CN115074022A - 一种地面警示用涂料及其应用 - Google Patents
一种地面警示用涂料及其应用 Download PDFInfo
- Publication number
- CN115074022A CN115074022A CN202210791746.3A CN202210791746A CN115074022A CN 115074022 A CN115074022 A CN 115074022A CN 202210791746 A CN202210791746 A CN 202210791746A CN 115074022 A CN115074022 A CN 115074022A
- Authority
- CN
- China
- Prior art keywords
- coating
- paint
- warning
- ground
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种地面警示用涂料及其应用，属于地面用涂料技术领域，本发明提供的地面警示用涂料包括以下原料：改性聚硅氧烷树脂、氨基硅烷固化剂、填料、分散剂、流平剂、消泡剂和溶剂。本发明所述涂料具有良好的保色性、耐沾污性、耐水侵蚀性、耐候性、耐久性以及与基层良好的粘结性的特点。同时，本发明所述涂料可涂刷于步砖道、混凝土路面或沥青路面，涂料在雨天等潮湿工况下显示涂料所绘警示信息，提醒驾驶员安全行驶，降低交通事故发生的概率。
Description
技术领域
本发明涉及地面用涂料技术领域，尤其涉及一种地面警示用涂料及其应用。
背景技术
涂料除了具有装饰和保护两种基本功能外，其涂膜还能够通过光、电、热、机械.化学或生物化学以及其他方式进行能量的相互作用、相互转换而产生某种所需要的特殊功能，这类涂料一般称为功能性涂料。相应地，除装饰和基本的保护作用外，还具有某种特殊功能作用的建筑涂料，则称为功能性建筑涂料。例如，防水涂料、防火涂料、建筑保温隔热涂料、防霉涂料等。地面用涂料直接暴露于大气环境中，时刻经受自然界各种环境，如风、雪、雨、紫外线及酸雨等的侵蚀，因而必须具有良好的物理力学性能、耐水、耐酸碱、耐洗刷和耐紫外线等耐老化性能。
道面在湿润的工况下摩擦力减少，若仍保持原工况下通行可能会造成人员事故。对于目前现有交通安全方式，主要采用类型包括路侧设置静态提示、警告及禁令标识，或相应易发事故位置设置动态显示屏在道面由于雨天潮湿工况下，为保障行驶安全进行提示等。
研究现有的交通安全设施可以发现，静态标识普遍存在成本较高、闲置工况时间长、常规工况下分散路用者注意力等问题；动态显示屏则存在造价昂贵、接线复杂等缺点。因此在交通安全技术领域亟需一种低成本、设置便捷、形式简单、专用于对应工况的警示用涂料。
发明内容
有鉴于此，本发明提供了一种地面警示用涂料及其应用，本发明提供的涂料具有良好的保色性、耐沾污性、耐水侵蚀性、耐候性、耐久性以及与基层良好的粘结性。同时，本发明提供的涂料在湿润道面上起到警示作用，保证雨天潮湿工况下的安全行驶，防止交通事故的发生。
本发明的第一个目的是提供一种地面警示用涂料，包括以下重量份数的原料：
改性聚硅氧烷树脂75～90份
氨基硅烷固化剂7-10份
填料37～41份
分散剂0.5-1份
流平剂0.5-1份
消泡剂0.5-1份
溶剂50-70份。
优选地，所述溶剂为乙醇、丁醇、醋酸乙酯、醋酸丁酯中的至少一种。
优选地，所述填料包括沉淀硫酸钡、滑石粉、高岭土、云母粉中的至少一种。本发明使用的填料不具有遮盖力和着色力，来自于工业上的副产品，价格便宜。填料能增加涂膜的厚度和体质，增加涂膜耐久性。提高涂层的耐磨性、耐水性和稳定性，降低成本。
优选地，所述填料的粒径≤2mm。本发明采用粒径在2毫米以下的不同大小粒径的粒料作为填料，耐候性优良，粒子较粗，能在路面中起色观及质感的作用。
优选地，所述改性聚硅氧烷树脂(818C，硅含量13.5wt％)。购买自上海华荣化工有限公司。
优选地，所述分散剂为BYK110分散剂。
优选地，所述流平剂为BYK358N流平剂。
优选地，所述消泡剂为BYK-1790消泡剂。所述分散剂、流平剂和消泡剂均购买自毕克公司。
优选地，所述氨基硅烷固化剂购买自德国瓦克化学公司。
