CN113818233A - Noctilucent fabric and preparation method thereof - Google Patents

Noctilucent fabric and preparation method thereof Download PDF

Info

Publication number
CN113818233A
CN113818233A CN202111034736.7A CN202111034736A CN113818233A CN 113818233 A CN113818233 A CN 113818233A CN 202111034736 A CN202111034736 A CN 202111034736A CN 113818233 A CN113818233 A CN 113818233A
Authority
CN
China
Prior art keywords
parts
component
fabric
noctilucent
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202111034736.7A
Other languages
Chinese (zh)
Inventor
徐海峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Huiying Textile Technology Co ltd
Original Assignee
Suzhou Huiying Textile Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Huiying Textile Technology Co ltd filed Critical Suzhou Huiying Textile Technology Co ltd
Priority to CN202111034736.7A priority Critical patent/CN113818233A/en
Publication of CN113818233A publication Critical patent/CN113818233A/en
Pending legal-status Critical Current

Abstract

The invention relates to the technical field of noctilucent fabrics, in particular to a noctilucent fabric and a preparation method thereof. The paint comprises a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent. The component A comprises warp basic fibers and weft basic fibers; the component B is luminous liquid; and the component C is protective spraying liquid. The invention adopts a dipping mode to attach the luminous liquid on the base fabric, and the luminous liquid is matched with the protective spraying liquid to form the waterproof film layer. The preparation process is simple, the noctilucent effect and the comfort of the fabric are guaranteed, the water resistance is good, and the functionality, the wear resistance and the practicability of the fabric are enhanced.

