CN113356381A - 一种建筑用复合防腐保温材料 - Google Patents
一种建筑用复合防腐保温材料 Download PDFInfo
- Publication number
- CN113356381A CN113356381A CN202110732414.3A CN202110732414A CN113356381A CN 113356381 A CN113356381 A CN 113356381A CN 202110732414 A CN202110732414 A CN 202110732414A CN 113356381 A CN113356381 A CN 113356381A
- Authority
- CN
- China
- Prior art keywords
- layer
- heat
- rock wool
- board
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种建筑用复合防腐保温材料，包括从内到外依次设置的基层、防潮层、加固层以及防腐层；所述基层为硅酸铝纤维板，所述防潮层为岩棉板，所述加固层为轻骨料混凝土板；所述硅酸铝纤维板通过聚合物防水砂浆与所述岩棉板连接，所述岩棉板通过聚合物防水砂浆与所述轻骨料混凝土板连接。该复合防腐保温材料利用硅酸铝纤维板的低热容量和低热导率的特点，达到保温的效果；利用岩棉板憎水性达到抗潮湿的效果，且岩棉板也具有导热系数低的特点，可以进一步加强保温效果；再利用轻骨料混凝土板加强整体结构的刚性，且尽量保持轻质；另外通过最***的防腐层进行防腐保护。
Description
技术领域
本发明涉及建筑复合材料技术领域，尤其涉及一种建筑用复合防腐保温材料。
背景技术
随着建筑行业的发展，以及人们对建筑环境要求的提高，对于建筑质量的考验也越高。目前是重视低碳经济的大环境，国家也在大力鼓励和推广环保，因此保温材料是现时常用的建筑材料。如公开号为CN211973868U所公开的一种建筑用防腐保温材料，包括墙体、聚合物砂浆层、泡沫玻璃保温层、聚合物抹面砂浆层、网格布层、防火层、防水层、防腐层，所述墙体上由内到外依次连接有聚合物砂浆层、泡沫玻璃保温层、聚合物抹面砂浆层、网格布层、防火层、防水层、防腐层，所述墙体与聚合物砂浆层、泡沫玻璃保温层、聚合物抹面砂浆层、网格布层、防火层、防水层、防腐层复合连接制成一体，所述网格布层采用耐碱纤维制成，所述防火层为改性聚丙烯腈纤维层，所述防水层为聚氨酯防水涂料层，所述防腐层为环氧防腐蚀涂料层。然而，其防腐和保温效果还是不够好。
发明内容
有鉴于此，本发明提出一种建筑用复合防腐保温材料，可以至少在一定程度上解决现有的建筑材料防腐性能和保温性能不足的问题。
本发明的技术方案是这样实现的：
一种建筑用复合防腐保温材料，包括从内到外依次设置的基层、防潮层、加固层以及防腐层；所述基层为硅酸铝纤维板，所述防潮层为岩棉板，所述加固层为轻骨料混凝土板；所述硅酸铝纤维板通过聚合物防水砂浆与所述岩棉板连接，所述岩棉板通过聚合物防水砂浆与所述轻骨料混凝土板连接。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述硅酸铝纤维板的密度大于250kg/m3，所述硅酸铝纤维板的厚度为30-80mm。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述岩棉板的厚度为20-40mm。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述轻骨料混凝土板由陶粒混凝土制成。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述陶粒混凝土的密度900-1200kg/m3。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述轻骨料混凝土板的厚度为10-20mm。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述防腐层为UHMWPE。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述防腐层的厚度为5-10mm。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述防腐层为PTFE。