本发明的第二个目的是提供所述地面警示用涂料的制备方法，按比例称量改性聚硅氧烷树脂、填料、分散剂、流平剂、消泡剂和溶剂混合后在1000-2000r/min转速下搅拌20-40min，静置至消泡后，再加入氨基硅烷固化剂，搅拌均匀，即得地面警示用涂料。
本发明的第三个目的是提供所述地面警示用涂料的应用方法，将所述涂料涂刷在地面，淋水后显现，起到警示行人的效果。
本发明提供的地面警示用涂料应用于步砖道、混凝土路面和沥青路面，涂刷方法可以采用已知的空气喷涂、高压无气喷涂、刷涂、辊涂等方式。涂覆上述混合物后使干膜厚度达到50～100um。
与现有技术相比，本发明具有以下有益效果：
1、本发明提供的地面警示用涂料可根据不同的路面，用防水疏水防护涂料涂刷相应警示类交通信息，使道面在潮湿的环境下，警示类信息与原路面通过色差而形成鲜明的颜色对比，从而满足道面使用者，在上述道面潮湿工况下，对于相关警示类信息的视认性，提醒路用者以减少交通事故的发生；
2、本发明提供的地面警示用涂料还可根据实际需求，扩展至潮湿地面工况下交通地面标识的各种类型，包括但不限于禁令、警告、指示及指路等地面标识及信息；
3、本发明提供的地面警示用涂料属于防水疏水涂料，具有优良的阻水性，可长久阻止雨水、流水对基材的侵蚀，同时可保证基材表面的“呼吸作用”，处理后的基材吸水率低，但是有很好的透气性；
4、本发明提供的地面警示用涂料适用基材范围较广，干燥成型后，防水疏水性能保持时间长；所述地面警示用涂料具有无毒、无异味、对环境及人体无刺激，无害的特点；在低用量下就有很好的水珠效果，可起到很好的水保护作用；持久美观，能长时间经受水滴落冲刷并保持基材本身颜色；对于基材渗透性优异，可增强基材表面隔热性能，干燥后基材表面不发粘。
5、本发明提供的地面警示用涂料作为一种道面涂装材料技术，相较原静态标志或动态显示屏可大规模减少工程造价。
附图说明
图1是本发明实验例1涂刷地面警示用涂料的效果图；
图2是本发明实验例1地面警示用涂料风干后的效果图；
图3是本发明实验例1地面警示用涂料淋水后的效果图；
图4是本发明实验例1地面警示用涂料使用一年后的效果图；
图5是本发明实验例2涂刷地面警示用涂料的效果图；
图6是本发明实验例2地面警示用涂料风干后的效果图；
图7是本发明实验例2地面警示用涂料淋水后的效果图；
图8是本发明实验例2地面警示用涂料使用一年后的效果图；
图9是本发明实验例3地面警示用涂料风干后的效果图；
图10是本发明实验例3地面警示用涂料淋水后的效果图。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将对本发明的技术方案进行清楚、完整的描述。显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所得到的所有其它实施例，都属于本发明所保护的范围。
下述实施例中所述试验方法或测试方法，如无特殊说明，均为常规方法；所述原料和助剂，如无特殊说明，均从常规商业途径获得，或以常规方法制备。
实施例1
一种地面警示用涂料的制备方法，由以下步骤制备而成：按比例称量改性聚硅氧烷树脂75份、粒径为1mm的高岭土37份、BYK110 0.5份、BYK358N 0.5份、BYK-1790 0.5份和乙醇50份，混合后在1000r/min转速下搅拌20min，静置至消泡后，再加入氨基硅烷固化剂7份，搅拌均匀，即得地面警示用涂料。
实施例2
一种地面警示用涂料的制备方法，由以下步骤制备而成：按比例称量改性聚硅氧烷树脂75～90份、粒径为1mm的沉淀硫酸钡37～41份、BYK110 0.5-1份、BYK358N 0.5-1份、BYK-1790 0.5-1份和丁醇50-70份，混合后在1000-2000r/min转速下搅拌20-40min，静置至消泡后，再加入氨基硅烷固化剂7-10份，搅拌均匀，即得地面警示用涂料。
实施例3
一种地面警示用涂料的制备方法，由以下步骤制备而成：按比例称量改性聚硅氧烷树脂90份、粒径为1mm的滑石粉41份、BYK110 1份、BYK358N 1份、BYK-1790 1份和醋酸乙酯70份，混合后在2000r/min转速下搅拌40min，静置至消泡后，再加入氨基硅烷固化剂10份，搅拌均匀，即得地面警示用涂料。
实验例1
将实施例1制备的地面警示用涂料分别在普通公路的路面进行涂覆，步骤如下：
(1)清理干净公路表面的杂物；
(2)然后涂刷地面警示用涂料，效果如图1所示；