Description

Noctilucent fabric and preparation method thereof
Technical Field
The invention relates to the technical field of noctilucent fabrics, in particular to a noctilucent fabric and a preparation method thereof.
Background
With the rise of street culture in recent years, some fabric and clothes breaking the traditional fashion trend are leaped into eyes of more consumers, namely one of the noctilucent fabric, the noctilucent fabric is the fabric which has the appearance the same as that of common fabric, can continuously emit light within a certain time under the condition of weak light or no light after being irradiated by strong light, and is particularly hot-melt by some young people who are young and unbounded. The existing noctilucent fabric is not lasting in noctilucent effect, and is not enough in functionality and comfort, so that the use feeling of people is affected.
Disclosure of Invention
Aiming at the problems in the background technology, a noctilucent fabric and a preparation method thereof are provided. According to the invention, a soaking mode is adopted, the noctilucent liquid is attached to the base fabric, and the protective spraying liquid is matched to form the waterproof film layer. The preparation process is simple, the noctilucent effect and the comfort of the fabric are guaranteed, the water resistance is good, and the functionality, the wear resistance and the practicability of the fabric are enhanced.
The invention provides a noctilucent fabric which comprises a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent. The component A comprises warp basic fibers and weft basic fibers; the warp basic fiber and the weft basic fiber both comprise any one or a mixture of a plurality of fibers of cotton, wool, spun silk, hemp, conventional viscose, lyocell, modal, bamboo fiber, nylon, terylene, acrylic fiber, polypropylene fiber and vinylon. The component B is luminous liquid which comprises 10-16 parts of luminous powder, 60-70 parts of deionized water, 3-5 parts of film forming auxiliary agent, 20-25 parts of water-based rosin resin emulsion, 10-15 parts of dispersing agent and 10-15 parts of adhesive. And the component C is a protective spraying liquid and comprises 5-8 parts of epoxy chloropropane, 4-7 parts of potassium hydroxide, 5-8 parts of methacrylic acid, 10-20 parts of higher fatty acid sodium, 8-16 parts of polyvinyl ether, 4-8 parts of methyl cellulose, 6-10 parts of wool grease, 4-8 parts of turpentine, 30-40 parts of deionized water, 5-7 parts of copper sulfate, 1-3 parts of nonylphenol polyoxyethylene ether and 10-15 parts of a nano waterproof agent.
Preferably, the component B is luminous liquid and comprises 10 parts of luminous powder, 60 parts of deionized water, 3 parts of film-forming aid, 20 parts of water-based rosin resin emulsion, 10 parts of dispersing agent and 10 parts of adhesive.
Preferably, the component B is luminous liquid and comprises 16 parts of luminous powder, 70 parts of deionized water, 5 parts of film-forming aid, 25 parts of water-based rosin resin emulsion, 15 parts of dispersing agent and 15 parts of adhesive.
Preferably, the component B is luminous liquid and comprises 13 parts of luminous powder, 65 parts of deionized water, 4 parts of film-forming aid, 23 parts of water-based rosin resin emulsion, 12 parts of dispersing agent and 12 parts of adhesive.
Preferably, the component C is a protective spraying liquid and comprises 5 parts of epoxy chloropropane, 4 parts of potassium hydroxide, 5 parts of methacrylic acid, 10 parts of sodium higher fatty acid, 8 parts of polyvinyl ether, 4 parts of methyl cellulose, 6 parts of lanolin, 4 parts of turpentine, 30 parts of deionized water, 5 parts of copper sulfate, 1 part of nonylphenol polyoxyethylene ether and 10 parts of a nano waterproof agent.
Preferably, the component C is a protective spraying liquid and comprises 8 parts of epoxy chloropropane, 7 parts of potassium hydroxide, 8 parts of methacrylic acid, 20 parts of sodium higher fatty acid, 16 parts of polyvinyl ether, 8 parts of methyl cellulose, 10 parts of lanolin, 8 parts of turpentine, 40 parts of deionized water, 7 parts of copper sulfate, 3 parts of nonylphenol polyoxyethylene ether and 15 parts of a nano waterproof agent.
Preferably, the component C is a protective spraying liquid and comprises 6 parts of epoxy chloropropane, 5 parts of potassium hydroxide, 6 parts of methacrylic acid, 15 parts of sodium higher fatty acid, 12 parts of polyvinyl ether, 5 parts of methyl cellulose, 8 parts of lanolin, 5 parts of turpentine, 35 parts of deionized water, 6 parts of copper sulfate, 2 parts of nonylphenol polyoxyethylene ether and 12 parts of a nano waterproof agent.
The invention also provides a preparation method of the noctilucent fabric, which is characterized by comprising the following steps:
s1, preparing luminous liquid and protective spraying liquid;
s2, weaving the warp basic fibers and the weft basic fibers into a basic fabric;
s3, soaking the base fabric in a padding machine groove filled with luminous liquid, and squeezing and rolling the base fabric through two rollers, wherein the rolling residual is 70%;
s4, carrying out steam drying, water washing, re-drying and tentering setting;
s5, spraying protective spraying liquid on the surface of the fabric;
and S6, drying again to obtain the finished fabric.
Compared with the prior art, the invention has the following beneficial technical effects:
according to the invention, a soaking mode is adopted, the noctilucent liquid is attached to the base fabric, and the protective spraying liquid is matched to form the waterproof film layer. The preparation process is simple, the noctilucent effect and the comfort of the fabric are guaranteed, the water resistance is good, and the functionality, the wear resistance and the practicability of the fabric are enhanced.
Drawings
FIG. 1 is a flow chart of a preparation method of a noctilucent fabric.
Detailed Description
Example one
The invention provides a noctilucent fabric and a preparation method thereof, wherein the noctilucent fabric comprises a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent. The component A comprises warp basic fibers and weft basic fibers; the warp basic fiber and the weft basic fiber both comprise any one or a mixture of a plurality of fibers of cotton, wool, spun silk, hemp, conventional viscose, lyocell, modal, bamboo fiber, nylon, terylene, acrylic fiber, polypropylene fiber and vinylon. The component B is luminous liquid which comprises 10-16 parts of luminous powder, 60-70 parts of deionized water, 3-5 parts of film forming auxiliary agent, 20-25 parts of water-based rosin resin emulsion, 10-15 parts of dispersing agent and 10-15 parts of adhesive. And the component C is a protective spraying liquid and comprises 5-8 parts of epoxy chloropropane, 4-7 parts of potassium hydroxide, 5-8 parts of methacrylic acid, 10-20 parts of higher fatty acid sodium, 8-16 parts of polyvinyl ether, 4-8 parts of methyl cellulose, 6-10 parts of wool grease, 4-8 parts of turpentine, 30-40 parts of deionized water, 5-7 parts of copper sulfate, 1-3 parts of nonylphenol polyoxyethylene ether and 10-15 parts of a nano waterproof agent.
In a further embodiment, the component B is luminous liquid and comprises 10 parts of luminous powder, 60 parts of deionized water, 3 parts of film-forming aid, 20 parts of aqueous rosin resin emulsion, 10 parts of dispersing agent and 10 parts of adhesive.
In a further embodiment, the component C is a protective spraying liquid and comprises 5 parts of epoxy chloropropane, 4 parts of potassium hydroxide, 5 parts of methacrylic acid, 10 parts of sodium higher fatty acid, 8 parts of polyvinyl ether, 4 parts of methyl cellulose, 6 parts of lanolin, 4 parts of turpentine, 30 parts of deionized water, 5 parts of copper sulfate, 1 part of nonylphenol polyoxyethylene ether and 10 parts of a nano waterproof agent.
As shown in fig. 1, the invention further provides a preparation method of the noctilucent fabric, which is characterized by comprising the following steps:
s1, preparing luminous liquid and protective spraying liquid;
s2, weaving the warp basic fibers and the weft basic fibers into a basic fabric;
s3, soaking the base fabric in a padding machine groove filled with luminous liquid, and squeezing and rolling the base fabric through two rollers, wherein the rolling residual is 70%;
s4, carrying out steam drying, water washing, re-drying and tentering setting;
s5, spraying protective spraying liquid on the surface of the fabric;
and S6, drying again to obtain the finished fabric.
Example two
The invention provides a noctilucent fabric and a preparation method thereof, wherein the noctilucent fabric comprises a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent. The component A comprises warp basic fibers and weft basic fibers; the warp basic fiber and the weft basic fiber both comprise any one or a mixture of a plurality of fibers of cotton, wool, spun silk, hemp, conventional viscose, lyocell, modal, bamboo fiber, nylon, terylene, acrylic fiber, polypropylene fiber and vinylon. The component B is luminous liquid which comprises 10-16 parts of luminous powder, 60-70 parts of deionized water, 3-5 parts of film forming auxiliary agent, 20-25 parts of water-based rosin resin emulsion, 10-15 parts of dispersing agent and 10-15 parts of adhesive. And the component C is a protective spraying liquid and comprises 5-8 parts of epoxy chloropropane, 4-7 parts of potassium hydroxide, 5-8 parts of methacrylic acid, 10-20 parts of higher fatty acid sodium, 8-16 parts of polyvinyl ether, 4-8 parts of methyl cellulose, 6-10 parts of wool grease, 4-8 parts of turpentine, 30-40 parts of deionized water, 5-7 parts of copper sulfate, 1-3 parts of nonylphenol polyoxyethylene ether and 10-15 parts of a nano waterproof agent.
