CN114656635B - Preparation method of polyimide printed circuit board with high peel strength and low dielectric constant - Google Patents
Preparation method of polyimide printed circuit board with high peel strength and low dielectric constant Download PDFInfo
- Publication number
- CN114656635B CN114656635B CN202210571917.1A CN202210571917A CN114656635B CN 114656635 B CN114656635 B CN 114656635B CN 202210571917 A CN202210571917 A CN 202210571917A CN 114656635 B CN114656635 B CN 114656635B
- Authority
- CN
- China
- Prior art keywords
- silicon
- printed circuit
- circuit board
- diamine monomer
- containing diamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the technical field of printed circuit boards, and particularly relates to a preparation method of a polyimide printed circuit board with high peel strength and low dielectric constant. The method synthesizes novel siloxane-containing fluorine-containing diamine 4,4' - (1, 3-dimethyl-1, 3-bis (3,3, 3-trifluoropropyl) disiloxane-1, 3-diacyl) diphenylamine, and utilizes the siloxane-containing diamine to modify polyimide to realize the functionalization and fluorine-containing of polyimide silicon oxide, so that the material and a copper foil have higher cohesiveness, and the prepared flexible printed circuit board has good peeling strength, and simultaneously adopts a fluorine-containing monomer with low electronic polarizability to ensure that the obtained material has lower dielectric constant. The printed circuit board prepared by the invention belongs to a glue-free printed circuit board, and can be applied to the field of high-frequency high-speed communication.
Description
Technical Field
The invention belongs to the technical field of printed circuit boards, and particularly relates to a preparation method of a polyimide printed circuit board with high peel strength and low dielectric constant.
Background
In recent years, the 5G technology has been rapidly advanced. The market demand for printed circuit boards as the main body of signal transmission structures is growing explosively, and the core of the printed circuit boards used in the field of high-frequency and high-speed communication such as 5G is that the insulating materials used have lower dielectric constant and dielectric loss on the basis of keeping the performance of the traditional materials. Polyimide has the advantages of excellent thermal stability, outstanding mechanical properties, lower dielectric constant and the like, and is a common material for preparing flexible printed circuit boards. Meanwhile, fluorine has the characteristics of large volume and low electronic polarizability, the dielectric constant and the dielectric loss of the polyimide material can be further reduced (the dielectric constant is less than 3.0, and the dielectric loss factor is less than 0.001) by introducing the fluorine, and the requirements of high frequency and high speed of 5G communication are met. Compared with the traditional glue type printed circuit board, the glue-free printed circuit board is lighter and thinner, is easier to fold, is more environment-friendly, has better dimensional stability, has higher processing difficulty, limits the development of the glue-free printed circuit board in the field of the glue-free printed circuit board due to poorer cohesiveness between the polyimide material and the copper foil, and particularly leads the cohesiveness to be worse after fluorine is introduced into the polyimide. Therefore, the development of polyimide materials with high adhesion and low dielectric properties is of great importance in the application of flexible printed circuit boards in the electronic industry.
Disclosure of Invention
Aiming at the requirements of low dielectric property, high peel strength and no gelation in the field of high-frequency and high-speed communication substrates, the invention provides a preparation method of a non-gel type polyimide printed circuit board with high peel strength and low dielectric constant.