(3)涂刷涂料后在自然环境下风干24小时，效果如图2所示，完全和原来的没有什么区别，基本不影响混凝土路面；
(4)淋水后如图3所示，所写的“小心”字完全没有水湿，可以起到警示行人的效果。
且经过一年多时间的使用，该材料视认性几无变化，如图4所示。本发明提供的涂料亦能起到防护步道砖的作用。
实验例2
将实施例2制备的地面警示用涂料分别在普通公路的路面进行涂覆，步骤如下：
(1)清理干净公路表面的杂物；
(2)然后涂刷地面警示用涂料，效果如图5所示；
(3)涂刷涂料后在自然环境下风干24小时，效果如图6所示，完全和原来的没有什么区别，基本不影响混凝土路面；
(4)淋水后如图7所示，所写的“小心”字完全没有水湿，可以起到警示行人的效果。
且经过一年多时间的使用，该材料视认性几无变化，如图8所示。本发明提供的涂料亦能起到防护步道砖的作用。
实验例3
将实施例3制备的地面警示用涂料分别在普通公路的路面进行涂覆，步骤如下：
(1)清理干净公路表面的杂物；
(2)然后涂刷地面警示用涂料；
(3)涂刷涂料后在自然环境下风干24小时，效果如图9所示，完全和原来的没有什么区别，基本不影响混凝土路面；
(4)淋水后如图10所示，所写的倒Y字完全没有水湿，可以起到警示行人的效果。
将本发明制备的地面警示用涂料涂覆于普通砖面上，涂覆厚度为80um，制备成测试样板，分别进行附着力、耐冲击性能、耐水性和耐酸碱性测试。测试所依据的方法如下：
1、附着力测试：使用天津市精科材料试验机厂生产的电动附着力测试仪，在涂层表面旋转划圈，根据GB/T 1720-1979评定其附着力等级。
2、耐冲击性能测试：使用天津市森日达试验设备有限公司生产的冲击试验机进行测试，观察漆膜有无裂纹、皱纹及剥落等现象，记录重锤落下的最高高度即为涂层的耐冲击性能强度。测试标准GB/T 1732-1993。
3、耐水性测试：将制得三块样板放入23+2℃恒温水槽中，样板浸入水中约三分之二，定期检查样板表面有无变色、起皱、起泡、脱落、生锈等现象，当三块板中两块已发生缺陷，记录其浸泡时间，则为涂层耐水时间。测试标准GB/T 1733-1993。
4、耐酸性测试：将制得样板放入50g/L H2SO4溶液中浸泡24h，取出后用三级水进行冲洗，待冲洗干净之后用布吸干样板表面水分，观察涂层表面情况若无缺陷，则通过测试。测试标准GB/T 9274-1988。
5、耐碱性测试：将制得样板放入50g/L NaOH溶液中浸泡168h，取出后用三级水进行冲洗，待冲洗干净之后用布吸干样板表面水分，观察涂层表面情况若无缺陷，则通过测试。
对实施例1-3制备的地面警示用涂料进行性能检测的结果如下：
由上述表格中的数据可知，本发明提供的地面警示用涂料的附着力、耐冲击性能、耐水性和耐酸碱性均符合本领域人员对涂料的性能要求。以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种地面警示用涂料，其特征在于，包括以下重量份数的原料：
改性聚硅氧烷树脂75～90份
氨基硅烷固化剂7-10份
填料37～41份
分散剂0.5-1份
流平剂0.5-1份
消泡剂0.5-1份
溶剂50-70份。
2.根据权利要求1所述的地面警示用涂料，其特征在于，所述溶剂为乙醇、丁醇、醋酸乙酯、醋酸丁酯中的至少一种。
3.根据权利要求1所述的地面警示用涂料，其特征在于，所述填料包括沉淀硫酸钡、滑石粉、高岭土、云母粉中的至少一种。
4.根据权利要求3所述的地面警示用涂料，其特征在于，所述填料的粒径≤2mm。
5.根据权利要求1所述的地面警示用涂料，其特征在于，所述改性聚硅氧烷树脂中硅含量为13.5wt％。
6.根据权利要求1所述的地面警示用涂料，其特征在于，所述分散剂为BYK-110分散剂。
7.根据权利要求1所述的地面警示用涂料，其特征在于，所述流平剂为BYK-358N流平剂。
8.根据权利要求1所述的地面警示用涂料，其特征在于，所述消泡剂为BYK-1790消泡剂。
9.根据权利要求1～8任意一项所述的地面警示用涂料的制备方法，其特征在于，按比例称量改性聚硅氧烷树脂、填料、分散剂、流平剂和消泡剂混合后在1000-2000r/min转速下搅拌20-40min，静置至消泡后，再加入氨基硅烷固化剂，搅拌均匀，即得地面警示用涂料。
10.根据权利要求1-8任意一项所述地面警示用涂料的应用，其特征在于，将所述涂料涂刷在地面，淋水后显现，起到警示路用者的效果。