CN114231175A - 用于磷石膏的防结块剂及其制备方法和使用方法 - Google Patents
用于磷石膏的防结块剂及其制备方法和使用方法 Download PDFInfo
- Publication number
- CN114231175A CN114231175A CN202111551348.6A CN202111551348A CN114231175A CN 114231175 A CN114231175 A CN 114231175A CN 202111551348 A CN202111551348 A CN 202111551348A CN 114231175 A CN114231175 A CN 114231175A
- Authority
- CN
- China
- Prior art keywords
- phosphogypsum
- caking agent
- agent
- caking
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种用于磷石膏的防结块剂及其制备方法和使用方法,其包括按质量计的以下原料:表面活性剂3~7%、挥发性溶剂2‑6%、成膜剂:1‑10%,其余为水;其中成膜剂为高含氢硅油;挥发性溶剂为乙醇和/或甲醇。采用本发明提供的防结块剂用于防磷石膏结块时,加入量为磷石膏的1~10%,采用喷雾方式加入,然后混匀,该防结块剂能够有效防止磷石膏结块,并且通过喷雾形式进行添加,使用方便,防结块效果好。
Description
技术领域
本发明涉及磷石膏技术领域,具体为用于磷石膏的防结块剂及其制备方法和使用方法。
背景技术
磷石膏是在磷酸生产中用硫酸处理磷矿时产生的固体废渣,制取1吨磷酸(以100%P2O5计)会产生4.8~5.0吨磷石膏。我国目前每年排放磷石膏约2000万吨,累计排量近亿吨,是石膏废渣中排量最大的一种,排出的磷石膏渣占用大量土地,形成渣山。
近年来磷石膏的堆存与综合利用问题受到国内外的重视,由于磷石膏含有一定的附着水和结晶水,系强酸金属盐,且常年露天堆积,风吹雨淋,在自然条件下晶体形状和结晶水含量发生变化,在外界环境温度湿度压力等因素影响下,形成晶桥,使颗粒带电,从而相互吸附结块。
随着磷石膏综合利用率提高,陈化的磷石膏被回采利用,磷石膏结块的问题逐渐暴露。目前针对各种材料如肥料、食品等均有防结块研究,有许多防结块剂产品,但是针对磷石膏防结块剂还未见报道。其中有大量专家学者,针对石膏防水性能差,吸水率高缺点进行了大量了研究,开发出一系列石膏防水剂,主要原理是在石膏制品表面涂刷防水功能涂料,或者在制作石膏制品过程中添加火山灰材料和憎水性物质,改变石膏特性,降低石膏制品的吸水性,如“石膏耐水粉”(CN1074235A)由水泥熟料、硫酸铝、硅铝酸盐、塑化剂和缓凝剂组成。公开号CN1051719A中添加钢渣粉到磷石膏中,具有较好的强度和防水性,但是它从根本上改变了石膏的特性,其水化产物已经不属于石膏凝胶材料的范畴。公开号CN103232260A中使用发泡剂、磷酸盐和有机硅等制得防水保温轻质高强α半水石膏板石膏板材。
发明内容
本发明提供一种用于磷石膏的防结块剂及其制备方法和使用方法,采用该防结块剂,能够有效防止磷石膏结块,其通过喷雾形式进行添加,使用方便,防结块效果好。
本发明的技术方案是,一种用于磷石膏的防结块剂,包括按质量计的以下原料:表面活性剂3~7%、挥发性溶剂2-6%、成膜剂:1-10%,其余为水;其中成膜剂为高含氢硅油。
进一步地,所述挥发性溶剂为甲醇和/或乙醇。
进一步地,表面活性剂为吐温-80、十二烷基硫酸钠、十二烷基苯磺酸钠、十二烷基氨酸钠中的一种或几种。
