CN114085407A - 一种新型防滑一次性手套的生产工艺 - Google Patents
一种新型防滑一次性手套的生产工艺 Download PDFInfo
- Publication number
- CN114085407A CN114085407A CN202111316135.5A CN202111316135A CN114085407A CN 114085407 A CN114085407 A CN 114085407A CN 202111316135 A CN202111316135 A CN 202111316135A CN 114085407 A CN114085407 A CN 114085407A
- Authority
- CN
- China
- Prior art keywords
- slip
- parts
- glove
- gloves
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于手套生产技术领域，涉及一种新型防滑一次性手套的生产工艺，包括：(1)制备胶乳；(2)制备防滑剂；(3)浸渍手模；(4)卷边脱模；(5)反转；(6)喷涂防滑剂；(7)烘烤；(8)包装。本发明提供的生产工艺，在脱模反转后喷涂了防滑剂，从而使得手套表面涂有防滑层，在抓握使用工具时，大大增加了摩擦力，提高了手套的防滑性能。防滑涂层仅在手套的外表面喷涂，在工艺上不需要对现有成熟工艺做较大改动，在合适位置增设半密闭的喷涂环境即可，相对现有的防滑技术大大节省了原料的使用，降低了能耗，通过本工艺制得的手套防滑性能和防护性都很好。
Description
技术领域
本发明属于手套生产技术领域，具体涉及一种新型防滑一次性手套的生产工艺。
背景技术
随着市场不同行业的需求，一次性手套的品种不断的增多，目前已经由最初的乳胶手套、PVC手套，发展到后期的丁腈胶手套，丁腈胶手套主要由丁腈橡胶加工而成，是应用在医疗、医药卫生、美容美发、食品加工、化工、生物等的科学研究行业中，起到对手部防护、防止交叉感染的必不可少的保护用品。因丁腈橡胶中不含蛋白质，故不会造成过敏反应，同时又具有抗静电、耐老化和耐油的性能，其造型根据人体手型而设计，具有较大的灵活性，较好的拉伸性能和耐穿刺性能，较高的抗张强度和较好的耐磨性能，使用广泛。
一次性手套在临床医学和实验中都起到不可或缺的作用。目前所使用的一次性手套由于外表面光滑，所以在使用一些光滑的工具时，容易脱落，进而发生危险。现有技术中，为了增加手套的摩擦力，常常在手套上制作麻点颗粒等，这样就增加了手套的制备工艺的复杂性和制作成本，且现有的一次性防滑手套的生产技术对目前投入使用的设备的改动较大，能耗较高。
发明内容
本发明的目的在于提供一种工艺简单，易于脱模，能耗和成本较低，且手套具有防滑功能的新型防滑一次性手套的生产工艺，以解决上述背景技术中提出的问题。
为达到上述技术目的，本发明的技术方案：
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：按比例取丁腈胶乳、研磨料和氢氧化钾，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳、研磨料和氢氧化钾，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍所述胶乳，烘烤定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，脱模；
(5)反转：将所述手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的所述手套送入喷涂设备，均匀地喷涂所述防滑剂；
(7)烘烤：将所述手模和涂有所述防滑剂的手套放入热油管式封闭烤箱内进行循环烘烤，直至防滑涂层彻底烘干；
(8)包装：将手套从所述手模上取下，进行包装。
作为一种改进，步骤(1)中，按重量份计，丁腈胶乳80-90份，研磨料5-10份，氢氧化钾3-5份。
作为一种改进，步骤(2)中，按重量份计，氯丁胶乳80-90份，研磨料5-10份，氢氧化钾3-5份。
作为进一步地改进，所述研磨料包括硫磺、氧化锌、促进剂、防老剂和钛白粉。
优选的，所述促进剂为促进剂BDBC、促进剂ZDEC、促进剂TBZTD或促进剂CA中的两种以上混合物。
优选的，所述防老剂为受阻酚类抗氧剂。
作为一种改进，步骤(3)中，所述凝固剂包括硝酸钙和脱模剂.
