CN114276279B - 夺氢型光引发剂及其制备方法和应用 - Google Patents
夺氢型光引发剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN114276279B CN114276279B CN202111636130.0A CN202111636130A CN114276279B CN 114276279 B CN114276279 B CN 114276279B CN 202111636130 A CN202111636130 A CN 202111636130A CN 114276279 B CN114276279 B CN 114276279B
- Authority
- CN
- China
- Prior art keywords
- photoinitiator
- hydrogen abstraction
- reaction
- diisocyanate
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及光引发剂合成技术领域,尤其是涉及一种夺氢型光引发剂及其制备方法和应用。本发明的夺氢型光引发剂,同时具备叔胺和聚天门冬氨酸酯结构,是具有光‑热双重固化的单组分引发剂,无需添加叔胺类助引发剂,具有极低的小分子迁移渗出率,极低的气味,同时具有良好的光引发活性和溶解性能。
Description
技术领域
本发明涉及光引发剂合成技术领域,尤其是涉及一种夺氢型光引发剂及其制备方法和应用。
背景技术
光引发剂是紫外光固化体系的关键组成部分,它直接关系到配方体系在光照射时低聚物及稀释剂能否迅速由液态转变成固态。随着技术的不断发展和市场提出的更高的要求,光引发剂在固化过程完成后,其迁移性和被夺取的倾向应尽量减少。
二苯甲酮作为广泛使用的夺氢型光引发剂,价廉且表面固化良好,不易泛黄、溶解性良好,是紫外光固化体系中最广泛使用的光引发剂之一。但二苯甲酮从已固化产品中迁移或被夺取的倾向严重。为了改善二苯甲酮的迁移性和气味问题,公开号为CN101012180A的专利申请公开了通过化学方法将二苯甲酮和胺结合在一个分子中,做成单组分夺氢型光引发剂。
显示器件全贴合技术分为OCA(Optical Clear Adhesive)和LOCA(LiquidOptical Clear Adhesive)全贴合。目前市场里面存在的LOCA胶属于UV胶的一种,需要通过UV光照射固化,但由于触摸屏TP结构设计的原因,导致屏幕边框与功能片FPC不透明,UV光无法穿透到达LOCA胶处,导致LOCA胶在后续存放或使用过程中缓慢溢出,造成外观污染甚至损坏产品内部,最后导致产品损坏。在固化时,屏幕边框处及传感器上不透明的软性线路板处难以彻底固化,需要再次固化,溢胶难以控制,溢到边缘的胶又难以清理,特别是对于大尺寸的贴合溢胶很难控制,生产成本高,生产效率低。
为解决产品挡光部件固化不干的溢胶问题,现有技术增加了侧面UV固化工序,以达到外边缘固化封边,减少溢胶的风险。但是侧固化存在两个问题:一是侧固化只能对边缘封边,面积较大的挡光部分里面仍然存在液体不干问题,在遇到需要加热加压(如后续贴合OCA时需加热加压脱泡)时,未固化的液态光学胶会溢出;二是侧固化需要较高的能量才能使边缘固化,但是高能量的侧固化会导致白色的盖板发黄,影响外观。因此,为解决侧固化存在的问题,需要液态光学胶搭配促进剂使用,通过促进剂加快液态光学胶的固化速度,解决挡光部分固化不干的问题。但目前的液态光学胶促进剂的促进效率低,接触氧气的外边缘固化效果差,同时现有的液态光学胶存在存储稳定性差的问题,导致无法更好地解决侧固化问题。
综上所述,目前商业化二苯甲酮类光引发剂存在迁移渗出问题造成的污染,同时在OCA的紫外线-热双重固化领域,多采用过氧化物为热引发剂,且需要预涂促进剂搭配使用,工艺步骤的增加带来了操作难度和贴合成本的上升。因此,如果通过光引发剂化学结构设计同时解决上述两种技术难题,将极大提升OCA产品的市场竞争力。
有鉴于此,特提出本发明。
发明内容
本发明的第一目的在于提供夺氢型光引发剂,以解决现有技术中存在的光引发剂的迁移渗出等技术问题。
本发明的第二目的在于提供夺氢型光引发剂的制备方法。
本发明的第三目的在于提供夺氢型光引发剂在OCA胶膜中的应用。
为了实现本发明的上述目的,特采用以下技术方案:
夺氢型光引发剂,其结构式如下:
Y1、Y2、Y3、Y4、Y5、Y6、Y7和Y8各自独立的选自H、烷基、烷氧基和芳香基团中的任一种。
本发明的夺氢型光引发剂,同时具备叔胺和聚天门冬氨酸酯结构,是具有光-热双重固化的单组分引发剂,无需添加叔胺类助引发剂,具有极低的小分子迁移渗出率,极低的气味,同时具有良好的光引发活性和溶解性能。
在本发明的具体实施方式中,R2选自碳数为2~12的支链亚烷基、直链亚烷基、支链亚烷氧基和直链亚烷氧基中的任一种。
在本发明的具体实施方式中,R3选自碳数为2~12的支链烷基、直链烷基、支链烷氧基和直链烷氧基中的任一种。
本发明还提供了上述任意一种所述夺氢型光引发剂的制备方法,包括如下步骤:
(b)聚天门冬氨酸酯多胺与所述二苯甲酮衍生物进行Michael加成反应得到所述光引发剂;
