CN112935702B - 一种电石锅的修补方法 - Google Patents
一种电石锅的修补方法 Download PDFInfo
- Publication number
- CN112935702B CN112935702B CN202110294800.9A CN202110294800A CN112935702B CN 112935702 B CN112935702 B CN 112935702B CN 202110294800 A CN202110294800 A CN 202110294800A CN 112935702 B CN112935702 B CN 112935702B
- Authority
- CN
- China
- Prior art keywords
- patch
- notch
- carbide pot
- opening end
- calcium carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种电石锅的修补方法,包括步骤:1)取电石锅待用;2)在电石锅的壁上对应烧蚀区和/或击穿孔洞的位置切割出缺口,使电石锅的烧蚀区和/或击穿孔洞位于缺口的延伸范围内,缺口呈斗形,缺口的小口端位于电石锅的外壁,大口端位于电石锅的内壁;3)取铸钢板,切割出第一、第二补块,第一、第二补块呈棱台体,第一补块的顶面与缺口的小口端相适应,第二补块的底面与缺口的大口端相适应;4)将第一、第二补块搁置在缺口中,使第一补块的顶面与缺口的小口端重合、第二补块的底面与缺口的大口端重合,且通过堆焊固定相连。本发明操作简单、修补成本低,可高效对因为内壁烧蚀或击穿而报废的电石锅进行重复修补,有效降低电石加工企业的生产成本。
Description
技术领域
本发明涉及电石加工领域,特别涉及一种电石锅的修补方法。
背景技术
电石的主要成分为碳化钙,遇水立即发生激烈反应,生成乙炔,并放出热量。是重要的基本化工原料,主要用于产生乙炔气,也用于有机合成、氧炔焊接等。
电石在工业加工过程中,一般用电炉熔炼法将焦炭与氧化钙置于2200℃的电炉中熔炼,生成碳化钙熔融液,碳化钙熔融液导入电石锅内,经冷凝成型,得到电石。
通常,电石锅采用碳钢材料制作,这种类型的电石锅在使用过程中,高温的碳化钙熔融液在导入过程中,对电石锅造成冲击,造成电石锅的内壁烧蚀,甚至击穿形成孔洞,导致电石锅报废。电石锅的售价较高,较高的损毁率导致电石加工企业的电石加工成本较高。
发明内容
本发明的目的是针对现有技术的不足,提供一种电石锅的修补方法,其操作简单、修补成本低,可高效对因为内壁烧蚀或击穿而报废的电石锅进行重复修补,有效降低电石加工企业的生产成本。
本发明的技术方案是:一种电石锅的修补方法,包括以下步骤:
1)取待修补的电石锅,清理、打磨,待用;
2)利用氧割或等离子切割在电石锅的壁上对应电石锅的烧蚀区和/或击穿孔洞的位置切割出缺口,使电石锅的烧蚀区和/或击穿孔洞位于缺口的延伸范围内,缺口呈斗形,呈斗形的缺口的小口端位于电石锅的外壁,呈斗形的缺口的大口端位于电石锅的内壁;
3)取铸钢板,切割出第一补块、第二补块,第一补块呈棱台体,且棱台体的顶面与缺口的小口端相适应,第二补块呈棱台体,且棱台体的底面与缺口的大口端相适应;
4)将第一补块搁置在缺口中,使第一补块的顶面与缺口的小口端重合,且通过堆焊固定相连,将第二补块搁置在缺口中,使第二补块的底面与缺口的大口端重合,且通过堆焊固定相连,修补完成。
步骤3)采用氧割或等离子切割在铸钢板上切割出第一补块、第二补块。
步骤3)第一补块、第二补块的厚度为电石锅的壁厚的一半。
步骤3)第一补块的厚度大于电石锅的壁厚的一半,小于电石锅的壁厚,第一补块、第二补块的厚度之和与电石锅的壁厚相适应。
步骤4)第一补块的底面与第二补块的顶面贴合。
采用上述技术方案具有以下有益效果:
1、本发明利用氧割或等离子切割,将电石锅对应烧蚀区和/或击穿孔洞的位置切割掉,形成缺口,再利用第一补块、第二补块与缺口配合,且通过堆焊固定,与电石锅形成整体,即对电石锅的烧蚀区或击穿孔洞形成替换,使报废的电石锅重新投入使用用于冷凝成型电石,极大的降低了电石企业更换电石锅的成本。
2、本发明在电石锅上切割得到的缺口,利用第一补块、第二补块对缺口形成封堵,保证修补后的电石锅可以正常使用。且第一补块与电石锅的外壁齐平,第二补块与电石锅的内壁齐平,在后续使用过程中,若第二补块再次被严重烧蚀甚至出现穿孔现象,可直接将第二补块切割掉,直接替换第二补块即完成修补作业,方便对电石锅进行重复修补,降低电石锅的修补成本,进一步降低电石锅生产企业的生产成本。
