CN114806294A - 一种防水隔热外墙涂料及其制备方法 - Google Patents
一种防水隔热外墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN114806294A CN114806294A CN202210369182.4A CN202210369182A CN114806294A CN 114806294 A CN114806294 A CN 114806294A CN 202210369182 A CN202210369182 A CN 202210369182A CN 114806294 A CN114806294 A CN 114806294A
- Authority
- CN
- China
- Prior art keywords
- parts
- exterior wall
- wall coating
- mixed solution
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防水隔热外墙涂料及其制备方法，其供于建筑外墙的防护和装饰使用。上述外墙涂料具备以下组分：水性乳液、云母粉、硅灰石粉、树脂填料、光稳定剂、中空陶瓷颗粒、复合助剂、防冻剂、颜料以及去离子水按比例制作得到所述外墙涂料。本发明的外墙涂料采用水性基底体系，具备对人体无害、环境无污染、柔韧性好、耐水和耐磨的优点，并且抗干裂和干缩效果优异，适合推广使用，此外，基于光反射隔热和中空隔热使得外墙涂料应用时的防水、隔热、防潮和防霉效果优异。
Description
技术领域
本发明涉及建筑涂料领域，特别是涉及一种防水隔热外墙涂料，还涉及所述涂料的制备方法。
背景技术
涂料是建筑领域不可或缺的材料之一，其主要作用是保护建筑物表面使其具有防水、耐污、隔热或抗紫外线等作用，高级一点的外墙涂料还有自涤性，脏污一冲就掉。
然而，现有的外墙涂料在应用时，抗干裂和干缩效果不佳，影响了耐用度，此外，外墙涂料应用时的防水、隔热、防潮和防霉效果差，不利于推广使用。
发明内容
基于此，有必要针对当下外墙涂料在应用时，抗干裂和干缩效果不佳，影响了耐用度，此外，外墙涂料应用时的防水、隔热、防潮和防霉效果差，不利于推广使用的问题，提供一种防水隔热外墙涂料及其制备方法。
一种防水隔热外墙涂料，其供于建筑外墙的防护和装饰使用，其特征在于，所述外墙涂料具备以下组分：水性乳液、云母粉、硅灰石粉、树脂填料、光稳定剂、中空陶瓷颗粒、复合助剂、防冻剂、颜料以及去离子水按比例制作得到所述外墙涂料；其中，所述水性乳液和所述树脂填料的重量份配比为10：1；
所述水性乳液采用醋酸乙烯和丙烯酸共聚乳液、苯乙烯和丙烯酸共聚乳液或纯丙烯酸乳液。
上述外墙涂料采用水性基底体系，具备对人体无害、环境无污染、柔韧性好、耐水和耐磨的优点，并且抗干裂和干缩效果优异，适合推广使用，此外，基于光反射隔热和中空隔热使得外墙涂料应用时的防水、隔热、防潮和防霉效果优异。
在其中一个实施例中，所述云母粉和所述硅灰石粉的重量份配比为1：1；所述树脂填料为氟树脂或合成树脂；所述光稳定剂采用水杨酸酯、苯酮和苯并***中的任意一种。
在其中一个实施例中，所述防冻剂采用甲醇、乙醇、异丙醇、乙二醇、丙二醇、二甘醇、乙二醇丁醚、丙二醇丁醚和乙二醇丁醚醋酸酯中的至少一种；所述颜料为喹吖啶酮、酞菁、钛白粉或锑白。
在其中一个实施例中，所述外墙涂料的重量份组成如下：水性乳液50～60份、云母粉10～12份、硅灰石粉10～12份、树脂填料5～6份、光稳定剂2～5份、中空陶瓷颗粒7～9份、复合助剂6～8份、防冻剂3～7份、颜料2～4份、去离子水25～30份。
进一步地，所述外墙涂料的重量份组成如下：水性乳液55份、云母粉11份、硅灰石粉11份、树脂填料5.5份、光稳定剂4份、中空陶瓷颗粒8份、复合助剂7份、防冻剂5份、颜料3份、去离子水28份。
