CN113941617A - 一种用于纺织的银铜合金长丝的生产工艺 - Google Patents
一种用于纺织的银铜合金长丝的生产工艺 Download PDFInfo
- Publication number
- CN113941617A CN113941617A CN202111239910.1A CN202111239910A CN113941617A CN 113941617 A CN113941617 A CN 113941617A CN 202111239910 A CN202111239910 A CN 202111239910A CN 113941617 A CN113941617 A CN 113941617A
- Authority
- CN
- China
- Prior art keywords
- silver
- copper alloy
- softening
- alloy wire
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及纺织技术领域，且公开了一种用于纺织的银铜合金长丝的生产工艺，包括以下步骤：一、前序准备：选择金属纺丝设备、原材料、纺丝模具、润滑剂和收线轴，所述原材料为银铜合金盘条；二、将所述银铜合金盘条加工成银铜合金线材；三、通过金属纺丝设备对银铜合金线材进行粗纺、细纺，直至纺到所需精度的银铜合金丝为止。本方案的生产工艺能使银铜合金长丝具有纺织用品的可纺性，从而填补了国内外现有纺织领域的空白，其织物可广泛应用于大众生活的穿戴，弥补了化学制剂应用范围的短板和现有金属纳米涂层应用于纺织所带来的缺陷。
Description
技术领域
本发明涉及纺织技术领域，具体为一种用于纺织的银铜合金长丝的生产工艺。
背景技术
目前国内外尚无用合金长丝混纺织物灭活各种病毒的实例，现有灭活病毒的材料都为化学液体药物制剂，这些化学制剂都只能在特定环境下使用，不能在人们日常生活中广泛应用。
且目前国内没有用于纺织的银铜合金长丝，国内外现有的相关技术，有银铜金属纳米涂层技术，但银铜等金属纳米涂层存在许多缺点，其缺陷包括不能洗涤、不能染色、不抗氧化，且纳米材料容易脱落，接触人体皮肤后容易被人体吸收，对人体健康造成危害。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种用于纺织的银铜合金长丝的生产工艺，使银铜合金长丝具有可纺性，以补了国内外现有纺织领域的空白，其织物可广泛应用于大众生活的穿戴，弥补化学制剂应用范围的短板和现有金属纳米涂层应用于纺织所带来的缺陷。
为实现上述目的，本发明提供如下技术方案：
一种用于纺织的银铜合金长丝的生产工艺，包括以下步骤：
一、前序准备：选择金属纺丝设备、原材料、纺丝模具、润滑剂和收线轴，所述原材料为银铜合金盘条；
二、将所述银铜合金盘条加工成银铜合金线材；
三、通过金属纺丝设备对银铜合金线材进行粗纺、细纺，直至纺到所需精度的银铜合金丝为止，所述银铜合金丝精度范围为直径0.02-0.07mm；
四、然后再把纺好的银铜合金丝放到高温退火软化炉中进行退火软化，软化温度为800-1060℃，软化速度为110-180m/s，在升温过程中向高温退火软化炉的炉管中输送纯化合格的氢气，以确银铜合金丝在高温炉中不被熔化；
五、收线。
优选的，步骤四所述退火软化具体步骤如下：
①先把制氢炉升温至850℃进行氨分解；
②再把纯化炉升温至350℃，把分解炉分解出的氢气进行纯化；
③同时把高温退火软化炉升温至800-1060℃，在升温过程中把步骤②纯化合格的氢气均匀送入到高温退火软化炉中，通过高温退火软化炉的炉管对直径0.02-0.07mm银铜合金丝进行高温纯氢真空中软化，软化速度为110-180m/s。
优选的，所述直径为0.02mm银铜合金丝、软化温度为900℃、软化速度为110m/s；
所述直径为0.025mm银铜合金丝、软化温度为950℃、软化速度为120m/s；
所述直径为0.03mm银铜合金丝、软化温度为1000℃、软化速度为130m/s；
所述直径为0.0035mm银铜合金丝、软化温度为1060℃、软化速度为180m/s；
所述直径为0.04mm银铜合金丝、软化温度为1060℃、软化速度为160m/s；
所述直径为0.05mm银铜合金丝、软化温度为1060℃、软化速度为140m/s；