3、本发明在电石锅的侧壁上切割出的缺口,呈斗形,且呈斗形的缺口的小口端位于电石锅的外壁,呈斗形的缺口的大口端位于电石锅的内壁,第一补块、第二补块与缺口的形状适应,当第一补块、第二补块装配在缺口的对应位置时,形成限位,可有效保证第一补块、第二补块在缺口的稳定性,进而保证第二补块的抗冲击强度,提高修补后电石锅的使用寿命。
下面结合附图和具体实施方式作进一步的说明。
附图说明
图1为本发明的缺口的结构示意图;
图2为本发明实施例1的修补示意图;
图3为本发明实施例2的修补示意图。
附图中,1为第一补块,2为第二补块,3为缺口。
具体实施方式
实施例1
参见图1和图2,为一种电石锅的修补方法的具体实施例。修补方法包括以下步骤:
1)取待修补的电石锅,清理、打磨,待用;
2)利用氧割或等离子切割在电石锅的壁上对应电石锅的烧蚀区和/或击穿孔洞的位置切割出缺口3,使电石锅的烧蚀区和/或击穿孔洞位于缺口3的延伸范围内,切割出的缺口3呈斗形,呈斗形的缺口的小口端位于电石锅的外壁,呈斗形的缺口的大口端位于电石锅的内壁,通常的,为了便于切割,将待修补的电石锅倒置架空,利用氧割或等离子切割从电石锅的外壁开始切割,最终使切割出的切块在重力作用下自电石锅脱落,得到缺口;
3)取一块铸钢板,利用氧割或等离子切割的方式切割出第一补块1、第二补块2,很显然的,第一补块、第二补块的厚度相同。第一补块1呈棱台体,且棱台体的顶面与缺口3的小口端相适应,第二补块2呈棱台体,且棱台体的底面与缺口3的大口端相适应;
4)将第一补块1搁置在缺口3中,使第一补块1的顶面与缺口3的小口端重合,且通过堆焊固定相连,将第二补块2搁置在缺口3中,且第二补块的顶面与第一补块的底面贴合,使第二补块2的底面与缺口3的大口端重合,且通过堆焊固定相连,修补完成。
实施例2
参见图1和图3,为另一种电石锅的修补方法的具体实施例。修补方法包括以下步骤:
1)取待修补的电石锅,清理、打磨,待用;
2)利用氧割或等离子切割在电石锅的壁上对应电石锅的烧蚀区和/或击穿孔洞的位置切割出缺口3,使电石锅的烧蚀区和/或击穿孔洞位于缺口3的延伸范围内,切割出的缺口3呈斗形,呈斗形的缺口的小口端位于电石锅的外壁,呈斗形的缺口的大口端位于电石锅的内壁,通常的,为了便于切割,将待修补的电石锅倒置架空,利用氧割或等离子切割从电石锅的外壁开始切割,最终使切割出的切块在重力作用下自电石锅脱落,得到缺口;
3)取两块铸钢板,利用氧割或等离子切割的方式分别在各铸钢板上切割出第一补块1、第二补块2,通常的,为了便于重复修复,第一补块1的厚度大于电石锅的壁厚的一半,小于电石锅的壁厚,第一补块1、第二补块2的厚度之和与电石锅的壁厚相适应,也即,第二补块的厚度小于电石锅的壁厚的一半。第一补块1呈棱台体,且棱台体的顶面与缺口3的小口端相适应,第二补块2呈棱台体,且棱台体的底面与缺口3的大口端相适应;
4)将第一补块1搁置在缺口3中,使第一补块1的顶面与缺口3的小口端重合,且通过堆焊固定相连,将第二补块2搁置在缺口3中,且第二补块的顶面与第一补块的底面贴合,使第二补块2的底面与缺口3的大口端重合,且通过堆焊固定相连,修补完成。
Claims (3)
1.一种电石锅的修补方法,其特征在于,包括以下步骤:
1)取待修补的电石锅,清理、打磨,待用;
2)将待修补的电石锅倒置架空,利用氧割或等离子切割在电石锅的壁上对应电石锅的烧蚀区和/或击穿孔洞的位置切割出缺口,使电石锅的烧蚀区和/或击穿孔洞位于缺口的延伸范围内,缺口呈斗形,呈斗形的缺口的小口端位于电石锅的外壁,呈斗形的缺口的大口端位于电石锅的内壁;
3)取铸钢板,切割出第一补块、第二补块,第一补块呈棱台体,且棱台体的顶面与缺口的小口端相适应,第二补块呈棱台体,且棱台体的底面与缺口的大口端相适应,第一补块的厚度大于电石锅的壁厚的一半,小于电石锅的壁厚,第一补块、第二补块的厚度之和与电石锅的壁厚相适应;
4)将第一补块搁置在缺口中,使第一补块的顶面与缺口的小口端重合,且通过堆焊固定相连,将第二补块搁置在缺口中,使第二补块的底面与缺口的大口端重合,且通过堆焊固定相连,修补完成。
2.根据权利要求1所述的电石锅的修补方法,其特征在于,步骤3)采用氧割或等离子切割在铸钢板上切割出第一补块、第二补块。
3.根据权利要求1所述的电石锅的修补方法,其特征在于,步骤4)第一补块的底面与第二补块的顶面贴合。