CN113365868B - 平视显示器装置 - Google Patents
平视显示器装置 Download PDFInfo
- Publication number
- CN113365868B CN113365868B CN202080012302.4A CN202080012302A CN113365868B CN 113365868 B CN113365868 B CN 113365868B CN 202080012302 A CN202080012302 A CN 202080012302A CN 113365868 B CN113365868 B CN 113365868B
- Authority
- CN
- China
- Prior art keywords
- glass
- glass plate
- light
- plate
- projection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种平视显示器装置,其搭载于移动体、使前述移动体的乘员确认S偏振光的在投影部的反射像的虚像,前述平视显示器装置具备:影像部,其照射由S偏振光构成的投影光;和,投影部,其投影前述投影光,前述投影部由夹层玻璃构成,所述夹层玻璃具备:配置于前述投影光的入射侧的第一玻璃板、配置于前述投影光的出射侧的第二玻璃板、和配置于前述第一玻璃板与前述第二玻璃板之间的半波长板,前述第一玻璃板和前述第二玻璃板由在组成中包含硅氧化物、铁氧化物和碱金属氧化物的玻璃组合物构成,前述第一玻璃板和前述第二玻璃板中的至少一者如下:厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%,前述半波长板具有可见光透射性,前述半波长板的CIE色度体系中的透射光的a*为‑2.5~4.5、b*为‑1.0~7.0,前述反射像形成于前述第一玻璃板的室内侧面,从前述第二玻璃板的室外侧面出射被转换为P偏振光的投影光。
Description
技术领域
本公开涉及一种平视显示器(此后有时记载为HUD)装置,该平视显示器装置搭载于车辆、飞机等移动体,将影像投影到乘员的前方视野内的投影部以使乘员确认该影像。
背景技术
作为HUD装置的前述投影部,使用了设置在移动体的前方部的挡风玻璃。乘员确认投影光在所述投影部处的反射像的虚像。在所述投影部中,由于可能在靠室内的一侧的主面上形成第一反射像、在靠室外的一侧的主面上形成第二反射像,因此所述虚像可能被乘员确认为双重像(关于产生双重像的机构,参照非专利文献1)。作为减轻该双重像的方法,提出了偏振光HUD方式(专利文献1、2、3等)。
利用如下的机构来减轻偏振光HUD方式的双重像。由具备第一透光板、第二透光板以及半波长板的层叠构件构成所述投影部,调整所述层叠构件的各材料,使得可见光区域内的折射率相同,其中,所述第一透光板配置在靠室内的一侧,由玻璃等构成,所述第二透光板配置在靠室外的一侧,所述半波长板配置在所述第一透光板与所述第二透光板之间。而且,投影光对于所述投影部以布鲁斯特角入射。
所入射的投影光由S偏振光构成时,在所述第一透光板的靠室内的一侧的主面上形成所述反射像。而且,经过所述投影部的投影光被变换为P偏振光。该P偏振光在到达了所述第二透光板的靠室外的一侧的主面时,不在该主面上反射而向靠室外的一侧射出。所述乘员确认在所述第一透光板的靠室内的一侧的主面上形成的、基于S偏振光的反射像的虚像。将该方式记载为S-HUD方式。
现有技术文献
专利文献
专利文献1:日本特开平2-141720号公报
专利文献2:日本特开平9-175844号公报
专利文献3:日本特开平10-96874号公报
非专利文献
非专利文献1:“新型主动驾驶显示的开发”、MAZDA技法、No.33(2016)、60页-65页
发明内容
发明要解决的问题
