO 0.5份、流平剂BYK370 0.05份、消泡剂TEGOfoamex 840 0.1份、抗氧剂703 0.03份、KH550 0.3份、1,6-己二醇二丙烯酸酯0.5份、对苯二酚0.03份。
所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯60份、丙烯酸羟乙酯25份、丙烯酸羟丁酯15份、甲基丙烯酸异冰片酯10份、丙烯酸异冰片酯10份、丙烯酸8份、丙烯酸正丁酯20份、甲基丙烯酸缩水甘油酯5份、甲基丙烯酸葵酯6份、正十二烷基硫醇2份、光引发剂184(1-羟基环己基苯基甲酮)0.7份。
制备方法与实施例1相同。
对比例1:一种曲面屏用OCA光学胶水,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂6992 0.5份、光引发剂TPO 1份、流平剂BYK3700.1份、消泡剂TEGO foamex840 0.2份、抗氧剂703 0.05份、KH550和KH560质量比为一比一的混合物0.5份、1,6-己二醇二丙烯酸酯1份。
所述丙烯酸酯预聚物的配比与实施例1相同。
制备方法与实施例1相同。
对实施例1-5和对比例1制得的光学胶进行性能测试,结果如表1和表2所示。
表1
表2
(注:表1中的蠕变值为OCA胶膜产品分别放置1天、7天、14天、30天、60天、120天分别进行测试的蠕变值;测试方法为:将OCA胶膜产品层叠成800um厚度,采用流变仪(TA公司型号ARES-G2)用平行板夹具测定蠕变值,测试条件为恒定应力1000Pa,温度40℃,应变时间360秒;
BF指二次固化前的半固化OCA胶膜产品;AF指二次固化前的OCA胶膜产品经过LED固化箱固化得到的固化胶膜;
表2中,BF 1D胶膜的产品为二次固化前的放置1D的OCA胶膜样条,AF 1D胶膜产品为将放置1天的二次固化前胶膜产品用LED固化箱固化而得,LED能量为3500mj/cm2;
表2中,BF 1D和AF 1D的拉伸强度为测试方法为OCA胶膜裁切成25mm*5cm的样条,贴在150um厚度的两个PET薄膜上,放置在恒温恒湿条件下30MIN后,用拉力机测试得到拉伸强度值;
表2中,粘结力测试方法为:将OCA胶膜产品裁切成25mm*15cm的样条,撕开轻离型膜后,将其帖在50umPET基材上,再撕开重离型膜贴合于裸的玻璃盖板上,采用2kg滚轮以300mm/min速度来回辊压三次,在恒温恒湿条件下静置30MIN,使用拉力机以300mm/min速度测试OCA胶膜对裸的玻璃盖板粘结力;表2中,常温油墨段差填充实验为将OCA胶膜贴合于油墨段差高度为20um的CG玻璃盖板上,使用自动真空贴合机进行贴合,设定贴合压力为2kg,负压100Kpa,贴合时间20秒;然后放入高压除泡机中进行脱泡处理,设置条件为0.4Mpa压力下常温加压脱泡30MIN;最后观察常温条件下的OCA胶膜对油墨段差CG盖板的填充性;
表2中,OCA胶膜的反拆性能为80℃*10sec的条件下进行反拆验证反拆性能。)
通过实施例1-5可以得出,阻聚剂含量的过低不能起到很好的阻聚效果,过高则会严重影响OCA胶膜的交联固化效果,使得拉伸强度很低,不利于OCA胶膜的下游返工使用;
实施例3具有很好的实施效果,添加了合适量的对苯二酚阻聚剂使得OCA胶膜中的未反应活性双健得到了有效阻聚,所以产品具有稳定的蠕变值,且随时间的变化较为稳定。实施例3在二次固化前后都具有较高的拉伸强度,这样就保证了OCA胶膜的反拆性能较为优异,且具有较高的粘结力,保证了对CG盖板和模组的有效粘接。
本发明重点在于筛选合适的光引发剂A和光引发剂B的种类和分量,并添加合适分量的阻聚剂,OCA光学胶在一次固化时,紫外线的波长只激活光引发剂B引发OCA光学胶进行一定的交联固化反应,得到半固化的胶膜;OCA光学胶在二次固化时,短波紫外线会激活光引发剂A,引发OCA光学胶里面的环氧基团进行进一步的交联固化反应,得到完全固化的胶膜;阻聚剂的作用使一次固化后的胶膜在长时间的放置过程中不会出现缓慢的交联固化反应,从而改善了胶膜的稳定蠕变性。
上述实施例是对本发明的说明,不是对本发明的限定,任何对本发明简单变换后的方案均属于本发明的保护范围。
Claims (10)
1.一种曲面屏用OCA光学胶水,其特征在于,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂A 0.3-1份、光引发剂B 0.5-3份、流平剂0.05-0.2份、消泡剂0.1-0.3份、抗氧剂0.03-0.06份、偶联剂0.3-1份、交联剂0.5-2份、阻聚剂0.01-0.05份。
2.如权利要求1所述的曲面屏用OCA光学胶水,其特征在于,包括以下重量份的组分:丙烯酸酯预聚物100份、光引发剂A 0.5份、光引发剂B 1份、流平剂0.1份、消泡剂0.2份、抗氧剂0.05份、偶联剂0.5份、交联剂1份、阻聚剂0.03份,所述光引发剂A为阳离子光引发剂。
