CN113135728A - 一种石膏基装饰砂浆及其制备方法 - Google Patents
一种石膏基装饰砂浆及其制备方法 Download PDFInfo
- Publication number
- CN113135728A CN113135728A CN202110449430.1A CN202110449430A CN113135728A CN 113135728 A CN113135728 A CN 113135728A CN 202110449430 A CN202110449430 A CN 202110449430A CN 113135728 A CN113135728 A CN 113135728A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- parts
- decorative mortar
- based decorative
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种石膏基装饰砂浆及其制备方法,所述砂浆按重量份数计算,包括建筑石膏粉80‑95份、铝酸盐水泥5‑20份和氨基纤维素2‑5份,其中所述建筑石膏粉可以采用脱硫石膏、磷石膏、钛石膏和原石膏中的一种生产制得,通过将建筑石膏粉粉碎过筛后与氨基纤维素混合即可得到本发明的石膏基装饰砂浆。本发明采用具有一定反应除醛效果的氨基纤维素作为缓凝剂和保水剂,可以使砂浆自身具有一定反应除醛作用,同时不会影响砂浆的其他性能,具有良好的应用前景。
Description
技术领域
本发明涉及建筑材料技术领域,尤其涉及一种石膏基装饰砂浆及其制备方法。
背景技术
装饰砂浆是应用涂刷在建筑墙面表层起到装饰作用的一类砂浆,适用于建筑、装修工程的内外墙等墙面处理。
随着家庭住房需求的增加,很多家庭的房间都选择采用精装修处理,由于房屋装修时需要用到各种涂料和粘接用胶料,这些涂料和胶料中难免会使用到甲醛作为溶剂,甲醛作为致癌物,其毒性较大,且甲醛的挥发过程极为缓慢,长期生活在甲醛含量偏高的环境中存在健康隐患,为了有效降低室内空气中的甲醛含量,一般采用甲醛去除剂,但是甲醛去除剂的有效时间太短,采用长效缓释去甲醛物质则无法及时对空气中的甲醛进行去除,甲醛从释放到被中和吸收仍然存在一个时间差。
通过改变装饰砂浆的配方达到对甲醛进行反应去除成为一种新的解决思路。
发明内容
有鉴于此,本发明提出了一种能够对甲醛进行吸附去除的石膏基装饰砂浆及其制备方法。
本发明的技术方案是这样实现的:本发明提供了一种石膏基装饰砂浆,按重量份数计算,其包括:
在以上技术方案的基础上,优选的,还包括碳酸氢铵0.2-0.5份。
在以上技术方案的基础上,优选的,还包括硅藻土10-20份。
在以上技术方案的基础上,优选的,所述硅藻土经过改性处理,改性处理的方法包括,将硅藻土与三聚氰胺混合后进行球磨处理,得到改性硅藻土。
更进一步优选的,以上改性处理方法中,所述硅藻土经过活化预处理,活化方法包括将硅藻土在0.5-2(wt)%的硫酸水溶液中浸泡,并加热至90-95℃,保温搅拌处理1-2h,得到活化硅藻土。
进一步优选的,球磨处理的球料比为(10-15):1。
在以上技术方案的基础上,优选的,所述硅藻土:三聚氰胺的用量比为1:(0.5-1.5)。
在以上技术方案的基础上,优选的,所述建筑石膏粉为β半水建筑石膏粉。
在以上技术方案的基础上,优选的,所述建筑石膏粉可以是脱硫石膏、磷石膏、钛石膏、原始稿等生产得到的石膏粉。
在以上技术方案的基础上,优选的,还包括多磷酸铵1-3份,其中所述多磷酸铵为三聚磷酸铵或四聚磷酸铵。
在以上技术方案的基础上,优选的,所述氨基纤维素为交联醇胺纤维素、二乙氨基乙基纤维素和三乙氨基乙基纤维素中的一种。
在以上技术方案的基础上,优选的,所述色粉为常见的颜料色粉,包括钛白粉、氧化锌、锌钡白、镉红、铁红、甲苯胺红、镉黄、铁黄、铅铬黄、氧化铬绿、铬绿、铁栏、群青、酞菁等。
