CN113013372A - Preparation method of aqueous anode and cathode slurry of lithium ion battery - Google Patents
Preparation method of aqueous anode and cathode slurry of lithium ion battery Download PDFInfo
- Publication number
- CN113013372A CN113013372A CN202110198046.9A CN202110198046A CN113013372A CN 113013372 A CN113013372 A CN 113013372A CN 202110198046 A CN202110198046 A CN 202110198046A CN 113013372 A CN113013372 A CN 113013372A
- Authority
- CN
- China
- Prior art keywords
- stirring
- stirrer
- negative electrode
- conductive agent
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of aqueous anode and cathode slurry of a lithium ion battery, which comprises the following steps: 1) the lithium ion battery aqueous anode slurry comprises 1-2 parts of aqueous binder, 6-8 parts of distilled water, 2-4 parts of anode conductive agent, 1-3 parts of anode active substance, 0.5-0.8 part of dispersant, 70-80 parts of organic solvent and 3-8 parts of thickener, 2) the lithium ion battery aqueous cathode slurry comprises 2-3 parts of aqueous binder, 7-8 parts of distilled water, 3-5 parts of cathode conductive agent, 0.8-1.5 parts of cathode active substance, 0.2-0.7 part of dispersant, 75-85 parts of organic solvent and 2-4 parts of thickener, the lithium ion battery aqueous anode and cathode slurry prepared by the method has uniform texture, meanwhile, the vibrating motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that bubbles in the slurry can be discharged conveniently, and the quality of the lithium ion battery aqueous anode and cathode slurry is ensured.
Description
Technical Field
The invention relates to the technical field of lithium battery slurry, in particular to a preparation method of aqueous anode and cathode slurry of a lithium ion battery.
Background
The lithium ion battery is used as a novel energy source with high voltage, high specific energy, long cycle life, environmental protection and no pollution, and is widely applied to portable electronic equipment, electric vehicles and energy storage equipment. With the increasing share of lithium ion batteries in the new energy market, researchers of lithium ion battery technology are increasing, and the requirements on the performance and safety of the lithium ion batteries are also increasing. Among them, the uniformity and stability of the electrode slurry have a great influence on the performance of the lithium ion battery. For a lithium ion battery, it is mainly composed of a positive electrode, a negative electrode, and a separator. Wherein the negative electrode comprises a copper foil as a current collector and an active film layer attached thereto. The composition of the upper film layer of the current collector is a negative active material, a conductive agent, a dispersing agent and a binder, which are dissolved in a solvent according to a certain proportion, thereby forming slurry for coating the negative electrode. At present, the negative electrode slurry is generally prepared by adding a binder, a solvent, a conductive electrode, active material powder and the like into a container at one time, and then stirring to prepare slurry, or by adding the negative electrode active material, the binder and the like in multiple times, and preparing the slurry by using a high-speed stirring method.
The texture of the aqueous positive and negative electrode paste of the lithium ion battery prepared by the existing preparation method of the aqueous positive and negative electrode paste of the lithium ion battery is not uniform enough, and meanwhile, bubbles easily exist, so that a preparation method of the aqueous positive and negative electrode paste of the lithium ion battery is urgently needed to be designed.
Disclosure of Invention
The invention aims to provide a preparation method of aqueous anode and cathode slurry of a lithium ion battery, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme:
a preparation method of aqueous anode and cathode slurry of a lithium ion battery comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 1-2 parts of aqueous binder, 6-8 parts of distilled water, 2-4 parts of anode conductive agent, 1-3 parts of anode active substance, 0.5-0.8 part of dispersant, 70-80 parts of organic solvent and 3-8 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring conditions of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
2) The lithium ion battery aqueous negative electrode slurry comprises 2-3 parts of aqueous binder, 7-8 parts of distilled water, 3-5 parts of negative electrode conductive agent, 0.8-1.5 parts of negative electrode active substance, 0.2-0.7 part of dispersant, 75-85 parts of organic solvent and 2-4 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring conditions of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
Compared with the prior art, the invention has the beneficial effects that: the lithium ion battery aqueous positive and negative electrode slurry prepared by the method is uniform in texture, and meanwhile, the vibrating motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that bubbles in the slurry are conveniently discharged, and the quality of the lithium ion battery aqueous positive and negative electrode slurry is ensured.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
In the embodiment of the invention, a preparation method of aqueous anode and cathode slurry of a lithium ion battery comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 1-2 parts of aqueous binder, 6-8 parts of distilled water, 2-4 parts of anode conductive agent, 1-3 parts of anode active substance, 0.5-0.8 part of dispersant, 70-80 parts of organic solvent and 3-8 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring conditions of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 50-60 ℃, and the liquid temperature is immediately detected by a temperature detector;
the positive electrode conductive agent and the positive electrode active material in step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of positive electrode conductive agent and positive electrode active substance into a ball mill;
step two: opening the ball mill to grind the positive electrode conductive agent and the positive electrode active substance for 30-45 min;
step three: filtering the ground positive electrode conductive agent and the positive electrode active substance for three times by using a 500-plus 800-mesh screen;
step four: and collecting the positive electrode conductive agent and the positive electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the vibration motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the aqueous anode slurry of the lithium ion battery is ensured.