作为所述建筑用复合防腐保温材料的进一步可选方案，所述防腐层的厚度为8-12mm。
本发明的有益效果有：该复合防腐保温材料利用硅酸铝纤维板的低热容量和低热导率的特点，达到保温的效果；利用岩棉板憎水性达到抗潮湿的效果，且岩棉板也具有导热系数低的特点，可以进一步加强保温效果；再利用轻骨料混凝土板加强整体结构的刚性，且尽量保持轻质；另外通过最***的防腐层进行防腐保护。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例。
图1为本发明一种建筑用复合防腐保温材料的结构示意图；
图中：1、基层；2、防潮层；3、加固层；4、防腐层。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例。
在本发明的描述中，需要理解的是，术语“上”、“下”、“前”、“后”、“竖直”、“水平”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
在本发明中，除非另有明确的规定和限定，术语“安装”、“相连”、“连接”、“固定”等术语应做广义理解，例如，可以是固定连接，也可以是可拆卸连接，或成一体；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通或两个元件的相互作用关系。对于本领域的普通技术人员而言，可以根据具体情况理解上述术语在本发明中的具体含义。
实施例一
参考图1，示出了一种建筑用复合防腐保温材料，包括从内到外依次设置的基层1、防潮层2、加固层3以及防腐层4；所述基层1为硅酸铝纤维板，所述防潮层2为岩棉板，所述加固层3为轻骨料混凝土板；所述硅酸铝纤维板通过聚合物防水砂浆与所述岩棉板连接，所述岩棉板通过聚合物防水砂浆与所述轻骨料混凝土板连接。
如此，该复合防腐保温材料利用硅酸铝纤维板的低热容量和低热导率的特点，达到保温的效果；利用岩棉板憎水性达到抗潮湿的效果，且岩棉板也具有导热系数低的特点，可以进一步加强保温效果；再利用轻骨料混凝土板加强整体结构的刚性，且尽量保持轻质；另外通过最***的防腐层4进行防腐保护。
上述方案具体的，所述硅酸铝纤维板的密度大于250kg/m3，所述硅酸铝纤维板的厚度为30-80mm。其中，硅酸铝纤维板的纤维分布均匀，保温性能稳定，且具有优良的吸音降噪性能，其设于内侧，可有效降低从室内传递到室外的声量。
上述方案具体的，所述岩棉板的厚度为20-40mm。其中，岩棉板具有大量的细长纤维，该些细长纤维形成了多孔连接结构，因此其具有出色的吸音降噪性能；同时，其憎水性可达99.9％，吸水率极低，无毛细渗透；岩棉按照ASTMC1104或ASTM1104M方法测试，质量吸湿率小于0.3％，其具有优异的防潮性能；并且，岩棉板的纤维细长柔韧，渣球含量低，导热系数低，具有极佳的保温性能。如此，所述岩棉板的吸音降噪性能和保温性能可以极好地加强所述硅酸铝纤维板的吸音降噪性能和保温性能，并使该复合防腐保温材料具备防潮性能。
上述方案具体的，所述轻骨料混凝土板由陶粒混凝土制成，所述陶粒混凝土的密度优选为900-1200kg/m3；所述轻骨料混凝土板的厚度优选为10-20mm。其中，轻骨料混凝土具有轻质、高强、保温、耐火、抗震等特点，而利用陶粒混凝土制成的轻骨料混凝土板的强度更是大于40MPa，保温及耐热性较好；陶粒砼导热系数一般为较低，可进一步增强该复合防腐保温材料的保温性能。
上述方案具体的，所述防腐层4为UHMWPE，其厚度优选为5-10mm；其中，超高分子量聚乙烯英文名ultra-high molecular weight polyethylene(简称UHMWPE)；UHMWPE的强度是化纤中最高的，具有耐磨、耐冲击、耐腐蚀、耐光等优良性能，可以确保该复合防腐保温材料具有足够的防腐性能。