所述直径为0.07mm银铜合金丝、软化温度为1060℃、软化速度为130m/s。
优选的，所述润滑剂为润滑油或润滑液
与现有技术相比，本发明提供了一种用于纺织的银铜合金长丝的生产工艺，具备以下有益效果：
（1）本发明通过将银铜合金盘条加工成线材，再经过金属纺丝机进行粗纺、细纺，直至纺到所需的精度为止，再把纺好的合金丝放到软化炉中用一定的温度和软化速度进行晶体还原软化，使银铜合金长丝具有纺织用品的可纺性，从而填补了国内外现有纺织领域的空白，其织物可广泛应用于大众生活的穿戴，弥补了化学制剂应用范围的短板和现有金属纳米涂层应用于纺织所带来的缺陷。
（2）本方案生产的银铜合金长丝的织物可以洗涤，可以染色，具有永久抗氧化功能，具有消臭性能，没有重金属脱落，不会被人体吸收，且具有抑菌功能，可以起到有效灭活新冠病毒、H3N2病毒、脊髓灰质炎病毒、H1N1病毒、肠道病毒71型、大肠杆菌、金黄色葡萄球菌、肺炎克雷伯氏菌、白色念珠菌等作用。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
一种用于纺织的银铜合金长丝的生产工艺，包括以下步骤：
一、前序准备：选择金属纺丝设备、原材料、纺丝模具、润滑剂和收线轴，原材料为银铜合金盘条，收线轴采用螺旋反锁扣方式使收线轴不易脱落、纺丝模具选择天然金刚钻石模具；
二、将银铜合金盘条加工成银铜合金线材；
三、通过金属纺丝设备对银铜合金线材进行粗纺、细纺，直至纺到所需精度的银铜合金丝为止，银铜合金丝精度范围为直径0.02-0.07mm；
四、然后再把纺好的银铜合金丝放到高温退火软化炉中进行退火软化，软化温度为800-1060℃，软化速度为110-180m/s，在升温过程中向高温退火软化炉的炉管中输送纯化合格的氢气，以确银铜合金丝在高温炉中不被熔化；
五、收线。
其中，在软化温度为800℃时，收线速度为6m/s；在软化过程中，可依据测试结果随时调整炉温和收线速度，以达到最佳的软化效果，并达到其进入纺织领域与各种纤维融合的可纺性。
六、银铜纤维长丝产成品的技术标准：
1.表面光滑洁净，没有纵向拉痕和毛刺，裂纹、节疤、折叠，锈蚀及其他明显疵点；
2.不得有影响拉伸强度的节头、凹陷；
3.表面呈金属光泽，颜色均匀一致；
4.轴丝排布均匀，平整扎实紧密；
5.纤维丝自由悬垂时不允许产生S型卷曲和影响编织的捻劲；
6.每轴只能有一根丝，单轴的重量应符合下表的规定；
7.直径允许偏差应符合下表的规定；
8.不圆度公差不得大于直径偏差的一半，偏差、单轴的重量范围表如下：
进一步的，步骤四退火软化具体步骤如下：
①先把制氢炉升温至850℃进行氨分解；
②再把纯化炉升温至350℃，把分解炉分解出的氢气进行纯化；
③同时把高温退火软化炉升温至800-1060℃，在升温过程中把步骤②纯化合格的氢气均匀送入到高温退火软化炉中，通过高温退火软化炉的炉管对直径0.02-0.07mm银铜合金丝进行高温纯氢真空中软化，软化速度为110-180m/s。
其中，不同直径的银铜合金长丝强力、强度的大小与银铜合金长丝在软化炉中的温度、速度有决定性关系，如以下成品测试表数据所示：
直径与软化温度、软化速度表：
直径与抗拉强度、延伸率表：
而在软化过程中，根据成品测试结果，随时调整速度和温度比，以达到最佳的软化效果，确保银铜合金长丝的柔软可纺性。
另外，润滑剂为润滑油或润滑液，冬季这两种润滑剂都需要加温到30℃使用，方能达到较好的润滑效果，润滑采用喷淋式，润滑油选用长城润滑油；润滑液选用乳化剂，它由矿物油等油份与表面活性剂配制而成，其主要成分有；油性添加剂如动植物油，脂肪酸及其皂、脂肪醇等；调制方法为1比25倍的温水搅匀。在使用过程中要常用手感测试，以保证其润滑度，随着生产的进度润滑液的润滑程度逐渐下降，则要及时添加和补充，若润滑液发黑磨损物增多，要及时更换。
需要说明的是，使银铜合金长丝的细度、克重、长度与棉线、桑蚕丝、化纤的细度、克重、长度相匹配具有可纺性，反复测算验证得知银铜合金长丝和棉线、桑蚕丝、化纤细度、克重、长度相匹配的数据参数，从而使其具有完全的可纺性。
经查询得知，化纤长丝习惯用定长制，即丝长9000米，重1克，为1个旦尼尔（D）；
化纤、棉短纤维习惯用定重制，有公制和英制两种，公制是丝线重1000克，长1000米，为1支（N），英制是丝线重1磅，长840码为1支（S），它们之间的换算公式为：
