CN112831243A - 一种环氧树脂基地坪涂料及其制备方法 - Google Patents
一种环氧树脂基地坪涂料及其制备方法 Download PDFInfo
- Publication number
- CN112831243A CN112831243A CN201911161832.0A CN201911161832A CN112831243A CN 112831243 A CN112831243 A CN 112831243A CN 201911161832 A CN201911161832 A CN 201911161832A CN 112831243 A CN112831243 A CN 112831243A
- Authority
- CN
- China
- Prior art keywords
- component
- coating
- epoxy resin
- agent
- based floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环氧树脂基地坪涂料及其制备方法，首先进行拌合，将涂料A组份与B组份混合好，用搅拌机搅拌均匀，再加入C组份，用搅拌机搅拌均匀，然后镘涂，将拌好的涂料铺在做好的中涂层上面，用5毫米的镘刀镘涂施工，然后消泡，用消泡辊筒在镘涂好的涂料表面来回拉动，让彩色有机骨料在涂层中分布均匀，最后水磨，待上述涂层完全干燥后，用2000目的树脂磨片水磨，待水份完全干燥后即得到成品；B组份为改性脂环胺环氧固化剂，脂环胺具有类似金刚烷类骨架结构，有极强的机械强度；C组份为密胺树脂砂，具有无毒无味，耐磕碰，耐腐蚀，结构紧密，有极强的硬度，很强的耐用性，色彩鲜艳，非常漂亮，而且抗划伤性能优异。
Description
技术领域
本发明涉及一种地坪涂料及其制备方法，具体是一种环氧树脂基地坪涂料及其制备方法。
背景技术
目前，国内各种专卖店、展示厅、办公室、酒店、学校、家庭与及商业建筑地面的装饰装修多采用水磨石、人造大理石、瓷砖的拼接地面，这些地面材料存在接缝，容易藏污纳垢，由于环氧树脂地坪具有弱析尘、整体无缝、容易清洁、耐磨损等特点，使得环氧树脂地坪得到了广泛的应用。
目前，现在环氧树脂地坪涂料主要有薄涂型，砂浆型和自流平型，但是这些地坪涂料只能做出单一颜色，没有磨石那种的立体感和艺术性，并且这些地坪涂料涂膜耐磨性虽然不错，但抗划伤性不好，表面很容易划花，美观性就大大下降了。
发明内容
本发明的目的在于提供一种环氧树脂基地坪涂料及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种环氧树脂基地坪涂料，包括A组份、B组份和C组份，其特征在于，所述A组份、B组份和C组份的重量比为4：1：2.5，所述A组份包括环氧树脂、活性稀释剂、助剂、颜料和填料，所述A组份的重量百分比如下：环氧树脂38％～50％、活性稀释剂2％～9％、助剂0.5％～1％、颜料0.5％～1％、填料40％～60％，所述B组份选用改性脂环胺环氧固化剂，所述C组份选用彩色有机骨料。
作为本发明进一步的方案：所述助剂包括消泡剂0.3～0.5％，润湿剂0.1～0.2％，流平剂0.2～0.4％和分散剂0.1～0.4％。
作为本发明再进一步的方案：所述环氧树脂选用双酚A型环氧树脂，其环氧值为0.48-0.54。
作为本发明再进一步的方案：所述活性稀释剂选用丁基缩水甘油醚、C12-14烷基缩水甘油醚、苯基缩水甘油醚、苄基缩水甘油醚或烯丙基缩水甘油醚中的一种或几种。
作为本发明再进一步的方案：所述填料选用石英粉、重质碳酸钙或重晶石粉中的一种或几种，所述石英粉的大小为325目至600目之间。
作为本发明再进一步的方案：所述颜料选用钛白粉、酞菁绿、中铬黄、柠檬黄、碳黑、酞菁蓝、永固红和钼铬红中的一种或几种。
作为本发明再进一步的方案：所述改性脂环胺环氧固化剂选用ancamine1618、ancamine2726或ancamine1784中的一种或几种。
作为本发明再进一步的方案：所述彩色有机骨料选用彩色密胺树脂砂，所述彩色密胺树脂砂的大小为40目至100目，所述分散剂选用EFKA4015或BYK163中的一种，所述润湿剂的型号为EFKA5065，所述消泡剂的型号为DEFOM6800，所述流平剂选用BYK361N或TEGO1484中的一种。
一种环氧树脂基地坪涂料的制备方法：
第一步，拌合，先将涂料A组份与B组份混合好，用搅拌机搅拌均匀，然后再加入C组份。再用搅拌机搅拌均匀；
第二步，镘涂，将拌好的涂料铺在做好的中涂层上面，用5毫米的镘刀镘涂施工；
第三步，消泡，用消泡辊筒在镘涂好的涂料表面来回拉动，让彩色有机骨料在涂层中分布均匀；
