CN113001848B - 一种厚度均匀的医用手套的制备方法 - Google Patents
一种厚度均匀的医用手套的制备方法 Download PDFInfo
- Publication number
- CN113001848B CN113001848B CN202110206679.XA CN202110206679A CN113001848B CN 113001848 B CN113001848 B CN 113001848B CN 202110206679 A CN202110206679 A CN 202110206679A CN 113001848 B CN113001848 B CN 113001848B
- Authority
- CN
- China
- Prior art keywords
- coagulant
- mould
- concentration
- mold
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种厚度均匀的医用手套的制备方法，包括如下步骤：S1、将模具垂直浸入高浓度的凝固剂一中；S2、将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，水平或接近水平取出后干燥处理。本发明将模具浸入高浓度的凝固剂一中，指部和掌部具有较高浓度的凝固剂一，之后，将附着有凝固剂一的模具浸入低浓度的凝固剂二中，形成浓度梯度，浓度梯度导致高浓度的溶质迅速向低浓度的方向扩散，并在较短时间内达到动态平衡，使得腕部、掌部和指部附着的凝固剂的厚度相对均匀一致，从而使得浸渍乳胶时，胶膜的厚度相对均匀一致，进而使得制备的手套的厚度比较均匀。
Description
技术领域
本发明涉及技术领域，具体地涉及一种厚度均匀的医用手套的制备方法。
背景技术
目前，国内外生产医用手套往往采用浸一次凝固剂法，凝固剂中带正电荷的离子与橡胶粒子表面的阴离子结合，快速地生成不易解离的物质，从而使胶粒失去电荷而凝固。采用凝固剂浸渍法，模具一般是垂直浸入凝固剂中，之后，垂直取出，模具的指部在凝固剂中浸渍的时间最长，再加上重力的作用，导致附着在指部上的凝固剂的浓度最大，且浸渍乳胶时，指部的胶膜最厚，造成一副手套指部、掌部和腕部的厚度不均匀，给使用者带来较差的触感，并且腕部区域的厚度较薄会降低强度以及破坏胶膜的完整性，导致在穿戴期间容易出现手套撕裂的现象。
发明内容
本发明旨在至少解决现有技术中存在的技术问题之一。为此，本发明提出了一种厚度均匀的医用手套的制备方法，包括如下步骤：
S1、将模具垂直浸入高浓度的凝固剂一中；
S2、将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，然后水平或接近水平取出后干燥处理，其中，所述凝固剂二浸渍的最高点位于所述模具的腕部的下方。
进一步地，所述凝固剂一中钙盐的质量百分浓度为14～18％，所述凝固剂二中钙盐的质量百分浓度为8～13％。
进一步地，步骤S1中，模具在凝固剂一中停留的时间为3～8秒；步骤S2中，模具在凝固剂二中停留的时间为5～8秒。
进一步地，所述凝固剂二浸渍的最高点与所述腕部的最底端之间的距离为30～60mm。
进一步地，步骤S1之前还包括清洗模具以及将清洗之后的模具浸入脱模剂中。
进一步地，步骤S2中，模具从凝固剂二中取出之后，包括如下步骤：
S3、将模具烘干后浸入乳胶中，将附着有乳胶的模具取出烘干；
S4、将烘干后带有乳胶的模具浸入涂层中，然后取出干燥硫化；
S5、将干燥硫化后带有涂层的模具浸入热水中，然后取出干燥、脱模。
进一步地，步骤1)中，按重量份数计，所述乳胶的原料组成包括：天然乳胶100份，促进剂10份，硫化剂10份，防老剂2份，消泡剂2份。
本发明将模具垂直浸入高浓度的凝固剂一中并垂直取出，指部和掌部具有较高浓度的凝固剂一，之后，将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，形成浓度梯度，浓度梯度导致高浓度的溶质迅速向低浓度的方向扩散，并在较短时间内达到动态平衡，使得腕部、掌部和指部附着的凝固剂的厚度相对均匀一致，且采用水平或接近水平取出模具，从而使得浸渍乳胶时，胶膜的厚度相对均匀一致，进而使得制备的手套的厚度比较均匀。
具体实施方式