偏振光HUD方式中,使入射至前述投影部的投影光的偏振光的方向旋转90度的、也被称为旋光膜的半波长板成为用于减轻双重像的重要的构件。以往的半波长板如专利文献2中公开那样,带有黄色的着色。因此,专利文献2中,为了使通过前述投影部的色调对于人的视觉来说自然,提出了将带有黄色调的半波长板与绿色的玻璃板组合而使用的方案。
前述投影部作为设置于前述移动体的前方部的挡风玻璃使用,因此,作为所使用的构件,优选使用无色、或接近于无色者。然而,逐渐可知:作为前述半波长板,如果使用无色、或接近于无色者,则可能产生双重像的问题。
对于此处的偏振光尝试了考察。在某个空间中,观察X轴、Y轴、Z轴时,如果将光的行进方向设为前述Z轴,则偏振光以X轴方向的极化波与Y轴方向的极化波的合成向量的形式形成。偏振光在介质中行进时,X轴方向的极化波传送速度与Y轴方向的极化波的传送速度存在差(作为带来该差的代表性的参数,有折射率差)时,两极化波的位相错位,偏振光的类型产生变化。入射至介质的光为S偏振光、在前述介质内X轴方向的极化波与Y轴方向的极化波的位相错位半波长时,S偏振光旋转90度,成为P偏振光。
以折射率等为代表的、对极化波的传送速度有影响的因素发生波长分散。在介质中,在某个光波长域中,X轴的前述因素与Y轴的前述因素的“差”如果恒定,则在该光波长域中,入射至介质的偏振光始终被转换为相同的偏振光。然而,在可见光波长域中,难以使前述“差”恒定。
对于难以使前述“差”恒定而言,如果尝试考虑折射率的波长分散曲线则容易理解。折射率越高的介质,越向短波长侧行进,可见分散曲线的上升。如此,随着向短波长侧行进,将会使分散曲线升高的材料称为正分散性材料。该升高从波长400nm附近可见,因此,前述半波长板为无色、或接近于无色的情况下,特别是蓝色的一部分中,变得容易产生无法从S偏振光转换为P偏振光的现象。半波长板如专利文献2中记载的半波长板等那样被着色为黄色时,其一部分蓝色被吸收到半波长板内,因此从S偏振光未转换为P偏振光,这样的现象未被本领域技术人员认识到成为课题。在前述半波长板为无色、或接近于无色的情况下,需要考虑的是,从S偏振光向P偏振光的转换不顺利的区域很可能作为使用无色、或接近于无色的半波长板的HUD装置的新课题出现。
本公开中,其课题在于,在考虑以上的基础上,提供前述半波长板为无色、或接近于无色时的、S-HUD方式中的HUD装置中,改善了双重像的HUD装置。
用于解决问题的方案
即,本公开的平视显示器装置为一种平视显示器装置,其搭载于移动体、使前述移动体的乘员确认S偏振光的在投影部的反射像的虚像,
前述平视显示器装置具备:
影像部,其照射由S偏振光构成的投影光;和,
投影部,其投影前述投影光,
前述投影部由夹层玻璃构成,所述夹层玻璃具备:配置于前述投影光的入射侧的第一玻璃板、配置于前述投影光的出射侧的第二玻璃板、和配置于前述第一玻璃板与前述第二玻璃板之间的半波长板,
前述第一玻璃板和前述第二玻璃板由在组成中包含硅氧化物、铁氧化物和碱金属氧化物的玻璃组合物构成,
前述第一玻璃板和前述第二玻璃板中的至少一者如下:
厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%,
前述半波长板具有可见光透射性,前述半波长板的CIE色度体系中的透射光的a*为-2.5~4.5、b*为-1.0~7.0,
前述反射像形成于前述第一玻璃板的室内侧面,
从前述第二玻璃板的室外侧面出射被转换为P偏振光的投影光。
前述半波长板具有可见光透射性,CIE色度体系中的透射光的a*为-2.5~4.5、b*为-1.0~7.0,因此,其色调确认为无色、或接近于无色。
因此,有利于使用前述投影部作为移动体的窗。而且,前述第一玻璃板和前述第二玻璃板中的至少一者如下:玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%,从而该玻璃板吸收前述半波长板的、从S偏振光转换为P偏振光的转换效率低的波长域的光,可以改善HUD装置中的双重像。
