CN114506573B - 一种防霉片及其应用 - Google Patents
一种防霉片及其应用 Download PDFInfo
- Publication number
- CN114506573B CN114506573B CN202210006238.XA CN202210006238A CN114506573B CN 114506573 B CN114506573 B CN 114506573B CN 202210006238 A CN202210006238 A CN 202210006238A CN 114506573 B CN114506573 B CN 114506573B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- extract
- mildew
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及防霉技术领域,具体涉及一种防霉片及其应用,包括由下而上依次复合的离型膜层、压敏胶层、载体层和透气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂。本发明的防霉片以大蒜、葡萄籽、香茅、葵花、樟脑以及辣椒等多种植物提取物作为防霉剂组成,安全无毒,对于常见较活跃之霉菌都有抑杀功效,可以广泛适用于棉毛丝麻、皮革制品、鞋类、木制品、成衣、电子零件产品、光学器材、机械零件产品以及军用品等之储运期防霉使用。
Description
技术领域
本发明涉及防霉技术领域,具体涉及一种防霉片及其应用。
背景技术
防霉包装是防止包装和内装物霉变而采取一定防护措施的包装。防霉包装 必须根据微生物的生理特点,改善生产和控制包装储存等环境条件,达到抑制 霉菌生长的目的。商品霉腐是微生物的作用引起的,它能够使商品的使用价值受 到不同程度的影响。据有关部门统计,国内仅纺织品的霉烂损失就达数百万元。, 影响商品质量的微生物主要有细菌、霉菌、酵母菌和部分放线菌。
现有的防霉包装的防霉性较差,而且防霉包装采用大量非降解材料,使用 完的防霉包装也对环境产生了不良的影响。
发明内容
为了克服现有技术中存在的缺点和不足,本发明的目的在于提供一种防霉 片及其应用。
本发明的目的通过下述技术方案实现:
一种防霉片,包括由下而上依次复合的离型膜层、压敏胶层、载体层和透 气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂,所述防霉剂包括 如下重量份数的组成:大蒜提取物10-18份、葡萄籽提取物8-12份、香茅提取物4-8份、葵花提取物2-6份、樟脑提取物2-6份、辣椒提取物1-5份以及溶剂100 份。
优选地,所述防霉剂包括如下重量份数的组成:大蒜提取物16-18份、葡 萄籽提取物10-12份、香茅提取物6-8份、葵花提取物4-6份、樟脑提取物4-6份、 辣椒提取物3-5份以及溶剂100份。
优选地,所述防霉剂包括如下重量份数的组成:大蒜提取物10-13份、葡 萄籽提取物8-10份、香茅提取物4-6份、葵花提取物2-3份、樟脑提取物2-3份、 辣椒提取物1-2份以及溶剂100份。
优选地,所述防霉剂包括如下重量份数的组成:大蒜提取物14-16份、葡 萄籽提取物10-12份、香茅提取物7-8份、葵花提取物4-5份、樟脑提取物2-3份、 辣椒提取物1-2份以及溶剂100份。
优选地,所述防霉剂包括如下重量份数的组成:大蒜提取物12-16份、葡 萄籽提取物9-11份、香茅提取物5-7份、葵花提取物3-5份、樟脑提取物3-5份、 辣椒提取物2-4份以及溶剂100份。
