CN114025942B - 打印和固化粘结剂试剂 - Google Patents
打印和固化粘结剂试剂 Download PDFInfo
- Publication number
- CN114025942B CN114025942B CN201980097800.0A CN201980097800A CN114025942B CN 114025942 B CN114025942 B CN 114025942B CN 201980097800 A CN201980097800 A CN 201980097800A CN 114025942 B CN114025942 B CN 114025942B
- Authority
- CN
- China
- Prior art keywords
- build
- temperature
- printing
- binder
- chamber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
根据一个示例，提供了一种3D打印构建单元，该3D打印构建单元包括：构建腔室；构建平台；以及加热元件，该加热元件能够控制以将构建腔室的内容物的一部分加热到处于或高于固化温度的温度，同时将构建腔室的上部层维持处于或低于打印温度。
Description
技术领域
本公开涉及三维(3D)打印领域。
背景技术
存在多种类型的三维(3D)打印技术，这些三维打印技术允许基于3D对象模型通过构建材料的选择性固化来生成3D对象。
一种技术在构建腔室中的构建平台上形成粉末状或颗粒状的构建材料的连续层，并且选择性地将能够热固化的粘结剂试剂施加在每层的将形成正在被生成的3D对象的一部分的区域上。能够热固化的粘结剂试剂必须被热固化以形成足够坚固的生坯零件，该生坯零件可以从构建腔室移除、清洁、并且然后在烧结炉中烧结以形成最终的3D对象。
发明内容
本公开的第一方面提出了一种3D打印***，所述3D打印***包括：构建材料分配器；粘结剂试剂分配器；和控制器，所述控制器用于：随着构建平台连续降低，控制构建材料分配器在构建腔室中的构建平台上形成构建材料的连续层；控制粘结剂试剂分配器以基于要生成的3D对象的层的图案来选择性地在每个所形成的层上打印能够热固化的粘结剂试剂的图案；以及控制加热器元件将所述构建腔室的内容物的一部分加热到适于固化所述构建腔室中所存在的任一粘结剂试剂的固化温度，同时将所述构建腔室的上部层维持处于适于在所述上部层上打印粘结剂试剂的较低的打印温度。
本公开的第二方面提出了一种控制3D打印***的方法，所述方法包括：在构建腔室中的构建平台上形成构建材料的连续层；根据从要生成的3D对象得到的数据，在每个所形成的层上选择性地打印能够热固化的粘结剂试剂；加热所述构建腔室的一部分以生成：固化区域，在所述固化区域内，构建材料被加热到处于或高于所述粘结剂试剂的固化温度的温度；以及打印区域，所述打印区域在所述构建腔室的顶部处，在所述打印区域内，构建材料被维持处于或低于打印温度。
本公开的第三方面提出了一种3D打印构建单元，所述3D打印构建单元包括：构建腔室；构建平台；和加热元件，所述加热元件能够控制以将所述构建腔室的内容物的一部分加热到处于或高于固化温度的温度，同时将所述构建腔室的上部层维持处于或低于打印温度。
附图说明
现在将参考附图仅通过非限制性示例的方式来描述示例，在附图中：
图1示出了根据一个示例的3D打印***100的简化图示的截面；
图2是概述根据一个示例的操作3D打印***的示例方法的流程图；
图3示出了根据一个示例的3D打印***100的简化图示的截面；