在本发明的具体实施方式中,所述聚天门冬氨酸酯多胺主要由双烷基三胺和丁烯二酸二酯反应得到;所述双烷基三胺和丁烯二酸二酯的结构式分别为 进一步的,所述双烷基三胺包括二乙烯三胺、二丙烯三胺、二亚丙基三胺和双六亚甲基三胺中的任一种或多种;所述丁烯二酸二酯包括马来酸二酯和/或富马酸二酯,其中马来酸二酯选自马来酸二乙酯、马来酸二丙酯、马来酸二丁酯和马来酸甲基丙基酯中的任一种或多种,富马酸二酯选自富马酸二乙酯、富马酸二丙酯、富马酸二丁酯和富马酸甲基丙基酯中的任一种或多种。
在本发明的具体实施方式中,所述双烷基三胺和丁烯二酸二酯的摩尔比为1﹕(1.8~2.2)。
在本发明的具体实施方式中,所述二异氰酸酯包括甲苯二异氰酸酯和/或异佛尔酮二异氰酸酯。
在本发明的具体实施方式中,所述含羟基(甲基)丙烯酸酯包括丙烯酸羟乙酯、丙烯酸羟丙酯、丙烯酸羟丁酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯和甲基丙烯酸羟丁酯中的至少一种。
在本发明的具体实施方式中,步骤(b)中,所述聚天门冬氨酸酯多胺与所述二苯甲酮衍生物的反应摩尔比为1﹕(0.9~1.1),优选为1﹕1。
在本发明的具体实施方式中,步骤(b)中,将所述聚天门冬氨酸酯多胺加入所述二苯甲酮衍生物中。
本发明还提供了上述任意一种所述夺氢型光引发剂的另一种制备方法,包括如下步骤:
(b1)聚天门冬氨酸酯多胺与所述二苯甲酮衍生物进行Michael加成反应得到所述光引发剂;
在本发明的具体实施方式中,所述含异氰酸酯及(甲基)丙烯酸酯的单体包括异氰酸酯丙烯酸乙酯和/或异氰酸酯甲基丙烯酸乙酯。
本发明还提供了上述任意一种所述夺氢型光引发剂在OCA胶膜中的应用。
本发明还提供了一种OCA组合物,包括按质量百分数计的夺氢型光引发剂1%~10%。
与现有技术相比,本发明的有益效果为:
(1)本发明的夺氢型光引发剂,作为可双重固化的单组分引发剂,无需添加叔胺类助引发剂,具有极低的小分子迁移渗出率<0.01%(即使是在遮光区域),极低的气味,同时具有良好的光引发活性和溶解性能;
(2)本发明的夺氢型光引发剂复配得到的OCA胶膜体系在存储期达到3个月以上,过程中粘度仅略微增加,可以很好的实现挡光部分的侧固化,避免贴合后的边缘溢胶以及黏附力不足的问题;
(3)本发明的夺氢型光引发剂得到的OCA胶膜结构中形成了聚氨酯/聚脲和丙烯酸酯的聚合物互穿网络(IPN)结构,聚氨酯/聚脲结构中的氨基甲酸酯和脲基间强氢键作用作为物理交联点,不但可以增强胶膜的内聚力从而提高持粘力和粘接可靠性,而且在保持良好弹性的基础上极大改善抗蠕变性能。
具体实施方式
下面将结合具体实施方式对本发明的技术方案进行清楚、完整地描述,但是本领域技术人员将会理解,下列所描述的实施例是本发明一部分实施例,而不是全部的实施例,仅用于说明本发明,而不应视为限制本发明的范围。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
夺氢型光引发剂,其结构式如下:
Y1、Y2、Y3、Y4、Y5、Y6、Y7和Y8各自独立的选自H、烷基、烷氧基和芳香基团中的任一种。
如在不同实施方式中,Y1、Y2、Y3、Y4、Y5、Y6、Y7和Y8各自独立的选自H、烷基、烷氧基和芳香基团中的任一种;其中,烷基可以为碳数为1~4的烷基,如甲基、乙基、丙基、丁基等;烷氧基可以为碳数为1~4的烷氧基,如甲氧基、乙氧基、丙氧基、丁氧基等;芳香基团可以为芳环如苯,芳稠环如萘等。
本发明的夺氢型光引发剂,同时具备叔胺和聚天门冬氨酸酯结构,是具有光-热双重固化的单组分引发剂,无需添加叔胺类助引发剂,具有极低的小分子迁移渗出率,极低的气味,同时具有良好的光引发活性和溶解性能。
在本发明的具体实施方式中,R2选自碳数为2~12的支链亚烷基、直链亚烷基、支链亚烷氧基和直链亚烷氧基中的任一种。
如在不同实施方式中,R2的碳数可以为2、3、4、5、6、7、8、9、10、11、12;如直链亚烷基结构式可为n为2~12之间的整数;如支链亚烷基结构式可为n1为1~11之间的整数,或者也可以有多个支链;如直链亚烷氧基结构式可为n2为2~12之间的整数;如支链亚烷氧基结构式可为n3为1~11之间的整数,或者也可以有多个支链。
在本发明的具体实施方式中,R2选自碳数为2~6的直链亚烷基。
在本发明的具体实施方式中,R3选自碳数为1~12的支链烷基、直链烷基、支链烷氧基和直链烷氧基中的任一种。
如在不同实施方式中,R3的碳数可以为1、2、3、4、5、6、7、8、9、10、11、12;如直链烷基可以为甲基、乙基、丙基、丁基、戊基、己基、庚基、辛基、壬基、癸基、十一烷基、十二烷基,如结构式为n4为0~11之间的整数;如支链烷基可以为异丙基、异丁基、异戊基、异己基、异庚基、异辛基等等,如结构式为n5为1~10之间的整数,或者也可以有多个支链。
在本发明的具体实施方式中,R3选自碳数为1~4的直链烷基。
如在不同实施方式中,R5可以为-CH2-、-CH2CH2-、-CH2CH2CH2-等等。
在本发明的具体实施方式中,R1中与二苯甲酮基团相连接的位点为氨基甲酸酯结构侧,与N相连接的位点为(甲基)丙烯酸酯侧。
在本发明的具体实施方式中,所述夺氢型光引发剂具有如下结构式中的任一种:
其中,对应的R2和R3位置的亚烷基链或烷基链的长度可根据R2和R3的碳数进行调整;且二苯甲酮骨架上,对应的X1、X2可一个为上述取代结构,另一个为H,也可X1、X2均为上述取代结构。如,具体可以如下:
本发明还提供了上述任意一种所述夺氢型光引发剂的制备方法,包括如下步骤:
(b)聚天门冬氨酸酯多胺与所述二苯甲酮衍生物进行Michael加成反应得到所述光引发剂;
在本发明的具体实施方式中,所述聚天门冬氨酸酯多胺主要由双烷基三胺和丁烯二酸二酯反应得到;所述双烷基三胺和丁烯二酸二酯的结构式分别为 进一步的,所述双烷基三胺包括二乙烯三胺、二丙烯三胺、二亚丙基三胺和双六亚甲基三胺中的任一种或多种;所述丁烯二酸二酯包括马来酸二酯和/或富马酸二酯,其中马来酸二酯选自马来酸二乙酯、马来酸二丙酯、马来酸二丁酯和马来酸甲基丙基酯中的任一种或多种,富马酸二酯选自富马酸二乙酯、富马酸二丙酯、富马酸二丁酯和富马酸甲基丙基酯中的任一种或多种。
在本发明的具体实施方式中,所述聚天门冬氨酸酯多胺主要由双烷基三胺和丁烯二酸二酯进行Michael加成反应得到。
在聚天门冬氨酸酯多胺的制备中,双烷基三胺的伯胺基团和丁烯二酸二酯发生反应,而仲胺基团由于位阻效应几乎不参与加成反应。继而,伯胺在Michael加成反应中生成的位阻型仲胺,与二苯甲酮衍生物中的(甲基)丙烯酸酯单元进一步Michael加成反应受到空间位阻效应的抑制,活性极低,而双烷基三胺中保留的仲胺却具备进一步和(甲基)丙烯酸酯单元的反应活性,因此可以高产率的得到目标产物。
聚天门冬氨酸酯多胺的制备中,反应过程如下所示:
在实际操作中,聚天门冬氨酸酯多胺的制备包括:将丁烯二酸二酯缓慢滴加至双烷基三胺中,滴加完成后,升温至40~60℃反应3~6h。进一步的,向体系中通入N210~30min;丁烯二酸二酯的滴加时间为0.5~1h,滴加过程中的温度控制在25~30℃。
在本发明的具体实施方式中,所述双烷基三胺和丁烯二酸二酯的摩尔比为1﹕(1.8~2.2),优选为1﹕2。
在本发明的具体实施方式中,步骤(a)中,化合物A1或化合物A2先与二异氰酸酯反应得到中间体,再与含羟基(甲基)丙烯酸酯反应。为了高产率的得到二苯甲酮衍生物,中间体需要为NCO封端产物,得到的含单官能度和双官能度NCO的中间体的结构式分别如下:
为了减少二苯甲酮封端产物或低聚物的生成(以化合物A2如4,4’-二羟基二苯甲酮为原料时),优先选用NCO反应活性存在差异的甲苯二异氰酸酯TDI、异佛尔酮二异氰酸酯IPDI作为合成用原料,出于耐黄变性能的考量,二异氰酸酯更优选为IPDI。
在本发明的具体实施方式中,步骤(a)中,所述反应在催化剂的作用下进行。以提高NCO反应活性的差异。进一步的,所述催化剂为有机锡类催化剂,如二月桂酸二丁基锡(DBTDL)。更进一步的,所述催化剂的用量为反应物总质量的0.02%~0.2%。
在本发明的具体实施方式中,步骤(a)中,化合物A1或化合物A2与二异氰酸酯的反应温度为30~60℃。在实际操作中,该步骤反应的时间通过红外光谱监测反应液的NCO峰面积进行调控,当反应液中NCO峰面积恒定不变,停止反应,再进行下一步与含羟基(甲基)丙烯酸酯的反应。
在本发明的具体实施方式中,所述含羟基(甲基)丙烯酸酯包括丙烯酸羟乙酯、丙烯酸羟丙酯、丙烯酸羟丁酯、甲基丙烯酸羟乙酯、甲基丙烯酸羟丙酯和甲基丙烯酸羟丁酯中的至少一种。
在本发明的具体实施方式中,步骤(a)中,所述中间体与所述含羟基(甲基)丙烯酸酯的反应温度为20~50℃。在实际操作中,该步骤的反应时间通过红外光谱监测反应液的NCO峰面积进行调控,当反应液中NCO峰面积消失,停止反应。
在本发明的具体实施方式中,步骤(b)中,所述聚天门冬氨酸酯多胺与所述二苯甲酮衍生物的反应摩尔比为1﹕(0.9~1.1),优选为1﹕1。其中,反应摩尔比是指聚天门冬氨酸酯多胺的非位阻型仲胺与所述二苯甲酮衍生物中的端烯基的摩尔数比例。
在本发明的具体实施方式中,所述聚天门冬氨酸酯多胺的制备中,所述反应的温度为25~60℃。在实际操作中,通过硫醇-碘滴定方法测得反应体系中不饱和值,得到反应转化率,调控反应时间。
在本发明的具体实施方式中,步骤(b)中,将所述聚天门冬氨酸酯多胺加入所述二苯甲酮衍生物中。在实际操作中,将所述聚天门冬氨酸酯多胺缓慢滴加至步骤(a)得到的二苯甲酮衍生物的反应液中。
在本发明的具体实施方式中,步骤(b)中,所述聚天门冬氨酸酯多胺的滴加时间为1~3h,滴加过程中,反应体系的温度控制在40℃以内;滴加完成后,于45~50℃保温反应2~4h。
聚天门冬氨酸酯多胺中的位阻型仲胺基团由于空间位阻效应导致反应活性低,与二苯甲酮衍生物中的(甲基)丙烯酸酯单元的反应活性远小于聚天门冬氨酸酯多胺中的其它仲胺,通过滴加的方式可进一步降低位阻型仲胺和(甲基)丙烯酸酯单元反应的概率。以单官能二苯甲酮衍生物为例,反应过程如下:
本发明还提供了上述任意一种所述夺氢型光引发剂的另一种制备方法,包括如下步骤:
(b1)聚天门冬氨酸酯多胺与所述二苯甲酮衍生物进行Michael加成反应得到所述光引发剂;
在本发明的具体实施方式中,所述含异氰酸酯及(甲基)丙烯酸酯的单体包括异氰酸酯丙烯酸乙酯和/或异氰酸酯甲基丙烯酸乙酯。
在本发明的具体实施方式中,步骤(a1)中,所述反应在催化剂的作用下进行。进一步的,所述催化剂为有机锡类催化剂,如二月桂酸二丁基锡(DBTDL)。更进一步的,所述催化剂的用量为反应物总质量的0.02%~0.2%。
在本发明的具体实施方式中,步骤(a1)中,所述反应的温度为20~30℃,如在室温下进行。在实际操作中,该步骤的反应时间可通过红外光谱监测反应液的NCO峰面积进行调控,当反应液中NCO峰面积消失,停止反应。