D=9000/N=5315/S N=1.693S S=0.591N S=5315/D D=5315/s。纺织常用计算公式分为定长制计算公式和定重制计算公式两种。定长制计算公式：
其中g为丝线的重量（克），L为丝线的长度（米）；圆钢线的表示法：Φxm ；圆钢重量计算公式：重量g=直径mm*直径mm*0.00617*长度L。 =g/L*9000， 旦尼尔（D）
由此可推出：长度L=重量g/（直径mm*直径mm*0.00617）
经反复验算：把圆钢线的计算公式代入化纤长丝用定长制计算公式D=g/L*9000测得银铜合金长丝的旦尼尔（D）数。
把银铜合金长丝的D数代入S=5315/D测得银铜合金长丝的英制S支数。
把银铜合金长丝的英制S支数代入N=1.693S 测得银铜合金长丝的公制N支数。
按照上述的计算方法，计算出银铜合金长丝的旦尼尔（D）数、英制S支数、公制N支数，即可纺出与棉线、桑蚕丝、化纤相匹配的细度、克重、长度的银铜合金长丝，使其具有完全的可纺。
与现有技术相比：由于银铜合金长丝的柔软性好，导电性强，因此，银铜合金长丝具有以下特性：①具有永久性防电磁波辐射功能；②具有永久性清除人体静电功能；③具有永久性抗氧化功能；④具有抑菌、除臭、除异味功能；⑤具有透气性好，恒干爽、恒体温、性功能；⑥可屏蔽X射线、Y射线等电离辐射；⑦具有阻燃耐高温功能；⑧能够屏蔽所有的手机辐射，而不屏蔽手机信号；⑨具有抗红外线探测功能；⑩具有屏蔽雷达波功能。以上功能是棉线、蚕丝、化纤所不具备的，因此它的用途也极为广泛，和凯夫拉纤维混纺的织物，具有极强的吸波吸光性能，广泛应用于航天航空，航海等国防军事领域的隐性工程。
银铜合金长丝与普通纱线混纺织成织物：
一、银铜纤维丝与莫代尔混纺织成的针织内衣、裤头、袜子经德国海恩斯坦研究院检测、认证；
二、银铜合金长丝与tc65/35混纺、织成的迷彩梭织布，与阻燃涤纶混纺织成的篷布，经北京航天二院203所、中国计量科学研究院、中国人民解放军国防工程电磁脉冲防护研究测试中心测试，具有屏蔽雷达波微米波段、红外波段、激光波段的探测功能。
三、银铜合金长丝和竹炭纤维复合的纱线，织造的梭织布做成的口罩有较强的抗病毒功能，经武汉产品质量监督检验所和国家红外及工业电热产品质量监督检查中心检测有释放远红外功能。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (4)
1.一种用于纺织的银铜合金长丝的生产工艺，其特征在于，包括以下步骤：
一、前序准备：选择金属纺丝设备、原材料、纺丝模具、润滑剂和收线轴，所述原材料为银铜合金盘条；
二、将所述银铜合金盘条加工成银铜合金线材；
三、通过金属纺丝设备对银铜合金线材进行粗纺、细纺，直至纺到所需精度的银铜合金丝为止，所述银铜合金丝精度范围为直径0.02-0.07mm；
四、然后再把纺好的银铜合金丝放到高温退火软化炉中进行退火软化，软化温度为800-1060℃，软化速度为110-180m/s，在升温过程中向高温退火软化炉的炉管中输送纯化合格的氢气，以确银铜合金丝在高温炉中不被熔化；
五、收线。
2.根据权利要求1所述的一种用于纺织的银铜合金长丝的生产工艺，其特征在于，步骤四所述退火软化具体步骤如下：
①先把制氢炉升温至850℃进行氨分解；
②再把纯化炉升温至350℃，把分解炉分解出的氢气进行纯化；
③同时把高温退火软化炉升温至800-1060℃，在升温过程中把步骤②纯化合格的氢气均匀送入到高温退火软化炉中，通过高温退火软化炉的炉管对直径0.02-0.07mm银铜合金丝进行高温纯氢真空中软化，软化速度为110-180m/s。
3.根据权利要求2所述的一种用于纺织的银铜合金长丝的生产工艺，其特征在于，所述直径为0.02mm银铜合金丝、软化温度为900℃、软化速度为110m/s；
所述直径为0.025mm银铜合金丝、软化温度为950℃、软化速度为120m/s；
所述直径为0.03mm银铜合金丝、软化温度为1000℃、软化速度为130m/s；
所述直径为0.0035mm银铜合金丝、软化温度为1060℃、软化速度为180m/s；
所述直径为0.04mm银铜合金丝、软化温度为1060℃、软化速度为160m/s；
所述直径为0.05mm银铜合金丝、软化温度为1060℃、软化速度为140m/s；
所述直径为0.07mm银铜合金丝、软化温度为1060℃、软化速度为130m/s。
4.根据权利要求1所述的一种用于纺织的银铜合金长丝的生产工艺，其特征在于，所述润滑剂为润滑油或润滑液。