图4示出了根据一个示例的3D打印***100的简化图示的截面；以及
图5示出了根据一个示例的3D打印***100的简化图示的截面。
具体实施方式
一些基于粉末的3D打印技术使用粘结剂试剂，以通过选择性地将液体粘结剂试剂施加在构建材料(诸如，金属、陶瓷或塑料粉末)的连续形成的层上，并且随后固化该粘结剂试剂，来形成所谓的生坯零件。粘结剂试剂的固化创建了由固化的粘结剂粘结在一起的构建材料颗粒的相对较弱的基质。当以这种方式生成3D对象时，该3D对象通常被称为生坯零件。例如，利用粉末的金属或陶瓷的构建材料生成的生坯零件必须在烧结炉中烧结，以将该生坯零件转变成高致密性的最终对象。
如果使用能够热固化的粘结剂试剂(诸如，基于胶乳的粘结剂试剂)来生成生坯零件，则必须将在其上施加有粘结剂试剂的构建材料加热到合适的温度来固化该粘结剂试剂。例如，如果使用基于胶乳的粘结剂试剂，则可能必须将在其上施加有粘结剂试剂的构建材料加热到高于100摄氏度(例如，高于120摄氏度、或高于150摄氏度)的温度。然而，如果粘结剂固化温度接近或高于粘结剂试剂中的载体流体的沸点，则这使得在施加粘结剂试剂之后不适合热固化每一层。这是因为以高于粘结剂试剂中的载体流体的沸点的温度将粘结剂试剂打印在构建材料的层上会导致：在打印时载体流体的快速蒸发或沸腾，这可以干扰构建材料的经形成的层。例如，这可能导致构建材料到空中，这可能污染打印头和3D打印机的其他零件，并且还可能导致粉末层中的缺陷，并最终导致生坯零件中的缺陷。在一个示例中，水基粘结剂试剂的载体流体的沸点可以是大约100摄氏度。
目前的技术将能够热固化的粘结剂试剂的打印与能够热固化的粘结剂试剂的热固化分离成分离且顺序执行的过程，由此基于3D对象模型将粘结剂试剂选择性地打印在构建材料的连续层中，并且所有的层随后在单个固化过程期间被加热到粘结剂固化温度。
本公开描述了3D打印***的示例，在该3D打印***中，在构建材料的连续形成的层上打印能够热固化的粘结剂试剂的过程和固化该粘结剂试剂的过程可以至少部分并行地执行。此类***可以显著减少生成准备用于烧结的生坯零件所需花费的时间量。
现在参考图1，示出了根据一个示例的3D打印***100的简化图示的截面。打印***100包括构建单元102，该构建单元是打印***100的一体部分。在另一示例中，构建单元102是可移除模块，该可移除模块可以被***到打印***100中的合适接口(未示出)中。
构建单元102包括侧壁104，该侧壁形成构建腔室106，可以由打印***100在该构建腔室中生成3D对象。在一个示例中，构建腔室106具有大致顶部敞开的立方体形状。由可移动构建平台108提供构建单元102的基部，在可移动该构建平台上可以形成构建材料的连续层，并且该构建材料的连续层具有(例如，通过打印)选择性地施加在该连续层上的粘结剂试剂。构建平台108可通过可控制驱动模块(未示出)在大致竖直的轴线或z轴(110)上移动。构建平台108最初可以被定位在构建腔室106的顶部的正下方、在与要在该构建平台上形成的构建材料的第一层的高度相对应的距离处。构建平台108可以连续降低与要形成的构建材料的每个连续层的高度相对应的高度，以允许在该构建平台上形成构建材料的连续层。
合适的构建材料(诸如，粉末金属、塑料或陶瓷构建材料)的层可以通过层形成设备112形成在构建平台108上或形成在先前形成的层上。在一个示例中，层形成设备112是可平移的重涂覆器辊或刮片，然而在其他示例中，层形成设备112可以包括构建材料沉积设备(诸如，料斗、喷洒器等)。粘结剂试剂(诸如，能够热固化的粘结剂试剂)可以通过可控制的试剂沉积设备114(诸如，热或压电打印头)而选择性地施加到构建材料的每个所形成的层。粘结剂试剂可以存储在粘结剂试剂存储容器(未示出)中，该粘结剂试剂存储容器与试剂沉积设备114流体联接。层形成设备112和试剂沉积设备114两者可以沿轴线116在构建平台108上平移。