上述方法中,步骤(b1)与前述方法中步骤(b)的操作条件相同。
在本发明的具体实施方式中,步骤(a)和步骤(a1)均是在有机溶剂的存在下进行的反应,如所述有机溶剂可以为乙酸乙酯。
在本发明的具体实施方式中,所述有机溶剂的加入量与所述化合物A1或化合物A2的比例为(0.9~1.1)L﹕1mol,如1L﹕1mol。
在本发明的具体实施方式中,在步骤(a)或步骤(a1)得到的含二苯甲酮衍生物的反应液中加入阻聚剂。其中,所述阻聚剂可以为对甲氧基苯酚。
在本发明的具体实施方式中,在步骤(b)或步骤(b1)反应完成后,除去溶剂,得到所述光引发剂。本发明制备得到的夺氢型光引发剂无需进一步分离纯化,即可用于后续产品的下游应用。
本发明还提供了上述任意一种所述夺氢型光引发剂在OCA胶膜中的应用。全贴合OCA胶膜贴合过程中为了更好地脱除气泡,需要OCA具备较好的流动性。本发明的光引发剂在贴合时,在OCA胶膜组成中可以起到增塑剂的作用,降低胶膜模量,提高流动性。而在贴合完成后,为了提高贴合的粘接可靠性,要求胶膜具备更高的模量,进行高温高压脱泡时,本发明的光-热双重夺氢型光引发剂不但可以起到光引发作用,位阻型仲胺与封闭型NCO发生反应生成脲基,还可以和叔C-H发生如下所示的光化学反应,从而进一步提高交联密度增大OCA胶膜模量,并大幅降低光引发剂的迁移率。因为遮光区域的热引发反应,即使在遮光区域依然表现出低的迁移率。
本发明中所涉及的波浪线表示该基团中与化合物其余部分的连接位置。
本发明还提供了一种OCA组合物,包括按质量百分数计的夺氢型光引发剂1%~10%。
在本发明的具体实施方式中,所述OCA组合物包括按质量百分数计的如下组分:丙烯酸酯类单体和预聚物70%~97%、夺氢型光引发剂1%~10%、以及封闭型异氰酸酯2%~20%。
在实际操作中,所述OCA组合物还包括辐照固化光引发剂或者热裂解自由基引发剂,如Irgacure 651,此处的光引发剂是在前端制备OCA胶膜时,采用低压汞灯固化;而本发明的夺氢型光引发剂在贴合完成后,采用高压汞灯固化;二者固化采用的波段及处于的流程不同。如在不同实施方式中,所述Irgacure 651光引发剂的用量为丙烯酸酯类单体、预聚物、夺氢型光引发剂和封闭型异氰酸酯质量和的0.1wt%~0.2wt%,如0.1wt%~0.15wt%。
采用所述OCA组合物制备OCA胶膜的方法可以包括:将丙烯酸酯类单体和预聚物、夺氢型光引发剂以及Irgacure 651光引发剂混合后,于70~100mJ/cm2条件下辐照处理3~6min,得到粘性液体;然后将粘性液体与封闭型异氰酸酯以及Irgacure 651光引发剂混合均匀,进行涂布后,以70~100mJ/cm2条件下辐照处理3~6min。第一次加入的Irgacure 651光引发剂的用量为丙烯酸酯类单体、预聚物、夺氢型光引发剂和封闭型异氰酸酯质量和的0.01wt%~0.02wt%,如0.02wt%;第二次加入的Irgacure 651光引发剂的用量为丙烯酸酯类单体、预聚物、夺氢型光引发剂和封闭型异氰酸酯质量和的0.09wt%~0.18wt%,如0.1wt%。
在本发明的具体实施方式中,所述封闭型异氰酸酯包括丙酮肟、环己酮肟、乙酰酮肟、甲乙酮肟、丙二酸二乙酯封闭六亚甲基二异氰酸酯、八亚甲基二异氰酸酯、十亚甲基二异氰酸酯、十二亚甲基二异氰酸酯、十四亚甲基二异氰酸酯、1,4-环己基二异氰酸酯、4,4’-二环己基甲烷二异氰酸酯和异氟尔酮二异氰酸酯中的任一种或多种。
在本发明的具体实施方式中,所述丙烯酸酯类单体包括含有叔碳的丙烯酸酯类单体。进一步的,所述丙烯酸酯类单体包括丙烯酸异辛酯和/或2-乙基己基丙烯酸酯。
在本发明的具体实施方式中,所述OCA组合物的光固化条件包括:UV固化能量为1000~2500mJ/cm2;所述OCA组合物的热固化条件包括:固化温度为70~90℃,固化时间为10~20min。
在实际操作中,所述OCA组合物可先进行热固化再进行光固化,也可光固化和热固化同时进行。
下述具体实施方式中采用的部分原料信息可以如下,但不局限于此:
二乙烯三胺、二丙烯三胺、双六亚甲基三胺,纯度大于98%,TCI;
马来酸二乙酯,纯度大于99%,安耐吉;
马来酸二丁酯,纯度大于99.5%,阿拉丁;
富马酸二乙酯,纯度大于98.5%,阿拉丁;
异氰酸酯丙烯酸乙酯AOI和异氰酸酯甲基丙烯酸乙酯MOI,纯度大于97%,张家港托普化工;
异氟尔酮二异氰酸酯IPDI,纯度>99%,万华化学;
4-羟基二苯甲酮和4,4’-二羟基二苯甲酮,纯度>98%,TCI;
二月桂酸二丁基锡DBTDL,纯度>95%,TCI;
4-(2-羟基乙氧基)二苯甲酮,纯度>98%,天津日久新材料有限公司;
丙烯酰氯,纯度>98%,TCI;
三乙胺,纯度>99%,TCI;
二乙醇胺,纯度>99%,TCI。
测试与表征:
1、红外:采用傅里叶变换红外光谱对产品结构进行定性表征。仪器型号:BrukerVector 33型FT-IR光谱仪;检测范围主要在400~4000cm-1之间,通过监测特征基团吸收峰面积的变化来检测反应程度。
2、核磁:采用核磁共振仪对PAE产品进行1H NMR定性表征。仪器型号:Bruker400MHz。测试条件:以氘代DMSO为溶剂制样。
3、紫外吸收光谱:
采用紫外分光光度计U-3900型,选用乙腈为溶剂,测试光引发剂在200~350nm范围内的紫外吸收光谱,即可得到引发剂的主要吸光范围和最大吸收波长处的吸光度值,通过下式计算可知其最大摩尔消光系数。测试过程中样品浓度均为5×10-5mol/L。