优选地,所述防霉剂包括如下重量份数的组成:大蒜提取物14份、葡萄籽 提取物10份、香茅提取物6份、葵花提取物4份、樟脑提取物4份、辣椒提取物3 份以及溶剂100份。
优选地,所述溶剂为乙醇。
优选地,所述压敏胶为可降解压敏胶,所述可降解压敏胶通过如下方法制 得:
(1)在100重量份的蒸馏水中加入70-80重量份的丙烯酸丁酯、20-30重量 份的甲基丙烯酸甲酯、5-7.5重量份的丙烯酸、7-8重量份的丙烯酸羟乙酯、1-2 重量份的十二烷基硫酸钠以及0.2-0.4重量份的过硫酸铵,升温至65-75℃,反 应2-3h,得到丙烯酸酯预聚体;
(2)在100重量份的蒸馏水中加入10-20重量份的纳米二氧化钛、20-30重 量份的淀粉、7-15重量份的聚乙烯醇以及1-3重量份的十二烷基硫酸钠,搅拌 均匀后升温至80-90℃进行糊化反应,持续30-50min,然后降温至35-45℃,加 入6-10重量份的丙烯酸酰胺、8-12重量份的丙烯酸丁酯、3-4重量份的丙烯酸 羟乙酯以及0.1-0.5重量份的过硫酸铵,升温至65-75℃,反应2-3h,得到丙烯 酸酯接枝改性淀粉;
(3)将100重量份的丙烯酸酯预聚体、65-75重量份的丙烯酸酯接枝改性 淀粉、20-30重量份的三羟甲基丙烷三甲基丙烯酸酯、6-12重量份的丙烯酸、 1-2重量份的过硫酸铵以及1-3重量份的十二烷基硫酸钠进行混合,升温至 65-75℃,反应2-4h,将其涂布至基体上进行烘干,即得到所述可降解压敏胶。
本发明的可降解胶以聚丙烯酸酯为基体,以淀粉作为填充物,基于淀粉的 可生物降解性,可以提高可降解压敏胶的生物可降解性。
但是对于丙烯酸酯-淀粉胶而言,如果采用淀粉直接与丙烯酸酯进行混合 的形式制备的话,淀粉的塑性以及流动性较差,会导致粘胶的内聚能不足,从 而导致粘结性能和机械性能不能达到要求,例如剥离强度、持粘力、拉伸强度、 断裂伸长率等,如果完全采用淀粉接枝丙烯酸酯形成聚合物的方式,虽然一定程度上能改善淀粉的分散性能,但是淀粉的分子量较多,相对的接枝位点较少, 形成的交联结构内聚能有所不足,因此导致压敏胶的机械性能也会有所不足。
本发明的可降解胶预聚体为双预聚体组合,即为丙烯酸酯预聚体以及丙烯酸酯接枝改性淀粉的组合,预聚体之间通过自由基引发聚合以及多官能团的三羟甲基丙烷三甲基丙烯酸酯的促进作用下,形成网络结构,相对于单一的丙烯酸酯预聚体或丙烯酸酯接枝改性淀粉来说,由于两种预聚体的塑性和弹性有很大的差异,在拉伸形变过程中基体会形成差异化的变形,即容易在内部产生应力集中现象,从而引发银纹而消耗能量,提高了压敏胶的韧性。尤其本发明在淀粉改性过程中,以丙烯酰胺作为硬单体,丙烯酸丁酯为软单体对淀粉进行接枝改性,形成的接枝聚丙烯酸酯分子链稳定,并且在淀粉接枝过程中,加入纳米二氧化钛和聚乙烯醇,聚乙烯醇可以塑化淀粉,在淀粉糊化时可以促使淀粉对纳米二氧化钛进行包覆,从而形成纳米二氧化硅为核,淀粉接枝改性丙烯酸酯为壳的核壳改性剂,具有刚性体和弹性体的双重性质,可以显著改善可降解胶的力学性能。此外,本发明利用了淀粉接枝丙烯酸酯的位点有限性,可以避免丙烯酸酯胶内发生过度交联,不会发生内聚能过大而导致粘附性能的下降的现象,从而保证了压敏胶的粘接性能。
如上所述的一种防霉片的应用,应用于皮革制品的防霉储运。