设置可控制的加热元件118(诸如，电阻加热器)以将热施加到构建腔室118的一部分。如图1中所图示的，加热元件118定位在构建腔室106的顶部下方的预定的距离处。在一个示例中，加热元件118绕着构建腔室106的一部分的***的全部或基本上全部***设置。在一个示例中，加热元件118可以包括多个加热元件，该多个加热元件被布置和能够控制成在一个示例中充当单个加热元件、并且在另一示例中充当多个可独立控制的加热元件。在一个示例中，加热元件118被定位在其处的预定距离可以在构建单元的顶部下方约5cm与20cm之间，然而在其他示例中，该距离可以是更大或更小的距离。在一个示例中，加热元件118可以是热包层，并且该加热元件可以包括在被供电时生成热的一个或多个加热元件、线圈等。在一个示例中，加热元件118具有在约10cm至30cm之间的高度，然而在其他示例中，该加热元件可以具有更高或更低的高度。在一个示例中，加热元件被配置以围绕构建腔室的***的与该加热元件热接触的部分施加基本上均匀量的热。
打印***100的操作通常由控制器120控制，这将在下面更详细地描述。控制器120可以包括处理器，诸如，微处理器、微控制器等。控制器120联接到存储器，在该存储器中存储处理器可执行的打印机控制指令122和处理器可执行的加热器控制指令。
当由控制器120运行打印机控制指令122时，该打印机控制指令使得控制器控制构建平台108的高度，以便控制层形成设备112在构建平台上形成构建材料的层，并且控制试剂沉积设备114以根据从要生成的对象的3D对象模型导出的数据来选择性地将粘结剂试剂施加到构建材料的所形成的层。
当由控制器120运行加热器控制指令124时，该加热器控制指令使得控制器控制加热元件118(如下所述)，以向构建腔室106的一部分施加热来固化在该构建腔室106的一部分中的粘结剂试剂，同时可以形成构建材料的其它层，并且该构建材料的其它层具有在该其它层上打印的粘结剂试剂。以这样的方式，粘结剂试剂的固化可以在构建单元100内执行，与在粘结剂试剂的打印之后作为分离的过程执行固化相比，这可以有助于显著加快生坯零件的生成。
在一个示例中，打印机控制指令122和加热器控制指令124可以并行运行。
现在将参考图2和图3的流程图来描述操作该***100的示例。
在框202处，控制器120运行打印机控制指令122来控制打印***100的元件以在构建平台108上选择性地形成构建材料的层，并且在每个所形成的层上选择性地打印粘结剂试剂304。可以基于从3D对象模型导出的数据，例如基于要生成的3D对象的层，来执行粘结剂试剂304的选择性打印。例如，3D对象模型可以被切片，并且每个切片可以限定接收粘结剂试剂的构建材料的每个层的部分，使得这些部分最终形成要生成的3D对象的实体部分。
在框204处，控制器120运行加热器控制指令124，以控制加热元件118来向构建腔室106的内容物的在由虚线308和310界定的固化区域306中的一部分施加热。构建单元100的设计和加热元件118的位置在构建单元内提供了以下一般条件，如图3所示：
a.固化区域306上方的构建材料的层被维持处于低于第一预定打印温度的温度。在一个示例中，打印温度是低于粘结剂试剂内的载体流体的沸点的温度。这确保了在构建材料的上部层上的良好的打印条件。在一个示例中，打印温度低于粘结剂试剂内的载体流体的沸点约10摄氏度、或约20摄氏度、或约30摄氏度、或40摄氏度。