A=c·ε·l
其中,A为吸光度;c为该物质浓度;ε为摩尔消光系数;l为光程长。
4、光引发剂的相对迁移率:
分别配制含有以下摩尔分数光引发剂的二缩三丙二醇二丙烯酯(TPGDA)溶液:
(1)1wt%二苯甲酮(BP)和1wt%三乙醇胺的TPGDA溶液;
(2)1wt%实施例光引发剂的TPGDA溶液;
(3)1wt%比较例光引发剂的TPGDA溶液。
将它们分别注入尺寸为40mm*6mm*1mm的硅胶垫模具中,在高压汞灯UV固化箱中光照5min,光强为40mW/cm2。然后将固化好的样条捣碎,称取0.1g,用10mL二氯甲烷室温浸泡5d,用紫外-可见分光光度计测量浸泡液中光引发剂在最大吸收峰处的吸光度。由下式计算出各种光引发剂的相对浓度,以光引发剂BP的相对浓度值作为参照基准,可测算出实施例和比较例合成光引发剂的相对迁移率。
C=A/(ε×L×V)×10-2;
R=C1/C2×100%。
式中:C为萃取液(前述浸泡液)中光引发剂的相对摩尔浓度;A为光引发剂最大吸收峰处的吸光度;L为光程长;ε为光引发剂最大吸收峰处的摩尔吸光系数;C1为本发明实施例和比较例合成光引发剂的相对摩尔浓度;C2为BP的相对摩尔浓度;R为的本发明实施例和比较例合成光引发剂相对迁移率。
实施例1
本实施例提供了夺氢型光引发剂及其制备方法,所述夺氢型光引发剂具有如下结构:
其合成路线如下:
具体的,所述夺氢型光引发剂的制备方法包括:
(1)氨基甲酸酯合成:溶剂乙酸乙酯用4A分子筛预先干燥除水;反应用玻璃器皿用鼓风烘箱干燥。称取142g(1.0mol)异氰酸酯丙烯酸乙酯(AOI)、2g二月桂酸二正丁基锡(DBTDL)加入到3L装配有机械搅拌且遮光的夹套玻璃反应釜中,室温搅拌,得到混合物。将107g(0.5mol)4,4’-二羟基二苯甲酮(4,4’-DHBP)加入到1L乙酸乙酯中溶解,置于1.5L恒压滴液漏斗中,逐滴加入到上述混合物中,2.5h滴完。滴完后继续反应至红外监测NCO峰面积(2268cm-1)减小至消失为止,加入0.3g对甲氧基苯酚阻聚剂,搅拌均匀。
(2)Michael加成1:将103.2g(1mol)二乙烯三胺加入1L四口圆底烧瓶中,烧瓶装配有机械搅拌桨、温度计、恒压滴液漏斗、连接有N2气路管、鼓泡器,将344.4g(2mol)马来酸二乙酯加入恒压滴液漏斗中,体系中通入N2 10min,置换体系中空气;在25℃搅拌条件下在烧瓶中缓慢滴入马来酸二乙酯,1h匀速滴完,控制反应温度为30℃,然后升温至60℃反应3h,通过硫醇-碘滴定方法测得反应体系中不饱和值为0.33mg马来酸/g树脂,表明马来酸酯反应转化率99.9%,停止反应,得到聚天门冬氨酸酯多胺。
(3)Michael加成2:在1L恒压滴液漏斗中加入步骤(2)得到的聚天门冬氨酸酯多胺,缓慢滴加至步骤(1)得到的反应液中,2h滴完,滴加时反应体系温度控制在30℃以内,滴加完成后,保温25℃反应5h,通过红外监测反应液,直至丙烯酸酯C=C双键特征峰(1637cm-1)反应至消失为止,停止搅拌,旋蒸脱除反应溶剂乙酸乙酯,得到夺氢型光引发剂。
制得的夺氢型光引发剂的结构表征数据:
红外光谱(KBr压片),ν(cm-1):3319(仲胺N-H的伸缩振动峰),2980、2920、2850(甲基、亚甲基、次甲基的伸缩振动峰),1725(酯基、酮、氨基甲酸酯的羰基C=O的伸缩振动峰),1538(氨基甲酸酯的酰胺N-H的变形振动峰和C-N伸缩振动峰的耦合)。
NMR表征结构为:1H NMR(DMSO),δ:7.72(d,4H),7.43(d,4H),6.76(s,2H),4.01~4.11(m,24H),3.76(m,4H),3.14(m,4H),2.90(m,8H),2.65(m,8H),2.48(m,12H),1.21(m,24H)。确认制得的夺氢型光引发剂为目标产物结构。
实施例2
本实施例提供了夺氢型光引发剂及其制备方法,所述夺氢型光引发剂具有如下结构:
其合成路线如下:
具体的,所述夺氢型光引发剂的制备方法包括:
(1)氨基甲酸酯合成:溶剂乙酸乙酯用4A分子筛预先干燥除水;反应用玻璃器皿用鼓风烘箱干燥。称取222.3g(1.0mol)异氟尔酮二异氰酸酯(IPDI)、2g二月桂酸二正丁基锡(DBTDL)加入到3L装配有机械搅拌且遮光的夹套玻璃反应釜中,室温搅拌,得到混合物。将198g(1mol)4-羟基二苯甲酮(4-HBP)加入到1L乙酸乙酯中溶解,置于1.5L恒压滴液漏斗中,逐滴加入到上述混合物中,2.5h滴完。滴完后继续反应至红外监测NCO峰面积(2268cm-1)不再变化为止;再在滴液漏斗中加入116.2(1mol)丙烯酸羟乙酯(HEA),室温下滴至反应液中,2.5h滴完,然后逐步升温至50℃,继续反应至红外监测NCO峰面积(2268cm-1)减小至消失为止,加入0.3g对甲氧基苯酚阻聚剂,搅拌均匀。
(2)Michael加成1:将215.38g(1mol)双六亚甲基三胺加入1L四口圆底烧瓶中,烧瓶装配有机械搅拌桨、温度计、恒压滴液漏斗、连接有N2气路管、鼓泡器,将344.36g(2mol)马来酸二乙酯加入恒压滴液漏斗中,体系中通入N2 10min,置换体系中空气;在25℃搅拌条件下在烧瓶中缓慢滴入马来酸二乙酯,1h匀速滴完,控制反应温度为30℃,然后升温至60℃反应3h,通过硫醇-碘滴定方法测得反应体系中不饱和值为0.33mg马来酸/g树脂,表明马来酸酯反应转化率99.9%,停止反应,得到聚天门冬氨酸酯多胺。