本发明的有益效果在于:本发明的防霉包以大蒜、葡萄籽、香茅、葵花、 樟脑以及辣椒等多种植物提取物作为防霉剂组成,安全无毒,对于常见较活跃 之霉菌如:黑曲菌(AspergillusNiger)、青霉菌属(Penicillium pinophilum)、白癣菌(Trichophytonmentagrophytes)、出芽短梗霉(Aureobasidium pullulans)、绿黏帚霉(Gliocladiumvirens)、球毛壳(Chaetomium globosum) 和细菌如:金黄色葡萄球菌(staphylococcusaureus)、绿脓杆菌(Pseudomonas aeruginosa)、大肠杆菌(Escherichia coli)等都有抑杀功效,可以广泛适 用于棉毛丝麻,皮革制品、鞋类、木制品、成衣、电子零件产品、光学器材、机械零件产品以及军用品等之储运期防霉使用。并且由于采用大量纤维纸等可降解材料,具有优良的生物可降解性,因此废弃也不会对环境造成不良影响。
具体实施方式
为了便于本领域技术人员的理解,下面结合实施例对本发明作进一步的说 明,实施方式提及的内容并非对本发明的限定。
实施例1
一种防霉片,包括由下而上依次复合的离型膜层、压敏胶层、载体层和透 气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂,所述防霉剂包括 如下重量份数的组成:大蒜提取物14份、葡萄籽提取物10份、香茅提取物6份、 葵花提取物4份、樟脑提取物4份、辣椒提取物3份以及溶剂100份。
优选地,所述溶剂为乙醇。
所述压敏胶为可降解压敏胶,所述可降解压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入75重量份的丙烯酸丁酯、25重量份的甲 基丙烯酸甲酯、6.5重量份的丙烯酸、7.5重量份的丙烯酸羟乙酯、1.5重量份 的十二烷基硫酸钠以及0.3重量份的过硫酸铵,升温至70℃,反应2.5h,得到 丙烯酸酯预聚体;
(2)在100重量份的蒸馏水中加入15重量份的纳米二氧化钛、25重量份的 淀粉、12重量份的聚乙烯醇以及2重量份的十二烷基硫酸钠,搅拌均匀后升温 至85℃进行糊化反应,持续40min,然后降温至40℃,加入8重量份的丙烯酸酰 胺、10重量份的丙烯酸丁酯、3.5重量份的丙烯酸羟乙酯以及0.3重量份的过硫 酸铵,升温至70℃,反应2.5h,得到丙烯酸酯接枝改性淀粉;
(3)将100重量份的丙烯酸酯预聚体、70重量份的丙烯酸酯接枝改性淀粉、 25重量份的三羟甲基丙烷三甲基丙烯酸酯、9重量份的丙烯酸、1.5重量份的过 硫酸铵以及2重量份的十二烷基硫酸钠进行混合,升温至70℃,反应3h,将其 涂布至基体上进行烘干,即得到所述可降解压敏胶。
实施例2
一种防霉片,包括由下而上依次复合的离型膜层、压敏胶层、载体层和透 气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂,所述防霉剂包括 如下重量份数的组成:大蒜提取物10份、葡萄籽提取物8份、香茅提取物4份、 葵花提取物2份、樟脑提取物2份、辣椒提取物1份以及溶剂100份。
优选地,所述溶剂为乙醇。
所述压敏胶为可降解压敏胶,所述可降解压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入70重量份的丙烯酸丁酯、20重量份的甲 基丙烯酸甲酯、5重量份的丙烯酸、7重量份的丙烯酸羟乙酯、1重量份的十二 烷基硫酸钠以及0.2重量份的过硫酸铵,升温至65℃,反应2h,得到丙烯酸酯 预聚体;
(2)在100重量份的蒸馏水中加入10重量份的纳米二氧化钛、20重量份的 淀粉、7重量份的聚乙烯醇以及1重量份的十二烷基硫酸钠,搅拌均匀后升温至 80℃进行糊化反应,持续30min,然后降温至35℃,加入6重量份的丙烯酸酰胺、8重量份的丙烯酸丁酯、3重量份的丙烯酸羟乙酯以及0.1重量份的过硫酸铵, 升温至65℃,反应2h,得到丙烯酸酯接枝改性淀粉;