The technical scheme adopted by the invention is as follows:
the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant comprises the following steps: synthesizing a silicon-containing diamine monomer B by using 4-bromo-N, N-bis (trimethylsilyl) aniline, dissolving the silicon-containing diamine monomer B and other diamine monomers in a polar aprotic solvent at normal temperature, and adding 4,4 '-hexafluoroisopropyl phthalic anhydride and other dianhydride monomers in a one-half feeding method in five times, wherein the molar ratio of the 4,4' -hexafluoroisopropyl phthalic anhydride to the other dianhydride monomers is 2: 1, regulating the temperature to 5-10 ℃ in ice water bath, polymerizing for 12 hours at low temperature to obtain precursor polyamic acid solution containing siloxane and fluorine with certain viscosity, removing bubbles in vacuum for 0.5 hour, coating the polyamic acid solution on a copper foil with the wet film thickness of 30-35 microns, drying the solvent at 80-150 ℃, transferring the copper-clad plate into a vacuum oven, imidizing at 180-300 ℃, and cooling to obtain the copper-clad plate.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the silicon-containing diamine monomer B is synthesized by the following method: under the protection of nitrogen, adding 4-bromo-N, N-bis (trimethylsilyl) aniline and magnesium into a dry reactor filled with fresh diethyl ether, reacting at 30 ℃ for 1h, and then refluxing and stirring to react for 3 h; cooling the system to room temperature, adding trifluoropropylmethyldichlorosilane with the same amount as 4-bromo-N, N-bis (trimethylsilyl) aniline into a reactor, reacting the reaction mixture at reflux temperature for 2 hours, and distilling to obtain a silicon-containing diamine precursor A; under the protection of nitrogen, adding the obtained silicon-containing diamine precursor A into a drying reactor filled with triethylamine, dropwise adding deionized water with the mole number of 1/2 of the silicon-containing diamine precursor A at 80 ℃, reacting for 5 hours, cooling the reaction mixture to room temperature, filtering to remove solids to obtain a viscous liquid crude product, adding ethanol into the crude product, stirring for 3 hours at room temperature, removing the ethanol by spin drying, and washing with deionized water to obtain the silicon-containing diamine monomer B.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the content of the silicon-containing diamine monomer B accounts for 5-20% of the total mole number of the silicon-containing diamine monomer and other diamine monomers.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the polar aprotic solvent is one of N-methylpyrrolidone, N-dimethylacetamide and N, N-dimethylformamide.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the other diamine monomers further comprise one or more of 2,2 '-bis (trifluoromethyl) -4,4' -diaminobiphenyl, 2 '-bis (trifluoromethyl) -4,4' -diaminophenyl ether, 4'- (hexafluoroisopropyl) bis (p-phenoxy) diphenylamine, 4' -diaminophenyl ether and p-phenylenediamine.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the other dianhydride monomers comprise one or more of 3,3',4,4' -benzophenone tetracarboxylic dianhydride, 2,3,3', 4-biphenyl tetracarboxylic dianhydride, pyromellitic dianhydride and 3,3',4,4' -biphenyl tetracarboxylic dianhydride.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the ratio of the total mole number of the silicon-containing diamine monomer and other diamine monomers to the total mole number of the 4,4' -hexafluoroisopropyl phthalic anhydride and other dianhydride monomers is 1.02: 1.
in the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, in the precursor polyamic acid solution, the solid content of the silicon-containing diamine monomer, the other diamine monomers, the 4,4' -hexafluoroisopropyl phthalic anhydride and the other dianhydride monomers accounts for 20% of the total mass of the precursor polyamic acid.
In the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the molar ratio of the 4-bromo-N, N-bis (trimethylsilyl) aniline to the magnesium is 1: 1.008.
according to the preparation method of the polyimide printed circuit board with high peel strength and low dielectric constant, the molar ratio of the silicon-containing diamine precursor A to triethylamine is 1: 4.
has the advantages that:
the novel siloxane chain segment is introduced, so that on one hand, the contact area of the polyimide material and other matrixes is remarkably increased, the adhesion is remarkably enhanced, the peeling strength between the polyimide film and the copper foil is improved, the preparation of the adhesive-free flexible printed circuit board is realized, on the other hand, the siloxane chain segment also contains fluorine, and the siloxane chain segment can be synergistically acted with other fluorine-containing monomers in a system, so that the dielectric constant and the dielectric loss of the obtained material are further reduced, the preparation of the adhesive-free high-frequency high-speed flexible printed circuit board is finally realized, and the peeling strength is very high.
Drawings
FIG. 1 is a structural formula and nuclear magnetic hydrogen spectrum of a silicon-containing diamine monomer B;
FIG. 2 is a structural formula and a carbon spectrum of a silicon-containing diamine monomer B.
