CN113621332A - 芯片封装用模封胶及封装结构 - Google Patents
芯片封装用模封胶及封装结构 Download PDFInfo
- Publication number
- CN113621332A CN113621332A CN202111177372.8A CN202111177372A CN113621332A CN 113621332 A CN113621332 A CN 113621332A CN 202111177372 A CN202111177372 A CN 202111177372A CN 113621332 A CN113621332 A CN 113621332A
- Authority
- CN
- China
- Prior art keywords
- parts
- chip
- epoxy resin
- chip packaging
- anhydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本申请公开了一种芯片封装用模封胶及封装结构，其中模封胶采用的环氧树脂中具有聚醚等柔性单元，结合固化剂和稀释剂等成分的复配，实现了良好的柔韧性和强度，且有效降低了翘曲，其中翘曲可降低至0mm，模量可达8GPa以上，具有良好的硅接着力，可有效保护硅片不因翘曲而弯曲裂纹。并且，通过加入对叔丁基苯酚型环氧树脂稀释剂，可进一步有效降低单官能脂肪族稀释剂对固化体系的影响，能进一步改善模封胶的柔韧性和模量。
Description
技术领域
本申请涉及半导体封装技术领域，尤其涉及一种芯片封装用模封胶及封装结构。
背景技术
随着半导体技术的发展，在电子零件装置的元件封装领域，树脂型密封因其生产便捷性、成本优势逐渐成为主流。今年来，印刷线路板上电子零件的安装逐渐高密度化。随之而来的是，在半导体装置中，相对于先前的引脚***型的封装，表面安装型的封装正快速发展。表面安装型的集成电路芯片（Integrated Circuit Chip，IC）可提高安装密度且降低安装高度，从而实现薄型、小型封装，减小封装壁厚。
通过树脂进行电子元件的封装，除了常用的转移成型法之外，还可以采用模压法，即将电子元件，例如已刻蚀芯片的硅片置于模具内，再给予树脂封装材料，并对树脂封装材料进行模压，以进行树脂密封。但是，在此过程中，由于模压操作和温度变化，容易使得模封材料发生翘曲，导致硅片弯曲过大而产生裂纹、裂缝，影响后续工段的操作，也容易导致芯片的不良率。
发明内容
本申请提供一种芯片封装用模封胶，具有高模量、低翘曲和良好的柔韧性，可有效减少硅片弯曲过大而导致的硅片裂纹裂缝。
本申请提供如下技术方案:
一方面，本申请提供一种芯片封装用模封胶，以重量份计包括如下组分：环氧树脂5-20重量份，固化剂 5-20重量份，固化促进剂 0.1-1.2重量份，无机填料 70- 100重量份，偶联剂 0.5-2.5重量份，稀释剂 0.1-15重量份；
其中，所述环氧树脂具有如式（I）所示的结构：
式（I）中，R1、R2各自独立地选自H或C1-C10的直链烷基或支链烷基，R3、R4、R5和R6各自独立地选自氢原子、甲基或卤素，X选自-O-，-COO-，或者-OCH(CH3)O-，并且R选自亚烷基、聚醚骨架中的任一种，n为1-10范围内的整数。
在一些实施例中，在式（I）中，所述R为-CH2CH2-(OCH2CH2)m-或者-CH(CH3)CH2-(OCH(CH3)CH2)m-，其中m为0-5范围内的整数。
在一些实施例中，所述环氧树脂具有如式（II）所示的结构：
其中，X为-OCH(CH3)O-，n为1-5范围内的整数。
在一些实施例中，所述无机填料为二氧化硅，其中二氧化硅的粒径范围为0.1-75μm。
