CN114347712A - 一种彩色立体瓷画的制作方法 - Google Patents
一种彩色立体瓷画的制作方法 Download PDFInfo
- Publication number
- CN114347712A CN114347712A CN202111586659.6A CN202111586659A CN114347712A CN 114347712 A CN114347712 A CN 114347712A CN 202111586659 A CN202111586659 A CN 202111586659A CN 114347712 A CN114347712 A CN 114347712A
- Authority
- CN
- China
- Prior art keywords
- engraving
- bottom plate
- firing
- dimensional
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种彩色立体瓷画的制作方法,包括选取板材、电脑制图、雕刻清洗、打印图案、烘干、最后烧制、冷却降温等步骤。本发明方法既耐高温,又适宜雕刻,画面立体感强,图案可自主选择,产品美观大方,坚固耐用,能长久保存,解决市售的板材画基材如碳化硅板材等,虽然耐火烧,但是质地较脆,无法雕刻制作绘画;另一些板材如大理石板材,虽然适合雕刻绘画,但是不耐高温等技术问题,对现有技术来说,具有很好的市场前景和发展空间。
Description
技术领域
本发明涉及瓷画技术领域,具体涉及一种彩色立体瓷画的制作方法。
背景技术
现有的装饰画一般为平面画,虽然制作方便,但是画面立体感不强,无法生动形象地表现画面的含义。市售的板材如碳化硅板材等,虽然耐火烧,但是质地硬脆,无法雕刻制作绘画;另一些板材如大理石板材,虽然适合雕刻绘画,但是不耐高温。
如何设计一种既耐高温,又适宜雕刻,画面立体感强,图案可自主选择,产品美观大方,坚固耐用,能长久保存的彩色立体瓷画是目前需要解决的问题。
发明内容
为了解决市售的板材画基材如碳化硅板材等,虽然耐火烧,但是质地硬脆,无法雕刻制作绘画;另一些板材如大理石板材,虽然适合雕刻绘画,但是不耐高温等技术问题,本发明提供一种彩色立体瓷画的制作方法,来实现既耐高温,又适宜雕刻,画面立体感强,图案可自主选择,产品美观大方,坚固耐用,能长久保存的目的。
本发明为解决上述技术问题所采用的技术方案是:一种彩色立体瓷画的制作方法,包括以下步骤:
步骤一,选取耐火底板,底板厚度5-20mm;
步骤二,使用电脑制图工具制作灰度立体雕刻图;
步骤三,底板固定在自动雕刻机上进行雕刻,雕刻完毕后进行吹风处理,然后将底板水洗,除去雕刻残渣;
步骤四,使用电脑制图工具对步骤二的灰度立体雕刻图进行雕刻;
步骤五,打印图案,利用纳米陶瓷打印机对步骤三处理后的底板进行高清图案喷绘打印;
步骤六,烘干处理,将步骤五处理后的底板水平放入烘道里进行烘干,烘道温度100-300℃,烘干时间10-30min,烘干后吹风冷却;
步骤七,最后烧制,将步骤六烘干处理后的耐火底板放入钢化炉内进行高温烧制,烧制温度700-1000℃,烧制时间10-30min,烧制后吹风冷却即可。
所述步骤一中使用的底板为耐火陶瓷板。
所述步骤五中打印图案也可采用人工手动彩绘完成。
与现有技术相比,本发明的有益效果是:
1)本发明选用的耐火陶瓷板既耐高温,又适宜雕刻,画面立体感强,图案可自主选择,产品美观大方,坚固耐用,能长久保存;
2)使用电脑制图工具制作灰度立体雕刻图并进行雕刻,操作方便快捷,省时省力,便于产品统一标准化;
3)利用纳米陶瓷打印机对板材进行高清图案打印,纳米陶瓷打印机打印清晰,误差小,易于操作控制,保证图案的美观大方。
具体实施方式
下面对本发明的具体实施方式作进一步详细的说明。
实施例一,
一种彩色立体瓷画的制作方法,包括以下步骤:
步骤一,选取耐火底板,底板厚度5mm;
步骤二,使用电脑制图工具制作灰度立体雕刻图;
步骤三,底板固定在自动雕刻机上进行雕刻,雕刻完毕后进行吹风处理,然后将底板水洗,除去雕刻残渣;