Detailed Description
In order to make the technical means, the characteristics, the objectives and the functions of the present invention easy to understand, the present invention will be further described with reference to the following embodiments.
Example 1
The embodiment provides a preparation method of a polyimide printed circuit board with high peel strength and low dielectric constant, which comprises the following steps:
1. preparing a silicon-containing diamine monomer B, wherein the silicon-containing diamine monomer B is 4,4' - (1, 3-dimethyl-1, 3-bis (3,3, 3-trifluoropropyl) disiloxane-1, 3-diacyl) diphenylamine: under the protection of nitrogen, 1.58g,5.00mmol of 4-bromo-N, N-bis (trimethylsilyl) aniline and 121mg,5.04mmol of magnesium are added into a dry reactor filled with fresh ether, and the mixture is reacted for 1 hour at 30 ℃ and then stirred under reflux for 3 hours; after cooling the system to room temperature, 1.06g,5.00mol of trifluoropropylmethyldichlorosilane was added to the reactor and the reaction mixture was reacted at reflux temperature for 2h, followed by distillation to give 118.0mg,3.25mmol of silicon-containing diamine precursor A with a yield of 65.1%. Under the protection of nitrogen, the obtained silicon-containing diamine precursor A is added into a dry reactor containing 1.21g of 12.00mmol of triethylamine, 27mg of 1.50mmol of deionized water is dropwise added at 80 ℃, the reaction is carried out for 5 hours, the reaction mixture is cooled to room temperature, and then the solid is removed by filtration to obtain a viscous liquid crude product. Adding ethanol into the crude product, stirring for 3h at room temperature, spin-drying to remove ethanol, and washing with deionized water for 3 times to obtain 1.04g and 2.16mmol of silicon-containing diamine monomer B.
Referring to fig. 1 and 2, the structural formula of the silicon-containing diamine monomer B and nuclear magnetic hydrogen and carbon spectrograms are shown: 1 H NMR (500 MHz, DMSO-d6) δ 0.26 (s, 6H), 1.21 (t, J = 9.5 Hz, 4H), 2.16-2.22 (m, 4H), 4.04 (s, 4H), 6.70 (d, J = 9.1 Hz, 4H), 7.35 (d, J = 9.1 Hz, 4H); 13 C NMR (125 MHz, DMSO-d6) δ 149.11, 135.40, 128.80, 128.46, 126.66, 114.66, 33.21, 33.13, 33.05, 32.97, 31.50, 31.28, 31.07, 30.85。
2. adding a silicon-containing diamine monomer composition into a reaction kettle, wherein the silicon-containing diamine monomer composition comprises a silicon-containing diamine monomer B and 2,2 '-bis (trifluoromethyl) -4,4' -diaminobiphenyl, and the molar ratio of the silicon-containing diamine monomer B to the 2: 8. n, N-dimethylacetamide was added and dissolved at room temperature with stirring for about 0.5 h. After complete dissolution, a dianhydride monomer composition comprising 4,4 '-hexafluoroisopropyl phthalic anhydride and 2,3,3', 4-biphenyl tetracarboxylic dianhydride in a molar ratio of 2: 1. the ratio of the total moles of dianhydride monomer composition to the total moles of silicon-containing diamine monomer composition is 1.02: 1. regulating the temperature in ice-water bath to 5-10 ℃. And (3) continuing stirring for 12 hours after the last dosing is finished, adjusting the solid content of the solution to be 20%, and polymerizing for 12 hours at low temperature to obtain the precursor polyamide acid solution containing siloxane and fluorine with certain viscosity. The precursor polyamic acid solution is vacuumed for 0.5 hour, then coated on a copper foil, the thickness of a wet film is 30 microns, the solvent is dried under the conditions of 80 ℃,1 hour, 120 ℃, 150 ℃ and 1 hour, and then the copper-clad plate is transferred into a vacuum oven and imidized at 180 ℃, 210 ℃, 240 ℃, 270 ℃ and 300 ℃ for 30min respectively. After cooling, the non-glue polyimide printed circuit board with high peeling strength and low dielectric constant of the embodiment can be obtained.