优选的，所述脱模剂包括硬脂酸钙。
作为一种改进，步骤(3)中，烘烤温度为115-140℃，烘烤时间为40-50分钟。
作为一种改进，步骤(7)中，烘烤温度为105-120℃，烘烤时间为8-12分钟。
由于采用上述技术方案，本发明的有益效果：
本发明提供的生产工艺，在脱模反转后喷涂了防滑剂，从而使得手套表面涂有防滑层，在抓握使用工具时，大大增加了摩擦力，提高了手套的防滑性能。防滑涂层仅在手套的外表面喷涂，在工艺上不需要对现有成熟工艺做较大改动，在合适位置增设半密闭的喷涂环境即可，相对现有的防滑技术大大节省了原料的使用，降低了能耗，通过本工艺制得的手套防滑性能和防护性都很好。
附图说明
图1是本发明提供的工艺流程图；
图2是本发明提供的手套反转时的结构示意图；
图3是本发明提供的手套反转后喷涂防滑剂时的结构示意图；
其中：1-手模，2-手套，3-手模手套连接处，4-喷壶。
具体实施方式
下面结合具体实施方式及附图对本发明作进一步的说明。其中，附图仅用于示例性说明，表示的仅是示意图，而非实物图，不能理解为对本专利的限制；为了更好地说明本发明的实施例，附图某些部件会有省略、放大或缩小，并不代表实际产品的尺寸；对本领域技术人员来说，附图中某些公知结构及其说明可能省略是可以理解的。
本发明实施例的附图中相同或相似的标号对应相同或相似的部件；在本发明的描述中，需要理解的是，若有术语“上”、“下”、“左”、“右”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此附图中描述位置关系的用语仅用于示例性说明，不能理解为对本专利的限制，对于本领域的普通技术人员而言，可以根据具体情况理解上述术语的具体含义。
实施例1
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳80份、研磨料5份和氢氧化钾5份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳85份、研磨料7份和氢氧化钾5份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于120℃下进行链式循环烘烤45分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于105℃下进行循环烘烤12分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
实施例2
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳83份、研磨料6份和氢氧化钾4份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳80份、研磨料5份和氢氧化钾5份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于115℃下进行链式循环烘烤50分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于110℃下进行循环烘烤10分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
实施例3
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳85份、研磨料7份和氢氧化钾4份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳87份、研磨料6份和氢氧化钾3份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于125℃下进行链式循环烘烤48分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于115℃下进行循环烘烤10分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
实施例4
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳87份、研磨料8份和氢氧化钾3份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳82份、研磨料8份和氢氧化钾4份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于130℃下进行链式循环烘烤46分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于120℃下进行循环烘烤8分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
实施例5
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳90份、研磨料9份和氢氧化钾3份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳90份、研磨料9份和氢氧化钾3份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于140℃下进行链式循环烘烤40分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于110℃下进行循环烘烤11分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
实施例6
一种新型防滑一次性手套的生产工艺，包括以下步骤：
(1)制备胶乳：取丁腈胶乳82份、研磨料10份和氢氧化钾5份，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳84份、研磨料10份和氢氧化钾3份，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍上述胶乳，放入热油管式封闭烤箱内于135℃下进行链式循环烘烤43分钟，定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，以便于脱模和穿戴；
(5)反转：将手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的手套送入喷涂设备，均匀地喷涂上述防滑剂；
(7)烘烤：将手模和涂有防滑剂的手套放入热油管式封闭烤箱内于115℃下进行循环烘烤10分钟，直至防滑涂层彻底烘干；
(8)包装：将手套从手模上取下，进行包装。
如图2所示，手套反转时，只需脱模脱至四指指尖部分未从手模上脱落，然后再如图3所示进行喷涂防滑剂，从而使得手套表面能喷涂一层防滑剂，增加了手套表面的摩擦力，提高了手套的防滑性能。
以上所述本发明的具体实施方式，并不构成对本发明保护范围的限定。任何根据本发明的技术构思所做出的各种其他相应的改变与变形，均应包含在本发明权利要求的保护范围内。
Claims (10)
1.一种新型防滑一次性手套的生产工艺，其特征在于，包括以下步骤：
(1)制备胶乳：按比例取丁腈胶乳、研磨料和氢氧化钾，混合，搅拌均匀，倒入料槽中待用；
(2)制备防滑剂：按比例取氯丁胶乳、研磨料和氢氧化钾，混合，搅拌均匀，倒入喷壶中待用；
(3)浸渍手模：手模先浸渍凝固剂，后再浸渍所述胶乳，烘烤定型；
(4)卷边脱模：用橡胶辊在120℃下摩擦卷边，脱模；
(5)反转：将所述手套脱模脱至除大拇指外的四指指尖部分未从手模上脱落；
(6)喷涂防滑剂：将未脱落的所述手套送入喷涂设备，均匀地喷涂所述防滑剂；
(7)烘烤：将所述手模和涂有所述防滑剂的手套放入热油管式封闭烤箱内进行循环烘烤，直至防滑涂层彻底烘干；
(8)包装：将手套从所述手模上取下，进行包装。
2.根据权利要求1所述的新型防滑一次性手套的生产工艺，其特征在于，步骤(1)中，按重量份计，丁腈胶乳80-90份，研磨料5-10份，氢氧化钾3-5份。
3.根据权利要求1所述的新型防滑一次性手套的生产工艺，其特征在于，步骤(2)中，按重量份计，氯丁胶乳80-90份，研磨料5-10份，氢氧化钾3-5份。
4.根据权利要求1-3任一项所述的新型防滑一次性手套的生产工艺，其特征在于，所述研磨料包括硫磺、氧化锌、促进剂、防老剂和钛白粉。
5.根据权利要求4所述的新型防滑一次性手套的生产工艺，其特征在于，所述促进剂为促进剂BDBC、促进剂ZDEC、促进剂TBZTD或促进剂CA中的两种以上混合物。
6.根据权利要求4所述的新型防滑一次性手套的生产工艺，其特征在于，所述防老剂为受阻酚类抗氧剂。
7.根据权利要求1所述的新型防滑一次性手套的生产工艺，其特征在于，步骤(3)中，所述凝固剂包括硝酸钙和脱模剂。
8.根据权利要求7所述的新型防滑一次性手套的生产工艺，其特征在于，所述脱模剂包括硬脂酸钙。
9.根据权利要求1所述的新型防滑一次性手套的生产工艺，其特征在于，步骤(3)中，烘烤温度为115-140℃，烘烤时间为40-50分钟。
10.根据权利要求1所述的新型防滑一次性手套的生产工艺，其特征在于，步骤(7)中，烘烤温度为105-120℃，烘烤时间为8-12分钟。