(3)Michael加成2:在1L恒压滴液漏斗中加入步骤(2)中得到的聚天门冬氨酸酯多胺,缓慢滴加至步骤(1)的反应液中,2h滴完,滴加时反应体系温度控制在30℃以内,滴加完成后,保温25℃反应5h,通过红外监测反应液,直至丙烯酸酯C=C双键特征峰(1637cm-1)反应至消失为止,停止搅拌,旋蒸脱除反应溶剂乙酸乙酯,得到夺氢型光引发剂。
制得的夺氢型光引发剂的结构表征数据:
红外光谱(KBr压片),ν(cm-1):3319(仲胺N-H的伸缩振动峰),2980、2920、2850(甲基、亚甲基、次甲基的伸缩振动峰),1725(酯基、酮、氨基甲酸酯的羰基C=O的伸缩振动峰),1538(氨基甲酸酯的酰胺N-H的变形振动峰和C-N伸缩振动峰的耦合)。
NMR表征结构为:1H NMR(DMSO),δ:7.81(d,2H),7.72(d,2H),7.61(m,1H),7.51(m,2H),7.43(m,2H),4.31(m,4H),4.01~4.11(m,10H),3.76(m,2H),3.54(m,1H),2.90~3.01(m,10H),2.5(m,6H),1.67(m,4H),1.29~1.39(m,16H),1.07(m,14H),0.94(s,3H),0.87(s,6H)。确认制得的夺氢型光引发剂为目标产物结构。
实施例3
本实施例提供了夺氢型光引发剂及其制备方法,所述夺氢型光引发剂具有如下结构:
其合成路线如下:
具体的,所述夺氢型光引发剂的制备方法包括:
(1)氨基甲酸酯合成:溶剂乙酸乙酯用4A分子筛预先干燥除水;反应用玻璃器皿用鼓风烘箱干燥。称取142g(1.0mol)异氰酸酯丙烯酸乙酯(AOI)、2g二月桂酸二正丁基锡(DBTDL)加入到3L装配有机械搅拌且遮光的夹套玻璃反应釜中,室温搅拌,得到混合物。将198.3g(1mol)4-羟基二苯甲酮(4-HBP)加入到1L乙酸乙酯中溶解,置于1.5L恒压滴液漏斗中,逐滴加入到上述混合物中,2.5h滴完。滴完后继续反应至红外监测NCO峰面积(2268cm-1)减小至消失为止,加入0.3g对甲氧基苯酚阻聚剂,搅拌均匀。
(2)Michael加成1:将131.2g(1mol)二丙烯三胺加入1L四口圆底烧瓶中,烧瓶装配有机械搅拌桨、温度计、恒压滴液漏斗、连接有N2气路管、鼓泡器,将456.6g(2mol)马来酸二丁酯加入恒压滴液漏斗中,体系中通入N2 10min,置换体系中空气;在25℃搅拌条件下在烧瓶中缓慢滴入马来酸二丁酯,1h匀速滴完,控制反应温度为30℃,然后升温至60℃反应24h,通过硫醇-碘滴定方法测得反应体系中不饱和值为0.33mg马来酸/g树脂,表明马来酸酯反应转化率99.9%,停止反应,得到聚天门冬氨酸酯多胺。
(3)Michael加成2:在1L恒压滴液漏斗中加入步骤(2)得到的聚天门冬氨酸酯多胺,缓慢滴加至步骤(1)得到的反应液中,2h滴完,滴加时反应体系温度控制在30℃以内,滴加完成后,保温25℃反应5h,通过红外监测反应液,直至丙烯酸酯C=C双键特征峰(1637cm-1)反应至消失为止,停止搅拌,旋蒸脱除反应溶剂乙酸乙酯,得到夺氢型光引发剂。
制得的夺氢型光引发剂的结构表征数据:
红外光谱(KBr压片),ν(cm-1):3319(仲胺N-H伸缩振动峰),2980、2920、2850(甲基、亚甲基、次甲基的伸缩振动峰),1725(酯基、酮、氨基甲酸酯的羰基C=O的伸缩振动峰),1538(氨基甲酸酯的酰胺N-H的变形振动峰和C-N伸缩振动峰的耦合)。
NMR表征结构为:1H NMR(DMSO),δ:7.81(d,2H),7.72(d,2H),7.61(m,1H),7.51(m,2H),7.43(m,2H),4.06~4.13(m,12H),3.15(m,2H),2.9(d,4H),2.75(m,2H),2.68(m,2H),2.54(m,4H),2.35(m,2H),1.54(m,8H),1.40(m,8H),1.11(d,6H),0.90(m,12H)。确认制得的夺氢型光引发剂为目标产物结构。
实施例4
本实施例提供了OCA组合物及其制备,其中,各组OCA组合物的配方体系见表1:
表1不同OCA组合物的配方体系
其中,EHA为2-乙基己基丙烯酸酯(长兴化学工业);HEA为2-羟乙基丙烯酸酯(长兴化学工业);THFA为丙烯酸四氢呋喃酯(长兴化学工业);ACMO为丙烯酰吗啉(日本科巨希);甲乙酮肟封闭IPDI(万华化学)。光引发剂为实施例1~实施例3制备得到的夺氢型光引发剂,1#(1-1#、2-1#、3-1#)、2#(1-2#、2-2#、3-2#)、3#(1-3#、2-3#、3-3#)分别对应实施例1~实施例3的光引发剂。
所述OCA组合物的制备包括:
(1)在反应器中充分混合上述配方体系Step1中的所有组分和0.02%质量百分数(此处的0.02%是指:Step1和Step2中所有组分的用量和的0.02%)的光引发剂(Irgacure651)。用N2置换其中的溶解氧后,使用低压汞灯辐照(辐照剂量约为70~100mJ/cm2)若干分钟(3~6min),从而制备25℃下具有2000~5000cp黏度的粘性液体。
