CN113338034A - Preparation method of modified cellulose facial mask base cloth with excellent moisturizing capability - Google Patents
Preparation method of modified cellulose facial mask base cloth with excellent moisturizing capability Download PDFInfo
- Publication number
- CN113338034A CN113338034A CN202110701576.0A CN202110701576A CN113338034A CN 113338034 A CN113338034 A CN 113338034A CN 202110701576 A CN202110701576 A CN 202110701576A CN 113338034 A CN113338034 A CN 113338034A
- Authority
- CN
- China
- Prior art keywords
- cellulose
- woven fabric
- preparation
- mask base
- carboxymethyl cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of natural polymer materials and cosmetics, and particularly relates to a preparation method of a modified cellulose facial mask base fabric with excellent moisturizing capability, which is characterized in that the cellulose facial mask base fabric is modified into a carboxymethyl cellulose woven fabric or non-woven fabric and contains high-content natural moisturizing ingredients as skin oil-soluble ingredients; the invention prepares carboxymethyl cellulose woven fabric or non-woven fabric which can be used for directly contacting with skin; the modified cellulose mask base cloth having excellent moisturizing ability is provided in a dry sheet form which is advantageous in maintaining the stability of soluble components in the skin and can be loaded with effective essences at a high content, uniformly disperse the effective essences by physical dispersion force upon contact with moisture and allow the effective absorption by the skin.
Description
Technical Field
The invention belongs to the field of natural polymer materials and cosmetics, and particularly relates to a preparation method of a modified cellulose facial mask base fabric with excellent moisturizing capability.
Background
Natural cellulose is the most abundant biological resource on the earth, and provides thousands of years of use value for human as a multifunctional, low-cost and renewable material; as an unlimited resource, cellulose can be repeatedly produced, decomposed, used and degraded according to the rules of nature; thus, cellulose derived from plants continues to become an energy source and be manufactured as a product as a renewable resource source; in particular, oxidized cellulose obtained by oxidizing such cellulose has an extremely strong ability to absorb moisture and store it, and is an optimum material as a material for the beauty field (e.g., mask base cloth).
As oxidized cellulose subjected to oxidation treatment, carboxymethyl cellulose (CMC) is a cellulose derivative, has recognized safety and efficacy, is simple to prepare, is biodegradable and harmless to a human body, and can replace all common non-woven fabric mask base fabrics appearing in the current market.
In particular, carboxymethyl cellulose (CMC) is a material obtained by reacting lignocellulose with NaOH alkali treatment of monochloroacetic acid (MCA), and has been widely used as a viscosity modifier and additive in the food industry, is safe and non-toxic, and has extremely high biocompatibility and use value.
Most of carboxymethyl cellulose (CMC) obtained by the above-mentioned method is in the form of powder, but when it is expanded to a wider range of applications such as cosmetic and medical uses, it is required to provide fibrous carboxymethyl cellulose such as carboxymethyl cellulose woven fabric, carboxymethyl cellulose nonwoven fabric and the like.
However, the methods for producing carboxymethyl cellulose woven fabrics and carboxymethyl cellulose nonwoven fabrics can only be produced in a laboratory scale, and currently, the total amount of industrial requirements of numerous production departments such as beauty treatment, medical treatment and the like is far from being met, so that the industrial production of carboxymethyl cellulose woven fabrics and carboxymethyl cellulose nonwoven fabrics is a problem which needs to be solved urgently at present.
In addition, in the case where a carboxymethyl cellulose woven fabric and a carboxymethyl cellulose non-woven fabric are used as a mask base fabric, there is no method of gradually releasing a functional active ingredient of a cosmetic onto the skin by uniformly mounting microcapsules of a polymer structure containing the functional ingredient of a skin care product on fibers.
Disclosure of Invention
In order to solve the above technical problems, there is provided a method for preparing a modified cellulose facial mask base fabric having excellent moisturizing ability, the production process of the facial mask base fabric using a technique of gelation of a natural cellulose derivative to prepare a carboxymethyl cellulose woven fabric or non-woven fabric that can be used in direct contact with the skin; the modified cellulose mask base cloth having excellent moisturizing ability is provided in a dry sheet form which is advantageous in maintaining the stability of soluble components in the skin and can be loaded with effective essences at a high content, uniformly disperse the effective essences by physical dispersion force upon contact with moisture and allow the effective absorption by the skin.