Example 2
The present embodiment is different from embodiment 1 in that: adding silicon-containing diamine monomer B and 4,4- (hexafluoroisopropyl) bis (p-phenoxy) diphenylamine into a reaction kettle in a molar ratio of 3: 7. n, N-dimethylformamide was added and the mixture was dissolved at room temperature with stirring for about 0.5 h. After complete dissolution, 4,4' -hexafluoroisopropylphthalic anhydride and 3,3',4,4' -benzophenonetetracarboxylic dianhydride were added in five portions by a one-half addition method in a molar ratio of 2: 1, and controlling the temperature to be 5-10 ℃. And (3) continuing stirring for 12 hours after the last dosing is finished, and adjusting the solid content of the solution to 20% to obtain a precursor polyamide acid solution. The polyamic acid solution was defoamed in vacuum for 0.5 hour, then coated on a copper foil with a wet film thickness of 32 μm, the solvent was dried at 80 ℃,1 hour, 120 ℃, 150 ℃,1 hour, and then the copper-clad plate was transferred to a vacuum oven and imidized at 180 ℃, 210 ℃, 240 ℃, 270 ℃, and 300 ℃ for 30min each. After cooling, the non-glue type polyimide printed circuit board with high peel strength and low dielectric constant of the embodiment can be obtained.
Example 3
Adding silicon-containing diamine monomer B and 4,4 '-diamino phenyl ether into a reaction kettle, wherein the molar ratio of the silicon-containing diamine monomer B to the 4,4' -diamino phenyl ether is: 6. n-methylpyrrolidone was added and dissolved at room temperature with stirring for about 0.5 h. After complete dissolution, 4' -hexafluoroisopropyl phthalic anhydride and pyromellitic dianhydride were added in five portions by a one-half addition method in a molar ratio of 2: 1, and controlling the temperature to be 5-10 ℃. And (3) after the last dosing is finished, continuously stirring for 12h, adjusting the solid content of the solution to be 20%, obtaining a polyamic acid solution, carrying out vacuum defoaming on the polyamic acid solution for 0.5h, then coating the polyamic acid solution on a copper foil, wherein the thickness of a wet film is 35 microns, drying the solvent at 80 ℃, 1h, 120 ℃, 150 ℃ and 1h, then transferring the copper-clad plate into a vacuum oven, and imidizing the copper-clad plate at 180 ℃, 210 ℃, 240 ℃, 270 ℃ and 300 ℃ for 30min respectively. Cooling to obtain the non-glue polyimide printed circuit board with high peel strength and low dielectric constant.
Comparative example 1
4,4' -diamino phenyl ether is added into the reaction kettle, and N, N-dimethyl acetamide is added, and the mixture is stirred and dissolved for about 0.5h at room temperature. After complete dissolution, adding pyromellitic dianhydride and 2,3,3', 4-biphenyl tetracarboxylic dianhydride in a one-half feeding method in a molar ratio of 2: 1, and controlling the temperature to be 5-10 ℃. And (3) continuing stirring for 12 hours after the last dosing is finished, and adjusting the solid content of the solution to be 20% to obtain the polyamic acid solution. The polyamic acid solution was defoamed in vacuum for 0.5 hour, then coated on a copper foil with a wet film thickness of 32 μm, the solvent was dried at 80 ℃,1 hour, 120 ℃, 150 ℃,1 hour, and then the copper-clad plate was transferred to a vacuum oven and imidized at 180 ℃, 210 ℃, 240 ℃, 270 ℃, and 300 ℃ for 30min each. After cooling, a flexible polyimide printed circuit board is obtained.