实施例二
参考图1，示出了一种建筑用复合防腐保温材料，包括从内到外依次设置的基层1、防潮层2、加固层3以及防腐层4；所述基层1为硅酸铝纤维板，所述防潮层2为岩棉板，所述加固层3为轻骨料混凝土板；所述硅酸铝纤维板通过聚合物防水砂浆与所述岩棉板连接，所述岩棉板通过聚合物防水砂浆与所述轻骨料混凝土板连接。
如此，该复合防腐保温材料利用硅酸铝纤维板的低热容量和低热导率的特点，达到保温的效果；利用岩棉板憎水性达到抗潮湿的效果，且岩棉板也具有导热系数低的特点，可以进一步加强保温效果；再利用轻骨料混凝土板加强整体结构的刚性，且尽量保持轻质；另外通过最***的防腐层4进行防腐保护。
上述方案具体的，所述硅酸铝纤维板的密度大于250kg/m3，所述硅酸铝纤维板的厚度为30-80mm。其中，硅酸铝纤维板的纤维分布均匀，保温性能稳定，且具有优良的吸音降噪性能，其设于内侧，可有效降低从室内传递到室外的声量。
上述方案具体的，所述岩棉板的厚度为20-40mm。其中，岩棉板具有大量的细长纤维，该些细长纤维形成了多孔连接结构，因此其具有出色的吸音降噪性能；同时，其憎水性可达99.9％，吸水率极低，无毛细渗透；岩棉按照ASTMC1104或ASTM1104M方法测试，质量吸湿率小于0.3％，其具有优异的防潮性能；并且，岩棉板的纤维细长柔韧，渣球含量低，导热系数低，具有极佳的保温性能。如此，所述岩棉板的吸音降噪性能和保温性能可以极好地加强所述硅酸铝纤维板的吸音降噪性能和保温性能，并使该复合防腐保温材料具备防潮性能。
上述方案具体的，所述轻骨料混凝土板由陶粒混凝土制成，所述陶粒混凝土的密度优选为900-1200kg/m3；所述轻骨料混凝土板的厚度优选为10-20mm。其中，轻骨料混凝土具有轻质、高强、保温、耐火、抗震等特点，而利用陶粒混凝土制成的轻骨料混凝土板的强度更是大于40MPa，保温及耐热性较好；陶粒砼导热系数一般为较低，可进一步增强该复合防腐保温材料的保温性能。
上述方案具体的，所述防腐层4为PTFE，其厚度优选为8-12mm；其中，聚四氟乙烯的英文名为Poly tetra fluoroethylene(简称为PTFE)；PTFE可在-180℃至260℃长期使用，具有优良的耐热耐寒性能，且其抗酸抗碱，几乎不溶于所有溶剂，因而具有极佳的耐腐蚀性能；可以确保该复合防腐保温材料具有足够的防腐性能。
以上所述仅为本发明的较佳实施方式而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种建筑用复合防腐保温材料，其特征在于，包括从内到外依次设置的基层、防潮层、加固层以及防腐层；所述基层为硅酸铝纤维板，所述防潮层为岩棉板，所述加固层为轻骨料混凝土板；所述硅酸铝纤维板通过聚合物防水砂浆与所述岩棉板连接，所述岩棉板通过聚合物防水砂浆与所述轻骨料混凝土板连接。
2.根据权利要求1所述的一种建筑用复合防腐保温材料，其特征在于，所述硅酸铝纤维板的密度大于250kg/m3，所述硅酸铝纤维板的厚度为30-80mm。
3.根据权利要求1所述的一种建筑用复合防腐保温材料，其特征在于，所述岩棉板的厚度为20-40mm。
4.根据权利要求1所述的一种建筑用复合防腐保温材料，其特征在于，所述轻骨料混凝土板由陶粒混凝土制成。
5.根据权利要求4所述的一种建筑用复合防腐保温材料，其特征在于，所述陶粒混凝土的密度900-1200kg/m3。
6.根据权利要求5所述的一种建筑用复合防腐保温材料，其特征在于，所述轻骨料混凝土板的厚度为10-20mm。
7.根据权利要求1所述的一种建筑用复合防腐保温材料，其特征在于，所述防腐层为UHMWPE。
8.根据权利要求7所述的一种建筑用复合防腐保温材料，其特征在于，所述防腐层的厚度为5-10mm。
9.根据权利要求1所述的一种建筑用复合防腐保温材料，其特征在于，所述防腐层为PTFE。
10.根据权利要求9所述的一种建筑用复合防腐保温材料，其特征在于，所述防腐层的厚度为8-12mm。