CN1133316A - 道路用反光标志带及其粘合剂的配制方法 - Google Patents
道路用反光标志带及其粘合剂的配制方法 Download PDFInfo
- Publication number
- CN1133316A CN1133316A CN 96100713 CN96100713A CN1133316A CN 1133316 A CN1133316 A CN 1133316A CN 96100713 CN96100713 CN 96100713 CN 96100713 A CN96100713 A CN 96100713A CN 1133316 A CN1133316 A CN 1133316A
- Authority
- CN
- China
- Prior art keywords
- road
- reflecting
- acrylic resin
- mixing machine
- mark band
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种以天然橡胶、丙烯酸树脂为基料,再配以颜料(钛白粉或铬黄),填充料(碳酸钙、硫酸钡、滑石粉、云丹粉),添加剂(邻苯二甲酸二辛酯、硅烷偶联剂、机油),反光材料(如:玻璃微珠)按一定配比,工艺加工而成的新型道路安全标志——反光标志带,同时还相应配制:反光标志带与道路路面载体之间相粘附(合)的粘合剂。所用原料为市售原料。反光标志带成本低、使用寿命长、无污染、夜间可见度高。采用这种白色或黄色反光标志带及其粘合剂,在道路上施工质量好、作业效率高。
Description
本发明涉及一种化合物,尤其为一种以天然橡胶和丙烯酸树脂为基料,再配以颜料、填充料、添加剂、反光材料加工而成的新型道路安全标志——道路用反光标志带及其粘合剂的配制方法。
目前,国内外交通发展迅速,对于标志安全设施的要求也越来越高。原来,用于道路表面的标线标志主要为溶剂型与热溶型两大类。溶剂型涂料常温下涂刷,干燥慢(30分钟左右),寿命短(不到三个月),成本高(两年内综合成本高于100元/m2)等不足之处;热溶涂料又需加温至180°-220℃高温下才能施工,施工难度大,安全系数小(用火加热)污染大,受气温影响严重等不足之处。所以,这两种类型的道路标线,很难适应当今交通的需要。
本发明的目的在于克服以上已有技术中的不足之处,而提供一种“道路用反光标志带及其粘合剂的配制方法”,这种反光标志带生产设备不复杂、产品成本低、使用寿命长、无污染、夜间可见度高,其粘合剂为用于反光标志带与道路路面载体粘附在一起的特制专用粘合剂。
现将道路用反光标志带及其粘合剂的组成成份、配制方法及某些原材料特征分述如下:
一、道路用反光标志带:
1、组成成分: (重量百分比)
A、基料:
BC-08-S热塑性丙烯酸树脂 18-23
天然橡胶 7-10
B、颜料:
钛白粉或铬黄: 13-18
C、填充料:
碳酸钙 10-15
硫酸钡 6-12
滑石粉 15-20
云丹粉 1-3
D、反光材料:
玻璃微珠 18-23
E、添加剂:
邻本二甲酸二辛酯 1.5-3
硅烷偶联剂 0.5-1
机油 2-5
2、配制方法:
①、将机油、钛白粉(或铬黄)在小型混合机中混合均匀,备用,
②、将天然橡胶在炼胶机上塑炼10-15分钟,而后将①中的混合物加至炼胶机上混匀、塑炼,脱辊备用,
③、将丙烯酸树脂、填充料(四种料)、邻本二甲酸二辛酯硅烷偶联剂加入“∨”型混合机中混合均匀,
④、将②、③中混合物在炼胶机上混炼,脱辊出“毛带”,即带毛边的带条,也就是非成型的带子,
⑤、将毛带在压延机上压至1.5mm厚度、切成100-300mm宽的带子,
⑥、将100-300mm宽、1.5mm厚的带子,在输送带上用喷枪喷涂上“市售”的丙烯酸漆作为防滑层,并用植珠器植上反光材料——玻璃微珠,用卷带轮将加工过的带子卷成5m2/卷,至此,完成了反光标志带的配制过程(参看工艺流程图)。
3、原材料的特征:
①、基料:丙烯酸树脂必须用热塑性树脂,在常温下,树脂的涂4杯粘度,不得低于300秒,固含量不能低于52%,天然橡胶以泰国三号烟片为最佳,
②、颜料:钛白粉选用金红石型,要求折光率为1.7-2.7,铬黄选用深铬黄,色泽相当于GR,耐光性5级,水溶性、油渗性为1级,耐酸性、耐碱性为3级,
③、反光材料:玻璃微珠选用折光率为1.5以上,粒子直径为0.1-0.3mm,