b.固化区域306内的层被维持处于或高于粘结剂试剂的固化温度的温度。因此，固化区域306中的任何粘结剂试剂将被热固化。在一个示例中，固化温度为约100摄氏度、或约120摄氏度、或约140摄氏度、或约160摄氏度，这取决于所使用的粘结剂试剂的类型。
c.固化区域306下方的层被允许冷却到低于粘结剂试剂的固化温度。
可以选择要被维持处于或低于打印温度的上部层的数量，以便考虑到粘结剂试剂渗透到先前形成的层中。例如，如果粘结剂试剂易于渗透到两个先前形成的层中，那么所有这些层的温度应该被维持低于第一预定温度。然而，由于精确确定和/或控制在固化区域306上方的层的温度方面的困难，在一个示例中，要维持低于打印温度的层的数量可以包括适当数量的缓冲层，例如10个、50个、100个或200个缓冲层。
图3示出了具有清晰界定的上部水平边界和下部水平边界的固化区域306的简化示意图。然而，应当理解的是，在使用中，热将从一个层辐射和/或传导到另一层，从而导致更复杂的热模式。然而，通过将加热元件118定位在构建单元102内的合适位置处，可以至少为该构建单元中的构建材料的层的一部分获得以上提及的温度区域。因此，在使用中，在固化区域306与在构建材料的(多个)上部层下方之间可以存在中间区域(未示出)，在该中间区域内，构建材料的温度可以低于固化温度，但是高于粘结剂试剂的载体流体的沸点。在一个示例中，中间区域可以不直接由加热元件加热，而是可以例如由于来自经加热的构建材料的辐射和/或传导加热而被加热。例如在粘结剂试剂的载体流体的成分蒸发时，中间区域中的粘结剂试剂可以开始干燥而不固化。
例如，当加热元件118施加热时，由于构建材料的上部层的环境辐射冷却，固化区域306上方的构建材料的层可以被维持处于低于打印温度的温度。类似地，由于通过构建单元壁104进行的冷却，因此固化区域306下方的构建材料的层可以被允许冷却到低于粘结剂试剂的固化温度。
随着构建材料的连续层被形成以及随着粘结剂试剂被选择性地打印在每一层上，构建材料的层将移动到固化区域306中，从而导致这些层被加热到高于粘结剂试剂的固化温度的温度，从而导致存在的任何粘结剂试剂被热固化。这些层然后将移出固化区域306，从而导致这些层冷却到低于粘结剂试剂的固化温度的温度。
这些层移动通过固化区域118的速度将取决于在每个层上处理(即，形成和选择性打印粘结剂试剂)所花费的时间。在一个示例中，层处理时间可以在5秒与10秒之间，然而在其他示例中，层处理时间可以更快或更慢。在一个示例中，构建平台可以被控制降低，以允许形成在大约50微米至150微米范围内的构建材料层，然而在其他示例中可以使用其他层厚度。构建材料层在固化区域118中花费的时间可以取决于诸如固化区域306的高度、层处理时间和层厚度等因素。
在一个示例中，为了确保在其上打印粘结剂试剂的所有构建材料的层在构建单元中被热固化，控制器120控制打印机100以使在其上打印粘结剂试剂的所有构建材料的层移动通过固化区域306。例如，控制器120可以控制打印机100，以当不再打印粘结剂试剂时，继续形成构建材料的连续层，直到在其上已经打印有粘结剂试剂的所有层都进入固化区域306中。在一个示例中，控制器120继续形成构建材料的连续层，直到在其上已经打印有粘结剂试剂的所有层都进入固化区域306并且离开该固化区域。以这样的方式，在其上打印有粘结剂试剂的所有层在固化区域306中花费基本上相同的时间长度。