进一步地,其中表面活性剂3%、挥发性溶剂6%、成膜剂1%,其余为水。
本发明还涉及所述用于磷石膏的防结块剂的制备方法,包括以下步骤:
S1、将水加热后加入表面活性剂,混匀后停止加热;
S2、S1中的溶液降至室温后,向溶液中加入成膜剂和挥发性溶剂,混匀即得防结块剂。
进一步地,S1中水加热至80℃以上。
本发明还涉及所述用于磷石膏的防结块剂的使用方法,将防结块剂以喷雾形式加入到磷石膏中,混合均匀。
进一步地,防结块剂的加入量为磷石膏质量的1~10%。
进一步地,磷石膏中含水量为10-25%。
进一步地,磷石膏的粒径为20-50μm。
本发明具有以下有益效果:
含氢硅油具有特别优良的疏水性,适合进行玻璃,金属,纤维,粉末的表面处理等很多场合,在各种物质表面形成防水膜,如在水泥、防水石膏板中应用,作为防水剂,在金属盐类催化剂作用下,低温可交联成膜,在表面形成防水膜。但含氢硅油因为本身的粘性和疏水性,不能与磷石膏进行混合,无法起到防结块效果。
本发明改变传统粉状或者油状防结块剂的缺陷,提供的防结块剂,通过加入表面活性剂和水,将其制备成水性液体,成膜剂含量少,而且防结块剂的用量低,成膜剂高含氢硅油的用量小,成本低,使用方便,防结块效果好,而且对磷石膏下一步综合利用无影响,适合工业化制备,有利于推广应用。
在防结块剂的制备过程中,通过将水加热后加入表面活性剂,有助于其与水的混合,通过表面活性剂挥发溶剂和水份复配,制备成水溶性溶液,喷雾使用时,不会堵塞喷头,同时能够确保均匀加入,加入及搅拌过程中还能起到将粉尘的效果。
在防结块剂制备过程中,增加挥发性溶剂,一方面,其有助于成膜剂与水的混合,促进防结块剂的均匀分散;另一方面,其在混合后能够快速挥发,挥发过程中还能带走部分水分,降低磷石膏中的水分,同时均匀混合后的成膜剂具有很好的疏水作用,随着陈化的进行水分含量越来越少,有效防止磷石膏结块。
附图说明
图1为防结块剂的制备流程及使用流程图。
具体实施方式
下面将结合实施例对本发明的实施方案进行详细描述,但是本领域技术人员将会理解,下列实施例仅用于说明本发明,而不应视为限定本发明的范围。
以下实施例中用到的磷石膏指标:二水硫酸钙(干基)92.19w%,附着水10.02wt%。
实施例1
防结块剂原料配方:水、表面活性剂、成膜剂和挥发性溶剂质量比为90:3:1:6。
制备时,先将水加热至80℃,加入表面活性剂吐温-80,搅拌至全部溶解后,搅拌均匀,停止加热,冷却至室温。再加入成膜剂高含氢硅油和挥发性溶剂乙醇搅拌均匀,即得。
其中水:高含氢硅油分子式为(CH3)3Si[(CH3)SiO][(CH3)(H)SiO2]ySi(CH3)3,含氢量1.58-1.60%,粘度, 25°C, 20-30mm2/s,密度, 25°C, 0.98-1.02g/cm3。
使用时,将配置好的防结块剂放入喷雾器中,磷石膏置于搅拌机中,在搅拌的条件下将防结块剂雾化后喷洒在磷石膏表面,防结块剂用量为1%,使磷石膏与防结块剂混合均匀。
实施例2:
防结块剂原料配方:水、表面活性剂、成膜剂、挥发性溶剂质量比为90:3:1:6。
将水加热至80℃,加入表面活性剂十二烷基硫酸钠,搅拌至全部溶解后,搅拌均匀,停止加热,冷却至室温,加入成膜剂高含氢硅油,性能参数同实施例1和挥发性溶剂乙醇,搅拌均匀后即可,将配置好的防结块剂放入喷雾器中,磷石膏置于搅拌机中,在搅拌的条件下将防结块剂雾化后喷洒在磷石膏表面,防结块剂用量为1%,使磷石膏与防结块剂混合均匀。
实施例3:
防结块剂使用时用量为磷石膏的0.5%,其余同实施例2。
实施例4:
防结块剂使用时用量为磷石膏的0.1%,其余同实施例2。
实施例5:
防结块剂原料配方:水、表面活性剂、成膜剂和挥发性溶剂质量比为82:7:5:6。