在一些实施例中，所述固化剂选自四氢苯酐、六氢苯酐、甲基六氢苯酐、邻苯二甲酸酐、四氢邻苯二甲酸酐、甲基纳迪克酸酐及苯酚-芳烷基酚醛树脂中的至少一种。
在一些实施例中，所述固化剂包括甲基纳迪克酸酐和甲基六氢苯酐，且二者的质量比为(1-2):1。
在一些实施例中，所述稀释剂为对叔丁基苯酚型环氧树脂稀释剂，总氯≤200ppm。
在一些实施例中，所述芯片封装用模封胶还含有0.02-0.1重量份的着色剂。
在一些实施例中，以重量份计由如下组分组成：所述环氧树脂 5-20重量份，所述固化剂 5-20重量份，所述固化促进剂 0.1-1.2重量份，所述无机填料 70- 100重量份，所述稀释剂 0.1-15重量份，所述着色剂0.02-0.1重量份。
另一方面，本申请还提供一种芯片封装结构，所述芯片封装结构包括蚀刻于硅片晶圆上的芯片，以及覆盖于所述硅片晶圆上的封装层，其中所述封装层与所述硅片晶圆接触并包覆所述芯片，所述封装层包括如权利要求1-9任一项所述的模封胶。
有益效果：
本申请的模封胶采用具有聚醚等柔性单元的环氧树脂，结合固化剂和稀释剂等成分的复配，实现了良好的柔韧性和强度，且有效降低了翘曲，其中翘曲可降低至0mm，模量可达8GPa以上，具有良好的硅接着力，可有效保护硅片不因翘曲而弯曲裂纹。并且，本申请的申请人还发现，加入对叔丁基苯酚型环氧树脂稀释剂，可进一步有效降低单官能脂肪族稀释剂对固化体系的影响，能进一步改善环氧树脂的柔韧性和模量。
附图说明
为了更清楚地说明本申请实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本申请的一些实施例，对于本领域技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本申请实施例中待封装的蚀刻有芯片的硅片俯视结构示意图；
图2为本申请实施例提供一种芯片封装结构。
具体实施方式
面对本申请实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分实施例，而不是全部的实施例。基于本申请中的实施例，本领域技术人员在没有作出创造性劳动的前提下所获得的所有其它实施例，都属于本申请保护的范围。此外，应当理解的是，此处所描述的具体实施方式仅用于说明和解释本申请，并不用于限制本申请。在本申请的描述中，术语“包括”是指“包括但不限于”。本发明的各种实施例可以以一个范围的形式存在；应当理解，以一范围形式的描述仅仅是因为方便及简洁，不应理解为对本发明范围的硬性限制；因此，应当认为所述的范围描述已经具体公开所有可能的子范围以及该范围内的单一数值。例如，应当认为从1到5的范围描述已经具体公开子范围，例如从1到3，从1到4，从1到5，从2到4，以及所数范围内的单一数字，例如1、2、3、4或5，此不管范围为何皆适用。另外，每当在本文中指出数值范围，是指包括所指范围内的任何引用的数字(分数或整数)。
本申请实施例提供一种芯片封装用模封胶，以重量份计包括如下组分：环氧树脂5-20重量份，固化剂 5-20重量份，固化促进剂 0.1-1.2重量份，无机填料 70- 100重量份，稀释剂 0.1-15重量份；
其中，所述环氧树脂具有如式（I）所示的结构：
式（I）中，R1、R2各自独立地选自H或C1-C10的直链烷基或支链烷基，R3、R4、R5和R6各自独立地选自氢原子、甲基或卤素，X选自-O-，-COO-，或者-OCH(CH3)O-，并且R选自亚烷基、聚醚骨架中的任一种，n为1-10范围内的整数。
本申请中，卤素选自氟原子或氯原子，其中氟原子是优选的。
本申请实施例提出的芯片封装用模封胶，采用式（I）所示的环氧树脂，通过X基团和R基团等柔性片段和低极性的链段，结合固化体系和稀释剂，使得模封胶具有良好的柔韧性和强度，且有效降低了翘曲，具有良好的硅接着力。