在另外的示例中，控制器120可以控制构建平台将最后打印的层移动到固化区域106中，而不在该最后打印的层上形成构建材料的任何附加层，例如通过控制构建平台108以预定的速度降低。在一个示例中，预定的速度可以是与在形成构建材料层和在该构建材料层上选择性打印粘结剂试剂期间降低构建平台108的速度基本上相同的速度。
在另一示例中，控制器120可以控制构建平台108将在其上打印有粘结剂试剂的最后的层移动到固化区域中，并且可以控制加热元件118以在合适的时间停止施加热，使得在其上打印有粘结剂试剂的所有层被加热持续基本上相同的时间长度。
在一个示例中，当构建平台108被移动接近加热元件118时，控制器120控制加热元件118开始施加热。以这样的方式，在形成和打印第一层的集合期间，可以不使用加热元件。
在另外的示例中，在图4中示出，可以提供辅助加热元件402，该辅助加热元件用于选择性地将热施加到构建单元102中的构建材料的上部层。在这个示例中，一旦所有的粘结剂试剂被打印，控制器120可以控制能量源402将热施加到构建材料的上部层，以便在没有将那些构建材料的层移动到固化区域306中的情况下，将构建材料的多个上部层加热到处于或高于粘结剂试剂的固化温度。在一个示例中，能量源402可以是位于构建腔室106上方的固定能量源。在另一示例中，能量源402可以是可以在构建腔室上进行扫描一次或多次的可平移的能量源。
在又另外的示例中，构建平台108可以设置有或者可以结合加热元件，以在来自控制器120的控制下，将热施加到接近该加热元件的构建材料层。以这样的方式，当已经在构建材料的下部层上形成合适数量的构建材料层时，可以执行对构建材料的下部层的固化。
在再另外的示例中，如图5中所示，构建单元102可以设置有多个水平布置的加热元件118A至118N。控制器120可以根据加热器控制指令124来控制多个加热元件118中的每一个以施加不同量的热，从而在不同的温度下生成多个区域。例如，控制器120可以将第一干燥区域502的温度控制为处于粘结剂试剂中的载体液体的沸点与粘结剂试剂的固化温度之间的干燥温度，并且可以将第二固化区域504的温度控制为处于或高于粘结剂试剂的固化温度。
在另一示例中，加热元件118可以被设置成使得固化区域306延伸到或接近构建单元102的基部。以这样的方式，在固化区上方的构建材料层将被维持处于低于粘结剂试剂的沸点的温度，并且固化区域内的构建材料将被维持高于粘结剂试剂的固化温度。
在另外的示例中，热传感器(未示出)(诸如，热摄像机)可以被用于监控构建材料的上部层的温度。以这样的方式，控制器120可以控制(多个)加热元件118的热输出，以确保构建材料的上部层的温度保持低于粘结剂试剂中的载体流体的沸点。
在又另外的示例中，可以设置真空源来通过构建平台和/或构建腔室中的至少一部分抽吸空气，以帮助移除在打印和固化过程期间形成的水蒸气和/或溶剂。
在一个示例中，粘结剂试剂可以包括用于施加到颗粒构建材料的液体载体或媒介物中的粘结剂。例如，在粘结剂试剂中，粘结剂可以以约1wt％至约50wt％、约2wt％至约30wt％、约5wt％至约25wt％、约10wt％至约20wt％、约7.5wt％至约15wt％、约15wt％至约30wt％、约20wt％至约30wt％、或约2wt％至约12wt％存在于粘结剂试剂中。
在一个示例中，粘结剂可以包括聚合物颗粒，诸如胶乳聚合物颗粒。聚合物颗粒可以具有范围可以从约100nm至约1μm的平均颗粒尺寸。在其它示例中，聚合物颗粒可以具有范围可以从约150nm至约300nm、约200nm至约500nm或约250nm至750nm的平均颗粒尺寸。
