CN114044675A - Carbon-ceramic insulating material - Google Patents
Carbon-ceramic insulating material Download PDFInfo
- Publication number
- CN114044675A CN114044675A CN202111380955.0A CN202111380955A CN114044675A CN 114044675 A CN114044675 A CN 114044675A CN 202111380955 A CN202111380955 A CN 202111380955A CN 114044675 A CN114044675 A CN 114044675A
- Authority
- CN
- China
- Prior art keywords
- molding
- carbon
- hot air
- ceramic
- insulating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a carbon-ceramic insulating material which is prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding in a mold, hot air drying after demolding, glazing, natural hot air drying for molding, and firing for 8 hours at the temperature of more than 1230 ℃ in a kiln for molding. The invention has the advantages that: the manufacturing is convenient, the design is reasonable, the waterproof, insulating and overwater floating micron ceramic sheet can be manufactured, and the waterproof, insulating and overwater floating micron ceramic sheet has the characteristics of high temperature resistance, extreme cold resistance, corrosion resistance, remelting, semi-transparent, radiation protection, wind resistance reduction and the like.
Description
Technical Field
The invention relates to a carbon-ceramic insulating material.
Background
An insulating ceramic, a ceramic having excellent insulating properties and good mechanical properties. Carbon ceramics are ceramic materials composed of carbon and carbides. Carbon ceramics have the dual advantages of carbon and ceramics. The wear resistance, corrosion resistance, oxidation resistance and mechanical property of the material are far superior to those of carbon materials; also has high conductivity, heat resistance and thermal shock resistance. How to provide a carbon-ceramic insulating material becomes a research direction.
Disclosure of Invention
The present invention aims to provide a carbon-ceramic insulating material to solve the problems in the background art.
In order to solve the technical problems, the technical scheme provided by the invention is as follows: a carbon-ceramic insulating material is prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding in a mold, hot air drying after demolding, glazing, natural hot air drying for molding, and firing for 8 hours at the temperature of more than 1230 ℃ in a kiln for molding.
The invention has the advantages that: the manufacturing is convenient, the design is reasonable, the waterproof, insulating and overwater floating micron ceramic sheet can be manufactured, and the waterproof, insulating and overwater floating micron ceramic sheet has the characteristics of high temperature resistance, extreme cold resistance, corrosion resistance, remelting, semi-transparency, radiation protection, wind resistance reduction and the like.
Detailed Description
The invention is illustrated below by means of specific examples, without being restricted thereto.
Example 1
A carbon-ceramic insulating material is prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding by a mold, stripping, quickly drying by hot air, glazing, drying by natural hot air, and firing for 8 hours in a kiln at 1230 ℃.
Example 2
A carbon-ceramic insulating material is prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding by a mold, hot air quick drying after demolding, glazing, natural hot air dry molding, and firing for 8 hours in a kiln at 1240 ℃ for molding.
Example 1
A carbon-ceramic insulating material is prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding by a mold, hot air quick drying after demolding, glazing, natural hot air dry molding, and firing for 8 hours in a kiln at 1250 ℃.
When the invention is implemented, the invention can be used for heat dissipation of a CPU base, electric appliance parts, automobile part materials, graphene battery diaphragms, common battery diaphragms, aviation materials and AI robot power-off safety switches. The shape can be square, round, three-dimensional and plane.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (1)
1. The carbon-ceramic insulating material is characterized by being prepared by the following steps: preparing ceramic slurry, preparing mixed lime feldspar glaze, molding in a mold, hot air drying after demolding, glazing, natural hot air drying for molding, and firing for 8 hours at the temperature of more than 1230 ℃ in a kiln for molding.