The water-based binder is polyacrylonitrile,
the positive electrode conductive agent is conductive graphite;
the positive active material is lithium manganate;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
2) The lithium ion battery aqueous negative electrode slurry comprises 2-3 parts of aqueous binder, 7-8 parts of distilled water, 3-5 parts of negative electrode conductive agent, 0.8-1.5 parts of negative electrode active substance, 0.2-0.7 part of dispersant, 75-85 parts of organic solvent and 2-4 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring condition of the negative electrode conductive agent and the negative electrode active substance in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 50-60 ℃, and the liquid temperature is immediately detected by a temperature detector;
the anode conductive agent and the anode active material in the step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of negative electrode conductive agent and negative electrode active substance into a ball mill;
step two: opening a ball mill to grind the negative electrode conductive agent and the negative electrode active substance for 30-45 min;
step three: filtering the ground negative electrode conductive agent and the ground negative electrode active substance for three times by using a 500-800-mesh screen;
step four: and collecting the negative electrode conductive agent and the negative electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the stirring barrel of the stirring machine is driven to vibrate by the vibration motor, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the lithium ion battery aqueous negative electrode slurry is ensured.
The water-based binder is polyacrylonitrile,
the negative electrode conductive agent is conductive graphite;
the negative active material is natural graphite;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
Example one
A preparation method of aqueous anode and cathode slurry of a lithium ion battery comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 1 part of aqueous binder, 6 parts of distilled water, 2 parts of anode conductive agent, 1 part of anode active substance, 0.5 part of dispersant, 70 parts of organic solvent and 3 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200r/min, and the stirring time is 10min, so as to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500r/min, the stirring time is 30min, observing the stirring condition of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000r/min, and the stirring time is 45min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800r/min, and the stirring time is 50min, so that the aqueous anode slurry of the lithium ion battery is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 50 ℃, and the liquid temperature is immediately detected by a temperature detector;
the positive electrode conductive agent and the positive electrode active material in step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of positive electrode conductive agent and positive electrode active substance into a ball mill;
step two: opening the ball mill to grind the positive electrode conductive agent and the positive electrode active substance for 30-45 min;
step three: filtering the ground positive electrode conductive agent and the positive electrode active substance for three times by using a 500-plus 800-mesh screen;
step four: and collecting the positive electrode conductive agent and the positive electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the vibration motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the aqueous anode slurry of the lithium ion battery is ensured.
The water-based binder is polyacrylonitrile,
the positive electrode conductive agent is conductive graphite;
the positive active material is lithium manganate;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
2) The lithium ion battery aqueous negative electrode slurry comprises 2 parts of aqueous binder, 7 parts of distilled water, 3 parts of negative electrode conductive agent, 0.8 part of negative electrode active substance, 0.2 part of dispersant, 75-85 parts of organic solvent and 2 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200r/min, and the stirring time is 10min, so as to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active material into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500r/min, the stirring time is 30min, observing the stirring condition of the negative electrode conductive agent and the negative electrode active material in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active material are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000r/min, and the stirring time is 45min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800r/min, and the stirring time is 50min, so that the lithium ion battery aqueous negative electrode slurry is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 50 ℃, and the liquid temperature is immediately detected by a temperature detector;
the anode conductive agent and the anode active material in the step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of negative electrode conductive agent and negative electrode active substance into a ball mill;
step two: opening a ball mill to grind the negative electrode conductive agent and the negative electrode active substance for 30-45 min;
step three: filtering the ground negative electrode conductive agent and the negative electrode active substance for three times by using a 500-mesh screen;
step four: and collecting the negative electrode conductive agent and the negative electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the stirring barrel of the stirring machine is driven to vibrate by the vibration motor, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the lithium ion battery aqueous negative electrode slurry is ensured.
The water-based binder is polyacrylonitrile,
the negative electrode conductive agent is conductive graphite;
the negative active material is natural graphite;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
Example two
A preparation method of aqueous anode and cathode slurry of a lithium ion battery comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 2 parts of aqueous binder, 8 parts of distilled water, 4 parts of anode conductive agent, 3 parts of anode active substance, 0.8 part of dispersant, 80 parts of organic solvent and 8 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1500r/min, and the stirring time is 30min, so as to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 700r/min, the stirring time is 60min, observing the stirring condition of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1200r/min, and the stirring time is 60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 1100r/min, and the stirring time is 80min, so that the aqueous anode slurry of the lithium ion battery is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 60 ℃, and the liquid temperature is immediately detected by a temperature detector;
the positive electrode conductive agent and the positive electrode active material in step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of positive electrode conductive agent and positive electrode active substance into a ball mill;
step two: opening the ball mill to grind the positive electrode conductive agent and the positive electrode active substance for 30-45 min;
step three: filtering the ground positive electrode conductive agent and the positive electrode active substance for three times by using a 800-mesh screen;
step four: and collecting the positive electrode conductive agent and the positive electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the vibration motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the aqueous anode slurry of the lithium ion battery is ensured.