将水加热至80℃,加入表面活性剂吐温-80,搅拌至全部溶解后,搅拌均匀,停止加热,冷却至室温,加入成膜剂高含氢硅油和挥发性溶剂乙醇,搅拌均匀后即可,将配置好的防结块剂放入喷雾器中,磷石膏置于搅拌机中,在搅拌的条件下将防结块剂雾化后喷洒在磷石膏表面,防结块剂用量为1%,使磷石膏与防结块剂混合均匀。
对比例1:
某种石膏防水剂粉剂主要成分为甲基硅酸,将其与磷石膏置于搅拌机中,防水剂用量为20%,使磷石膏与防结块剂混合均匀,因为磷石膏中含水10.02wt%,在混合过程中粉剂容易结块,难以均匀分散。
对比例2:
将磷石膏加入搅拌机中,不停搅拌,逐滴加入实施例1中的成膜剂高含氢硅油,高含氢硅油:磷石膏的质量比为1:1000,加入后继续搅拌,尽量使二者混合均匀。
对比例3:
将磷石膏加入搅拌机中,不停搅拌,逐滴加入实施例2中的防结块剂,防结块剂:石膏质量比为1:100。
分别对实施例1~5和对比案例1-3所得到的含有防结块剂的磷石膏样品进行结块试验,具体操作如下:用包装袋将处理后的磷石膏进行装袋,放入恒温恒湿箱内,温度为40℃,相对湿度为50%,压上重物,一段时间后取出,从1米高处正反两面各自由摔落2次,烘干,用标准筛筛分,测试结块率,同时做空白对照试验。其中,结块率计算方法为:结块磷石膏质量/磷石膏质量;根据计算公式计算得到实施例1~5、对比例1~3及空白对照的结块率分别为10.21%、7.25%、9.82%、12.51、5.75%、75.21%、72.25%、15.52、85.76%。从结果来看,加入防结块剂可以明显改善磷石膏结块现象,防结块剂粉因为粉剂和含水磷石膏不能混合均匀,效果较差,而单独采用成膜剂,虽然用量1:1000,较实施例中添加的成膜剂用量大,但是防结块效果不佳,主要是疏水性太强,没有分散开,不能与磷石膏混合均匀,而采用滴管式加入实施例2 中的防结块剂,发现防结块效果较喷雾式略差,主要是因为滴入时,防结块剂与磷石膏接触面积小,混合的得不够均匀,实施例5中水:表面活性剂十二烷基硫酸钠:成膜剂:挥发性溶剂乙醇质量比为82:7:5:6时,效果最好,结块率为5.75%,此时高含氢硅油相对于磷石膏添加量为0.5‰,而实施例2中,高含氢硅油相对于磷石膏添加量为0.1‰,结块率从5.75%上升到7.25%。
Claims (10)
1.一种用于磷石膏的防结块剂,其特征在于,包括按质量计的以下原料:表面活性剂3~7%、挥发性溶剂2-6%、成膜剂:1-10%,其余为水;其中成膜剂为高含氢硅油。
2.根据权利要求1所述的防结块剂,其特征在于:所述挥发性溶剂为甲醇和/或乙醇。
3.根据权利要求1所述的防结块剂,其特征在于:表面活性剂为吐温-80、十二烷基硫酸钠、十二烷基苯磺酸钠、十二烷基氨酸钠中的一种或几种。
4.根据权利要求1~3任意一项所述的防结块剂,其特征在于:其中表面活性剂3%、挥发性溶剂6%、成膜剂1%,其余为水。
5.权利要求1~4任意一项所述用于磷石膏的防结块剂的制备方法,其特征在于,包括以下步骤:
S1、将水加热后加入表面活性剂,混匀后停止加热;
S2、S1中的溶液降至室温后,向溶液中加入成膜剂和挥发性溶剂,混匀即得防结块剂。
6.根据权利要求1所述的用于磷石膏的防结块剂的制备方法,其特征在于:S1中水加热至80℃以上。
7.权利要求1~4任意一项所述用于磷石膏的防结块剂的使用方法,其特征在于:将防结块剂以喷雾形式加入到磷石膏中,混合均匀。
8.根据权利要求7所述的使用方法,其特征在于,防结块剂的加入量为磷石膏质量的1~10%。
9.根据权利要求7所述的使用方法,其特征在于:磷石膏中含水量为10-25%。
10.根据权利要求7所述的使用方法,其特征在于:磷石膏的粒径为20-50μm。