发明的效果
根据本公开,S-HUD方式中的HUD装置中,可以改善双重像。而且,可以使S-HUD方式中使用的投影部形成对于乘员来说中性的色调,可以适合使用前述投影部作为移动体的窗。
附图说明
图1为示出本发明的实施方式的HUD装置的概要、和该装置中的光路的示意图。
具体实施方式
利用附图对本发明的实施方式的HUD装置进行说明。
图1为示出本发明的实施方式的HUD装置的概要、和该装置中的光路的示意图。
图1中,投影光的光路用实线表示,成为双重像的原因的投影光的光路用虚线表示。另外,作为双重像的虚像521也用虚线表示。
HUD装置1中,投影部4具备:半波长板44、隔着半波长板44对置的配置的、配置于移动体的室内侧的第一玻璃板41、和配置于移动体的室外侧的第二玻璃板42。
在半波长板44与第一玻璃板41之间夹持有中间膜431,在半波长板44与第二玻璃板42之间夹持有中间膜432。
第一玻璃板41具备:在室内侧露出的第一主面411、和第一主面的相反侧的第二主面412,第二玻璃板42具备:在室外侧露出的第四主面424、和第四主面424的相反侧的第三主面423。
投影光50从影像部3照射至第一主面411,在第一主面411形成第一反射像。第一主面411为第一玻璃板41的室内侧面。
而且,乘员6观察位于基于第一反射像的光路51的延长上的虚像511。
作为本发明的实施方式之一的HUD装置以观察基于第一反射像的虚像的方式进行光学设计而成,是S-HUD方式的HUD装置。
作为本发明的实施方式之一的HUD装置中,投影光由S偏振光构成。
投影光由S偏振光构成,未必是指在来自影像部的投影光的时刻就由S偏振光构成,也可以为从影像部作为包含P偏振光和S偏振光的投影光照射的光利用偏振片转换为由S偏振光构成的投影光的光。
作为包含P偏振光和S偏振光的投影光的例子,可以举出随机包含所有偏振光者(无偏振光)、圆偏振光、椭圆偏振光、P偏振光与S偏振光的混合光、不是P偏振光、S偏振光的直线偏振光等。
通过在投影光通过的通路配置偏振片,从而可以将包含P偏振光和S偏振光的投影光转换为由S偏振光构成的投影光。
通过将投影光调整为由S偏振光构成的投影光,从而进行对S-HUD方式的切换。
偏振片具有对一个直线偏振光的透射窗,该透射窗以面对投影光的行进方向的方式配置。
作为影像部,适合使用可以照射由S偏振光构成的投影光、或包含P偏振光和S偏振光的投影光的投影仪。作为这种投影仪的例子,可以举出由DMD投影***方式投影仪、激光扫描型MEMS投影***方式投影仪、或反射型液晶方式投影仪构成者。
本发明的实施方式之一的HUD装置中,优选使由S偏振光构成的投影光对于第一主面以布鲁斯特角入射。另外,作为由S偏振光构成的投影光对于投影部入射的角度,可以具有使形成布鲁斯特角的入射角度位于中心的程度的幅度。
例如,可以以布鲁斯特角±10°左右的入射角度入射。
作为一例,布鲁斯特角为56°的情况下,可以使投影光以46°~66°的入射角度入射。
该情况下,在投影部的第一主面形成反射像,移动体的乘员确认基于第一主面处的反射像的虚像。在第一主面透射、在投影部内行进的投影光在半波长板中被转换为P偏振光,在投影部的第四主面不产生反射而投影光直接作为P偏振光向第二玻璃板的第四主面、即室外侧放出。因此,防止产生双重像。
以下,对用于实施本发明的实施方式之一的平视显示器装置中使用的投影部的适合的方式的构成和材料进行说明。
投影部由夹层玻璃构成,所述夹层玻璃具备:配置于投影光的入射侧的第一玻璃板、配置于投影光的出射侧的第二玻璃板、和配置于第一玻璃板与第二玻璃板之间的半波长板。
<玻璃板>
第一玻璃板和第二玻璃板由在组成中包含硅氧化物、铁氧化物和碱金属氧化物的玻璃组合物构成。
作为玻璃板的材质,优选由ISO16293-1中规定的玻璃组成的、钠钙硅酸盐玻璃构成。换言之,优选为ISO16293-1中规定的玻璃组成的钠钙硅酸盐玻璃、且为在组成中包含铁氧化物的钠钙硅酸盐玻璃。