(2)将Step2中的组分以及0.1%质量百分数(此处的0.1%是指:Step1和Step2中所有组分的用量和的0.1%)的光引发剂Irgacure 651加入到反应器中,充分混合均匀,从而制备得到OCA组合物。
(3)将步骤(2)得到的组合物涂布到轻、重两层对苯二甲酸乙二醇(PET)离型膜之间,形成175μm厚度的OCA涂层膜。用低压UV汞灯以1000mJ/cm2的剂量辐照,从而制备OCA胶膜。
比较例1
比较例1提供了光引发剂及其制备方法,光引发剂具有如下结构:
其合成路线如下:
具体的,光引发剂的制备方法包括:
将484.6g(2mol)4-(2-羟基乙氧基)二苯甲酮、222.6g(2.2mol)三乙胺和1kg二氯甲烷加入3L夹套玻璃反应釜中,夹套釜装配有机械搅拌桨、温度计、恒压滴液漏斗、连接有N2气路管、鼓泡器,降温至0℃,将199.2g(2.2mol)丙烯酰氯加入恒压滴液漏斗中,体系中通入N2 20min,置换体系中空气;在0~5℃搅拌条件下向玻璃反应釜中缓慢滴入丙烯酰氯,2h匀速滴完,然后自然升温至10℃反应过夜,过滤除去三乙胺盐酸盐,并用NaHCO3饱和溶液萃取,旋蒸除去溶剂,用正己烷/二氯甲烷混合溶剂重结晶,得到白色颗粒状晶体,即得光引发剂。
制得的光引发剂的结构的表征数据:
红外光谱(KBr压片),ν(cm-1):1725(酯基羰基C=O的伸缩振动峰),1650(酮羰基C=O的伸缩振动峰),808(碳碳双键=C-H的弯曲振动峰)。
NMR表征结构为:1H NMR(DMSO),δ:7.84(d,2H),7.77(d,2H),7.59(t,1H),7.49(t,2H),7.00(d,2H),6.48(d,1H),6.19(dd,1H),5.89(d,1H),4.57(m,2H),4.32(m,2H)。确认制得的光引发剂为目标产物结构。
比较例2
比较例2提供了光引发剂及其制备方法,光引发剂具有如下结构:
其合成路线如下:
具体的,光引发剂的制备方法包括:
将比较例1得到的光引发剂4296.5g(1mol)和500g乙醇加入2L夹套玻璃反应釜中,夹套釜装配有机械搅拌桨、温度计、恒压滴液漏斗、鼓泡器,降温至0℃,将105.2(1mol)二乙醇胺加入恒压滴液漏斗中,在0~5℃搅拌条件下向玻璃反应釜中缓慢滴入二乙醇胺,2h匀速滴完,然后保持0℃反应过夜,旋蒸除去溶剂,用乙酸乙酯溶剂重结晶,得到浅黄色固体,即为单组分光引发剂。
制得的光引发剂的结构表征数据:
红外光谱(KBr压片),ν(cm-1):3449(羟基O-H伸缩振动峰),1725(酯基羰基C=O的伸缩振动峰),1650(酮羰基C=O的伸缩振动峰),1351(叔胺C-N的伸缩振动峰)。
NMR表征结构为:1H NMR(DMSO),δ:7.81(d,2H),7.73(d,2H),7.60(t,1H),7.50(t,2H),7.01(d,2H),4.43(m,4H),3.76(m,2H),3.42(m,4H),2.57(m,4H),2.49(m,2H)。确认制得的光引发剂为目标产物结构。
比较例3
比较例3参考实施例4,提供了OCA组合物,各组OCA组合物的配方体系见表2,制备方法同实施例4。
表2不同OCA组合物的配方体系
其中,4#(1-4#、2-4#、3-4#)、5#(1-5#、2-5#、3-5#)分别对应比较例1和比较例2的光引发剂。
实验例1
性能表征用试样的制备:
未固化试样:通过实施例4和比较例3的方法制备的OCA胶膜,将其裁切成尺寸为100mm×25mm×175μm(长×宽×厚)的胶膜,剥离除去轻型PET离型膜,贴合在玻璃薄片上,然后60℃/0.5MPa高温高压条件下进行脱泡30min,自然冷却至室温。
热固化后试样:将上述未固化试样,遮光条件下进一步在85℃热固化10min,自然冷却至室温。
光-热双重固化后试样:将上述未固化试样,进一步在85℃,高压汞灯下光-热固化10min,高压UV汞灯辐照能量为2000mJ/cm2,自然冷却至室温。
对制备得到的OCA胶膜进行性能评价,具体制样和表征方法如下:
1、油墨润湿性能:
将未固化的OCA胶膜进行此测试,评估贴合时OCA胶膜对油墨梯级的填充和润湿能力,在较大油墨梯级处变形后防止新的气泡形成的能力。使用真空层合机(13N/cm2压力下层合15s,30Pa真空),在普通矩形(19cm×12cm)玻璃面板和沿四个边缘具有黑色油墨(50μm高×0.6cm宽)的矩形(19cm×12cm)玻璃面板之间层合OCA样品。然后,将层合制品高压脱泡(60℃和0.5MPa压力下进行30min),随后检查形成在靠近油墨边缘的OCA胶层中的气泡,这些气泡将妨碍显示器的可视区。通过以下符号表示润湿效果:0意指油墨周围有最少的气泡(<5),△意指油墨周围有一些气泡(>5但<10),以及X意指油墨周围有大量的气泡(>10)。
2、粘接可靠性检验:
为了对比说明本发明不同实施例和比较例的光引发剂制得的OCA胶膜的粘接可靠性,采用实施例4和比较例3制得的OCA胶膜进行贴合后固化后,对耐高温高湿老化性能进行测试。
测试标准:GBT2423.3-2006《电工电子产品环境试验》。
将样品置于温度为85℃、相对湿度为85%的恒温湿热箱中,1000h后进行外观观察、透光率和雾度测试和180°剥离力测试。
外观检验:
检验方法:将经过可靠性实验后的样条进行外观检验,检验人员在普通光源(背景为黑色)下与成品成0~90°角目测。
判断标准:有无气泡;边缘有无发白。
