CN114989353B - 一种改性丁吡胶乳及其制备方法和应用 - Google Patents
一种改性丁吡胶乳及其制备方法和应用 Download PDFInfo
- Publication number
- CN114989353B CN114989353B CN202210654865.4A CN202210654865A CN114989353B CN 114989353 B CN114989353 B CN 114989353B CN 202210654865 A CN202210654865 A CN 202210654865A CN 114989353 B CN114989353 B CN 114989353B
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene
- modified butadiene
- pyridine
- pyridine latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明揭示了一种改性丁吡胶乳及其制备方法和应用。所述改性丁吡胶乳，包括如下重量份的组分：丁二烯65‑75份、苯乙烯10‑15份、2‑乙烯基吡啶10‑15份、分子量调节剂0.5‑1.0份、马来酸酐1‑5份、阴离子乳化剂3.8‑4.5份，非离子乳化剂0.5‑1.5份，扩散剂0.4‑0.6份，电解质0.05‑0.5份和引发剂0.1‑0.5份；其中，所述阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠、烷基苯磺酸钠等阴离子乳化剂组成的混合体系。本发明提供的改性丁吡胶乳，通过丁二烯、苯乙烯、2‑乙烯基吡啶、马来酸酐四元共聚乳液，从而赋予丁吡胶乳某些新的性能，如改善帘帆布的耐热性、耐老化性、耐疲劳性等。
Description
技术领域
本发明属于高分子化合物技术领域，具体涉及一种改性丁吡胶乳及其制备方法和应用。
背景技术
丁吡胶乳作为轮胎、三角带、胶管、胶带等橡胶制品的骨架材料即纤维帘线、帆布、线绳浸胶粘合剂的重要组成材料，是橡胶与纤维粘合的重要配套材料，其品质的优劣对浸胶骨架材料的粘合性能和浸胶工艺性能起重要作用。
发明内容
本发明的主要目的在于提供一种改性丁吡胶乳及其制备方法和应用，以克服现有技术中存在的不足。
为实现前述发明目的，本发明实施例采用的技术方案包括：
本发明实施例提供了一种改性丁吡胶乳，包括如下重量份的组分：丁二烯65-75份、苯乙烯10-15份、2-乙烯基吡啶10-15份、分子量调节剂0.5-1.0份、马来酸酐1-5份、阴离子乳化剂3.8-4.5份，非离子乳化剂0.5-1.5份，扩散剂0.4-0.6份，电解质0.05-0.5份和引发剂0.1-0.5份；其中，所述阴离子乳化剂包括松香钾皂、脂肪酸钾皂、烷基磺酸钠、烷基苯磺酸钠等阴离子中的一种或多种的组合。
进一步地，所述分子量调节剂包括叔十二烷基硫醇、巯基丁酸酯等中的任意一种或多种的组合。
进一步地，所述引发剂包括过硫酸钾、过氧化氢二异丙苯、叔丁基过氧化氢、偶氮二异庚腈中的任意一种或多种的组合。
进一步地，所述非离子乳化剂包括烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚类中的任意一种或多种的组合。
进一步地，所述电解质包括氯化钾、硫酸钾、磷酸钾中的任意一种或多种的组合。
本发明实施例还提供了一种前述的改性丁吡胶乳的制备方法，包括：
将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应15-20h，获得所述改性丁吡胶乳。
本发明实施例还提供了前述的改性丁吡胶乳于橡胶制品的骨架材料中的应用。
与现有技术相比，本发明具有如下有益效果：
(1)本发明改性丁吡胶乳，通过丁二烯、苯乙烯、2-乙烯基吡啶、马来酸酐四元共聚乳液，从而赋予丁吡胶乳某些新的性能，如改善帘帆布的耐热性、耐老化性、耐疲劳性等；具体地，采用热聚合工艺，由去离子水、松香皂液、脂肪酸皂液等优先形成胶束、增容胶束等；引发剂加入后促进了胶乳粒的形成，藉由马来酸酐的酸酐基团引入，对胶乳粒进行改性处理，进而完成整个胶乳体系的改性。
(2)本发明改性丁吡胶乳的制备方法，主体采用采用质量配比为70:15:15的丁二烯、苯乙烯和2-乙烯基吡啶，再加入电解质、去离子水以及调节剂等，以松香钾皂、脂肪酸钾皂、烷基磺酸钠、烷基苯磺酸钠等作为阴离子乳化剂，硫醇作为调节剂，辅以适量的马来酸酐来提升产品性能。
具体实施方式