Comparative example 2
Adding 2,2 '-bis (trifluoromethyl) -4,4' -diaminobiphenyl into a reaction kettle, adding N, N-dimethylacetamide, and stirring and dissolving for about 0.5h at room temperature. After complete dissolution, adding pyromellitic dianhydride and 2,3,3', 4-biphenyl tetracarboxylic dianhydride in a half-feeding method for five times, wherein the molar ratio is 2: 1, and controlling the temperature to be 5-10 ℃. And (5) after the last dosing is finished, continuously stirring for 12 hours, and adjusting the solid content of the solution to be 20% to obtain the polyamide acid solution. The polyamic acid solution was defoamed in vacuum for 0.5 hour, then coated on a copper foil with a wet film thickness of 32 μm, the solvent was dried at 80 ℃,1 hour, 120 ℃, 150 ℃,1 hour, and then the copper-clad plate was transferred to a vacuum oven and imidized at 180 ℃, 210 ℃, 240 ℃, 270 ℃, and 300 ℃ for 30min each. And cooling to obtain the flexible polyimide printed circuit board.
Comparative example 3
The reaction kettle is added with 2,2 '-bis (trifluoromethyl) -4,4' -diaminophenyl ether, then added with N, N-dimethylacetamide, and stirred and dissolved for about 0.5h at room temperature. After complete dissolution, adding pyromellitic dianhydride and 2,3,3', 4-biphenyl tetracarboxylic dianhydride in a half-feeding method for five times, wherein the molar ratio is 2: 1, and controlling the temperature to be 5-10 ℃. And (3) continuing stirring for 12 hours after the last dosing is finished, and adjusting the solid content of the solution to be 20% to obtain the polyamic acid solution. The polyamic acid solution was defoamed in vacuum for 0.5 hour, then coated on a copper foil with a wet film thickness of 32 μm, the solvent was dried at 80 ℃,1 hour, 120 ℃, 150 ℃,1 hour, and then the copper-clad plate was transferred to a vacuum oven and imidized at 180 ℃, 210 ℃, 240 ℃, 270 ℃, and 300 ℃ for 30min each. And cooling to obtain the flexible polyimide printed circuit board.
The properties of the materials tested in this example and comparative example are shown in the following table:
as can be seen from the above table, the novel siloxane chain segment is introduced, so that the contact area between the polyimide material and other matrixes is remarkably increased, the adhesion of the polyimide material is remarkably enhanced, the peeling strength between the polyimide film and the copper foil is improved, the preparation of the flexible printed circuit board without glue is realized, on the other hand, the siloxane chain segment also contains fluorine, and the siloxane chain segment can be cooperated with other fluorine-containing monomers in a system to further reduce the dielectric constant and the dielectric loss of the obtained material, and finally, the preparation of the flexible printed circuit board without glue at high frequency and high speed is realized, and the peeling strength is very high.
Further, the content of the silicon-containing diamine monomer B accounts for 5-20% of the total mole number of the silicon-containing diamine monomer and other diamine monomers.
Further, the polar aprotic solvent used is one of N-methylpyrrolidone, N-dimethylacetamide, or N, N-dimethylformamide.
Further, the other diamine monomer also comprises one or more of 2,2 '-bis (trifluoromethyl) -4,4' -diaminobiphenyl, 2 '-bis (trifluoromethyl) -4,4' -diaminophenyl ether, 4'- (hexafluoroisopropyl) bis (p-phenoxy) diphenylamine, 4' -diaminophenyl ether and p-phenylenediamine.
Further, the other dianhydride monomer comprises one or more of 3,3',4,4' -benzophenone tetracarboxylic dianhydride, 2,3,3', 4-biphenyl tetracarboxylic dianhydride, pyromellitic dianhydride and 3,3',4,4' -biphenyl tetracarboxylic dianhydride.
Further, in the precursor polyamic acid solution, the solid content of the silicon-containing diamine monomer, the other diamine monomer, the 4,4' -hexafluoroisopropyl phthalic anhydride, and the other dianhydride monomer accounts for 20% of the total mass of the precursor polyamic acid.
Finally, it is noted that the above-mentioned preferred embodiments illustrate rather than limit the invention, and that, while the invention has been described in detail with reference to the above-mentioned preferred embodiments, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the scope of the invention as defined by the appended claims.