3.如权利要求1所述的曲面屏用OCA光学胶水,其特征在于,所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯30-60份、丙烯酸羟乙酯10-25份、丙烯酸羟丁酯5-15份、甲基丙烯酸异冰片酯3-10份、丙烯酸异冰片酯3-10份、丙烯酸3-8份、丙烯酸丁酯5-20份、甲基丙烯酸缩水甘油酯1-5份、甲基丙烯酸葵酯1-6份、分子量调节剂0.5-2份、光引发剂C 0.3-0.7份。
4.如权利要求1所述的曲面屏用OCA光学胶水,其特征在于,所述丙烯酸酯预聚物包括以下重量份的组分:丙烯酸-2-乙基己酯40份、丙烯酸羟乙酯15份、丙烯酸羟丁酯10份、甲基丙烯酸异冰片酯5份、丙烯酸异冰片酯5份、丙烯酸5份、丙烯酸正丁酯15份、甲基丙烯酸缩水甘油酯3份、甲基丙烯酸葵酯2份、分子量调节剂1份、光引发剂C 0.5份。
5.如权利要求3所述的曲面屏用OCA光学胶水,其特征在于:所述光引发剂A为光引发剂6992、9-(4一羟乙氧苯基)六氟磷酸酯、4-异丁基苯基-4'-甲基苯基碘六氟磷酸盐、二苯基-(4-苯基硫)苯基锍六氟锑酸盐、双(4-(二苯基锍)苯基)硫醚-双六氟磷酸盐、双(4-叔丁基苯基)碘对甲苯磺酸盐、硫鎓六氟锑酸盐、双(4-叔丁苯基)碘鎓六氟磷酸盐、二苯基碘鎓六氟砷酸盐、二苯基碘嗡三氟甲烷磺酸盐、2-(3,4-二甲氧基苯乙烯基)-4,6-双(三氯甲基)-1,3,5-三嗪、4-异丙基-4'-甲基二苯基碘鎓四(五氟苯基)硼酸盐、三苯基溴化锍、三对甲苯基锍六氟磷酸盐、三对甲苯基锍三氟甲烷磺酸盐中的一种或多种;所述光引发剂B为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、二苯甲酮、a,a-二甲氧基-a-苯基苯乙酮、二苯基-(2,4,6-三甲基苯甲酰)氧磷、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮中的一种或多种;所述流平剂为BYK-358N、BYK371、BYK370、BYK3700中的一种或多种;所述消泡剂为TEGO Foamex 842、tego foamex 840、BYK-054中的一种或者多种;所述抗氧剂为抗氧化剂1076、抗氧化剂703、抗氧化剂1010中的一种或多种;所述偶联剂为KH550、KH560、KH570中的一种或多种;交联剂为1,4-丁二醇二丙烯酸酯、1,6-己二醇二丙烯酸酯、双-三羟甲基丙烷四丙烯酸酯、三羟甲基丙烷三丙烯酸酯中的一种或多种;所述阻聚剂为对苯二酚、对羟基苯甲醚、甲基氢醌、2-叔丁基对苯二酚、2,5-二叔丁基对苯二酚中的一种或多种;所述分子量调节剂为正十二烷基硫醇、巯基乙酸异辛酯、叔十二烷基硫醇中的一种或多种;所述光引发剂C为1-羟基环己基苯基甲酮、2-羟基-2-甲基-1-苯基-1-丙酮、苯基双(2,4,6-三甲基苯甲酰基)氧化膦中的一种或多种。
6.如权利要求5所述的曲面屏用OCA光学胶水,其特征在于:所述光引发剂A为光引发剂6992;所述光引发剂B为二苯基-(2,4,6-三甲基苯甲酰)氧磷;所述流平剂为BYK370;所述消泡剂为TEGO foamex 840;所述抗氧剂为抗氧化剂703;所述偶联剂为KH550和KH560的一比一混合物;交联剂为1,6-己二醇二丙烯酸酯;所述阻聚剂为对苯二酚;所述分子量调节剂为正十二烷基硫醇;所述光引发剂C为1-羟基环己基苯基甲酮。
7.一种曲面屏用OCA光学胶水的制备方法,其特征在于,包括以下步骤:
a、制备丙烯酸酯预聚物:按照配比称取预聚物的原料;将原料依次加入到玻璃反应釜中,在氮气氛围保护下搅拌均匀后,进行UV紫外光照射发生自由基聚合反应,控制反应的预聚物粘度为3000-30000mpa﹒s,重均分子量在60-300万之间,玻璃化转变温度在-40℃-20℃之间;
b、按照配比依次将步骤a得到的丙烯酸酯预聚物、光引发剂A、光引发剂B、流平剂、消泡剂、抗氧剂、偶联剂、交联剂、阻聚剂加入到玻璃反应釜中,常温下搅拌1-3小时,得到OCA胶水。
8.一种曲面屏用OCA光学胶膜,其特征在于:包括重离型膜(1)和轻离型膜(2),所述重离型膜(1)和轻离型膜层(2)之间设有光学胶层(3),所述光学胶层(3)由权利要求1至6中任意一项所述的曲面屏用OCA光学胶水水涂布制得。
9.一种曲面屏用OCA光学胶膜的制备方法,其特征在于,包括以下步骤:将权利要求8制得的OCA胶水静置消泡,将OCA胶水涂布于重离型膜和轻离型膜之间,通过紫外光照射一定的时间进行一次固化,得到半固化的曲面屏OCA光学胶膜,紫外光的波长为330-420nm。
10.一种曲面屏用OCA光学胶膜的制备方法,其特征在于,包括以下步骤:将权利要求9制得的OCA胶膜对屏幕进行初步粘接后,通过紫外光照射一定的时间进行二次固化,紫外光的波长为200-310nm。