对于本申请实施例所用的环氧树脂，式（I）中的R基团可以为-CH2CH2-(OCH2CH2)m-或者-CH(CH3)CH2-(OCH(CH3)CH2)m-，其中m为0-5范围内的整数。例如当m=0时，R基团为直链或支链的亚烷基。当m=1-5中任一整数时，R基团为聚醚骨架。
在一些具体实施例中，环氧树脂可具有如式（II）所示的结构：
其中，X为-OCH(CH3)O-，n为1-5范围内的整数。
在一些实施例中，出于芯片封装工艺中固化速率和强度的考虑，环氧树脂的环氧当量为400-450g/eq。环氧树脂的粘度（25℃, E型粘度计）为10000-15000mPa.s，数均分子量为700-900。这样的环氧树脂可以实现良好的柔韧性和高模量。在一些具体实施例中，可选用DIC株式会社的EXA-4850-150。
本申请实施例中，无机填料可选用二氧化硅，粒径范围为0.1-75μm，二氧化硅的用量为70-100重量份。在本申请的环氧树脂模封胶中，由于选用柔性链段的环氧树脂，粘度低、柔韧性好，因而可实现较高比例的二氧化硅填充量，进一步使得封装层具有低的热膨胀系数。在一些实施例中，二氧化硅可以为气相二氧化硅或熔融二氧化硅，粒径为0.1-75μm，或者1-50μm。
固化剂选自四氢苯酐、六氢苯酐、甲基六氢苯酐、邻苯二甲酸酐、四氢邻苯二甲酸酐、甲基纳迪克酸酐（甲基-5-降冰片烯-2,3-二羧酸酐）及苯酚-芳烷基酚醛树脂中的至少一种。固化剂用量为5-20重量份，例如10-12份。固化剂的用量没有特别的限定，本领域技术人员能够根据施工条件和固化速率选择确定固化剂的用量。在一些实施例中，固化剂优选甲基纳迪克酸酐与甲基六氢苯酐的复配物，复配比例为（1-2）:1，更优选1:1。在一些实施例中，环氧树脂与固化剂的用量为（1-2）：1，优选1:1。
本申请实施例中还可以进一步加入固化促进剂，固化促进剂的种类没有特别的限定，可选自咪唑或N,N-二甲基苯胺。固化剂和固化促进剂结合本申请实施例的环氧树脂一同实现封装材料所需的固化速率和流动性等加工性能。
模封胶中含有0.5-2.5重量份的偶联剂。偶联剂可以增加各组分之间的相容性，尤其是加入较大比重的二氧化硅填料和增韧剂的情况下，偶联剂可帮助这些粒子均匀地分散在环氧树脂体系当中，改善体系的相容性。在本申请实施例中，偶联剂为具有环氧基团的硅烷偶联剂，例如选自γ-环氧丙氧基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三乙氧基硅烷、γ-环氧丙氧基丙基三丙氧基硅烷、γ-环氧丙氧基丙基三丁氧基硅烷的任一种，但不限于此。具有环氧基团的硅烷偶联剂所带有的环氧官能团可以在固化过程中较好地与环氧树脂形成固化交联网络，进一步改善体系的相容性。
模封胶中含有0.1-1.5重量份的稀释剂，可在尽量不改变材料性能的情况下，降低封装材料的粘度。该稀释剂可以选自本领域已知的环氧稀释剂，例如对叔丁基苯酚型环氧树脂稀释剂或者单官能脂肪族稀释剂、双官能脂肪族稀释剂中的任一种。值得说明的是，对叔丁基苯酚型环氧树脂稀释剂在本申请实施例的模封胶体系中体现出更加优异的效果，其可能的原因在于叔丁基苯酚型环氧树脂稀释剂对固化体系的影响更小，可以保持环氧树脂较稳定的固化特性。并且稀释剂应该是不含卤素或低卤素含量的，期望的是总氯≤200ppm。在一些实施例中，可选择的稀释剂为ADEKA ED-509S或ERISYS GE-11。稀释剂的用量应不超过1.5%，以保持较低的总氯含量。
芯片封装材料还包括着色剂0.02-0.1重量份。在一些实施例中，颜料为炭黑。着色剂赋予封装层以颜色，以便封装层呈现不同颜色的外观，并且方便在芯片上印刷文字。