在一个示例中，胶乳颗粒可以包括多种共聚单体中的任何一种，并且在一些情况下可以包括共聚型表面活性剂，例如聚氧乙烯化合物、聚氧乙烯烷基苯基硫酸铵、聚氧乙烯烷基醚硫酸酯钠、聚氧乙烯苯乙烯基苯基醚硫酸铵等。共聚单体可以来自单体，诸如苯乙烯、对甲基苯乙烯、a-甲基苯乙烯、甲基丙烯酸、丙烯酸、丙烯酰胺、甲基丙烯酰胺、丙烯酸2-羟丙酯、甲基丙烯酸2-羟乙酯、丙烯酸2-羟丙酯、甲基丙烯酸2-羟丙酯、甲基丙烯酸甲酯、丙烯酸己酯、甲基丙烯酸己酯、丙烯酸丁酯、甲基丙烯酸丁酯、丙烯酸乙酯、甲基丙烯酸乙酯、丙烯酸2-乙基己酯、甲基丙烯酸2-乙基己酯、丙烯酸丙酯、甲基丙烯酸丙酯、丙烯酸十八酯、甲基丙烯酸十八酯、甲基丙烯酸硬脂酯、乙烯基苄基氯、丙烯酸异冰片酯、丙烯酸四氢糠酯、甲基丙烯酸2-苯氧基乙酯、甲基丙烯酸苄酯、丙烯酸苄酯、乙氧基化壬基酚甲基丙烯酸酯、乙氧基化甲基丙烯酸二十二烷基酯、聚丙二醇单丙烯酸酯、甲基丙烯酸异冰片酯、甲基丙烯酸环己酯、丙烯酸环己酯、甲基丙烯酸叔丁酯、甲基丙烯酸正辛酯、甲基丙烯酸月桂酯、甲基丙烯酸十三酯、烷氧化四氢糠基丙烯酸酯、丙烯酸异癸酯、甲基丙烯酸异冰片酯、丙烯酸异冰片酯、马来酸二甲酯、马来酸二辛酯、乙酰乙酰氧乙基甲基丙烯酸酯(acetoacetoxyethylmethacrylate)、双丙酮丙烯酰胺、N-乙烯基咪唑、N-乙烯基咔唑、N-乙烯基己内酰胺、或它们的组合。在一些示例中，乳胶颗粒可以包括丙烯酸乳胶颗粒。在其他示例中，胶乳颗粒可以包括甲基丙烯酸2-苯氧基乙酯、甲基丙烯酸环己酯、丙烯酸环己酯、甲基丙烯酸、它们的组合、它们的衍生物、或它们的混合物。在另一示例中，胶乳颗粒可以包括苯乙烯、甲基丙烯酸甲酯、丙烯酸丁酯、甲基丙烯酸、它们的组合、它们的衍生物、或它们的混合物。
应当理解的是，本文所描述的示例可以以硬件、软件、或硬件和软件的组合的形式来实现。任何这样的软件可以以易失性或非易失性存储装置的形式存储，例如像ROM的存储设备，无论是否可擦除或可重写；或者以存储器的形式存储，例如RAM、存储芯片、设备或集成电路；或者被存储在光学或磁性可读介质上，例如CD、DVD、磁盘或磁带。应当理解的是，存储设备和存储介质是适于存储在被运行时时实施本文中描述的示例的一个或多个程序的机器可读存储的示例。因此，一些示例提供了一种包括用于实施如任何前述权利要求所要求保护的***或方法的代码的程序、和一种存储这种程序的机器可读存储装置。再进一步，本文所描述的一些示例可以经由任何介质(诸如通过有线或无线连接携载的通信信号)以电子方式传送。
本说明书(包括任何所附权利要求、摘要和附图)中公开的所有特征、和/或如此公开的任何方法或过程的所有步骤可以以任何组合(除了这样的特征和/或步骤中的至少一些相互排斥的组合)进行组合。
除非另外明确说明，否则本说明书(包括任何所附权利要求、摘要和附图)中公开的每个特征可以由用于相同、等同或类似目的的替代性特征代替。因此，除非另外明确说明，否则所公开的每个特征仅仅是通用系列的等同或类似特征的一个示例。
Claims (15)
1.一种3D打印***，所述3D打印***包括：
构建材料分配器；
粘结剂试剂分配器；和
控制器，所述控制器用于：
随着构建平台连续降低，控制构建材料分配器在构建腔室中的构建平台上形成构建材料的连续层；
控制粘结剂试剂分配器以基于要生成的3D对象的层的图案来选择性地在每个所形成的层上打印能够热固化的粘结剂试剂的图案；以及
控制加热元件将所述构建腔室的内容物的一部分加热到适于固化所述构建腔室中所存在的任一粘结剂试剂的固化温度，同时将所述构建腔室的上部层维持处于适于在所述上部层上打印粘结剂试剂的较低的打印温度，其中，所述打印温度是低于所述粘结剂试剂内的载体流体的沸点的温度，其中，被加热到所述固化温度的所述构建腔室的所述内容物的所述部分限定所述粘结剂试剂的固化区域，并且所述构建腔室的上部层限定所述粘结剂试剂的打印区域。