Claims (10)
1. A preparation method of a polyimide printed circuit board with high peel strength and low dielectric constant is characterized by comprising the following steps: synthesizing a silicon-containing diamine monomer B by using 4-bromo-N, N-bis (trimethylsilyl) anilineDissolving the mixture and other diamine monomers in a polar aprotic solvent at normal temperature, and adding 4,4 '-hexafluoroisopropyl phthalic anhydride and other dianhydride monomers in a one-half feeding method in five times, wherein the molar ratio of the 4,4' -hexafluoroisopropyl phthalic anhydride to the other dianhydride monomers is 2: 1, regulating the temperature to 5-10 ℃ in ice water bath, polymerizing for 12 hours at low temperature to obtain precursor polyamic acid solution containing siloxane and fluorine with certain viscosity, removing bubbles in vacuum for 0.5 hour, coating the polyamic acid solution on a copper foil with the wet film thickness of 30-35 microns, drying the solvent at 80-150 ℃, transferring the copper-clad plate into a vacuum oven, imidizing at 180-300 ℃, and cooling to obtain the copper-clad plate.
2. The method for preparing a polyimide printed circuit board with high peel strength and low dielectric constant as claimed in claim 1, wherein the silicon-containing diamine monomer B is synthesized by the following method: under the protection of nitrogen, adding 4-bromo-N, N-bis (trimethylsilyl) aniline and magnesium into a dry reactor filled with fresh diethyl ether, reacting at 30 ℃ for 1h, and then refluxing and stirring to react for 3 h; cooling the system to room temperature, adding trifluoropropylmethyldichlorosilane with the same amount as 4-bromo-N, N-bis (trimethylsilyl) aniline into a reactor, reacting the reaction mixture at reflux temperature for 2h, and distilling to obtain a silicon-containing diamine monomer precursor A; under the protection of nitrogen, adding the obtained silicon-containing diamine monomer precursor A into a drying reactor filled with triethylamine, dropwise adding deionized water with the mole number of 1/2 of the silicon-containing diamine monomer precursor A at 80 ℃, reacting for 5 hours, cooling the reaction mixture to room temperature, filtering to remove solids to obtain a viscous liquid crude product, adding ethanol into the crude product, stirring for 3 hours at room temperature, removing the ethanol by rotary drying, and washing with deionized water to obtain the silicon-containing diamine monomer B.
3. The method for preparing a polyimide printed circuit board with high peel strength and low dielectric constant as claimed in claim 1, wherein the content of the silicon-containing diamine monomer B is 5-20% of the total molar amount of the silicon-containing diamine monomer and other diamine monomers.
4. The method as claimed in claim 1, wherein the polar aprotic solvent is one of N-methylpyrrolidone, N-dimethylacetamide and N, N-dimethylformamide.
5. The method as claimed in claim 1, wherein the other diamine monomers further comprise one or more of 2,2 '-bis (trifluoromethyl) -4,4' -diaminobiphenyl, 2 '-bis (trifluoromethyl) -4,4' -diaminophenyl ether, 4'- (hexafluoroisopropyl) bis (p-phenoxy) diphenylamine, 4' -diaminophenyl ether and p-phenylenediamine.
6. The method as claimed in claim 1, wherein the other dianhydride monomers include one or more of 3,3',4,4' -benzophenone tetracarboxylic dianhydride, 2,3,3', 4-biphenyl tetracarboxylic dianhydride, pyromellitic dianhydride, and 3,3',4,4' -biphenyl tetracarboxylic dianhydride.
7. The method of claim 1, wherein the ratio of the total moles of the silicon-containing diamine monomer and other diamine monomers to the total moles of the 4,4' -hexafluoroisopropylphthalic anhydride and other dianhydride monomers is 1.02: 1.
8. the method as claimed in claim 1, wherein the precursor polyamic acid solution has a solid content of 20%.
9. The method of claim 2, wherein the molar ratio of 4-bromo-N, N-bis (trimethylsilyl) aniline to magnesium is 1: 1.008.
10. the method of claim 2, wherein the molar ratio of the silicon-containing diamine monomer precursor A to triethylamine is 1: 4.