本申请实施例进一步提供一种芯片封装结构，参阅图1和图2，该封装结构包括硅片10及蚀刻于该硅片上的芯片20，封装层30与硅片10部分接触，所述封装层30包括本申请实施例提供的模封胶。
本领域技术人员可以理解，如图1所示，在硅片10上可间隔蚀刻多个芯片20，本申请实施例的模封胶可用于晶圆级封装，或者是单个、多个芯片的封装。
一些实施例中，封装层30的厚度为50-200μm。
一些实施例中，封装层30覆盖所述芯片背面；在另一些实施例中，封装层30覆盖及所述芯片20的四周，并且填充芯片20之间的间隙，即模封胶将芯片20完全包覆以便为芯片20提供完全的保护。
相应地，本申请实施例请还提供一种芯片封装方法，以形成上述封装结构。该芯片封装方法包括如下步骤：
将待封装的芯片置于模具中，其中该芯片设置于硅片上；
提供本申请实施例的模封胶，将液体模封胶加入到模具中，使其填充芯片间隙并覆盖芯片的待封装表面；
采用模压机进行模压；以及
固化，完成芯片封装。
一些实施例中，提供本申请实施例的模封胶的步骤包括：按比例提供所述封装材料的各组分，混合均匀，形成模封胶。
在一些实施例中，混合的步骤包括：包括先搅拌混合均匀，混炼，经真空脱泡，制得该模封胶。
本领域技术人员可以理解，可采用本领域已知的方式实现上述混合步骤，只要可提供各组分分散均匀且相容性良好的模封胶分散体系即可。
例如可采用在公转自转式离心搅拌机进行搅拌混合，温度控制在70℃以下。可采用三辊或双辊混炼机进行混炼，辊的间隙由填料的最大粒径决定，例如等于二氧化硅的最大粒径或略大于二氧化硅的最大粒径，在一些实施方式中，进料端的辊间隙为填料最大粒径的2-3倍，出料端为填料最大粒径的1.5-2倍，例如在本申请实施例中辊间隙为30-80μm，以便可充分分散无机填料在树脂体系中的分布。混炼时控制温度≤50℃，避免因温度过高而引起物料提前固化。真空搅拌脱泡的温度控制在≤50℃。
可选的，在本申请的一些实施例中，所述固化步骤中固化温度为120-180℃。该固化过程可进一步提高封装材料的硬度，使其对芯片进行更好的保护。
可选的，在本申请的一些实施例中，在所述芯片的背面施用封装材料，固化，形成封装层是指将所述封装材料流延在芯片背面及周围，然后采用模压工艺使其封装材料填入模具中，并固化，形成所述封装层。
可选的，在本申请的一些实施例中，所述模压工艺包括：采用模压机进行预压和压合，再泄压取出，烘箱内加热固化。对于模压工艺的参数没有特别的限定，本领域技术人员可根据本领域已知的模压工艺及晶圆、模具的具体规模确定模压机的工作参数。
下面通过具体实施例来对本申请进行具体说明，以下实施例仅是本申请的部分实施例，不是对本申请的限定。
实施例
根据表1称取封装材料的各组分，配料，混合，脱泡，装管制备成环氧树脂模封胶。
混合工艺为：70℃下离心搅拌30min，公转转速1200-1300r/min；三辊筒混炼温度50℃下混炼1.5h，辊间距40μm；离心搅拌脱泡温度为50℃，搅拌10min；公转转速1200-1500r/min。
对实施例及对比例的封装胶进行热膨胀系数CTE1测试，测试方法为：将封装胶经130℃/1h固化后，制备符合标准ASTM E831-2019要求的样品，然后测试样品的热膨胀系数。
对实施例及对比例的封装胶进行翘曲测试，测试方法为：
Si片上面覆盖200μm厚度的封装胶，在130℃下固化1h，冷却后取出，放在水平的桌面上，用重物按住载玻片一边，卡尺测量另一边到桌面的距离。
测定实施例及对比例的封装胶的粘度，参考标准ASTM D2196-2018进行测量，样品恒温 25℃，用Brookfield 粘度计，选择 SC4-14 转子，转速为 2-10 rpm。
模量测试方法：制备测试样品的尺寸为 55mm*10mm* 2mm，采用ASTME2254-2018标准方法测试储存模量。