另外,第一玻璃板和第二玻璃板中的至少一者如下:厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%。
这种玻璃为所谓绿玻璃,在400nm附近具有吸收。因此,通过使用这种玻璃作为至少一个玻璃,从而可以吸收成为双重像的原因的波长的光。
玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%,从而可以吸收成为双重像的原因的波长的光。另外,FeO含量为0.1质量%~0.5质量%,从而玻璃的色调从黄色变为绿,成为自然的色调的玻璃。
另外,第一玻璃板和第二玻璃板中的一者优选如下:厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0质量%~0.15质量%、FeO含量为0质量%~0.05质量%。
这种玻璃为所谓透明玻璃。
而且,这种透明玻璃优选为第一玻璃板、即配置于室内侧的玻璃板。
通过将透明玻璃配置于室内侧的面,从而可以使基于第一反射像的虚像的RGB更自然。
<半波长板>
半波长板配置于第一玻璃板与第二玻璃板之间。
半波长板的形状可以为板状,也可以为薄膜状。
作为半波长板,可以使用:将聚碳酸酯、聚丙烯酸酯、聚醚砜、环烯烃聚合物等塑料薄膜进行单轴或双轴拉伸而得到的相位差元件;使液晶聚合物沿特定方向取向并使取向状态固定化而得到的相位差元件。
作为使聚合物取向的方法,例如能够列举对聚酯薄膜、纤维素薄膜等透明塑料薄膜进行摩擦处理的方法、在玻璃板或塑料薄膜上形成取向膜并对上述取向膜进行摩擦处理或光取向处理的方法等。作为使取向固定的方法,例如能够列举在存在光聚合引发剂的条件下对紫外线固化型的液晶聚合物进行紫外线照射来通过聚合反应使其固化的方法、通过加热使其交联的方法、在高温状态下对其进行取向之后快速冷却的方法等。
作为液晶聚合物使用的化合物只要是在向特定方向取向时示出液晶性的化合物即可,没有特别地限定。例如能够使用在液晶状态下进行扭转向列取向、并在液晶转变点以下成为玻璃状态的化合物,能够列举光学活性的聚酯、聚酰胺、聚碳酸酯、聚酯酰亚胺等主链型液晶聚合物、光学活性的聚丙烯酸酯、聚甲基丙烯酸酯、聚丙二酸酯、聚硅氧烷、聚醚等侧链型液晶聚合物、聚合性液晶等。另外,能够例示在非光学活性的这些主链型或侧链型聚合物中添加其它低分子或高分子的光学活性化合物而得到的聚合物组合物等。
半波长板具有可见光透射性,半波长板的CIE色度体系中的透射光的a*为-2.5~4.5、b*为-1.0~7.0。前述半波长板优选以投影部4的可见光透射率、即夹层玻璃的可见光透射率成为70%以上的方式具有可见光透射率。例如,前述半波长板的可见光透射率可以成为70%以上,也可以成为80%以上。需要说明的是,此处的可见光透射率是指,以JISR3212(2015年)中规定的方法得到者。作为可见光透射率的测定装置,可以使用分光光度计(日立制作所制U-4100)。
另外,透射光的a*和b*可以使用上述可见光透射率、基于JIS Z8781-4(2013年)中记载的方法而算出。可以说这种半波长板为无色、或接近于无色的半波长板。因此,是对用于设置于移动体的前方部的挡风玻璃优选的颜色的半波长板。
另外,半波长板中,优选从S偏振光转换为P偏振光的转换率最高的光波长域处于500nm~600nm。
从S偏振光转换为P偏振光的转换率最高的光波长域处于500nm~600nm时,在可见光波长的中心域变得存在转换率最高的光波长域,因此,遍及可见光波长整体地从S偏振光向P偏振光的转换效率良好地进行。
从S偏振光转换为P偏振光的转换率最高的光波长域处于可见光波长区域的一端时,在可见光波长区域的另一端转换效率变差。
半波长板只要配置于第一玻璃板与第二玻璃板之间即可,配置于第一玻璃板与第二玻璃板之间的2张中间膜中也可以夹持半波长板。另外,中间膜为1张、且在另一个玻璃板与中间膜中也可以夹持有半波长板。