步骤四,使用电脑制图工具对步骤二的灰度立体雕刻图进行雕刻;
步骤五,打印图案,利用纳米陶瓷打印机对步骤三处理后的底板进行高清图案喷绘打印;
步骤六,烘干处理,将步骤五处理后的底板水平放入烘道里进行烘干,烘道温度100℃,烘干时间10min,烘干后吹风冷却;
步骤七,最后烧制,将步骤六烘干处理后的耐火底板放入钢化炉内进行高温烧制,烧制温度700-℃,烧制时间10min,烧制后吹风冷却即可。
所述步骤一中使用的底板为耐火陶瓷板。
所述步骤五中打印图案也可采用人工手动彩绘完成。
实施例二,
一种彩色立体瓷画的制作方法,包括以下步骤:
步骤一,选取耐火底板,底板厚度15mm;
步骤二,使用电脑制图工具制作灰度立体雕刻图;
步骤三,底板固定在自动雕刻机上进行雕刻,雕刻完毕后进行吹风处理,然后将底板水洗,除去雕刻残渣;
步骤四,使用电脑制图工具对步骤二的灰度立体雕刻图进行雕刻;
步骤五,打印图案,利用纳米陶瓷打印机对步骤三处理后的底板进行高清图案喷绘打印;
步骤六,烘干处理,将步骤五处理后的底板水平放入烘道里进行烘干,烘道温度200℃,烘干时间20min,烘干后吹风冷却;
步骤七,最后烧制,将步骤六烘干处理后的耐火底板放入钢化炉内进行高温烧制,烧制温度850℃,烧制时间20min,烧制后吹风冷却即可。
所述步骤一中使用的底板为耐火陶瓷板。
所述步骤五中打印图案也可采用人工手动彩绘完成。
实施例三,
一种彩色立体瓷画的制作方法,包括以下步骤:
步骤一,选取耐火底板,底板厚度20mm;
步骤二,使用电脑制图工具制作灰度立体雕刻图;
步骤三,底板固定在自动雕刻机上进行雕刻,雕刻完毕后进行吹风处理,然后将底板水洗,除去雕刻残渣;
步骤四,使用电脑制图工具对步骤二的灰度立体雕刻图进行雕刻;
步骤五,打印图案,利用纳米陶瓷打印机对步骤三处理后的底板进行高清图案喷绘打印;
步骤六,烘干处理,将步骤五处理后的底板水平放入烘道里进行烘干,烘道温度300℃,烘干时间30min,烘干后吹风冷却;
步骤七,最后烧制,将步骤六烘干处理后的耐火底板放入钢化炉内进行高温烧制,烧制温度1000℃,烧制时间30min,烧制后吹风冷却即可。
所述步骤一中使用的底板为耐火陶瓷板。
所述步骤五中打印图案也可采用人工手动彩绘完成。
实际操作中,步骤七最后烧制步骤中,采用玻璃钢化炉滚动方式对板材进行烧制,烧制温度和烧制时间由选取的板材厚度而定,板材越薄,烧制时间越短,板材越厚,烧制时间越长。
在打印步骤中,本发明采用的打印染料为无机染料,在打印和烧制时,不会产生有机废气,对环境友好,绿色环保,符合企业绿色发展方向。
本发明方法既耐高温,又适宜雕刻,画面立体感强,图案可自主选择,产品美观大方,坚固耐用,能长久保存,解决市售的板材画基材如碳化硅板材等,虽然耐火烧,但是质地较脆,无法雕刻制作绘画;另一些板材如大理石板材,虽然适合雕刻绘画,但是不耐高温等技术问题,对现有技术来说,具有很好的市场前景和发展空间。
上面对本发明优选的具体实施方式和实施例作了详细说明,但是本发明并不限于上述实施方式和实施例,在本领域技术人员所具备的知识范围内,还可以在不脱离本发明构思的前提下作出各种变化。
Claims (3)
1.一种彩色立体瓷画的制作方法,其特征在于:包括以下步骤:
步骤一,选取耐火底板,底板厚度5-20mm;
步骤二,使用电脑制图工具制作灰度立体雕刻图;
步骤三,底板固定在自动雕刻机上进行雕刻,雕刻完毕后进行吹风处理,然后将底板水洗,除去雕刻残渣;
步骤四,使用电脑制图工具对步骤二的灰度立体雕刻图进行雕刻;
步骤五,打印图案,利用纳米陶瓷打印机对步骤三处理后的底板进行高清图案喷绘打印;
步骤六,烘干处理,将步骤五处理后的底板水平放入烘道里进行烘干,烘道温度100-300℃,烘干时间10-30min,烘干后吹风冷却;
步骤七,最后烧制,将步骤六烘干处理后的耐火底板放入钢化炉内进行高温烧制,烧制温度700-1000℃,烧制时间10-30min,烧制后吹风冷却即可。
2.如权利要求1所述的一种彩色立体瓷画的制作方法,其特征在于:所述步骤一中使用的底板为耐火陶瓷板。
3.如权利要求1所述的一种彩色立体瓷画的制作方法,其特征在于:所述步骤五中打印图案也可采用人工手动彩绘完成。