再进一步地，所述复合助剂的重量份组成如下：十二烷基苯磺酸4～8份、二丙二醇丁醚9～12份、增稠剂3～5份、消泡剂1～3份、流平剂1～3份。
在其中一个实施例中，所述增稠剂为木质纤维素、石棉纤维或羟丙甲基纤维；所述消泡剂为正辛醇、丁醇和磷酸三丁酯中的至少一种；所述流平剂为丁基纤维素或聚丙烯酸。
一种涂料的制备方法，包括以下步骤：
S1混配得到复合助剂，备用；
S2依次于容器中加入水性乳液、云母粉、硅灰石粉和树脂填料，均匀搅拌10～15min，获得混合液A；
S3于所述混合液A中加入光稳定剂和中空陶瓷颗粒，混合搅拌10～12min，获得混合液B；
S4将所述复合助剂加入所述混合液B中，离心分散8～10min，获得混合液C；
S5依次于所述混合液C中缓慢加入防冻剂，混合搅拌10～12min，获得混合液D；
S6取颜料和去离子水加入所述混合液D中，搅拌20～22min，获得粘稠液，即外墙涂料。
在其中一个实施例中，S2～S6中，所述搅拌均在水热反应釜中进行；S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉；或，当粘度过高时，加入95％乙醇进行稀释。
在其中一个实施例中，所述制备方法应用于所述的一种防水隔热外墙涂料的制备中。
与现有技术相比，本发明的有益效果是：
本发明，基于水性乳液和树脂填料构成的水性基底体系，从而使得外墙涂料具备无毒无刺激气味、对人体无害、环境无污染、柔韧性好、耐水、耐磨和耐黄变的优点，并且，基于树脂填料对水性乳液干燥后的基材进行增韧，改善外墙涂料的性能，使得其抗干裂和干缩效果优异，适合推广使用。
本发明，基于掺入中空陶瓷颗粒和光稳定剂，协同配合进行光反射隔热和中空隔热，通过光稳定剂来反射紫外光，从而提高外墙涂料的抗老化和耐用度，此外，结合中空陶瓷颗粒基于中空的微珠结构来阻隔热传导，并实现防水、防潮和防霉等综合防护。
综上，本发明的外墙涂料采用水性基底体系，具备对人体无害、环境无污染、柔韧性好、耐水和耐磨的优点，并且抗干裂和干缩效果优异，适合推广使用，此外，基于光反射隔热和中空隔热使得外墙涂料应用时的防水、隔热、防潮和防霉效果优异。
具体实施方式
下面对本发明进行详细的描述。
本发明提供了一种防水隔热外墙涂料，其供于建筑外墙的防护和装饰使用，所述外墙涂料具备以下组分：水性乳液、云母粉、硅灰石粉、树脂填料、光稳定剂、中空陶瓷颗粒、复合助剂、防冻剂、颜料以及去离子水按比例制作得到所述外墙涂料，其中，所述水性乳液和所述树脂填料的重量份配比为10：1，所述云母粉和所述硅灰石粉的重量份配比为1：1。所述水性乳液采用醋酸乙烯和丙烯酸共聚乳液、苯乙烯和丙烯酸共聚乳液或纯丙烯酸乳液。所述树脂填料为氟树脂或合成树脂。所述光稳定剂采用水杨酸酯、苯酮和苯并***中的任意一种。所述防冻剂采用甲醇、乙醇、异丙醇、乙二醇、丙二醇、二甘醇、乙二醇丁醚、丙二醇丁醚和乙二醇丁醚醋酸酯中的至少一种。所述颜料为喹吖啶酮、酞菁、钛白粉或锑白。
本发明，基于水性乳液和树脂填料构成的水性基底体系，从而使得外墙涂料具备无毒无刺激气味、对人体无害、环境无污染、柔韧性好、耐水、耐磨和耐黄变的优点，并且，基于树脂填料对水性乳液干燥后的基材进行增韧，改善外墙涂料的性能，使得其抗干裂和干缩效果优异，适合推广使用。
外墙涂料的重量份组成如下：水性乳液50～60份、云母粉10～12份、硅灰石粉10～12份、树脂填料5～6份、光稳定剂2～5份、中空陶瓷颗粒7～9份、复合助剂6～8份、防冻剂3～7份、颜料2～4份、去离子水25～30份。本发明，基于掺入中空陶瓷颗粒和光稳定剂，协同配合进行光反射隔热和中空隔热，通过光稳定剂来反射紫外光，从而提高外墙涂料的抗老化和耐用度，此外，结合中空陶瓷颗粒基于中空的微珠结构来阻隔热传导，并实现防水、防潮和防霉等综合防护。所述复合助剂的重量份组成如下：十二烷基苯磺酸4～8份、二丙二醇丁醚9～12份、增稠剂3～5份、消泡剂1～3份、流平剂1～3份。所述增稠剂为木质纤维素、石棉纤维或羟丙甲基纤维。所述消泡剂为正辛醇、丁醇和磷酸三丁酯中的至少一种。所述流平剂为丁基纤维素或聚丙烯酸。