2.根据权利要求1所述的3D打印***，其中，所述控制器用于：
控制所述加热元件将所述构建腔室的所述内容物的一部分加热到固化温度或加热到高于固化温度，同时将所述构建腔室的上部层维持处于或低于打印温度，并且允许所述部分下方的构建材料冷却到低于所述固化温度。
3.根据权利要求1所述的3D打印***，其中，所述控制器用于控制所述加热元件以：
控制所述加热元件将所述构建腔室的所述内容物的一部分加热到固化温度或加热到高于固化温度，将所述构建腔室的上部层维持处于或低于打印温度，并且使得在所述上部层下方的构建材料处于所述固化温度与所述打印温度之间的干燥温度。
4.根据权利要求1所述的3D打印***，其中，固化温度处于或高于120摄氏度，并且其中所述打印温度处于或低于80摄氏度。
5.根据权利要求1所述的3D打印***，其中，所述控制器用于移动打印有粘结剂试剂的构建材料的所有层通过所述固化区域。
6.根据权利要求1所述的3D打印***，还包括能量源，所述能量源用于将热施加到所述构建腔室中的构建材料的顶部层，并且其中所述控制器用于控制所述能量源以将能量施加到打印有粘结剂试剂的构建材料的最后的层。
7.根据权利要求1所述的3D打印***，还包括热传感器，所述热传感器用于测量所述构建腔室中的构建材料的顶部层的温度，所述控制器用于控制所述加热元件的加热，以将所述顶部层的温度维持处于或低于所述打印温度。
8.根据权利要求1所述的3D打印***，还包括构建单元，所述构建单元包括构建腔室、构建平台和用于向构建腔室施加热的加热元件。
9.根据权利要求1所述的3D打印***，还包括接口，所述接口用于接收构建单元，所述构建单元具有构件腔室、构建平台和用于向所述构建腔室施加热的加热元件。
10.一种控制3D打印***的方法，所述方法包括：
在构建腔室中的构建平台上形成构建材料的连续层；
根据从要生成的3D对象得到的数据，在每个所形成的层上选择性地打印能够热固化的粘结剂试剂；
加热所述构建腔室的一部分以生成：
所述粘结剂试剂的固化区域，在所述固化区域内，构建材料被加热到处于或高于所述粘结剂试剂的固化温度的温度；以及
所述粘结剂试剂的打印区域，所述打印区域在所述构建腔室的顶部处，在所述打印区域内，构建材料被维持处于或低于打印温度，其中，所述打印温度是低于所述粘结剂试剂内的载体流体的沸点的温度。
11.根据权利要求10所述的方法，还包括将所述固化区域加热到处于或高于120摄氏度的温度，并且将所述打印区域维持处于或低于80摄氏度的温度。
12.根据权利要求10所述的方法，还包括移动打印有粘结剂试剂的构建材料的所有层通过所述固化区域。
13.根据权利要求12所述的方法，其中，移动打印有试剂的构建材料的所有层通过所述固化区域还包括：控制所述3D打印机以继续在所述构建平台上形成构建材料的连续层。
14.根据权利要求10所述的方法，还包括：一旦所有粘结剂试剂已经被打印，将能量施加到构建材料的顶部层，以将所述顶部层加热到所述固化温度或加热到高于所述固化温度。
15.一种3D打印构建单元，所述3D打印构建单元包括：
构建腔室；
构建平台；和
加热元件，所述加热元件能够控制以将所述构建腔室的内容物的一部分加热到处于或高于固化温度的温度，同时将所述构建腔室的上部层维持处于或低于打印温度，其中，
所述打印温度是低于粘结剂试剂内的载体流体的沸点的温度，其中，被加热到所述固化温度的所述构建腔室的所述内容物的所述部分限定所述粘结剂试剂的固化区域，并且所述构建腔室的上部层限定所述粘结剂试剂的打印区域。