为了更好地理解本发明，下面结合实施例进一步阐明本发明的内容，但本发明的内容不仅仅局限于下面的实施例。
实施例1：
本发明提出了一种厚度均匀的医用手套的制备方法，包括如下步骤：
(1)清洗模具，将清洗之后的模具浸入脱模剂中，之后，取出烘干；
(2)将烘干之后的模具垂直浸入高浓度的凝固剂一中，凝固剂一的温度为65℃，模具在凝固剂一中停留的时间为8秒；
(3)将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，凝固剂二的温度为60℃，模具在凝固剂二中停留的时间为8秒，所述凝固剂二浸渍的最高点与所述模具腕部的最底端之间的距离为60mm，然后转动模具朝向，最终将模具水平方向取出；
(4)将附着有凝固剂二的模具烘干，之后，浸入乳胶中，乳胶的温度为40℃，模具在乳胶中停留的时间为15秒，将附着有乳胶的模具取出烘干，之后，将烘干之后的模具浸入软化水中进行前沥滤形成预沥滤的乳胶膜，之后，取出烘干，前沥滤持续时间为30秒，软化水的温度为80℃；
(5)将烘干后带有预沥滤的乳胶膜的模具浸入涂层中，模具在涂层中停留的时间为12秒，之后，将预沥滤的乳胶膜进行卷边，以形成卷边乳胶膜；
(6)将带有卷边乳胶膜的模具干燥硫化，之后，将干燥硫化之后带有卷边乳胶膜的模具浸入热水中，热水的温度为80℃，模具在热水中停留的时间为20秒；
(7)将进入热水中的模具取出，将模具浸入隔离剂中，然后取出干燥、脱模，隔离剂的温度为65℃，模具在隔离剂中停留的时间为12秒。
其中，按重量份数计，所述乳胶的原料组成包括：天然乳胶100份，促进剂10份，硫化剂10份，防老剂2份，消泡剂2份；
所述凝固剂一、凝固剂二包括钙盐、润湿剂、附型剂以及水，所述凝固剂一与凝固剂二不同之处在于所含钙盐的质量百分浓度不同，所述凝固剂一中钙盐的质量百分浓度为18％，所述凝固剂二中钙盐的质量百分浓度为13％；所述钙盐为硝酸钙、乙酸钙、氯化钙中的至少一种，所述润湿剂为平平加O溶液、渗透剂JFC、吐温-20、吐温-40、吐温-60和吐温-80中的至少一种，所述附型剂为淀粉、甘油、桃胶、羧甲基纤维素和甲基纤维素中的至少一种；
所述脱模剂为硬脂酸钙、硬脂酸钾、硬脂酸锌中的至少一种；
所述涂层为北京迪芬特有限公司的水溶性PU1536涂层；
所述隔离剂为北京迪芬特有限公司的1627型隔离剂。
实施例2：
本发明提出了一种厚度均匀的医用手套的制备方法，包括如下步骤：
(1)清洗模具，将清洗之后的模具浸入脱模剂中，之后，取出烘干；
(2)将烘干之后的模具垂直浸入高浓度的凝固剂一中，凝固剂一的温度为50℃，模具在凝固剂一中停留的时间为5秒；
(3)将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，凝固剂二的温度为50℃，模具在凝固剂二中停留的时间为6秒，所述凝固剂二浸渍的最高点与所述模具腕部的最底端之间的距离为45mm，然后转动模具朝向，最终将模具水平方向取出；
(4)将附着有凝固剂二的模具烘干，之后，浸入乳胶中，乳胶的温度为30℃，模具在乳胶中停留的时间为12秒，将附着有乳胶的模具取出烘干，之后，将烘干之后的模具浸入软化水中进行前沥滤形成预沥滤的乳胶膜，之后，取出烘干，前沥滤持续时间为20秒，软化水的温度为75℃；
(5)将烘干后带有预沥滤的乳胶膜的模具浸入涂层中，模具在涂层中停留的时间为10秒，之后，将预沥滤的乳胶膜进行卷边，以形成卷边乳胶膜；
(6)将带有卷边乳胶膜的模具干燥硫化，之后，将干燥硫化之后带有卷边乳胶膜的模具浸入热水中，热水的温度为75℃，模具在热水中停留的时间为16秒；
(7)将进入热水中的模具取出，将模具浸入隔离剂中，然后取出干燥、脱模，隔离剂的温度为60℃，模具在隔离剂中停留的时间为10秒。
其中，按重量份数计，所述乳胶的原料组成包括：天然乳胶100份，促进剂10份，硫化剂10份，防老剂2份，消泡剂2份；
所述凝固剂一、凝固剂二包括钙盐、润湿剂、附型剂以及水，所述凝固剂一与凝固剂二不同之处在于所含钙盐的质量百分浓度不同，所述凝固剂一中钙盐的质量百分浓度为16％，所述凝固剂二中钙盐的质量百分浓度为10％；所述钙盐为硝酸钙、乙酸钙、氯化钙中的至少一种，所述润湿剂为平平加O溶液、渗透剂JFC、吐温-20、吐温-40、吐温-60和吐温-80中的至少一种，所述附型剂为淀粉、甘油、桃胶、羧甲基纤维素和甲基纤维素中的至少一种；