④、填充料:细度选用300目,吸油量小于20。
现将生产道路用白色的和黄色的反光标志带实施例分述如下:
实施例1:道路用白色反光标志带的配制方法:
1、成分、配比: (重量百分比)
BC-08-S热塑性丙烯酸树脂 18
泰国三 号烟片天然橡胶 7
钛白粉 14
碳酸钙 13
硫酸钡 8
滑石粉 17
云丹粉 1
玻璃微珠 18
邻本二甲酸二辛脂 1.5
三甲氧基乙烯基硅烷 0.5
机油 2
2、配制方法同以上所述。
实施例2:道路用黄色反光标志带的配制方法:
1、成分、配比: (重量百分比)
BC-08-S热塑性丙烯树脂 18
泰国三号烟片 7
钛白粉 14
碳酸钙 13
硫酸钡 8
滑石粉 17
云丹粉 1
玻璃微珠 18
邻本二甲酸二辛脂 1.5
三甲氧基乙烯基硅烷 0.5
机油 22、配制方法同以上所述。二、道路反光标志带所用粘合剂的配制方法:1、组成的成分、配比: (重量百分比)①、基料:
BC-08-S丙烯酸树脂 45-55②、稀料:
甲苯 8-15
二甲苯 20-28
丙酮 5-8
醋酸乙酯 8-15
丁醇 5-8③、添加剂:
邻本二甲酸二丁酯: 0.5-2
钛酸酯偶联剂: 1.5-22:配制方法:
将上述的各种原材料依次按量加入至密闭的搅拌器中,混合均匀即成粘合剂。
3、材料特征:
①、基料:BC-08-S丙烯酸树脂系热塑性树脂,粘度(CPS)为250-1000、固含量为52%
②、钛酸酯:偶联剂的一种,粘度为250厘泊,可与烃类溶剂混合,加强标志带与路面的结合。
实施例3:道路用反光标志带与道路路面载体粘合时所用的粘合剂的配制方法(重量百分比)
1、成分、配比: (重量百分比)
BC-08-S丙烯酸树脂 45
邻本二甲酸二丁酯 0.5
钛酸酯偶联剂 1.5
二甲苯 23
丙酮 5
甲苯 10
醋酸乙酯 10
丁醇 5
2、配制方法同上述“道路用反光标志带粘合剂”的制法相同。
3、使用方法:将粘合剂作为底胶用毛刷、辊子、或喷涂在沥表路面、混凝土路面上(每公斤粘合剂可涂布3-5平方米),而后用反光标志带粘附上即可。
本发明积极效果:
1、道路用反光标志带在生产配制过程中所需用的设备、工具不复杂、建厂投资小,
2、所生产出的反光标志带,其原料均为市售原料,易购到。其产品的成本低、使用寿命长、无污染、夜间可见度高,
3、道路用粘合剂为用于:反光标志带与道路路面载体粘附在一起的特制专用粘合剂。其粘合剂易生产、成本低、所用原料为市售原料,易购到。其粘合剂在常温下可使用,且粘合性能好,不污染环境,
4、采用这种“道路用反光标志带及其粘合剂”,在道路上施工快、效率高,能适应改革开放年代高速发展“地面道路交通事业”的需要。
Claims (2)
1、一种道路用反光标志带,其特点是:
(1)、组成的成分: 重量百分比
A、基料:
BC-08-S热塑性丙烯酸树脂 18-23
天然橡胶 7-10
B、颜料:
钛白粉或铬黄: 13-18
C、填充料:
碳酸钙 10-15
硫酸钡 6-12
滑石粉 15-20
云丹粉 1-3
D、反光材料:
玻璃微珠 18-23
E、添加剂:
邻本二甲酸二辛酯 1.5-3.0
硅烷偶联剂 0.5-1.0
机油 2-5
(2)、配制方法:
①、将机油、钛白粉(或铬黄)在小型混合机中混合均匀,备用,
②、将天然橡胶在炼胶机上塑炼10-15分钟,而后将①中的混合物加至炼胶机上混匀、塑炼,脱滚备用,
③、将丙烯酸树脂、四种填充料、邻本二甲酸二辛酯、硅烷偶联剂(如:三甲氧基乙烯基硅烷),加入混合机中混合均匀,
④、将②、③中混合物在炼胶机上混炼,脱辊出“毛带”,
⑤、将毛带在压延机上压至1.5mm厚度、切成100-300mm宽的带子,
⑥、将100-300mm宽、1.5mm厚的带子在输送带上用喷枪喷涂上“市售”的丙烯酸漆作为防滑层,并用植珠器植上反光材料——玻璃微珠,用卷带轮将加工过的带子卷成5m2卷。
2、根据权利要求1所述的道路用反光标志带,其特点是这种白色或黄色反光标志带与道路路面载体粘附(合)时,需用一种特制专用粘合剂,该粘合剂的成分、配比(重量%):
①、基料:
BC-08-S丙烯酸树脂: 45-55
②、稀料:
甲苯 8-15
甲苯 20-28
丙酮: 5-2
醋酸乙酯: 8-15
丁醇: 5-8
③、添加剂:
邻本二甲酸二丁酯: 0.5-2.0
钛酸酯偶联剂: 1.5-2.0
该粘合剂的配制方法:
将上述①、③、②中的各种原料依次按比例量加入至密闭的搅拌器内,混合均匀即为所配制的粘合剂。