CN113024957A - Easy-to-clean ethylene propylene diene monomer sizing material - Google Patents
Easy-to-clean ethylene propylene diene monomer sizing material Download PDFInfo
- Publication number
- CN113024957A CN113024957A CN201911355603.2A CN201911355603A CN113024957A CN 113024957 A CN113024957 A CN 113024957A CN 201911355603 A CN201911355603 A CN 201911355603A CN 113024957 A CN113024957 A CN 113024957A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene propylene
- diene monomer
- propylene diene
- easy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an easy-to-clean ethylene propylene diene monomer sizing material, and belongs to the technical field of chemical industry. It has solved prior art and has had the clean frequent problem of mould. The easy-to-clean ethylene propylene diene monomer rubber material comprises the following components: 512F ethylene propylene diene monomer: 80-110 parts; zinc oxide: 3-8 parts; stearic acid: 1 part; an anti-aging agent CPL: 1 part; n550 carbon black: 60-80 parts; naphthenic oil: 10-25 parts; lubricant LUBE-2: 2-4 parts; a flowing exhaust agent: 1-2 parts; accelerator EG-4: 3.5 parts; and (3) sulfur: 1.5 parts. The easily cleaned ethylene propylene diene monomer rubber material can reduce the cleaning frequency of a die.
Description
Technical Field
The invention belongs to the technical field of chemical industry, and relates to an easy-to-clean ethylene propylene diene monomer sizing material.
Background
When the mould is used for preparing the ethylene propylene diene monomer sizing material workpiece, the ethylene propylene diene monomer sizing material is easy to pollute the mould.
Therefore, the mold needs to be cleaned regularly. Because epdm compounds are more contaminating to the mold, the mold typically needs to be cleaned once a week. Frequent die cleaning affects production efficiency and improves production cost.
Disclosure of Invention
The invention aims to provide an easy-to-clean ethylene propylene diene monomer rubber material with good cleaning effect aiming at the problems in the prior art.
The purpose of the invention can be realized by the following technical scheme:
an easy-to-clean ethylene propylene diene monomer rubber material is characterized by comprising the following components:
512F ethylene propylene diene monomer: 80-110 parts;
zinc oxide: 3-8 parts;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 60-80 parts;
naphthenic oil: 10-25 parts;
lubricant LUBE-2: 2-4 parts;
a flowing exhaust agent: 1-2 parts;
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
The easy-to-clean ethylene propylene diene monomer rubber material comprises the following components:
512F ethylene propylene diene monomer: 100 parts of (A);
zinc oxide: 5 parts of a mixture;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 70 parts of (B);
naphthenic oil: 20 parts of (1);
lubricant LUBE-2: 3 parts of a mixture;
a flowing exhaust agent: 2 parts of (1);
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
Compared with the prior art, the easy-to-clean ethylene propylene diene monomer rubber material contains the lubricant and the flow exhaust meter in the components, so that the cleaning time of a die is prolonged to three months, the production efficiency is effectively improved, and the production cost is reduced.
Meanwhile, under the action of other components, the ethylene propylene diene monomer rubber material remained on the die is convenient to clean, and has high practical value.
Detailed Description
Example one
The easy-to-clean ethylene propylene diene monomer rubber material comprises the following components:
512F ethylene propylene diene monomer: 80 parts of a mixture;
zinc oxide: 3 parts of a mixture;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 60 parts;
naphthenic oil: 10 parts of (A);
lubricant LUBE-2: 2 parts of (1);
a flowing exhaust agent: 1 part;
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
Aiming at the defect that ethylene propylene diene monomer rubber material is easy to pollute a mould, a lubricant and a flowing exhaust agent are applied to the formula through the optimized combination of the formula. The mold is cleaned once a week during the previous product vulcanization, and the mold is cleaned once in three months, so that the production efficiency is improved, and the production cost is reduced.
Example two
The easy-to-clean ethylene propylene diene monomer rubber material comprises the following components:
512F ethylene propylene diene monomer: 110 parts of (A);
zinc oxide: 8 parts of a mixture;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 80 parts of a mixture;
naphthenic oil: 25 parts of (1);
lubricant LUBE-2: 4 parts of a mixture;
a flowing exhaust agent: 2 parts of (1);
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
Aiming at the defect that ethylene propylene diene monomer rubber material is easy to pollute a mould, a lubricant and a flowing exhaust agent are applied to the formula through the optimized combination of the formula. The mold is cleaned once a week during the previous product vulcanization, and the mold is cleaned once in three months, so that the production efficiency is improved, and the production cost is reduced.
EXAMPLE III
The easy-to-clean ethylene propylene diene monomer rubber material comprises the following components:
512F ethylene propylene diene monomer: 100 parts of (A);
zinc oxide: 5 parts of a mixture;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 70 parts of (B);
naphthenic oil: 20 parts of (1);
lubricant LUBE-2: 3 parts of a mixture;
a flowing exhaust agent: 2 parts of (1);
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
Aiming at the defect that ethylene propylene diene monomer rubber material is easy to pollute a mould, a lubricant and a flowing exhaust agent are applied to the formula through the optimized combination of the formula. The mold is cleaned once a week during the previous product vulcanization, and the mold is cleaned once in three months, so that the production efficiency is improved, and the production cost is reduced.
Claims (2)
1. An easy-to-clean ethylene propylene diene monomer rubber material is characterized by comprising the following components:
512F ethylene propylene diene monomer: 80-110 parts;
zinc oxide: 3-8 parts;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 60-80 parts;
naphthenic oil: 10-25 parts;
lubricant LUBE-2: 2-4 parts;
a flowing exhaust agent: 1-2 parts;
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.
2. The easy-to-clean ethylene propylene diene monomer compound according to claim 1, comprising the following components:
512F ethylene propylene diene monomer: 100 parts of (A);
zinc oxide: 5 parts of a mixture;
stearic acid: 1 part;
an anti-aging agent CPL: 1 part;
n550 carbon black: 70 parts of (B);
naphthenic oil: 20 parts of (1);
lubricant LUBE-2: 3 parts of a mixture;
a flowing exhaust agent: 2 parts of (1);
accelerator EG-4: 3.5 parts;
and (3) sulfur: 1.5 parts.