The water-based binder is polyacrylonitrile,
the positive electrode conductive agent is conductive graphite;
the positive active material is lithium manganate;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
2) The lithium ion battery aqueous negative electrode slurry comprises 3 parts of aqueous binder, 8 parts of distilled water, 5 parts of negative electrode conductive agent, 1.5 parts of negative electrode active substance, 0.7 part of dispersant, 85 parts of organic solvent and 4 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1500r/min, and the stirring time is 30min, so as to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active material into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 700r/min, the stirring time is 60min, observing the stirring condition of the negative electrode conductive agent and the negative electrode active material in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active material are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1200r/min, and the stirring time is 60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 1100r/min, and the stirring time is 80min, so that the aqueous negative electrode slurry of the lithium ion battery is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 60 ℃, and the liquid temperature is immediately detected by a temperature detector;
the anode conductive agent and the anode active material in the step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of negative electrode conductive agent and negative electrode active substance into a ball mill;
step two: opening a ball mill to grind the negative electrode conductive agent and the negative electrode active substance for 30-45 min;
step three: filtering the ground negative electrode conductive agent and the negative electrode active substance for three times by using a 800-mesh screen;
step four: and collecting the negative electrode conductive agent and the negative electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the stirring barrel of the stirring machine is driven to vibrate by the vibration motor, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the lithium ion battery aqueous negative electrode slurry is ensured.
The water-based binder is polyacrylonitrile,
the negative electrode conductive agent is conductive graphite;
the negative active material is natural graphite;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
EXAMPLE III
A preparation method of aqueous anode and cathode slurry of a lithium ion battery comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 1.5 parts of aqueous binder, 7 parts of distilled water, 3 parts of anode conductive agent, 2 parts of anode active substance, 0.7 part of dispersant, 75 parts of organic solvent and 5 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1300r/min, and the stirring time is 15min, so as to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 600r/min, the stirring time is 50min, observing the stirring condition of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1100r/min, and the stirring time is 50min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000r/min, and the stirring time is 60min, so that the lithium ion battery aqueous anode slurry is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 55 ℃, and the liquid temperature is immediately detected by a temperature detector;
the positive electrode conductive agent and the positive electrode active material in step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of positive electrode conductive agent and positive electrode active substance into a ball mill;
step two: opening the ball mill to grind the positive electrode conductive agent and the positive electrode active substance for 30-45 min;
step three: filtering the ground positive electrode conductive agent and the positive electrode active substance for three times by using a 700-mesh screen;
step four: and collecting the positive electrode conductive agent and the positive electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the vibration motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the aqueous anode slurry of the lithium ion battery is ensured.
The water-based binder is polyacrylonitrile,
the positive electrode conductive agent is conductive graphite;
the positive active material is lithium manganate;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
2) The lithium ion battery aqueous negative electrode slurry comprises 1.5 parts of aqueous binder, 7.5 parts of distilled water, 4 parts of negative electrode conductive agent, 1.2 parts of negative electrode active substance, 0.5 part of dispersant, 80 parts of organic solvent and 3 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1400r/min, and the stirring time is 20min, so as to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active material into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 600r/min, the stirring time is 50min, observing the stirring condition of the negative electrode conductive agent and the negative electrode active material in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active material are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 110r/min, and the stirring time is 50min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000r/min, and the stirring time is 70min, so that the lithium ion battery aqueous negative electrode slurry is finally prepared.
In the step S1, the water-bath heating is carried out on the stirring barrel of the stirrer in the process of mixing the water-based binder and the distilled water, the temperature in the process of stirring and mixing the water-based binder and the distilled water is kept at 55 ℃, and the liquid temperature is immediately detected by a temperature detector;
the anode conductive agent and the anode active material in the step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of negative electrode conductive agent and negative electrode active substance into a ball mill;
step two: opening a ball mill to grind the negative electrode conductive agent and the negative electrode active substance for 30-45 min;
step three: filtering the ground negative electrode conductive agent and the negative electrode active substance for three times by using a 700-mesh screen;
step four: and collecting the negative electrode conductive agent and the negative electrode active substance filtered by the mesh screen.
And after the consistency adjustment in the step S4 is completed, the stirring barrel of the stirring machine is driven to vibrate by the vibration motor, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the lithium ion battery aqueous negative electrode slurry is ensured.