可以使用树脂中间膜作为中间膜,作为树脂中间膜,优选使用热塑性的透明的聚合物。作为聚合物,可以使用聚乙烯醇缩丁醛(PVB)、乙烯乙酸乙烯酯(EVA)、丙烯酸类树脂(PMMA)、聚氨酯树脂、聚对苯二甲酸乙二醇酯(PET)、环烯烃聚合物(COP)等。
通常,对于树脂中间膜的表面事先进行凹凸状的压花加工,使得不产生源自一体化加工为夹层玻璃时发生的脱气不良的失透、泡缺陷,本实施方式中,也可以使用进行了压花加工的树脂中间膜。
另外,树脂中间膜可以使用其一部分着色而成者、夹心具有隔音功能的层而成者、厚度有倾斜者等。另外,树脂中间膜中可以适宜添加紫外线吸收剂、红外线吸收剂、抗氧化剂、抗静电剂、热稳定剂、着色剂、粘接调整剂等并配混。另外,树脂中间膜可以施加松紧度进行拉伸,也可以通过伞状的加压辊之间而变形为扇型。
<夹层玻璃的制作步骤>
以下,对制作成为本公开的平视显示器装置的投影部的夹层玻璃的方法的适合的一例进行说明。
将玻璃板中的1张以水平放置,然后将用中间膜夹持的半波长板放置于该玻璃板上,然后,以将上述半波长板夹持于上述玻璃板和另1张玻璃板之间的方式放置另1张玻璃板,以夹心状层叠玻璃板、中间膜和半波长板。
需要说明的是,在将PVB用作树脂中间膜的情况下,为了最佳地保持PVB的含水率,优选将作业时的温度维持为恒温恒湿。之后,一边对层叠为夹心状的玻璃板与树脂中间膜之间存在的空气进行脱气,一边以温度成为80℃~100℃的方式进行加热,并进行预粘接。对空气进行脱气的方法有脱气袋法(bag method)、脱气环法(ring method)以及脱气辊法(roller method)等,可以使用其中任一种方法,其中,脱气袋法是利用由耐热橡胶等制成的橡胶袋将玻璃板与树脂中间膜的层叠物包裹起来进行脱气的方法,脱气环法是用橡胶环仅覆盖层叠物的玻璃板的端部并进行密封的方法,脱气辊法是使层叠物在辊之间经过来自作为最外层的2片玻璃板的两侧进行加压的方法。
在预粘接结束之后,在使用了脱气袋法的情况下,从橡胶袋中取出层叠物,在使用了脱气环法的情况下,从层叠物取下橡胶环。之后,将层叠物放入高压釜中,进行加压和加热使得该高压釜内的压力成为10~15kg/cm2、温度成为120℃~150℃,在该条件下进行20分~40分钟的加热/加压处理(最终粘接)。处理后,将高压釜内的温度降温至50℃以下后进行除压,将夹层玻璃从高压釜取出。
需要说明的是,半波长板只要配置于形成有反射像的区域即可,半波长板的面积可以与玻璃板的面积相同的大小,也可以小于玻璃板的面积。
实施例
使用换算为Fe2O3的全部铁氧化物含量不同的玻璃板,制作各种夹层玻璃。向该夹层玻璃入射S偏振光,评价换算为Fe2O3的全部铁氧化物含量与双重像的关系。将评价步骤示于以下。
夹层玻璃的制作
作为换算为Fe2O3的全部铁氧化物含量不同的玻璃板,准备任意组成中均由包含硅氧化物、铁氧化物和碱金属氧化物的玻璃组合物构成的玻璃板1(全部铁氧化物含量:0.483质量%、FeO含量0.193质量%)、玻璃板2(全部铁氧化物含量:0.358质量%、FeO含量0.130质量%)、玻璃板3(全部铁氧化物含量:0.065质量%、FeO含量0.028质量%)、玻璃板4(全部铁氧化物含量:2.055质量%、FeO含量0.736质量%)。
接着,制作在2张各玻璃板(100mm×100mm、板厚2mm)之间以依次成为clear PVB中间膜(积水化学工业株式会社制S-LEC Film HI RZN-10厚度0.38mm)、半波长板(EdmundOptics Japan Co.,Ltd.制聚合物相位差薄膜延迟量1/2λ#88-256a*=0.18b*=0.54)、clear PVB中间膜(积水化学工业株式会社制S-LEC Film HI RZN-10厚度0.38mm)的方式层叠的层叠体。