本发明还提供一种石膏基装饰砂浆的制备方法,其特征在于,包括如下步骤:
步骤一、将建筑石膏粉原料粉碎过筛后加入至研磨机中研磨,得到建筑石膏粉粉料;
步骤二、向建筑石膏粉粉料中加入其他辅料按照重量配比进行混合研磨,研磨完毕得到石膏基装饰砂浆。
本发明的石膏基装饰砂浆及其制备方法相对于现有技术具有以下有益效果:
(1)本发明的石膏基装饰砂浆采用氨基纤维素作为基础辅助添加剂,其具有一定的缓凝作用和保水作用,可以满足建筑石膏粉砂浆的性能需求,同时氨基纤维素对甲醛具有天然的吸附能力,与常规缓释除醛成分的装饰砂浆不同,本发明从原料出发,无线缓释,即可满足除甲醛的需求,同时氨基纤维素所具备的缓凝和保水作用也能直接改善石膏基装饰砂浆的性能;
(2)为了进一步改善石膏基装饰砂浆的长效除醛效果,本发明还在原料中加入了碳酸氢铵,碳酸氢铵可以缓慢分解出部分氨气,氨气能够甲醛反应,从而中和甲醛达到除醛的目的;
(3)在加入碳酸氢铵的同时,本申请中还加入了硅藻土,硅藻土一方面可以作为填料,另一方面,硅藻土作为载体成分可以承载部分吸醛成分,本申请中采用三聚氰胺作为改性剂,三聚氰胺具有良好的甲醛反应吸附性能,将其作为改性剂与硅藻土进行混合,可以利用硅藻土的多孔吸附性能达到吸附三聚氰胺的目的,同时在硅藻土可以吸附甲醛,从而促进三聚氰胺与甲醛反应;
(4)由于甲醛吸附剂以及对应缓释物料的加入,装饰砂浆使用性能以及固化后砂浆的机械性能均受到影响,为了改善该缺陷,本申请还加入了多磷酸铵作为改性剂多磷酸铵的加入不仅改善了β半水建筑石膏粉固化后机械性能差的问题,同时还延长了其可操作时间,提高了缓凝效果,使本发明的装饰砂浆具有良好的使用性能;
(5)本发明的装饰砂浆中可以加入不同颜色的色粉,从而使装饰砂浆具有良好的装饰效果。
具体实施方式
下面将结合本发明实施方式,对本发明实施方式中的技术方案进行清楚、完整地描述,显然,所描述的实施方式仅仅是本发明一部分实施方式,而不是全部的实施方式。基于本发明中的实施方式,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施方式,都属于本发明保护的范围。
实施例1
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取80份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入2份交联醇胺纤维素、5份铝酸盐水泥和5份色粉,研磨混合均匀,得到石膏基装饰砂浆。
实施例2
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取85份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入3份二乙氨基乙基纤维素、10份铝酸盐水泥、4份色粉和0.2份碳酸氢铵,研磨混合均匀,得到石膏基装饰砂浆。
实施例3
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取90份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入4份三乙氨基乙基纤维素、15份铝酸盐水泥、3份色粉和10份硅藻土,研磨混合均匀,得到石膏基装饰砂浆。
实施例4
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取90份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入4份交联醇胺纤维素、20份铝酸盐水泥、0.3份碳酸氢铵、2份色粉和10份硅藻土,研磨混合均匀,得到石膏基装饰砂浆。
实施例5
称取20份硅藻土,浸没在0.5wt%的的硫酸水溶液中,加热至90℃,保温搅拌1h,得到活化硅藻土,将活化硅藻土干燥。