In a further embodiment, the component B is luminous liquid and comprises 16 parts of luminous powder, 70 parts of deionized water, 5 parts of film-forming aid, 25 parts of aqueous rosin resin emulsion, 15 parts of dispersing agent and 15 parts of adhesive.
In a further embodiment, the component C is a protective spraying liquid and comprises 8 parts of epichlorohydrin, 7 parts of potassium hydroxide, 8 parts of methacrylic acid, 20 parts of sodium higher fatty acid, 16 parts of polyvinyl ether, 8 parts of methyl cellulose, 10 parts of lanolin, 8 parts of turpentine, 40 parts of deionized water, 7 parts of copper sulfate, 3 parts of nonylphenol polyoxyethylene ether and 15 parts of a nano waterproof agent.
As shown in fig. 1, the invention further provides a preparation method of the noctilucent fabric, which is characterized by comprising the following steps:
s1, preparing luminous liquid and protective spraying liquid;
s2, weaving the warp basic fibers and the weft basic fibers into a basic fabric;
s3, soaking the base fabric in a padding machine groove filled with luminous liquid, and squeezing and rolling the base fabric through two rollers, wherein the rolling residual is 70%;
s4, carrying out steam drying, water washing, re-drying and tentering setting;
s5, spraying protective spraying liquid on the surface of the fabric;
and S6, drying again to obtain the finished fabric.
EXAMPLE III
The invention provides a noctilucent fabric and a preparation method thereof, wherein the noctilucent fabric comprises a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent. The component A comprises warp basic fibers and weft basic fibers; the warp basic fiber and the weft basic fiber both comprise any one or a mixture of a plurality of fibers of cotton, wool, spun silk, hemp, conventional viscose, lyocell, modal, bamboo fiber, nylon, terylene, acrylic fiber, polypropylene fiber and vinylon. The component B is luminous liquid which comprises 10-16 parts of luminous powder, 60-70 parts of deionized water, 3-5 parts of film forming auxiliary agent, 20-25 parts of water-based rosin resin emulsion, 10-15 parts of dispersing agent and 10-15 parts of adhesive. And the component C is a protective spraying liquid and comprises 5-8 parts of epoxy chloropropane, 4-7 parts of potassium hydroxide, 5-8 parts of methacrylic acid, 10-20 parts of higher fatty acid sodium, 8-16 parts of polyvinyl ether, 4-8 parts of methyl cellulose, 6-10 parts of wool grease, 4-8 parts of turpentine, 30-40 parts of deionized water, 5-7 parts of copper sulfate, 1-3 parts of nonylphenol polyoxyethylene ether and 10-15 parts of a nano waterproof agent.
In a further embodiment, the component B is luminous liquid and comprises 13 parts of luminous powder, 65 parts of deionized water, 4 parts of film-forming aid, 23 parts of aqueous rosin resin emulsion, 12 parts of dispersing agent and 12 parts of adhesive.
In a further embodiment, the component C is a protective spraying liquid and comprises 6 parts of epoxy chloropropane, 5 parts of potassium hydroxide, 6 parts of methacrylic acid, 15 parts of sodium higher fatty acid, 12 parts of polyvinyl ether, 5 parts of methyl cellulose, 8 parts of lanolin, 5 parts of turpentine, 35 parts of deionized water, 6 parts of copper sulfate, 2 parts of nonylphenol polyoxyethylene ether and 12 parts of a nano waterproof agent.
As shown in fig. 1, the invention further provides a preparation method of the noctilucent fabric, which is characterized by comprising the following steps:
s1, preparing luminous liquid and protective spraying liquid;
s2, weaving the warp basic fibers and the weft basic fibers into a basic fabric;
s3, soaking the base fabric in a padding machine groove filled with luminous liquid, and squeezing and rolling the base fabric through two rollers, wherein the rolling residual is 70%;
s4, carrying out steam drying, water washing, re-drying and tentering setting;
s5, spraying protective spraying liquid on the surface of the fabric;
and S6, drying again to obtain the finished fabric.
According to the invention, a soaking mode is adopted, the noctilucent liquid is attached to the base fabric, and the protective spraying liquid is matched to form the waterproof film layer. The preparation process is simple, the noctilucent effect and the comfort of the fabric are guaranteed, the water resistance is good, and the functionality, the wear resistance and the practicability of the fabric are enhanced.
The embodiments of the present invention have been described in detail with reference to the drawings, but the present invention is not limited thereto, and various changes can be made within the knowledge of those skilled in the art without departing from the gist of the present invention.

