CN114018913A - 一种快速气体检测管载体前处理方法 - Google Patents
一种快速气体检测管载体前处理方法 Download PDFInfo
- Publication number
- CN114018913A CN114018913A CN202111319940.3A CN202111319940A CN114018913A CN 114018913 A CN114018913 A CN 114018913A CN 202111319940 A CN202111319940 A CN 202111319940A CN 114018913 A CN114018913 A CN 114018913A
- Authority
- CN
- China
- Prior art keywords
- carrier
- gas detection
- rapid gas
- detection tube
- washing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于环保检测领域，具体涉及一种快速气体检测管载体前处理方法。包括快速气体检测管的载体的选取及前处理工艺，具体包括筛分、水洗、酸洗、二次水洗、醇洗、抽滤、烘干等过程。本发明通过对快速气体检测管载体进行前处理，筛分后地颗粒均匀，无粉末状颗粒，气体通过均匀，变色界面一致。采用混酸进行酸洗后的载体比表面积会增大，变色更加明显。醇洗后地载体，灵敏度增加，可进一步降低检出限。
Description
技术领域
本发明属于环保检测领域，具体涉及一种快速气体检测管载体前处理方法。
背景技术
气体检测管是一种填充显色指示粉的细玻璃管，是一种用于测定气体浓度的简便装置。当被测物质通过检测管时，被测物质与指示剂迅速反生化学反应生成有色物质，根据变色长度直接读出气体浓度。检测管法测定有害气体的浓度具有测定迅速、操作简便、采气量小等优点，同时又能保证一定的谁确度和精密度，现已广泛用于以下方面：
1、劳动安全卫生检测
气体检测管可测定工矿企业作业环境中的有毒有害气体。特别是在进行日常安全检测时，由于被测气体成分及气体浓度范围相对固定，便于使用气体检测管进行测定。同时，由于日常监测采样点较多，又多处在工人呼吸带附近，如采用化学分析方法进行测定，既增大检测人员的工作量，又因长时间采样影响正常操作。而采用检测管法测定，一个采样点只需几分钟即可完成测定。
2、突发性事故检测
在突发性事故中，对有毒有害、易燃易爆气体的监测及控制是减少事故损失及进行事故救援工作的重要依据。突发性事故中，气体种类复杂，气体浓度较高且变化很快，因此只有快速测定污染气体浓度，使指挥部门及时了解掌握现场情况，才能有效地实施救援工作，以达到控制事故，减少损失的目的。由于气体检测管具有测量快速、简便、直读等特点，因而在突发性事故检测中能为指挥决策部门及时提供第一手的监测数据。
3、生产过程及工艺过程的气体质量检测
气体检测管可用于生产过程及工艺过程的气体质量检测工作
4、环境污染监测
气体检测管可测量空气中的二氧化硫、一氧化碳、甲醛、氮氧化物、二氧化碳、氨气等气体
检测管载体是指检测管内用以吸附指示剂的固体物质。作为检测管载体必须满足下面要求：载体本身必须为具有一定机械强度、颜色较浅 (以白色为宜)的隋性物质，与试剂及被测物质均不发生化学反应；载体还必须具有多孔或粗糙的表面，有一定的吸附能力。 能够用作检测管的材料有许多种类，如粗孔硅胶、素陶瓷、活性氧化铝、树脂、石英砂、沸石、硅藻土、酸性白土、玻璃粉等。
现有技术中，对于气体快速检测管载体的前处理工艺描述较少，未经处理或简单处理的载体制作检测管存在以下不足：
1、检测管变色不明显；
2、检测管变色界面长度不一，造成无法准确读数、误差较大；
3、检测管灵敏度不够，检出限高，无法准确检测低浓度污染物。
