CN113732083B - 一种提高热轧钢板瓢曲性能的超快冷方法 - Google Patents
一种提高热轧钢板瓢曲性能的超快冷方法 Download PDFInfo
- Publication number
- CN113732083B CN113732083B CN202111009233.4A CN202111009233A CN113732083B CN 113732083 B CN113732083 B CN 113732083B CN 202111009233 A CN202111009233 A CN 202111009233A CN 113732083 B CN113732083 B CN 113732083B
- Authority
- CN
- China
- Prior art keywords
- head
- time
- steel plate
- ultra
- fast cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种提高热轧钢板瓢曲性能的超快冷方法,其特征在于:在设置头尾遮蔽距离和系数后,设置头部遮蔽时间t;所述头部遮蔽时间t为流量提升开始至钢板头部进入超快冷的时间,且0<t<t1+t2;其中,t1为阀响应时间,t2为流量达到目标值时间。所述头部遮蔽时间t=t0+Δt;其中,t0为初始设定值,Δt为调整值,Δt与钢板出水后黑头的长度L黑或红头的长度L红关系如下:Δt=—0.1*(L黑/100)或Δt=0.1*(L红/100)。本方案通过增设时间调整参数,有效的解决了在超快冷过程中,因阀相应、流量爬升过程对钢板冷却质量的影响,提高了钢板头尾和板身温度的均匀性,降低钢板头尾瓢曲量,提高了产品的质量。
Description
技术领域
本发明属于冶金制造技术领域,具体涉及一种提高热轧钢板瓢曲性能的超快冷方法。
背景技术
近年来,随着薄规格低温水冷钢板开发的需要,在冷却速度、冷却均匀性等方面对冷却技术提出了更高的需求,以超快冷为特征的新一代多功能中厚板轧后冷却技术能满足多种冷却工艺需求,已成为国内外中厚板轧后冷却技术的发展趋势。
但在现有工艺过程中,经超快冷装置水冷后的钢板通常会出现黑头下扣、红头上翘等头尾水冷不均的情况。在此水冷条件下连续生产,受头尾遮蔽硬伤的限制,钢板头尾瓢曲严重,甚至严重的可达瓢曲率27%+,严重影响产品质量,且被迫需要额外增加冷矫或挽救工序,不能很好的满足生产需求。
发明内容
本发明的目的是提供一种提高热轧钢板瓢曲性能的超快冷方法,以解决现有技术中的问题。
本发明是通过如下技术方案实现的:一种提高热轧钢板瓢曲性能的超快冷方法,其特征在于:在设置头尾遮蔽距离和系数后,设置头部遮蔽时间t;所述头部遮蔽时间t为流量提升开始至钢板头部进入超快冷的时间, 且0<t<t1+t2;其中,t1为阀响应时间,t2为流量达到目标值时间。
进一步的:所述头部遮蔽时间t=t0+Δt;其中,t0为初始设定值,Δt为调整值,Δt与钢板出水后黑头的长度L黑或红头的长度L红关系如下:
Δt=—0.1*(L黑/100)或Δt=0.1*(L红/100)。
本发明的优点是:本发明中,通过增设时间调整参数,有效的解决了在超快冷过程中,因阀相应、开启、到流量达到目标值过程所带来的时间差,减少了流量爬升过程对钢板冷却质量的影响,提高了钢板头尾和板身温度的均匀性。本发明在原头尾遮蔽调整距离和水流量系数基础上,增加时间调整参数,在水流量曲线爬坡阶段,通过对头尾遮蔽时间的调整,选择0~6秒内任意时间参数,提前触发头部流量的提升信号,达到各规格钢板头部需要流量参数的目的,降低钢板头尾瓢曲量,确保工艺的稳定执行。
具体实施方式
本发明提供一种提高热轧钢板瓢曲性能的超快冷方法,在通过超快冷方式对钢板进行冷却时,在设置头尾遮蔽距离和系数后,还增加设置头部遮蔽时间t;所述头部遮蔽时间t为流量提升开始时钢板所在位置至钢板头部进入超快冷的时间,也就是说,钢板在这个位置时,即进入流量爬升阶段。本方案中,头部遮蔽时间t的范围如下:0<t<t1+t2;其中,t1为阀响应时间,t2为流量达到目标值时间,即流量从设定的流量系数到该系数为最高值(通常为1)的时间。
优选的:所述头部遮蔽时间t=t0+Δt;其中,t0为初始设定值,且0< t0<t1+t2;Δt为调整值,根据出水后钢板的状态进行修改调整,其中,Δt与钢板出水后黑头的长度L黑或红头的长度L红关系如下:
Δt=—0.1*(L黑/100)或Δt=0.1*(L红/100)。
本方案中,长度的单位为mm,时间的单位为s。
实施例
1)首先设定好头尾遮蔽参数。
如某规格钢板,其参数如下:
头部距离*头部流量上系数/下系数=400*0.3/0.3;
尾部距离*尾部流量上系数/下系数=800*0.4/0.4;
头部遮蔽时间2。其中,阀响应时间1,流量爬升时间6。
本方案中,阀响应时间为阀本身的参数,可根据不同的阀具体确定。流量爬升时间,是指,当阀开启后,流量从设定的流量系数到该系数为最高值(通常为1)的时间,如本实施例中,以头部为例,指的是流量从30%提升至100%的时间,冷却过程的流量曲线近似为”几”字形,该时间为如初始的低流量至最高流量所用的时间,在曲线中近似一个陡坡向上攀升,故称流量爬升时间,通常为6。
2)在上述参数状态下,若钢板出水时黑头,应减少时间参数,每次调整0.2。即时间参数调整至1.8/1.6/1.4/1.2/1.0等。根据黑头的距离可增加调整的幅度,黑头200mm,时间参数按0.2s调整,黑头每增加100mm,时间参数调整增加0.1s。
3)在上述参数状态下,若钢板出水时红头,应增加时间参数,每次调整0.2。即时间参数调整至2.2/2.4/2.6/2.8/3.0等。根据红头的距离可增加调整的幅度,红头200mm,时间参数按0.2调整,红头每增加100mm,时间参数调整增加0.1。
4)在调整过程中,应始终合格证时间参数的范围,若在相应范围内,时间参数调整效果不明显时,需及时调整头尾遮蔽距离和水流量系数。
综上所述,本发明为解决钢板头尾瓢曲问题,在超快冷***中,提取水阀相应时间和水流量达到目标值时间。并根据水流量曲线爬坡阶段的时间长短,在头尾遮蔽程序中增加时间调整参数,根据规格的不同,设定不同的时间参数,消除头部黑头下扣和红头上翘的瓢曲情况。本方案中,先按规格先固化头尾遮蔽距离和系数,再进行头尾遮蔽时间参数调整,且头尾遮蔽时间参数调整优先后期的头尾遮蔽距离和系数调整,整个过程中,还可根据钢板头尾实际水冷情况,调整头尾遮蔽时间参数,调整灵活,适应性好,有效的提高了对钢板头尾瓢曲的控制效果。
Claims (1)
1.一种提高热轧钢板瓢曲性能的超快冷方法,其特征在于:在设置头尾遮蔽距离和系数后,设置头部遮蔽时间t;所述头部遮蔽时间t为流量提升开始至钢板头部进入超快冷的时间, 且0<t<t1+t2;其中,t1为阀响应时间,t2为流量达到目标值时间;
所述头部遮蔽时间t=t0+Δt;其中,t0为初始设定值,Δt为调整值,Δt与钢板出水后黑头的长度L黑或红头的长度L红关系如下:
Δt=—0.1*(L黑/100)或Δt=0.1*(L红/100)。