(3)将100重量份的丙烯酸酯预聚体、65重量份的丙烯酸酯接枝改性淀粉、 20重量份的三羟甲基丙烷三甲基丙烯酸酯、6重量份的丙烯酸、1重量份的过硫 酸铵以及1重量份的十二烷基硫酸钠进行混合,升温至65℃,反应2h,将其涂 布至基体上进行烘干,即得到所述可降解压敏胶。
实施例3
一种防霉片,包括由下而上依次复合的离型膜层、压敏胶层、载体层和透 气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂,所述防霉剂包括 如下重量份数的组成:大蒜提取物18份、葡萄籽提取物12份、香茅提取物8份、 葵花提取物6份、樟脑提取物6份、辣椒提取物5份以及溶剂100份。
优选地,所述溶剂为乙醇。
所述压敏胶为可降解压敏胶,所述可降解压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入80重量份的丙烯酸丁酯、30重量份的甲 基丙烯酸甲酯、7.5重量份的丙烯酸、8重量份的丙烯酸羟乙酯、2重量份的十 二烷基硫酸钠以及0.4重量份的过硫酸铵,升温至75℃,反应3h,得到丙烯酸 酯预聚体;
(2)在100重量份的蒸馏水中加入20重量份的纳米二氧化钛、30重量份的 淀粉、15重量份的聚乙烯醇以及3重量份的十二烷基硫酸钠,搅拌均匀后升温 至90℃进行糊化反应,持续50min,然后降温至45℃,加入10重量份的丙烯酸 酰胺、12重量份的丙烯酸丁酯、4重量份的丙烯酸羟乙酯以及0.5重量份的过硫 酸铵,升温至75℃,反应3h,得到丙烯酸酯接枝改性淀粉;
(3)将100重量份的丙烯酸酯预聚体、75重量份的丙烯酸酯接枝改性淀粉、 30重量份的三羟甲基丙烷三甲基丙烯酸酯、12重量份的丙烯酸、2重量份的过 硫酸铵以及3重量份的十二烷基硫酸钠进行混合,升温至75℃,反应4h,将其 涂布至基体上进行烘干,即得到所述可降解压敏胶。
对比例1
本对比例的压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入50重量份的丙烯酸丁酯、30重量份的甲 基丙烯酸甲酯、6.5重量份的丙烯酸、7.5重量份的丙烯酸羟乙酯、1.5重量份 的十二烷基硫酸钠以及0.3重量份的过硫酸铵,升温至70℃,反应2.5h,得到 丙烯酸酯预聚体;
(3)将100重量份的丙烯酸酯预聚体、35重量份的三羟甲基丙烷三甲基丙 烯酸酯、13重量份的丙烯酸、1.5重量份的过硫酸铵以及2重量份的十二烷基硫 酸钠进行混合,升温至70℃,反应3h,将其涂布至基体上进行烘干,即得到所 述可降解压敏胶。
对比例2
本对比例的压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入15重量份的纳米二氧化钛、25重量份的 淀粉、12重量份的聚乙烯醇以及2重量份的十二烷基硫酸钠,搅拌均匀后升温 至85℃进行糊化反应,持续40min,然后降温至40℃,加入12重量份的丙烯酸 酰胺、16重量份的丙烯酸丁酯、5重量份的丙烯酸羟乙酯以及0.3重量份的过硫 酸铵,升温至70℃,反应2.5h,得到丙烯酸酯接枝改性淀粉;
(2)将100重量份的丙烯酸酯接枝改性淀粉、30重量份的三羟甲基丙烷三 甲基丙烯酸酯、15重量份的丙烯酸、1.5重量份的过硫酸铵以及2重量份的十二 烷基硫酸钠进行混合,升温至70℃,反应3h,将其涂布至基体上进行烘干,即 得到所述可降解压敏胶。
将通过实施例1、对比例1和对比例2可降解胶涂覆在马口铁上并进行固 化,对胶膜的拉伸强度、断裂伸长率以及180°剥离强度进行测试,测试结果 如下:
拉伸强度(MPa) | 断裂伸长率(%) | 180°剥离强度(N/25mm) | |
实施例1 | 8.8 | 123 | 108.9 |
对比例1 | 10.3 | 105 | 115.2 |
对比例2 | 5.1 | 84 | 75.4 |
上述实施例为本发明较佳的实现方案,除此之外,本发明还可以其它方式 实现,在不脱离本发明构思的前提下任何显而易见的替换均在本发明的保护范 围之内。
Claims (8)
1.一种防霉片,其特征在于:包括由下而上依次复合的离型膜层、压敏胶层、载体层和透气保护膜层,所述载体层包括基纸和喷涂在基纸上的防霉剂,所述防霉剂包括如下重量份数的组成:大蒜提取物10-18份、葡萄籽提取物8-12份、香茅提取物4-8份、葵花提取物2-6份、樟脑提取物2-6份、辣椒提取物1-5份以及溶剂100份;
所述压敏胶为可降解压敏胶,所述可降解压敏胶通过如下方法制得:
(1)在100重量份的蒸馏水中加入70-80重量份的丙烯酸丁酯、20-30重量份的甲基丙烯酸甲酯、5-7.5重量份的丙烯酸、7-8重量份的丙烯酸羟乙酯、1-2重量份的十二烷基硫酸钠以及0.2-0.4重量份的过硫酸铵,升温至65-75℃,反应2-3h,得到丙烯酸酯预聚体;
(2)在100重量份的蒸馏水中加入10-20重量份的纳米二氧化钛、20-30重量份的淀粉、7-15重量份的聚乙烯醇以及1-3重量份的十二烷基硫酸钠,搅拌均匀后升温至80-90℃进行糊化反应,持续30-50min,然后降温至35-45℃,加入6-10重量份的丙烯酸酰胺、8-12重量份的丙烯酸丁酯、3-4重量份的丙烯酸羟乙酯以及0.1-0.5重量份的过硫酸铵,升温至65-75℃,反应2-3h,得到丙烯酸酯接枝改性淀粉;
(3)将100重量份的丙烯酸酯预聚体、65-75重量份的丙烯酸酯接枝改性淀粉、20-30重量份的三羟甲基丙烷三甲基丙烯酸酯、6-12重量份的丙烯酸、1-2重量份的过硫酸铵以及1-3重量份的十二烷基硫酸钠进行混合,升温至65-75℃,反应2-4h,将其涂布至基体上进行烘干,即得到所述可降解压敏胶。
2.根据权利要求1所述的一种防霉片,其特征在于:所述防霉剂包括如下重量份数的组成:大蒜提取物16-18份、葡萄籽提取物10-12份、香茅提取物6-8份、葵花提取物4-6份、樟脑提取物4-6份、辣椒提取物3-5份以及溶剂100份。
3.根据权利要求1所述的一种防霉片,其特征在于:所述防霉剂包括如下重量份数的组成:大蒜提取物10-13份、葡萄籽提取物8-10份、香茅提取物4-6份、葵花提取物2-3份、樟脑提取物2-3份、辣椒提取物1-2份以及溶剂100份。
4.根据权利要求1所述的一种防霉片,其特征在于:所述防霉剂包括如下重量份数的组成:大蒜提取物14-16份、葡萄籽提取物10-12份、香茅提取物7-8份、葵花提取物4-5份、樟脑提取物2-3份、辣椒提取物1-2份以及溶剂100份。
5.根据权利要求1所述的一种防霉片,其特征在于:所述防霉剂包括如下重量份数的组成:大蒜提取物12-16份、葡萄籽提取物9-11份、香茅提取物5-7份、葵花提取物3-5份、樟脑提取物3-5份、辣椒提取物2-4份以及溶剂100份。
6.根据权利要求1所述的一种防霉片,其特征在于:所述防霉剂包括如下重量份数的组成:大蒜提取物14份、葡萄籽提取物10份、香茅提取物6份、葵花提取物4份、樟脑提取物4份、辣椒提取物3份以及溶剂100份。
7.根据权利要求1所述的一种防霉片,其特征在于:所述溶剂为乙醇。
8.权利要求1-7所述的一种防霉片的应用,其特征在于:应用于皮革制品的防霉储运。