通过以下具体实施方式将更完整地理解本发明。本文中揭示本发明的详细实施例；然而，应理解，所揭示的实施例仅具本发明的示范性，本发明可以各种形式来体现。因此，本文中所揭示的特定功能细节不应解释为具有限制性，而是仅解释为权利要求书的基础且解释为用于教示所属领域的技术人员在事实上任何适当详细实施例中以不同方式采用本发明的代表性基础。
本发明实施例的一个方面提供了一种改性丁吡胶乳，包括如下重量份的组分：丁二烯65-75份、苯乙烯10-15份、2-乙烯基吡啶10-15份、分子量调节剂0.5-1.0份、马来酸酐1-5份、阴离子乳化剂3.8-4.5份，非离子乳化剂0.5-1.5份，扩散剂0.4-0.6份，电解质0.05-0.5份和引发剂0.1-0.5份；其中，所述阴离子乳化剂包括松香钾皂、脂肪酸钾皂、烷基磺酸钠、烷基苯磺酸钠等阴离子中的一种或多种的组合。
在一些优选实施例中，所述分子量调节剂可以包括叔十二烷基硫醇、巯基丁酸酯中的任意一种或多种的组合，但不局限于此。
在一些优选实施例中，所述引发剂可以包括过硫酸钾、过氧化氢二异丙苯、叔丁基过氧化氢、偶氮二异庚腈等中的任意一种或多种的组合，但不局限于此。
在一些优选实施例中，所述非离子乳化剂可以包括烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚类中的任意一种或多种的组合，但不局限于此。
在一些优选实施例中，所述电解质可以包括氯化钾、硫酸钾、磷酸钾等中的任意一种或多种的组合，但不局限于此。
在一些优选实施例中，所述扩散剂包括亚甲基二萘磺酸钠、木质素磺酸钠等中的任意一种或多种的组合，但不局限于此。
本发明实施例的另一个方面提供了一种前述的改性丁吡胶乳的制备方法，包括：
将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应15-20h，获得所述改性丁吡胶乳。
本发明实施例的另一个方面还提供了前述的改性丁吡胶乳于橡胶制品的骨架材料中的应用。
在一些优选实施例中，所述橡胶制品可以包括轮胎、三角带、胶管、胶带等中的任意一种，但不局限于此。
本发明实施例提供的改性丁吡胶乳，通过丁二烯、苯乙烯、2-乙烯基吡啶、马来酸酐四元共聚乳液，从而赋予丁吡胶乳某些新的性能，如改善帘帆布的耐热性、耐老化性、耐疲劳性等。
实施例1
本实施例改性丁吡胶乳，包括如下重量份的组分：丁二烯70份、苯乙烯15份、2-乙烯基吡啶15份、分子量调节剂0.5份、马来酸酐1份、阴离子乳化剂4份、非离子乳化剂0.5份、扩散剂0.4份、电解质0.08份和引发剂0.3份；其中，阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠和烷基苯磺酸钠组成的混合体系；在本实施例中，分子量调节剂为十二烷基硫醇，引发剂为过硫酸钾，非离子乳化剂为OP-10，扩散剂为NNO，电解质为磷酸钾。
本实施例改性丁吡胶乳，通过如下步骤制备而成：
(1)乳化液配制：将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
(2)油相溶液配制：将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
(3)胶乳合成：将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应15h，获得所述改性丁吡胶乳。
实施例2
本实施例改性丁吡胶乳，包括如下重量份的组分：丁二烯70份、苯乙烯15份、2-乙烯基吡啶15份、分子量调节剂0.8份、马来酸酐3份、阴离子乳化剂4份、非离子乳化剂0.5份、扩散剂0.4份、电解质0.08份和引发剂0.4份；其中，阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠和烷基苯磺酸钠组成的混合体系；在本实施例中，分子量调节剂为十二烷基硫醇，引发剂为过硫酸钾，非离子乳化剂为OP-10，扩散剂为NNO，电解质为磷酸钾。
本实施例改性丁吡胶乳，通过如下步骤制备而成：
(1)乳化液配制：将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
(2)油相溶液配制：将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
(3)胶乳合成：将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应18h，获得所述改性丁吡胶乳。
实施例3
本实施例改性丁吡胶乳，包括如下重量份的组分：丁二烯70份、苯乙烯15份、2-乙烯基吡啶15份、分子量调节剂1.0份、马来酸酐4.5份、阴离子乳化剂4份、非离子乳化剂0.5份、扩散剂0.4份、电解质0.1份和引发剂0.5份；其中，阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠和烷基苯磺酸钠组成的混合体系；在本实施例中，分子量调节剂为十二烷基硫醇，引发剂为过硫酸钾，非离子乳化剂为OP-10，扩散剂为NNO，电解质为磷酸钾。