分别称取20份活化处理后的硅藻土和1份三聚氰胺,混合后加入到球磨机中进行球磨处理,球料比为10:1,球磨处理2h,得到改性硅藻土。
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取95份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入5份二乙氨基乙基纤维素、15份铝酸盐水泥、1份色粉和15份改性硅藻土,研磨混合均匀,得到石膏基装饰砂浆。
实施例6
称取20份硅藻土,浸没在1wt%的的硫酸水溶液中,加热至92℃,保温搅拌1.5h,得到活化硅藻土,将活化硅藻土干燥。
分别称取20份活化处理后的硅藻土和2份三聚氰胺,混合后加入到球磨机中进行球磨处理,球料比为15:1,球磨处理2h,得到改性硅藻土。
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取90份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入5份三乙氨基乙基纤维素、15份铝酸盐水泥、15份改性硅藻土、0.5份色粉和1份三聚磷酸铵,研磨混合均匀,得到石膏基装饰砂浆。
实施例7
称取20份硅藻土,浸没在2wt%的的硫酸水溶液中,加热至95℃,保温搅拌1.5h,得到活化硅藻土,将活化硅藻土干燥。
分别称取20份活化处理后的硅藻土和3份三聚氰胺,混合后加入到球磨机中进行球磨处理,球料比为12:1,球磨处理2h,得到改性硅藻土。
将β半水建筑石膏粉,加入到粉碎机中,粉碎后过筛,取90份过筛后的β半水建筑石膏粉,加入到研磨机中进行研磨,再加入5份交联醇胺纤维素、15份铝酸盐水泥、15份改性硅藻土、0.05份色粉和3份四聚磷酸铵,研磨混合均匀,得到石膏基装饰砂浆。
对比例1
采用市售石膏基装饰砂浆干混砂浆作为对比例。
分别将上述实施例1-7以及对比例1的石膏基装饰砂浆与拌合水进行混合,配置成砂浆,分别对八组砂浆进行凝结时间、保水率、抗折强度和抗压强度的测试,以比对相互之间的使用性能和机械强度,具体结果如下表所示:
同时,分别将实施例1-7以及对比例1的石膏基装饰砂浆与拌合水进行混合,配置成砂浆,涂刷在八个房间内,房间的面积相同,涂刷的厚度一致,同时设置第九个房间作为空白对照,在房间内中央位置放置一广口瓶,瓶内装入甲醛,检测房间内的甲醛含量,分别得到如下数据:
综上,采用本发明的石膏基装饰砂浆不仅具有良好的使用性能和机械强度,同时还具有较强的甲醛吸附效果,相比常规的物理吸附而言,本发明的吸附效果更佳持久,除醛率较高。
以上所述仅为本发明的较佳实施方式而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (9)
2.如权利要求1所述的石膏基装饰砂浆,其特征在于,还包括碳酸氢铵0.2-0.5份。
3.如权利要求1所述的石膏基装饰砂浆,其特征在于,还包括硅藻土10-20份。
4.如权利要求3所述的石膏基装饰砂浆,其特征在于,所述硅藻土经过改性处理,改性处理方法包括,将硅藻土与三聚氰胺混合后进行球磨处理,得到改性硅藻土。
5.如权利要求4所述的石膏基装饰砂浆,其特征在于,所述硅藻土:三聚氰胺的用量比为1:(0.5-1.5)。
6.如权利要求1所述的石膏基装饰砂浆,其特征在于,所述建筑石膏粉为β半水建筑石膏粉。
7.如权利要求1所述的石膏基装饰砂浆,其特征在于,还包括多磷酸铵1-3份。
8.如权利要求1所述的石膏基装饰砂浆,其特征在于,所述氨基纤维素为交联醇胺纤维素、二乙氨基乙基纤维素和三乙氨基乙基纤维素中的一种。
9.如权利要求1-8中任一所述的石膏基装饰砂浆的制备方法,其特征在于,包括如下步骤:
步骤一、将建筑石膏粉原料粉碎过筛后加入至研磨机中研磨,得到建筑石膏粉粉料;
步骤二、向建筑石膏粉粉料中加入其他辅料按照重量配比进行混合研磨,研磨完毕得到石膏基装饰砂浆。