The specific technical scheme of the invention is as follows:
(a) the carboxymethyl cellulose woven or non-woven fabric is made of a material having a weight of 30 to 40 g/m2The method comprises the steps of immersing a cellulose woven fabric or a non-woven fabric into an alkali solution and padding for 30-60 min at 20-50 ℃;
(b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, curing for 30-60 min at 20-50 ℃ in order to dissociate hydrogen bonds of cellulose molecules;
(c) after the cellulose woven fabric or the non-woven fabric after dissociation is aged, a certain amount of carboxymethylation solution (monochloroacetic acid) is dissolved in a mixed solution of isopropanol and hyaluronic acid, and soaking is carried out for 30-90 min at the temperature of 50-80 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load;
(d) after the reaction is completed, washing twice or three times with a water washing solution of isopropyl alcohol and water to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
Preferably, the alkaline solution in the step (a) is 15-40% of NaOH, but if the concentration of the alkaline solution (NaOH) is less than 15%, the required substitution degree of the carboxymethyl cellulose cannot be obtained; if it exceeds 40%, the side reaction of NaOH is more and the substitution degree of carboxymethyl cellulose is too high, making it unsuitable for production; when the filling rate is less than 300%, the hydrophobic bond of the cellulose molecule is not sufficiently dissociated by the alkali, and thus the substitution degree of the hydrophilic carboxyl group is low, and when it exceeds 400%, the nonwoven fabric is damaged.
In the step (a), the carboxymethyl cellulose woven or nonwoven fabric of the present invention is composed of a material having a weight of 30 to 40 g/m2The low weight of the natural cellulose of (1) is obtained because if the weight range is out of the above range, gelation occurs upon contact with moisture, the degree is low and the mechanical properties are poor, and the preparation conditions are not preferred.
In the step (b), in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 30-60 min at 20-50 ℃; the aging temperature is performed at a lower temperature than the conventional continuous alkali treatment method, in which the reaction is insufficient if the aging temperature is lower than 20 ℃ and the reaction is rapidly and uniformly performed in the production of carboxymethyl cellulose if it exceeds 50 ℃.
Preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-97: 3, and the MCA content is 20-60%.
Compared with the prior art, the invention has the beneficial effects that:
the invention provides a modified cellulose facial mask base cloth with excellent moisturizing capability, wherein a dry film of the modified cellulose facial mask is changed into a semi-gel shape when meeting water; more effective in skin absorption due to excellent hydrogel properties, finely dispersed and dissolved in the skin by physical dispersion force upon contact with moisture; in the preparation process, the hyaluronic acid microspheres are added to the carboxymethyl cellulose woven or non-woven fabric fibers, so that the modified cellulose mask base cloth is endowed with excellent water retention capacity to a great extent; more specifically, the modified cellulose mask base fabric having excellent moisturizing ability of the present invention can ensure the stability and natural decomposition of the skin due to the use of the environment-and human-friendly cellulose material. And due to physical dispersion ability, the carboxymethyl cellulose woven or nonwoven fabric is uniformly dispersed in a state invisible to the naked eye and can be simply removed by washing with running water after use.
Detailed Description
The technical solution of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are some, not all, embodiments of the present invention; all other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
(a) The carboxymethyl cellulose of the present invention is woven or nonwoven fabric having a thickness of 30 g/m2A woven or nonwoven cellulose fabric is immersed in an alkali solution and padded at 30 ℃ for 60 min;
(b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 60 min at 30 ℃;
(c) after the cellulose woven fabric or the non-woven fabric after dissociation is aged, a certain amount of carboxymethylation solution (monochloroacetic acid) is dissolved in a mixed solution of isopropanol and hyaluronic acid, and soaking is carried out for 50 min at the temperature of 50 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load;
(d) after the reaction is completed, washing twice with a water washing solution of isopropyl alcohol and water is repeated to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
Preferably, the alkaline solution of step (a) is 40% NaOH;
preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-99: 1, and the MCA content is 60%.
Example 2
(a) The carboxymethyl cellulose of the present invention is woven or nonwoven fabric having a thickness of 34 g/m2A woven or nonwoven cellulose fabric is immersed in an alkali solution and padded at 20 ℃ for 30 min;
(b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 30 min at the temperature of 20 ℃;
(c) after the cellulose woven fabric or the non-woven fabric after dissociation is aged, a certain amount of carboxymethylation solution (monochloroacetic acid) is dissolved in a mixed solution of isopropanol and hyaluronic acid, and soaking is carried out for 30 min at the temperature of 70 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load;
(d) after the reaction is completed, washing with a water washing solution of isopropyl alcohol and water is repeated three times to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
Preferably, the alkaline solution of step (a) is 15% NaOH;
preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-98: 2, and the MCA content is 30%.
Example 3
(a) The carboxymethyl cellulose of the present invention is woven or nonwoven fabric having a weight of 40 g/m2Is made of natural cellulose with a low weight,immersing a cellulose woven fabric or a non-woven fabric in an alkali solution and padding for 40 min at 40 ℃;
(b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 40 min at the temperature of 45 ℃;
(c) after the cellulose woven fabric or the non-woven fabric after dissociation is aged, a certain amount of carboxymethylation solution (monochloroacetic acid) is dissolved in a mixed solution of isopropanol and hyaluronic acid, and soaking is carried out for 75 min at the temperature of 60 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load;
(d) after the reaction is completed, washing twice with a water washing solution of isopropyl alcohol and water is repeated to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
Preferably, the alkaline solution of step (a) is 20% NaOH;
preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-97.5: 2.5, and the MCA content is 50%.