本实施例改性丁吡胶乳，通过如下步骤制备而成：
(1)乳化液配制：将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
(2)油相溶液配制：将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
(3)胶乳合成：将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应20h，获得所述改性丁吡胶乳。
对比例1
本对比例丁吡胶乳，包括如下重量份的组分：丁二烯60份、苯乙烯20份、2-乙烯基吡啶20份、分子量调节剂0.7份、阴离子乳化剂5份、非离子乳化剂0.5份、扩散剂0.4份、电解质0.08份和引发剂0.3份；其中，阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠和烷基苯磺酸钠组成的混合体系；在本实施例中，分子量调节剂为十二烷基硫醇，引发剂为过硫酸钾，非离子乳化剂为OP-10，扩散剂为NNO，电解质为硫酸钾。
对比例2
本对比例丁吡胶乳，包括如下重量份的组分：丁二烯75份、苯乙烯12.5份、2-乙烯基吡啶12.5份、分子量调节剂0.8份、马来酸酐0.5份、阴离子乳化剂6份、非离子乳化剂0.5份、扩散剂0.4份、电解质0.08份和引发剂0.3份；其中，阴离子乳化剂为松香钾皂，在本实施例中，分子量调节剂为十二烷基硫醇，引发剂为过硫酸钾，非离子乳化剂为OP-10，扩散剂为NNO，电解质为硫酸钾。
将实施例1-实施例3的改性丁吡胶乳与对比例1和对比例2的丁吡胶乳进行老化性能测试，其测试结果见下表。
由上表可知，使用马来酸酐改性处理后胶乳的老化性能有了明显的提升，相较于未使用马来酸酐改性，耐老化性能提升15％以上；皂液比例适度调整后耐老化性能提升仅10％左右。
此外，本案发明人还参照前述实施例，以本说明书述及的其它原料、工艺操作、工艺条件进行了试验，并均获得了较为理想的结果。
尽管已参考说明性实施例描述了本发明，但所属领域的技术人员将理解，在不背离本发明的精神及范围的情况下可做出各种其它改变、省略及/或添加且可用实质等效物替代所述实施例的元件。另外，可在不背离本发明的范围的情况下做出许多修改以使特定情形或材料适应本发明的教示。因此，本文并不打算将本发明限制于用于执行本发明的所揭示特定实施例，而是打算使本发明将包含归属于所附权利要求书的范围内的所有实施例。此外，除非具体陈述，否则术语第一、第二等的任何使用不表示任何次序或重要性，而是使用术语第一、第二等来区分一个元素与另一元素。
Claims (8)
1.一种改性丁吡胶乳，其特征在于，包括如下重量份的组分：丁二烯65-75份、苯乙烯10-15份、2-乙烯基吡啶 10-15份、分子量调节剂0.5-1.0份、马来酸酐1-5份、阴离子乳化剂3.8-4.5份，非离子乳化剂0.5-1.5份，扩散剂0.4-0.6份，电解质0.05-0.5份和引发剂0.1-0.5份；其中，所述阴离子乳化剂为松香钾皂、脂肪酸钾皂、烷基磺酸钠和烷基苯磺酸钠组成的混合体系；且所述改性丁吡胶乳通过如下步骤制备而成：
将去离子水、阴离子乳化剂、非离子乳化剂、扩散剂和电解质组成的混合体系配制成乳化液；
将丁二烯、苯乙烯、2-乙烯基吡啶、分子量调节剂和马来酸酐混合，配制成油相溶液；
将乳化液和油相溶液置于反应容器中，并滴加引发剂，混合反应15-20h，获得所述改性丁吡胶乳。
2.根据权利要求1所述的改性丁吡胶乳，其特征在于：所述分子量调节剂包括叔十二烷基硫醇、巯基丁酸酯中的任意一种或多种的组合。
3.根据权利要求1所述的改性丁吡胶乳，其特征在于：所述引发剂包括过硫酸钾、过氧化氢二异丙苯、叔丁基过氧化氢、偶氮二异庚腈中的任意一种或多种的组合。
4.根据权利要求1所述的改性丁吡胶乳，其特征在于：所述非离子乳化剂包括烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚类中的任意一种或多种的组合。
5.根据权利要求1所述的改性丁吡胶乳，其特征在于：所述扩散剂包括亚甲基二萘磺酸钠、木质素磺酸钠中的任意一种或多种组合。
6.根据权利要求1所述的改性丁吡胶乳，其特征在于：所述电解质包括氯化钾、硫酸钾、磷酸钾中的任意一种或多种的组合。
7.权利要求1-6中任意一项所述的改性丁吡胶乳于橡胶制品的骨架材料中的应用。
8.根据权利要求7所述的应用，其特征在于：所述橡胶制品包括轮胎、三角带、胶管或胶带中的任意一种。