CN113305963A - Production process of composite batten keel for building - Google Patents
Production process of composite batten keel for building Download PDFInfo
- Publication number
- CN113305963A CN113305963A CN202110695248.4A CN202110695248A CN113305963A CN 113305963 A CN113305963 A CN 113305963A CN 202110695248 A CN202110695248 A CN 202110695248A CN 113305963 A CN113305963 A CN 113305963A
- Authority
- CN
- China
- Prior art keywords
- batten
- production process
- battens
- hot
- keel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of a composite batten keel for buildings, which comprises the production process of batten assembly, batten hot pressing, primary cooling, specification determination, fiber cloth coating, batten hot press molding and secondary cooling, wherein the batten assembly is to integrate and assemble battens to be processed, the batten hot pressing is to coat hot pressing glue between the assembled battens, and the assembled battens are hot pressed by a hot press, in the invention, when the composite batten keel is produced, the battens are cooled, so that the battens can enter the next working procedure more quickly, yarns in a yarn layer are vertically and crossly woven, the strength of the yarn layer can be better enhanced, the battens are measured in advance and the specification is determined, battens suitable for practical use can be directly produced, and the battens and the fiber cloth do not need to be cut after production, thereby reducing the loss of the fiber cloth.
Description
Technical Field
The invention relates to a production process of a composite batten keel for a building, and belongs to the technical field of buildings.
Background
A building keel is a building material for supporting modeling and fixing structures, and is generally applied to building systems needing to be reinforced by reinforced concrete and building construction architecture systems such as house buildings, bridge buildings, interior decoration and the like, the building keel is rich in types and can be divided into a traditional batten keel, a light steel keel, an aluminum alloy keel, a steel keel and the like according to different manufacturing materials, wherein the traditional batten keel is low in cost and light in weight and is widely used, however, the traditional batten keel is too low in strength and easy to corrode and damp, fibers or felt cloth can be coated outside a batten in order to improve the strength and avoid the damp corrosion, when the composite batten keel is produced, the composite batten keel can be cooled in order to enter the next working procedure more quickly, and yarns in a yarn layer are vertically and crosswise woven, the strength of the reinforcing yarn layer can be better, the battens are measured in advance, specifications are determined, and battens suitable for actual use can be directly produced.
Disclosure of Invention
The invention aims to provide a production process of a composite batten keel for a building, and aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme:
a production process of a composite batten keel for a building comprises the production process, wherein the production process comprises batten assembling, batten hot-pressing, primary cooling, specification determination, fiber cloth coating, batten hot-press forming and secondary cooling.
Furthermore, the batten assembly is to integrate and assemble the battens to be processed.
Further, the batten hot pressing is to coat hot-pressing glue among the assembled battens, and the assembled battens are hot-pressed through a hot press.
Further, the first cooling is to cool the hot-pressed battens through a cooling machine, so that the battens can enter the next working procedure more quickly.
Further, the specification determination is to measure the specification of the cooled wood strips, cut the wood strips to a preset specification through a cutting machine, and collect generated scraps through a dust collector during cutting.
Further, the fiber cloth is wrapped by arranging a yarn layer on the surface of the batten, the yarn layer is made by vertically and alternately weaving yarns, the yarn layer is fixed on the surface of the batten by using an adhesive, and the fiber cloth is wrapped outside the yarn layer.
Further, the batten is formed by hot-press molding, namely, the batten coated with the fiber cloth is subjected to hot-press molding treatment.
Further, the secondary cooling is to cool the hot-press formed battens through a cooling machine.
The invention has the beneficial effects that:
1. when the composite batten keel is produced, the battens are cooled, so that the battens can enter the next step more quickly, yarns in the yarn layers are vertically and crossly woven, and the strength of the yarn layers can be better enhanced.
2. The batten is measured in advance and the specification is confirmed, the batten suitable for actual use can be directly produced, the batten and the fiber cloth are not required to be cut after production, therefore, the loss of the fiber cloth can be reduced, and when the specification is confirmed and the cutting is carried out, the generated chips are collected through the dust collector, the pollution of the chips to the working environment during the cutting can be reduced, the cleaning of the chips is convenient, and the protection to workers can be better.
3. After flitch hot briquetting, through secondary cooling, make the staff can be faster arrange in order the compound flitch fossil fragments of production and place.
Drawings
The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the invention without limiting the invention.