透光率和雾度测试:
测试标准:GB/T 2410-2008《透明塑料透光率和雾度的测定》,测试光波长范围380~780nm。
180℃剥离强度(单位N/25mm):
测试标准:GB/T2792-1998《压敏胶粘带180°剥离强度试验方法》。
引发剂迁移率表征结果如下表3所示:
表3 OCA固化胶膜的引发剂相对迁移率
通过以上各个实施例和比较例的引发剂迁移率对比结果表明,本发明制备的光-热双重固化引发剂相比于比较例1的可聚合光引发剂或比较例2的单组分光引发剂,具备低得多的溶剂萃取率,即显著低的引发剂迁移率。这主要是因为本发明的双重固化引发剂不但分子量相对更大,在体系中的相容性和分散更好,并且双重固化效果更赋予引发剂更充足的整合进高分子链中的途径,因而导致游离的引发剂比例大幅降低。即使是在单纯热固化后,也具备相对更低的迁移率。
为了对比不同引发剂对OCA胶膜性能的影响,对按照表1和表2配方所得到的OCA胶膜性能进行评估,结果见表4。
表4光-热双重后固化前后OCA胶膜的性能测试结果
通过以上各个实施例和比较例的引发剂得到的OCA胶膜的性能测试结果表明,本发明制备的光-热双重固化引发剂相比于比较例1的可聚合光引发剂或比较例2的单组分光引发剂,由于良好的增塑效果,贴合时对油墨段差的润湿性以及粘接后的剥离力明显优于相同配方体系下的比较例1中的可聚合光引发剂或比较例2中的单组分光引发剂。光-热双重固化后,由于交联的产生,会导致胶膜收缩产生应力,剥离力略有降低。但交联的产生同时赋予了在贴合胶膜在双85实验(85℃/85%RH湿度)条件下更优异的粘接可靠性。本发明中实施例中的光-热双重固化剂,在可靠试验后,在外观、透光率、雾度以及剥离力方面均优于比较例。
为了考察在遮光条件下,单纯热固化对于OCA胶膜性能的影响,通过表征得到如表5所示的性能数据。
表5热固化前后OCA胶膜的性能测试结果
通过上述对比结果表明,相同配方体系下,本发明引发剂使胶膜热固化后形成丙烯酸酯聚合物和聚氨酯互穿网络结构,从而赋予遮光区域胶膜具备了更优的贴合粘接剥离强度,可以更好地阻挡水汽的渗透,在双85试验后更好地粘接可靠性,具体表现在外观无可见劣化,并且保持了令人满意的粘接强度。而比较例1和比较例2的引发剂由于并不具备热固化效果,容易在高温高湿下造成脱层,出现气泡,粘接力大幅下滑,这就有可能造成显示器边框处出现溢胶和粘接缺陷。
综上所述,相比于现有的光引发剂,本发明的光-热双重固化引发剂,可以解决不透明区域更好的固化效果,赋予OCA胶膜组合物更加优异的油墨段差填充性能、粘接力以及粘接可靠性。
最后应说明的是:以上各实施例仅用以说明本发明的技术方案,而非对其限制;尽管参照前述各实施例对本发明进行了详细的说明,本领域的普通技术人员应当理解:其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分或者全部技术特征进行等同替换;而这些修改或者替换,并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (17)
3.根据权利要求2所述的夺氢型光引发剂,其特征在于,R5为-CH2CH2-。
6.根据权利要求5所述的夺氢型光引发剂的制备方法,其特征在于,所述双烷基三胺选自二乙烯三胺、二丙烯三胺和双六亚甲基三胺中的任一种或多种。
7.根据权利要求5所述的夺氢型光引发剂的制备方法,其特征在于,所述丁烯二酸二酯选自马来酸二酯和/或富马酸二酯,所述马来酸二酯选自马来酸二乙酯、马来酸二丙酯、马来酸二丁酯和马来酸甲基丙基酯中的任一种或多种,所述富马酸二酯选自富马酸二乙酯、富马酸二丙酯、富马酸二丁酯和富马酸甲基丙基酯中的任一种或多种。
8.根据权利要求5所述的夺氢型光引发剂的制备方法,其特征在于,所述双烷基三胺和丁烯二酸二酯的摩尔比为1﹕(1.8~2.2)。
9.根据权利要求5所述的夺氢型光引发剂的制备方法,其特征在于,步骤(b)中,所述聚天门冬氨酸酯多胺与所述二苯甲酮衍生物的反应摩尔比为1﹕(0.9~1.1)。
10.根据权利要求4所述的夺氢型光引发剂的制备方法,其特征在于,所述二异氰酸酯为异佛尔酮二异氰酸酯。
11.根据权利要求4所述的夺氢型光引发剂的制备方法,其特征在于,所述含羟基丙烯酸酯选自丙烯酸羟乙酯和丙烯酸羟丙酯中的至少一种。
13.权利要求1-3任一项所述的夺氢型光引发剂在制备OCA胶膜中的应用。
14.OCA组合物,其特征在于,包括权利要求1-3任一项所述的夺氢型光引发剂1wt%~10wt%。
15.根据权利要求14所述的OCA组合物,其特征在于,所述OCA组合物包括按质量百分数计的如下组分:丙烯酸酯类单体和预聚物70%~97%、所述夺氢型光引发剂1%~10%、以及封闭型异氰酸酯2%~20%。
16.根据权利要求15所述的OCA组合物,其特征在于,所述封闭型异氰酸酯选自采用丙酮肟、环己酮肟、乙酰酮肟、甲乙酮肟和丙二酸二乙酯中的任一种封闭的六亚甲基二异氰酸酯、八亚甲基二异氰酸酯、十亚甲基二异氰酸酯、十二亚甲基二异氰酸酯、十四亚甲基二异氰酸酯、1,4-环己基二异氰酸酯、4,4’-二环己基甲烷二异氰酸酯和异佛尔酮二异氰酸酯中的任一种。
17.根据权利要求14所述的OCA组合物,其特征在于,所述OCA组合物的光固化条件包括:UV固化能量为1000~2500mJ/cm2;所述OCA组合物的热固化条件包括:固化温度为70~90℃,固化时间为10~20min。