Example 4
(a) The carboxymethyl cellulose of the present invention is woven or nonwoven fabric having a thickness of 38 g/m2A woven or nonwoven cellulose fabric is immersed in an alkaline solution and padded at 50 ℃ for 50 min;
(b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 55 min at 50 ℃;
(c) after the cellulose woven fabric or the non-woven fabric after dissociation is aged, a certain amount of carboxymethylation solution (monochloroacetic acid) is dissolved in a mixed solution of isopropanol and hyaluronic acid, and the mixture is soaked for 90 min at the temperature of 80 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load;
(d) after the reaction is completed, washing with a water washing solution of isopropyl alcohol and water is repeated three times to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
Preferably, the alkaline solution of step (a) is 30% NaOH;
preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-97: 3, and the MCA content is 20%.
Claims (6)
1. A preparation method of modified cellulose mask base cloth with excellent moisturizing capability is characterized by comprising the following steps: the production process of the mask base cloth utilizes the gelation technology of natural cellulose derivatives to prepare carboxymethyl cellulose woven fabric or non-woven fabric which can be directly contacted with skin; the modified cellulose mask base cloth having excellent moisturizing ability is provided in a dry sheet form which is advantageous in maintaining the stability of soluble components in the skin and can be loaded with effective essences at a high content, uniformly disperse the effective essences by physical dispersion force upon contact with moisture and allow the effective absorption by the skin.
2. The preparation method of the modified cellulose facial mask base cloth with excellent moisturizing capability according to claim 1, which comprises the following specific technical scheme: (a) the carboxymethyl cellulose woven or non-woven fabric is made of a material having a weight of 30 to 40 g/m2The method comprises the steps of immersing a cellulose woven fabric or a non-woven fabric into an alkali solution and padding for 30-60 min at 20-50 ℃; (b) after the cellulose woven fabric or the non-woven fabric is completely filled with alkali liquor, curing for 30-60 min at 20-50 ℃ in order to dissociate hydrogen bonds of cellulose molecules; (c) after the cellulose woven fabric or the non-woven fabric is aged after dissociation, the cellulose woven fabric or the non-woven fabric is passedDissolving a certain amount of carboxymethylated solution (monochloroacetic acid) in a mixed solution of isopropanol and hyaluronic acid, and soaking for 30-90 min at the temperature of 50-80 ℃; obtaining a carboxymethyl cellulose woven fabric or non-woven fabric with hyaluronic acid load; (d) after the reaction is completed, washing twice or three times with a water washing solution of isopropyl alcohol and water to remove unreacted substances in the natural cellulose derivative; at this time, phosphoric acid may be added during washing with water to adjust the pH to neutrality; after completion, the wet carboxymethyl cellulose woven or nonwoven fabric may be pressed using an automatic hand shaking and continuously dried at a temperature of 120 ℃ to obtain a dry sheet-like carboxymethyl cellulose woven or nonwoven fabric.
3. The preparation method of the modified cellulose mask base cloth with excellent moisturizing ability according to claim 2, wherein the preparation method comprises the following steps: using 15-40% NaOH as an alkaline solution in the step (a), but if the concentration of the alkaline solution (NaOH) is less than 15%, the required carboxymethyl cellulose substitution degree cannot be obtained; if it exceeds 40%, the side reaction of NaOH is more and the substitution degree of carboxymethyl cellulose is too high, making it unsuitable for production; when the filling rate is less than 300%, the hydrophobic bond of the cellulose molecule is not sufficiently dissociated by the alkali, and thus the substitution degree of the hydrophilic carboxyl group is low, and when it exceeds 400%, the nonwoven fabric is damaged.
4. The preparation method of the modified cellulose mask base cloth with excellent moisturizing ability according to claim 2, wherein the preparation method comprises the following steps: in the step (a), the carboxymethyl cellulose woven or nonwoven fabric of the present invention is composed of a material having a weight of 30 to 40 g/m2The low weight of the natural cellulose of (1) is obtained because if the weight range is out of the above range, gelation occurs upon contact with moisture, the degree is low and the mechanical properties are poor, and the preparation conditions are not preferred.
5. The preparation method of the modified cellulose mask base cloth with excellent moisturizing ability according to claim 2, wherein the preparation method comprises the following steps: in the step (b), in order to dissociate hydrogen bonds of cellulose molecules, curing is carried out for 30-60 min at 20-50 ℃; the aging temperature is performed at a lower temperature than the conventional continuous alkali treatment method, in which the reaction is insufficient if the aging temperature is lower than 20 ℃ and the reaction is rapidly and uniformly performed in the production of carboxymethyl cellulose if it exceeds 50 ℃.
6. The preparation method of the modified cellulose mask base cloth with excellent moisturizing ability according to claim 2, wherein the preparation method comprises the following steps: preferably, the ratio of isopropanol in step (c): the volume ratio of hyaluronic acid is controlled to be 99: 1-97: 3, and the MCA content is 20-60%.