本发明还提供了一种涂料的制备方法，其用于上述一种防水隔热外墙涂料的制备中。制备方法包括以下步骤：
S1混配得到复合助剂，备用。
S2依次于容器中加入水性乳液、云母粉、硅灰石粉和树脂填料，均匀搅拌10～15min，获得混合液A。
S3于所述混合液A中加入光稳定剂和中空陶瓷颗粒，混合搅拌10～12min，获得混合液B。
S4将所述复合助剂加入所述混合液B中，离心分散8～10min，获得混合液C。
S5依次于所述混合液C中缓慢加入防冻剂，混合搅拌10～12min，获得混合液D。
S6取颜料和去离子水加入所述混合液D中，搅拌20～22min，获得粘稠液，即外墙涂料。
S2～S6中，所述搅拌均在水热反应釜中进行，S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉，或，当粘度过高时，加入95％乙醇进行稀释。
实施例1
本实施例提供了一种防水隔热外墙涂料，其供于建筑外墙的防护和装饰使用。外墙涂料的重量份组成如下：水性乳液(醋酸乙烯和丙烯酸共聚乳液)50份、云母粉10份、硅灰石粉10份、合成树脂5份、苯酮2份、中空陶瓷颗粒7份、复合助剂6份、防冻剂(甲醇+乙醇)3份、喹吖啶酮2份、去离子水25份。
其中，所述复合助剂的重量份组成如下：十二烷基苯磺酸4份、二丙二醇丁醚9份、木质纤维素3份、正辛醇1份、丁基纤维素1份。
上述外墙涂料的制备方法，包括以下步骤：
S1混配得到复合助剂，备用。
S2依次于容器中加入水性乳液(醋酸乙烯和丙烯酸共聚乳液)、云母粉、硅灰石粉和合成树脂，均匀搅拌10min，获得混合液A。
S3于所述混合液A中加入苯酮和中空陶瓷颗粒，混合搅拌10min，获得混合液B。
S4将所述复合助剂加入所述混合液B中，离心分散8min，获得混合液C。
S5依次于所述混合液C中缓慢加入防冻剂(甲醇+乙醇)，混合搅拌10min，获得混合液D。
S6取喹吖啶酮和去离子水加入所述混合液D中，搅拌20min，获得粘稠液，即外墙涂料。
S2～S6中，所述搅拌均在水热反应釜中进行，S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉，或，当粘度过高时，加入95％乙醇进行稀释。
实施例2
本实施例提供了一种防水隔热外墙涂料，其供于建筑外墙的防护和装饰使用。外墙涂料的重量份组成如下：水性乳液(纯丙烯酸乳液)55份、云母粉11份、硅灰石粉11份、氟树脂5.5份、水杨酸酯4份、中空陶瓷颗粒8份、复合助剂7份、乙二醇丁醚5份、钛白粉3份、去离子水28份。
其中，所述复合助剂的重量份组成如下：十二烷基苯磺酸6份、二丙二醇丁醚11份、石棉纤维4份、丁醇2份、聚丙烯酸2份。
上述外墙涂料的制备方法，包括以下步骤：
S1混配得到复合助剂，备用。
S2依次于容器中加入水性乳液(纯丙烯酸乳液)、云母粉、硅灰石粉和氟树脂，均匀搅拌12min，获得混合液A。
S3于所述混合液A中加入水杨酸酯和中空陶瓷颗粒，混合搅拌11min，获得混合液B。
S4将所述复合助剂加入所述混合液B中，离心分散9min，获得混合液C。
S5依次于所述混合液C中缓慢加入乙二醇丁醚，混合搅拌12min，获得混合液D。
S6取钛白粉和去离子水加入所述混合液D中，搅拌21min，获得粘稠液，即外墙涂料。
S2～S6中，所述搅拌均在水热反应釜中进行，S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉，或，当粘度过高时，加入95％乙醇进行稀释。
实施例3
本实施例提供了一种防水隔热外墙涂料，其供于建筑外墙的防护和装饰使用。外墙涂料的重量份组成如下：水性乳液(苯乙烯和丙烯酸共聚乳液)60份、云母粉12份、硅灰石粉12份、合成树脂6份、苯并***5份、中空陶瓷颗粒9份、复合助剂8份、防冻剂(乙二醇、丙二醇)7份、锑白4份、去离子水30份。
其中，所述复合助剂的重量份组成如下：十二烷基苯磺酸8份、二丙二醇丁醚12份、羟丙甲基纤维5份、磷酸三丁酯3份、丁基纤维素3份。