发明内容
为解决现有技术的问题，本发明提供一种快速气体检测管载体前处理方法，可有效解决检测管变色不明显及变色界面不一等问题。
为了达到上述目的，本发明采用以下技术方案：一种快速气体检测管载体前处理方法，包括快速气体检测管的载体的选取及前处理工艺，具体包括筛分、水洗、酸洗、二次水洗、醇洗、抽滤、烘干等过程。
包括依次筛分、水系、酸洗、二次水洗、醇洗、烘干处理过程。
进一步地，快速气体检测管载体为粗孔硅胶、陶瓷粉、活性氧化铝、石英砂、沸石粉、硅藻土、酸性白土、玻璃粉中的一种或几种的混合物。
进一步地，快速气体检测管载体的粒径为60~120目。
进一步地，快速气体检测管酸洗采用的为盐酸、硫酸、硝酸中的一种或几种的混合液。
进一步地，快速气体检测管酸洗采用的为酸浓度为5%~20%。
进一步地，快速气体检测管酸洗采用回流冷凝装置，回流时间在0.5~3H。
进一步地，二次水洗采用去离子水，洗涤至PH为7。
进一步地，快速气体检测管醇洗采用50%~95%的乙醇溶液。
进一步地，快速气体检测管载体干燥温度为100~180摄氏度。
进一步地，快速气体检测管载体干燥时间为2~5h。
快速气体检测管载体前处理，包括以下步骤：
（1）把载体根据不同气体检测管地需要，采用不锈钢分样筛进行筛分，去除粉末状载体，筛分后地载体，粒径均匀，透气性好。
（2）筛分后地载体加入去离子水进行清洗，去除载体中地杂质。
（3）载体进一步加入稀酸，连接冷凝回流装置，加热，回流1h进行酸洗。
（4）酸洗后的载体加入去离子水，洗去残留的酸，边洗边用PH试纸进行检测，直至水溶溶呈中性。
（5）在上述载体中加入50%~95%的乙醇溶液中，利用乙醇地挥发性，带走大部分水分。
（6）放入到鼓风干燥箱中，干燥2~5h至无水分。
与现有技术相比，发明的有益效果是：本发明通过对快速气体检测管载体进行前处理，筛分后地颗粒均匀，无粉末状颗粒，气体通过均匀，变色界面一致。采用混酸进行酸洗后的载体比表面积会增大，变色更加明显。醇洗后地载体，灵敏度增加，可进一步降低检出限。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显。
图1是本发明工艺流程示意图。
具体实施方式
下面通过实施例对本发明做进一步详细说明,实施例仅用来说明本发明，并不限制本发明的范围。
所示实施例1
请参阅图1所示，快速气体检测管载体的前处理方法，包括以下步骤：
（1）将外购的60~100目的硅胶加入到不锈钢分样筛中，分样筛的目数为60~80目，筛除掉不符合粒径要求的硅胶，其余硅胶进行下一步处理；
（2）筛分后地硅胶加入去离子水进行反复多次清洗，去除载体中地杂质。
（3）在水洗后的硅胶中加入稀硫酸与稀盐酸的混合溶液，其中硫酸的浓度为10%，盐酸的浓度为5%，连接回流冷凝装置，加热，回流1H，酸洗后的硅胶冷却后进行下一步处理。
（4）酸洗后地硅胶加入去离子水，洗去残留的酸，边洗边用PH试纸进行检测，直至水溶溶PH为7。
（5）水洗至中性的硅胶加入浓度为50%的乙醇溶液，充分搅拌后进行抽滤。
（6）抽滤后的硅胶放入鼓风干燥箱中，温度105摄氏度，干燥2h。
实施例2
请参阅图1所示，快速气体检测管载体的前处理方法，包括以下步骤：
（1）将外购的80~120目的陶瓷粉加入到不锈钢分样筛中，分样筛的目数为80~100目，筛除掉不符合粒径要求的陶瓷粉，其余陶瓷粉进行下一步处理；
（2）筛分后地陶瓷粉加入去离子水进行反复多次清洗，去除载体中地杂质。
（3）在水洗后的陶瓷粉中加入15%的稀硫酸溶液，连接回流冷凝装置，加热，回流2H，酸洗后的陶瓷粉冷却后进行下一步处理。
（4）酸洗后地陶瓷粉加入去离子水，洗去残留的酸，边洗边用PH试纸进行检测，直至水溶溶PH为7。
（5）水洗至中性的陶瓷粉加入浓度为75%的乙醇溶液，充分搅拌后进行抽滤。