对实施例及对比例的封装胶的硅界面粘着力，测试方法参考标准ASTM D1002-2010，将液态模封胶分别点在测试界面硅片上大小为5mm×5mm的方形区域，经150℃固化1小时后，用万能拉力机测试剪切粘结强度。
表1 模封胶成分表及性能测试结果
由上表可知，选用实施例1-5比对比例1-2相比具有更加优异性能，实施例1-5因采用了一定含量比例的带柔性链段的环氧树脂，结合固化体系和稀释体系，实现了更加优异的模量和翘曲，且硅界面附着力也明显优于对比例。并且，根据实施例1和实施例4可以看出，复配的固化剂可以具有更加稳定的固化效果，模封胶的效果更佳。另外，本申请的发明人还发现带芳香基的稀释剂在本申请的模封胶体系中表现出更优异的效果。本申请所提供的模封胶通过良好的硅界面附着力可对芯片实现更加稳定的保护，且高模量和低翘曲改善了因硅片弯曲引起的裂缝。且该模封胶常温下呈液态，粘度低，具有良好的流动性，可适用于模压封装。
以上对本申请实施例所提供的芯片封装用模封胶及封装结构进行了详细介绍，本文中应用了具体个例对本申请的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本申请的方法及其核心思想；同时，对于本领域的技术人员，依据本申请的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本申请的限制。
Claims (10)
1.一种芯片封装用模封胶，其特征在于，以重量份计包括如下组分：环氧树脂 5-20重量份，固化剂 5-20重量份，固化促进剂 0.1-1.2重量份，无机填料70- 100重量份，偶联剂0.5-2.5重量份，稀释剂 0.1-15重量份；
其中，所述环氧树脂具有如式（I）所示的结构：
式（I）中，R1、R2各自独立地选自H或C1-C10的直链烷基或支链烷基，R3、R4、R5和R6各自独立地选自氢原子、甲基或卤素，X选自-O-，-COO-，或者-OCH(CH3)O-，并且R选自亚烷基、聚醚骨架中的任一种，n为1-10范围内的整数。
2.根据权利要求1所述的芯片封装用模封胶，其特征在于，在式（I）中，所述R为-CH2CH2-(OCH2CH2)m-或者-CH(CH3)CH2-(OCH(CH3)CH2)m-，其中m为0-5范围内的整数。
3.根据权利要求2所述的芯片封装用模封胶，其特征在于，所述环氧树脂具有如式（II）所示的结构：
其中，X为-OCH(CH3)O-，n为1-5范围内的整数。
4.根据权利要求1所述的芯片封装用模封胶，其特征在于，所述无机填料为二氧化硅，其中二氧化硅的粒径范围为0.1-75μm。
5.根据权利要求1所述的芯片封装用模封胶，其特征在于，所述固化剂选自四氢苯酐、六氢苯酐、甲基六氢苯酐、邻苯二甲酸酐、四氢邻苯二甲酸酐、甲基纳迪克酸酐及苯酚-芳烷基酚醛树脂中的至少一种。
6.根据权利要求5所述的芯片封装用模封胶，其特征在于，所述固化剂包括甲基纳迪克酸酐和甲基六氢苯酐，且二者的质量比为1:1。
7.根据权利要求1所述的芯片封装用模封胶，其特征在于，所述稀释剂为对叔丁基苯酚型环氧树脂稀释剂，总氯≤200ppm。
8.根据权利要求1所述的芯片封装用模封胶，其特征在于，所述芯片封装用模封胶还含有0.02-0.1重量份的着色剂。
9.根据权利要求1-8任一项所述的芯片封装用模封胶，其特征在于，以重量份计由如下组分组成：所述环氧树脂 5-20重量份，所述固化剂 5-20重量份，所述固化促进剂 0.1-1.2重量份，所述无机填料70- 100重量份，所述稀释剂 0.1-15重量份，所述着色剂0.02-0.1重量份。
10.一种芯片封装结构，其特征在于，所述芯片封装结构包括蚀刻于硅片上的芯片，以及覆盖于所述硅片上的封装层，其中所述封装层与所述硅片接触并包覆所述芯片，所述封装层包括如权利要求1-9任一项所述的模封胶。