所述脱模剂为硬脂酸钙、硬脂酸钾、硬脂酸锌中的至少一种；
所述涂层为北京迪芬特有限公司的水溶性PU1536涂层；
所述隔离剂为北京迪芬特有限公司的1627型隔离剂。
实施例3：
本发明提出了一种厚度均匀的医用手套的制备方法，包括如下步骤：
(1)清洗模具，将清洗之后的模具浸入脱模剂中，之后，取出烘干；
(2)将烘干之后的模具垂直浸入高浓度的凝固剂一中，凝固剂一的温度为45℃，模具在凝固剂一中停留的时间为3秒；
(3)将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，凝固剂二的温度为40℃，模具在凝固剂二中停留的时间为5秒，所述凝固剂二浸渍的最高点与所述模具腕部的最底端之间的距离为30mm，然后转动模具朝向，最终将模具接近水平方向时取出；
(4)将附着有凝固剂二的模具烘干，之后，浸入乳胶中，乳胶的温度为20℃，模具在乳胶中停留的时间为8秒，将附着有乳胶的模具取出烘干，之后，将烘干之后的模具浸入软化水中进行前沥滤形成预沥滤的乳胶膜，之后，取出烘干，前沥滤持续时间为12秒，软化水的温度为70℃；
(5)将烘干后带有预沥滤的乳胶膜的模具浸入涂层中，模具在涂层中停留的时间为8秒，之后，将预沥滤的乳胶膜进行卷边，以形成卷边乳胶膜；
(6)将带有卷边乳胶膜的模具干燥硫化，之后，将干燥硫化之后带有卷边乳胶膜的模具浸入热水中，热水的温度为70℃，模具在热水中停留的时间为12秒；
(7)将进入热水中的模具取出，将模具浸入隔离剂中，然后取出干燥、脱模，隔离剂的温度为60℃，模具在隔离剂中停留的时间为8秒。
其中，按重量份数计，所述乳胶的原料组成包括：天然乳胶100份，促进剂10份，硫化剂10份，防老剂2份，消泡剂2份；
所述凝固剂一、凝固剂二包括钙盐、润湿剂、附型剂以及水，所述凝固剂一与凝固剂二不同之处在于所含钙盐的质量百分浓度不同，所述凝固剂一中钙盐的质量百分浓度为14％，所述凝固剂二中钙盐的质量百分浓度为8％；所述钙盐为硝酸钙、乙酸钙、氯化钙中的至少一种，所述润湿剂为平平加O溶液、渗透剂JFC、吐温-20、吐温-40、吐温-60和吐温-80中的至少一种，所述附型剂为淀粉、甘油、桃胶、羧甲基纤维素和甲基纤维素中的至少一种；
所述脱模剂为硬脂酸钙、硬脂酸钾、硬脂酸锌中的至少一种；
所述涂层为北京迪芬特有限公司的水溶性PU1536涂层；
所述隔离剂为北京迪芬特有限公司的1627型隔离剂。
本发明所制备的不同尺寸的医用手套和常规手套的厚度进行对比，对比结构如表1至表3所示：
表1
表2
表3
由表1至表3可知，本发明所制备的医用手套的厚度较均为。
尽管已经示出和描述了本发明的实施例，本领域的普通技术人员可以理解：在不脱离本发明的原理和宗旨的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由权利要求及其等同物限定。
Claims (6)
1.一种厚度均匀的医用手套的制备方法，其特征在于，包括如下步骤：
S1、将模具垂直浸入高浓度的凝固剂一中；
S2、将附着有凝固剂一的模具垂直浸入低浓度的凝固剂二中，然后水平或接近水平取出后干燥处理，其中，所述凝固剂二浸渍的最高点位于所述模具的腕部的下方；
所述凝固剂二浸渍的最高点与所述腕部的最底端之间的距离为30～60mm。
2.根据权利要求1所述的厚度均匀的医用手套的制备方法，其特征在于，所述凝固剂一中钙盐的质量百分浓度为14～18％，所述凝固剂二中钙盐的质量百分浓度为8～13％。
3.根据权利要求1所述的厚度均匀的医用手套的制备方法，其特征在于，步骤S1中，模具在凝固剂一中停留的时间为3～8秒；步骤S2中，模具在凝固剂二中停留的时间为5～8秒。
4.根据权利要求1所述的厚度均匀的医用手套的制备方法，其特征在于，步骤S1之前还包括清洗模具以及将清洗之后的模具浸入脱模剂中。
5.根据权利要求1所述的厚度均匀的医用手套的制备方法，其特征在于，还包括如下步骤：
S3、将模具烘干后浸入乳胶中，将附着有乳胶的模具取出烘干；
S4、将烘干后带有乳胶的模具浸入涂层中，然后取出干燥硫化；
S5、将干燥硫化后带有涂层的模具浸入热水中，然后取出干燥、脱模。
6.根据权利要求5所述的厚度均匀的医用手套的制备方法，其特征在于，步骤S3中，按重量份数计，所述乳胶的原料组成包括：天然乳胶100份，促进剂10份，硫化剂10份，防老剂2份，消泡剂2份。