上述外墙涂料的制备方法，包括以下步骤：
S1混配得到复合助剂，备用。
S2依次于容器中加入水性乳液(苯乙烯和丙烯酸共聚乳液)、云母粉、硅灰石粉和合成树脂，均匀搅拌15min，获得混合液A。
S3于所述混合液A中加入苯并***和中空陶瓷颗粒，混合搅拌12min，获得混合液B。
S4将所述复合助剂加入所述混合液B中，离心分散10min，获得混合液C。
S5依次于所述混合液C中缓慢加入防冻剂(乙二醇、丙二醇)，混合搅拌12min，获得混合液D。
S6取锑白和去离子水加入所述混合液D中，搅拌22min，获得粘稠液，即外墙涂料。
S2～S6中，所述搅拌均在水热反应釜中进行，S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉，或，当粘度过高时，加入95％乙醇进行稀释。
实施例4，对实施例1-3分别制备的防水隔热外墙涂料的性能进行检测，检测结果如下：
Claims (10)
1.一种防水隔热外墙涂料，其特征在于，所述外墙涂料具备以下组分：水性乳液、云母粉、硅灰石粉、树脂填料、光稳定剂、中空陶瓷颗粒、复合助剂、防冻剂、颜料以及去离子水按比例制作得到所述外墙涂料；其中，所述水性乳液和所述树脂填料的重量份配比为10：1；
所述水性乳液采用醋酸乙烯和丙烯酸共聚乳液、苯乙烯和丙烯酸共聚乳液或纯丙烯酸乳液。
2.根据权利要求1所述的一种防水隔热外墙涂料，其特征在于，所述云母粉和所述硅灰石粉的重量份配比为1：1；
所述树脂填料为氟树脂或合成树脂；所述光稳定剂采用水杨酸酯、苯酮和苯并***中的任意一种。
3.根据权利要求1所述的一种防水隔热外墙涂料，其特征在于，所述防冻剂采用甲醇、乙醇、异丙醇、乙二醇、丙二醇、二甘醇、乙二醇丁醚、丙二醇丁醚和乙二醇丁醚醋酸酯中的至少一种；
所述颜料为喹吖啶酮、酞菁、钛白粉或锑白。
4.根据权利要求1所述的一种防水隔热外墙涂料，其特征在于，所述外墙涂料的重量份组成如下：水性乳液50~60份、云母粉10~12份、硅灰石粉10~12份、树脂填料5~6份、光稳定剂2~5份、中空陶瓷颗粒7~9份、复合助剂6~8份、防冻剂3~7份、颜料2~4份、去离子水25~30份。
5.根据权利要求4所述的一种防水隔热外墙涂料，其特征在于，所述外墙涂料的重量份组成如下：水性乳液55份、云母粉11份、硅灰石粉11份、树脂填料5.5份、光稳定剂4份、中空陶瓷颗粒8份、复合助剂7份、防冻剂5份、颜料3份、去离子水28份。
6.根据权利要求5所述的一种防水隔热外墙涂料，其特征在于，所述复合助剂的重量份组成如下：十二烷基苯磺酸4~8份、二丙二醇丁醚9~12份、增稠剂3~5份、消泡剂1~3份、流平剂1~3份。
7.根据权利要求6所述的一种防水隔热外墙涂料，其特征在于，所述增稠剂为木质纤维素、石棉纤维或羟丙甲基纤维；
所述消泡剂为正辛醇、丁醇和磷酸三丁酯中的至少一种；所述流平剂为丁基纤维素或聚丙烯酸。
8.一种涂料的制备方法，其特征在于，包括以下步骤：
S1混配得到复合助剂，备用；
S2依次于容器中加入水性乳液、云母粉、硅灰石粉和树脂填料，均匀搅拌10~15min，获得混合液A；
S3于所述混合液A中加入光稳定剂和中空陶瓷颗粒，混合搅拌10~12min，获得混合液B；
S4将所述复合助剂加入所述混合液B中，离心分散8~10min，获得混合液C；
S5依次于所述混合液C中缓慢加入防冻剂，混合搅拌10~12min，获得混合液D；
S6取颜料和去离子水加入所述混合液D中，搅拌20~22min，获得粘稠液，即外墙涂料。
9.根据权利要求8所述的一种涂料的制备方法，其特征在于，S2~S6中，所述搅拌均在水热反应釜中进行；
S6中，对获得粘稠液的进行粘度测试，当粘度过低时，继续加入硅灰石粉；
或，当粘度过高时，加入95%乙醇进行稀释。
10.根据权利要求8所述的一种涂料的制备方法，其特征在于，所述制备方法应用于如权利要求1至7中任意一项所述的一种防水隔热外墙涂料的制备中。