（6）抽滤后的硅胶放入鼓风干燥箱中，温度120摄氏度，干燥1.5h。
实施例3
请参阅图1所示，快速气体检测管载体的前处理方法，包括以下步骤：
（1）将外购的80~120目的石英粉与陶瓷粉按照1：1的比例混合，加入到不锈钢分样筛中，分样筛的目数为80~100目，筛除掉不符合粒径要求的粉末，其余混合载体进行下一步处理；
（2）筛分后地混合载体加入去离子水进行反复多次清洗，去除载体中地杂质。
（3）在水洗后的混合载体中加入10%的稀硝酸溶液，连接回流冷凝装置，加热，回流1.5H，酸洗后的混合载体冷却后进行下一步处理。
（4）酸洗后地混合载体加入去离子水，洗去残留的酸，边洗边用PH试纸进行检测，直至水溶溶PH为7。
（5）水洗至中性的混合载体加入浓度为95%的乙醇溶液，充分搅拌后进行抽滤。
（6）抽滤后的硅胶放入鼓风干燥箱中，温度180摄氏度，干燥2h。
本发明具有以下创新点：
1、增加了快速气体检测管载体的筛分过程，处理后的载体的颗粒更加均匀，气体通过性更好，变色稳定，重复性好。
2、采用硫酸、盐酸、硝酸的混酸对载体进行酸洗，酸洗后的载体变色更灵敏。
3、采用回流冷凝方式处理载体，酸洗更彻底。
4、前处理方式中采用乙醇溶液进行洗涤，醇洗后的载体变色界面明显且长度一致。
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但是凡是未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。
Claims (10)
1.一种快速气体检测管载体前处理方法，包括依次筛分、水系、酸洗、二次水洗、醇洗、烘干处理过程。
2.根据权利要求1所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管载体为粗孔硅胶、陶瓷粉、活性氧化铝、石英砂、沸石粉、硅藻土、酸性白土、玻璃粉中的一种或几种的混合物。
3.根据权利要求2所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管载体的粒径为60~120目。
4.根据权利要求3所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管酸洗采用的为盐酸、硫酸、硝酸中的一种或几种的混合液。
5.根据权利要求4所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管酸洗采用的为酸浓度为5%~20%。
6.根据权利要求4所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管酸洗采用回流冷凝装置，回流时间在0.5~3H。
7.根据权利要求6所述的快速气体检测管载体前处理方法，其特征在于，二次水洗采用去离子水，洗涤至PH为7。
8.根据权利要求7所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管醇洗采用50%~95%的乙醇溶液。
9.根据权利要求9所述的快速气体检测管载体前处理方法，其特征在于，快速气体检测管载体干燥温度为100~180摄氏度；快速气体检测管载体干燥时间为2~5h。
10.根据权利要求9所述的快速气体检测管载体前处理方法，其特征在于，还包括以下步骤：
把载体根据不同气体检测管地需要，采用不锈钢分样筛进行筛分，去除粉末状载体，筛分后地载体，粒径均匀，透气性好；
筛分后地载体加入去离子水进行清洗，去除载体中地杂质；
载体进一步加入稀酸，连接冷凝回流装置，加热，回流1h进行酸洗；
酸洗后的载体加入去离子水，洗去残留的酸，边洗边用PH试纸进行检测，直至水溶溶呈中性；
在上述载体中加入50%~95%的乙醇溶液中，利用乙醇地挥发性，带走大部分水分；放入到鼓风干燥箱中，干燥2~5h至无水分。