CN1150083A - Baseboard material for plastic composite floor - Google Patents
Baseboard material for plastic composite floor Download PDFInfo
- Publication number
- CN1150083A CN1150083A CN 95112221 CN95112221A CN1150083A CN 1150083 A CN1150083 A CN 1150083A CN 95112221 CN95112221 CN 95112221 CN 95112221 A CN95112221 A CN 95112221A CN 1150083 A CN1150083 A CN 1150083A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- plasticizer
- inorganic filler
- haloflex
- chlorinated paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A substrate for composite plastic floor tiles is made of chlorinated polyethylene (1-60 wt.%), polyvinyl chloride (1-30), plasticizer (1-15), inorganic filler (9-80), chlorowax or coupling agent (0.1-2), and stabilizer (0.1-1.5), and features good flexibility, elasticity, weatherability and impact resistance, low expansibility and absorbency, and long service life. The pattern floor board made up by combining it with wooden veneer or the plastic cement floor board with polyvinyl chloride features high elasticity, not deforming and low cost.
Description
The invention belongs to a kind of chemical material, particularly a kind of plastics composite decoration floor baseboard material.
Plastic composite floor bottom surface material mainly by polyvinyl chloride, inorganic filler, plasticizer, stabilization agent, stearic acid etc. by proper proportion through banburying, open processes such as refining and make.The problem of its existence is quality more not folding; Matter is close, compact conformation, inorganic filler can not be contained by the polyvinyl chloride molecule fully, so impact resistance is poor, coefficient of thermal expansion and suction rate of change are bigger, just the less stable of final products; Ageing-resistant performance, weatherability, cold resistance are all undesirable.In order to increase its flexibility, if adopt then cost height of foamed plastic, the general content that increases plasticizer that adopts is obtained, but combining between igelite and plasticizer can be firm inadequately, separate out than very fast, plasticization effect is poor, and influencing service life, the selection differences of plasticizer also influences its weather resistance simultaneously.Therefore, the floor that is composited with such bed material and surface layer, not only stable not ideal enough, and since the relation of bed material paved surface is had relatively high expectations, also selective to the requirement of surface layer, as in order to save timber resources, the characteristic on reserve floor, if select for use wooden skin to make surface layer, then can not be compound with wooden skin well with above-mentioned bed material.
The purpose of this invention is to provide the baseboard material that a kind of plastic composite floor is used, have excellent weatherability, cold resistance, resistance to impact etc., coefficient of thermal expansion and suction rate of change are little, long service life, and also cost is low.
The baseboard material of this composite floor board comprises following component: polyvinyl chloride, plasticizer, inorganic filler, stabilization agent, its technical characterstic are to add the modifier haloflex, and also add coupling agent or chlorinated paraffin.
The weight percent of the above each component consists of: haloflex 1～60%, polyvinyl chloride 1～30%, plasticizer 1～15%, inorganic filler 9～80%, chlorinated paraffin or coupling agent 0.1～2%, stabilization agent 0.1～1.5%.
The present invention cooperates with other component by adding modifier, make product show as soft folding, high resilience, good weatherability, cold resistance, flame resistance, resistance to impact, oil resistivity, chemical proofing and electric property are arranged, coefficient of thermal expansion and suction rate of change are very little, combine firmly long service life with plasticizer.After polyvinyl chloride is modified, make the viscosity of product, elasticity relatively good, therefore add to have when coupling agent or chlorinated paraffin make out refining and peel off effect preferably, simultaneously the combination between inorganic, organic molecule is played certain firm effect.
Best percentage composition of the present invention is: haloflex 13%, polyvinyl chloride 3.5%, plasticizer 4.3%, inorganic filler 78.3%, chlorinated paraffin or coupling agent 0.45%, stabilization agent 0.45%, and not only make the cost of product low, and excellent performance.
Plasticizer the best is selected dioctyl phthalate (DOP) for use, it not only with combine more firmly between igelite, and cost is low.Preferably select chlorinated paraffin for use and do not adopt coupling agent (referring to titanate ester), because use the chlorinated paraffin better effects if, and cost is low.Stabilization agent is as three salt (lead sulfate tribasic) or disalt (dibasic lead stearate), inorganic filler such as Paris white.
This product is because high resilience, thereby as the base plate of composite floor board the flatness on ground etc. required so harshly, and feel is good.(thick about 0.2～0.3mm) floor that is composited reaches the Elastic plastic-rubber floor that is composited with polyvinyl chloride book film, and is indeformable, long service life for it and wooden cortex.
Advantage of the present invention: technology is simple, cost is low; Soft folding, high resilience; Good weatherability, cold resistance, flame resistance, resistance to impact, oil resistivity, chemical proofing and electric property are arranged; Coefficient of thermal expansion and suction rate of change are very little; Combine firmly with auxiliary agents such as plasticizer; Long service life, parquet floor (compound with the wooden cortex that 0.2～0.3mm is thick), the Elastic plastic-rubber floor that especially be suitable for to make have good springiness, indeformable, advantage that cost is low, are easier to apply.
Embodiment one:
Haloflex 13%, polyvinyl chloride 3.5%, DOP4.3%, CaCO
3Powder 78.3%, chlorinated paraffin 0.45%, three salt 0.45%.
Each component is mixed after 140～150 ℃ of banburyings are opened refining through mill again, makes through the two roll calender calendering then.
Embodiment two:
Haloflex 40%, polyvinyl chloride 15%, DOP1.5%, CaCO
340%, chlorinated paraffin 2%, three salt 1.5%
Embodiment three:
Haloflex 60%, polyvinyl chloride 25%, DOP1%, CaCO
312%, coupling agent 1%, three salt 1%.
Embodiment four:
Haloflex 10%, polyvinyl chloride 5%, DOP8%, CaCO
375.9%, chlorinated paraffin 0.1%, three salt 1%.
Embodiment five:
Haloflex 20%, polyvinyl chloride 1%, DOP15%, CaCO
362.4%, chlorinated paraffin 1.5%, three salt 0.1%.
Embodiment six:
Haloflex 1%, polyvinyl chloride 30%, DOP12%, CaCO
354.7%, chlorinated paraffin 2%, disalt 0.3%.
Embodiment seven:
Haloflex 55.2%, polyvinyl chloride 30%, DOP3%, CaCO
39%, chlorinated paraffin 2%, three salt 0.8%.
Claims (4)
1, a kind of baseboard material of composite floor board comprises following component: polyvinyl chloride, plasticizer, inorganic filler, stabilization agent is characterized in that adding the modifier haloflex, and add coupling agent or chlorinated paraffin.
2, baseboard material according to claim 1 is characterised in that its weight percent consists of: haloflex 1～60%, polyvinyl chloride 1～30%, plasticizer 1～15%, inorganic filler 9～80%, chlorinated paraffin or coupling agent 0.1～2%, stabilization agent 0.1～1.5%.
3, baseboard material according to claim 2 is characterised in that best group becomes: haloflex 13%, polyvinyl chloride 3.5%, plasticizer 4.3%, inorganic filler 78.3%, chlorinated paraffin or coupling agent 0.45%, stabilization agent 0.45%.
4, according to claim 1,2,3 described baseboard materials, be characterised in that described plasticizer preferably is selected from dioctyl phthalate, inorganic filler with Paris white, stabilization agent with three salt or disalt.