接着,将该层叠体放入高压釜中,利用真空袋进行脱气处理后,在约90℃、0.25MPa下,实施约10分钟的加压/加热处理,制作组合使用玻璃板1~4的任一者的夹层玻璃。
双重像的评价方法
作为光源,以成为S偏振光的方式,将直线偏光板(Mecan Imaging Inc.制SHLP44)设置于iPad pro(注册商标)(Apple Inc.制A1670)的画面上后,将白色的格子状的图像作为投影光,在入射角56°下向夹层玻璃的室内侧投影,对于从夹层玻璃向室内侧射出的投影光,对于是否可以确认双重像,实施目视评价。作为评价基准,记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)、×(可以明确地确认)。
另外,对于从夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景是否可以没有问题地进行确认,实施目视评价。作为评价基准,记作〇(可以没有问题地确认室外侧的风景)、×(无法确认室外侧的风景)。
(实施例1)
对于2张玻璃板为玻璃板1(全部铁氧化物含量:0.483质量%)的夹层玻璃,实施目视评价,结果无法确认双重像。因此,评价记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)。另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果可以没有问题地进行确认。因此,将评价记作〇。
(实施例2)
对于2张玻璃板为玻璃板2(全部铁氧化物含量:0.358质量%)的夹层玻璃,实施目视评价,结果无法确认双重像。因此,评价记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)。另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果可以没有问题地进行确认。因此,将评价记作〇。
(比较例1)
对于2张玻璃板为玻璃板3(全部铁氧化物含量:0.065质量%)的夹层玻璃,实施目视评价,结果明确地确认到双重像。因此,评价记作×(明确地确认)。另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果可以没有问题地进行确认。因此,将评价记作〇。
(比较例2)
对于2张玻璃板为玻璃板4(全部铁氧化物含量:2.055质量%)的夹层玻璃,实施目视评价,结果无法确认双重像。因此,评价记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)。
另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果变得无法确认室外侧的风景,因此,判断为不适合作为搭载于移动体的平视显示器装置,将评价记作×。
(实施例3-1)
作为换算为Fe2O3的全部铁氧化物含量不同的玻璃板的夹层玻璃,制作第一玻璃板(室内侧)使用玻璃板3(全部铁氧化物含量:0.065质量%)、第二玻璃板(室外侧)使用玻璃板2(全部铁氧化物含量:0.358质量%)的夹层玻璃,实施双重像的评价。
实施目视评价,结果微弱的确认到双重像,但为实际使用上没有问题的水平。因此,评价记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)。另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果可以没有问题地进行确认。因此,将评价记作〇。
(实施例3-2)
与实施例3-1相反地,制作第一玻璃板(室内侧)使用玻璃板2(全部铁氧化物含量:0.358质量%)、第二玻璃板(室外侧)使用玻璃板3(全部铁氧化物含量:0.065质量%)的夹层玻璃,实施双重像的评价。