FIG. 1 is a flow chart of a manufacturing process of the composite batten keel for building of the invention;
Detailed Description
The preferred embodiments of the present invention will be described in conjunction with the accompanying drawings, and it will be understood that they are described herein for the purpose of illustration and explanation and not limitation. In the description of the present invention, it should be noted that the terms "upper", "lower", "inner", "outer", "front", "rear", "both ends", "one end", "the other end", and the like indicate orientations or positional relationships based on those shown in the drawings, and are only for convenience of description and simplicity of description, but do not indicate or imply that the referred device or element must have a specific orientation, be constructed in a specific orientation, and be operated, and thus, should not be construed as limiting the present invention. Furthermore, the terms "first" and "second" are used for descriptive purposes only and are not to be construed as indicating or implying relative importance.
Referring to fig. 1, the present invention provides a technical solution: a production process of a composite batten keel for a building comprises the production process, wherein the production process comprises batten assembling, batten hot-pressing, primary cooling, specification determination, fiber cloth coating, batten hot-press forming and secondary cooling.
Specifically, as shown in fig. 1, the batten splicing is to integrate and splice battens to be processed.
Specifically, as shown in fig. 1, the batten hot pressing is to coat hot-pressing glue between the assembled battens, and the assembled battens are hot-pressed by a hot press.
Specifically, as shown in fig. 1, the primary cooling is to cool the hot-pressed battens by a cooling machine, so that the battens can enter the next step more quickly.
Specifically, as shown in fig. 1, confirm that the specification is for carrying out the specification measurement to the stuff after the cooling to pass through the cutting machine with the stuff and cut predetermined specification, directly produce the flitch that is applicable to in-service use, need not cut flitch and fibre cloth after the production, thereby can reduce the loss of fibre cloth, during the cutting, collect the piece that produces through the dust catcher, the pollution that the piece led to the fact operating environment when reducing the cutting, the clastic clearance of not only being convenient for, can also be better protect the staff.
Specifically, as shown in fig. 1, the fiber cloth cladding is to set up the yarn layer on the stuff surface, and the yarn layer is made for the perpendicular alternately weaving of yarn, the better intensity on yarn layer of strengthening to use gluing agent to fix the yarn layer on the stuff surface, with the fiber cloth cladding outside the yarn layer.
Specifically, as shown in fig. 1, the batten is formed by hot-press forming the batten coated with the fiber cloth.
Specifically, as shown in fig. 1, the secondary cooling cools off for the flitch through the cooler to hot briquetting, makes the staff can be faster arrange in order the compound flitch fossil fragments of production and place.
The above embodiments are preferred embodiments of the present invention, and those skilled in the art can make variations and modifications to the above embodiments, therefore, the present invention is not limited to the above embodiments, and any obvious improvements, substitutions or modifications made by those skilled in the art based on the present invention are within the protection scope of the present invention.
Claims (8)
1. A production process of a composite batten keel for buildings comprises the production process and is characterized in that: the production process comprises batten assembly, batten hot pressing, primary cooling, specification determination, fiber cloth coating, batten hot press forming and secondary cooling.
2. The production process of the composite batten keel for the building according to claim 1, wherein the production process comprises the following steps: and the batten splicing is to integrate and splice the battens to be processed.
3. The production process of the composite batten keel for the building according to claim 2, wherein the production process comprises the following steps: and the batten hot pressing is to coat hot-pressing glue among the assembled battens and carry out hot pressing on the assembled battens through a hot press.
4. The production process of the composite batten keel for the building according to claim 3, wherein the production process comprises the following steps: the primary cooling is to cool the hot-pressed battens through a cooling machine, so that the battens can enter the next step more quickly.
5. The production process of the composite batten keel for the building according to claim 4, wherein the production process comprises the following steps: and the determined specification is to measure the specification of the cooled wood strips, cut the wood strips to a preset specification through a cutting machine, and collect generated scraps through a dust collector during cutting.
6. The production process of the composite batten keel for the building according to claim 5, wherein the production process comprises the following steps: the fiber cloth is wrapped by arranging a yarn layer on the surface of the batten, the yarn layer is made by vertically and alternately weaving yarns, the yarn layer is fixed on the surface of the batten by using an adhesive, and the fiber cloth is wrapped outside the yarn layer.
7. The production process of the composite batten keel for the building according to claim 6, wherein the production process comprises the following steps: the batten hot-press molding is to carry out hot-press molding treatment on the battens coated with the fiber cloth.
8. The production process of the composite batten keel for buildings according to claim 7, is characterized in that: and the secondary cooling is to cool the hot-press formed battens through a cooling machine.