Claims (8)

1. A noctilucent fabric is characterized by comprising a component A, a component B and a component C; the mass sum of the official moisture regain of the component A, the component B and the component C is 100 percent, the component A accounts for 72 to 85 percent, the component B accounts for 10 to 20 percent, and the component C accounts for 5 to 8 percent;
the component A comprises warp basic fibers and weft basic fibers; the warp basic fiber and the weft basic fiber both comprise any one or a mixture of a plurality of fibers of cotton, wool, spun silk, hemp, conventional viscose, lyocell, modal, bamboo fiber, nylon, terylene, acrylic fiber, polypropylene fiber and vinylon;
the component B is noctilucent liquid which comprises 10-16 parts of noctilucent powder, 60-70 parts of deionized water, 3-5 parts of film forming auxiliary agent, 20-25 parts of water-based rosin resin emulsion, 10-15 parts of dispersing agent and 10-15 parts of adhesive;
and the component C is a protective spraying liquid and comprises 5-8 parts of epoxy chloropropane, 4-7 parts of potassium hydroxide, 5-8 parts of methacrylic acid, 10-20 parts of higher fatty acid sodium, 8-16 parts of polyvinyl ether, 4-8 parts of methyl cellulose, 6-10 parts of wool grease, 4-8 parts of turpentine, 30-40 parts of deionized water, 5-7 parts of copper sulfate, 1-3 parts of nonylphenol polyoxyethylene ether and 10-15 parts of a nano waterproof agent.
2. The noctilucent fabric according to claim 1, wherein the component B is noctilucent liquid, and comprises 10 parts of noctilucent powder, 60 parts of deionized water, 3 parts of film forming aid, 20 parts of aqueous rosin resin emulsion, 10 parts of dispersing agent and 10 parts of adhesive.
3. The noctilucent fabric according to claim 1, wherein the component B is noctilucent liquid comprising 16 parts of noctilucent powder, 70 parts of deionized water, 5 parts of film forming aid, 25 parts of aqueous rosin resin emulsion, 15 parts of dispersing agent and 15 parts of adhesive.
4. The noctilucent fabric according to claim 1, wherein the component B is noctilucent liquid and comprises 13 parts of noctilucent powder, 65 parts of deionized water, 4 parts of film forming aid, 23 parts of aqueous rosin resin emulsion, 12 parts of dispersing agent and 12 parts of adhesive.
5. A luminous fabric as defined in claim 1, wherein the component C is a protective spray solution comprising 5 parts of epichlorohydrin, 4 parts of potassium hydroxide, 5 parts of methacrylic acid, 10 parts of sodium higher fatty acid, 8 parts of polyvinyl ether, 4 parts of methyl cellulose, 6 parts of lanolin, 4 parts of turpentine, 30 parts of deionized water, 5 parts of copper sulfate, 1 part of nonylphenol polyoxyethylene ether and 10 parts of nano water repellent.
6. A luminous fabric as defined in claim 1, wherein the component C is a protective spray solution comprising 8 parts of epichlorohydrin, 7 parts of potassium hydroxide, 8 parts of methacrylic acid, 20 parts of sodium higher fatty acid, 16 parts of polyvinyl ether, 8 parts of methyl cellulose, 10 parts of lanolin, 8 parts of turpentine, 40 parts of deionized water, 7 parts of copper sulfate, 3 parts of nonylphenol polyoxyethylene ether and 15 parts of nano water repellent.
7. A luminous fabric as defined in claim 1, wherein the component C is a protective spray solution comprising 6 parts of epichlorohydrin, 5 parts of potassium hydroxide, 6 parts of methacrylic acid, 15 parts of sodium higher fatty acid, 12 parts of polyvinyl ether, 5 parts of methyl cellulose, 8 parts of lanolin, 5 parts of turpentine, 35 parts of deionized water, 6 parts of copper sulfate, 2 parts of nonylphenol polyoxyethylene ether and 12 parts of nano water repellent.
8. The preparation method of the noctilucent fabric comprising any one of claims 1-7 is characterized by comprising the following steps:
s1, preparing luminous liquid and protective spraying liquid;
s2, weaving the warp basic fibers and the weft basic fibers into a basic fabric;
s3, soaking the base fabric in a padding machine groove filled with luminous liquid, and squeezing and rolling the base fabric through two rollers, wherein the rolling residual is 70%;
s4, carrying out steam drying, water washing, re-drying and tentering setting;
s5, spraying protective spraying liquid on the surface of the fabric;
and S6, drying again to obtain the finished fabric.
CN202111034736.7A 2021-09-04 2021-09-04 Noctilucent fabric and preparation method thereof Pending CN113818233A (en)