The water-based binder is polyacrylonitrile,
the negative electrode conductive agent is conductive graphite;
the negative active material is natural graphite;
the organic solvent is N-methyl pyrrolidone.
The dispersing agent is polyvinylpyrrolidone.
The thickening agent is sodium carboxymethyl cellulose.
Although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that various changes in the embodiments and/or modifications of the invention can be made, and equivalents and modifications of some features of the invention can be made without departing from the spirit and scope of the invention.
Claims (7)
1. A preparation method of aqueous anode and cathode slurry of a lithium ion battery is characterized by comprising the following steps: the preparation method comprises the following steps:
1) the lithium ion battery aqueous anode slurry comprises 1-2 parts of aqueous binder, 6-8 parts of distilled water, 2-4 parts of anode conductive agent, 1-3 parts of anode active substance, 0.5-0.8 part of dispersant, 70-80 parts of organic solvent and 3-8 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of positive electrode conductive agent and positive electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring conditions of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the positive electrode conductive agent and the positive electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
2) The lithium ion battery aqueous negative electrode slurry comprises 2-3 parts of aqueous binder, 7-8 parts of distilled water, 3-5 parts of negative electrode conductive agent, 0.8-1.5 parts of negative electrode active substance, 0.2-0.7 part of dispersant, 75-85 parts of organic solvent and 2-4 parts of thickener, and the preparation method comprises the following steps:
s1: pouring a certain amount of the water-based binder and distilled water into a stirrer, wherein the stirring speed of the stirrer is 1200-1500r/min, and the stirring time is 10-30min to obtain a mixed solution;
s2: adding a certain amount of negative electrode conductive agent and negative electrode active substance into the mixed solution prepared in the step S1, further stirring by using a stirrer, wherein the stirring speed of the stirrer is 500-700r/min, the stirring time is 30-60min, observing the stirring conditions of the positive electrode conductive agent and the positive electrode active substance in the stirrer, and entering the next step after the negative electrode conductive agent and the negative electrode active substance are completely fused in the mixed solution to form a new mixed solution;
s3: adding a certain amount of dispersant and organic solvent into the mixed solution finally prepared in the step S2, and further stirring by using a stirrer, wherein the stirring speed of the stirrer is 1000-1200r/min, and the stirring time is 45-60min, so as to form a new mixed solution;
s4: and adding a certain amount of thickening agent into the mixed solution prepared in the step S3 to adjust the final consistency of the mixed solution, and stirring by using a stirrer, wherein the stirring speed of the stirrer is 800-.
2. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: and S1, heating the stirring barrel of the stirrer in a water bath manner in the process of mixing the aqueous binder and the distilled water, ensuring that the temperature of the aqueous binder and the distilled water is kept between 50 and 60 ℃ in the stirring and mixing process, and immediately detecting the liquid temperature through a temperature detector.
3. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: the positive electrode conductive agent and the positive electrode active material in step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of positive electrode conductive agent and positive electrode active substance into a ball mill;
step two: opening the ball mill to grind the positive electrode conductive agent and the positive electrode active substance for 30-45 min;
step three: filtering the ground positive electrode conductive agent and the positive electrode active substance for three times by using a 500-plus 800-mesh screen;
step four: and collecting the positive electrode conductive agent and the positive electrode active substance filtered by the mesh screen.
4. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: and after the consistency adjustment in the step S4 is completed, the vibration motor is utilized to drive the stirring barrel of the stirring machine to vibrate, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the aqueous anode slurry of the lithium ion battery is ensured.
5. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: and S1, heating the stirring barrel of the stirrer in a water bath manner in the process of mixing the aqueous binder and the distilled water, ensuring that the temperature of the aqueous binder and the distilled water is kept between 50 and 60 ℃ in the stirring and mixing process, and immediately detecting the liquid temperature through a temperature detector.
6. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: the anode conductive agent and the anode active material in the step S2 need to be pretreated before use, and the pretreatment method and steps are as follows:
the method comprises the following steps: putting a certain amount of negative electrode conductive agent and negative electrode active substance into a ball mill;
step two: opening a ball mill to grind the negative electrode conductive agent and the negative electrode active substance for 30-45 min;
step three: filtering the ground negative electrode conductive agent and the ground negative electrode active substance for three times by using a 500-800-mesh screen;
step four: and collecting the negative electrode conductive agent and the negative electrode active substance filtered by the mesh screen.
7. The preparation method of the aqueous positive and negative electrode paste for the lithium ion battery according to claim 1, wherein the preparation method comprises the following steps: and after the consistency adjustment in the step S4 is completed, the stirring barrel of the stirring machine is driven to vibrate by the vibration motor, so that the air bubbles in the slurry can be conveniently discharged, and the quality of the lithium ion battery aqueous negative electrode slurry is ensured.