实施目视评价,结果微弱地确认到双重像,但为实际使用上没有问题的水平。因此,评价记作〇(完全无法确认、或微弱地进行确认但实际使用上没有问题的水平)。另外,从上述夹层玻璃的室内侧观察透过该夹层玻璃观察室外侧的风景,结果可以没有问题地进行确认。因此,将评价记作〇。
实施例3-1与实施例3-2相比,结果确认了第一玻璃板(室内侧)使用全部铁氧化物含量低的玻璃(玻璃板3)的实施例3-1与实施例3-2相比,可以透明地确认投影光。认为这是由于,第一玻璃板的全部铁氧化物含量低,从而投影光背后的透明度变高,变得可以透明地确认投影光。
另外,实施例3-1、3-2与实施例1、2相比,作为夹层玻璃的透明度高,与实施例1、2相比,投影光透明。此次的实施例1、2、3-1、3-2中,实施例3-1可以最透明地确认投影光。
由实施例3-1、实施例3-2的结果确认了,即使一个玻璃板的换算为Fe2O3的全部铁氧化物含量低于0.2质量%,只要另一个玻璃板的全部铁氧化物含量为0.2质量%~2.0质量%,就可以抑制双重像。
另外,此时,适合使变得能透明地确认投影光的室内侧形成换算为Fe2O3的全部铁氧化物含量低至0质量%~0.15质量%的玻璃板。
将结果归纳于表时,如以下所述。
[表1]
产业上的可利用性
可以提供改善了投影至汽车等车辆的挡风玻璃部的投影光的双重像的HUD装置。
附图标记说明
1 HUD装置
3 影像部
4 投影部
6 乘员
41 第一玻璃板
411 第一主面
412 第二主面
42 第二玻璃板
423 第三主面
424 第四主面
431、432 中间膜
44 半波长板
50 投影光
51 基于第一反射像的光路
511 基于第一反射像的虚像
521 作为双重像的虚像
Claims (6)
1.一种平视显示器装置,其搭载于移动体、使所述移动体的乘员确认S偏振光的在投影部的反射像的虚像,
所述平视显示器装置具备:
影像部,其照射由S偏振光构成的投影光;和,
投影部,其投影所述投影光,
所述投影部由夹层玻璃构成,所述夹层玻璃具备:配置于所述投影光的入射侧的第一玻璃板、配置于所述投影光的出射侧的第二玻璃板、和配置于所述第一玻璃板与所述第二玻璃板之间的半波长板,
所述第一玻璃板和所述第二玻璃板由在组成中包含硅氧化物、铁氧化物和碱金属氧化物的玻璃组合物构成,
所述第一玻璃板和所述第二玻璃板中的至少一者如下:
厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%,
所述半波长板具有可见光透射性,所述半波长板的CIE色度体系中的透射光的a*为-2.5~4.5、b*为-1.0~7.0,
所述反射像形成于所述第一玻璃板的室内侧面,
从所述第二玻璃板的室外侧面出射被转换为P偏振光的投影光。
2.根据权利要求1所述的平视显示器装置,其中,
所述第一玻璃板和所述第二玻璃板中的一者如下:
厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0.2质量%~2.0质量%、FeO含量为0.1质量%~0.5质量%,
所述第一玻璃板和所述第二玻璃板中的另一者如下:
厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0质量%~0.15质量%、FeO含量为0质量%~0.05质量%。
3.根据权利要求2所述的平视显示器装置,其中,所述第一玻璃板如下:厚度为0.3mm~3mm,且玻璃组成中的换算为Fe2O3的全部铁氧化物含量为0质量%~0.15质量%、FeO含量为0质量%~0.05质量%。
4.根据权利要求1~3中任一项所述的平视显示器装置,其中,所述第一玻璃板和所述第二玻璃板由ISO16293-1中规定的玻璃组成的、钠钙硅酸盐玻璃构成。
5.根据权利要求1~3中任一项所述的平视显示器装置,其中,在所述半波长板中,从S偏振光转换为P偏振光的转换率最高的光波长域处于500nm~600nm。
6.根据权利要求1~3中任一项所述的平视显示器装置,其中,所述夹层玻璃的可见光透射率为70%以上。