第四步，水磨，待上述涂层在25℃下，经历48小时完全干燥后，用2000目的树脂磨片水磨，待水份完全干燥后即得到美观耐用的地坪成品。
与现有技术相比，本发明的有益效果是：
本发明中，B组份为改性脂环胺环氧固化剂，脂环胺具有类似金刚烷类骨架结构，有极强的机械强度；C组份为密胺树脂砂，具有无毒无味，耐磕碰，耐腐蚀，结构紧密，有极强的硬度，很强的耐用性，色彩鲜艳，非常漂亮，而且抗划伤性能优异。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种环氧树脂基地坪涂料，包括A组份、B组份和C组份，其特征在于，所述A组份、B组份和C组份的重量比为4：1：2.5，所述A组份包括环氧树脂、活性稀释剂、助剂、颜料和填料，所述A组份的重量百分比如下：环氧树脂40％、活性稀释剂5％、助剂1％、颜料1％、填料53％，所述B组份选用改性脂环胺环氧固化剂，所述C组份选用彩色有机骨料。
根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述助剂包括消泡剂0.3％，润湿剂0.1％，流平剂0.2％和分散剂0.4％。
所述环氧树脂选用双酚A型环氧树脂，其环氧值为0.5。
所述活性稀释剂选用丁基缩水甘油醚、C12-14烷基缩水甘油醚、苯基缩水甘油醚、苄基缩水甘油醚或烯丙基缩水甘油醚中的一种或几种。
所述填料选用石英粉、重质碳酸钙或重晶石粉中的一种或几种，所述石英粉的大小为350目之间。
所述颜料选用钛白粉、酞菁绿、中铬黄、柠檬黄、碳黑、酞菁蓝、永固红和钼铬红中的一种或几种。
所述改性脂环胺环氧固化剂选用ancamine1618、ancamine2726或ancamine1784中的一种或几种。
所述彩色有机骨料选用彩色密胺树脂砂，所述彩色密胺树脂砂的大小为50目，所述分散剂选用EFKA4015或BYK163中的一种，所述润湿剂的型号为EFKA5065，所述消泡剂的型号为DEFOM6800，所述流平剂选用BYK361N或TEGO1484中的一种。
一种环氧树脂基地坪涂料的制备方法：
第一步，拌合，先将涂料A组份与B组份混合好，用搅拌机搅拌均匀，然后再加入C组份。再用搅拌机搅拌均匀；
第二步，镘涂，将拌好的涂料铺在做好的中涂层上面，用5毫米的镘刀镘涂施工；
第三步，消泡，用消泡辊筒在镘涂好的涂料表面来回拉动，让彩色有机骨料在涂层中分布均匀；
第四步，水磨，待上述涂层在25℃下，经历48小时完全干燥后，用2000目的树脂磨片水磨，待水份完全干燥后即得到美观耐用的地坪成品。
实施例2：
一种环氧树脂基地坪涂料，包括A组份、B组份和C组份，其特征在于，所述A组份、B组份和C组份的重量比为4：1：2.5，所述A组份包括环氧树脂、活性稀释剂、助剂、颜料和填料，所述A组份的重量百分比如下：环氧树脂45％、活性稀释剂5％、助剂1％、颜料0.5％、填料48.5％，所述B组份选用改性脂环胺环氧固化剂，所述C组份选用彩色有机骨料。
所述助剂包括消泡剂0.4％，润湿剂0.1％，流平剂0.2％和分散剂0.3％。
所述环氧树脂选用双酚A型环氧树脂，其环氧值为0.48。
所述活性稀释剂选用丁基缩水甘油醚、C12-14烷基缩水甘油醚、苯基缩水甘油醚、苄基缩水甘油醚或烯丙基缩水甘油醚中的一种或几种。
所述填料选用石英粉、重质碳酸钙或重晶石粉中的一种或几种，所述石英粉的大小为400目之间。
所述颜料选用钛白粉、酞菁绿、中铬黄、柠檬黄、碳黑、酞菁蓝、永固红和钼铬红中的一种或几种。
所述改性脂环胺环氧固化剂选用ancamine1618、ancamine2726或ancamine1784中的一种或几种。
所述彩色有机骨料选用彩色密胺树脂砂，所述彩色密胺树脂砂的大小为60目，所述分散剂选用EFKA4015或BYK163中的一种，所述润湿剂的型号为EFKA5065，所述消泡剂的型号为DEFOM6800，所述流平剂选用BYK361N或TEGO1484中的一种。
一种环氧树脂基地坪涂料的制备方法：
第一步，拌合，先将涂料A组份与B组份混合好，用搅拌机搅拌均匀，然后再加入C组份。再用搅拌机搅拌均匀；
第二步，镘涂，将拌好的涂料铺在做好的中涂层上面，用5毫米的镘刀镘涂施工；
第三步，消泡，用消泡辊筒在镘涂好的涂料表面来回拉动，让彩色有机骨料在涂层中分布均匀；
第四步，水磨，待上述涂层在25℃下，经历48小时完全干燥后，用2000目的树脂磨片水磨，待水份完全干燥后即得到美观耐用的地坪成品。
实施效果
从上述实施例1和实施例2可以看出，按本发明制备的地坪涂料各项性能指标均可以满足使用需求，本发明中，B组份为改性脂环胺环氧固化剂，脂环胺具有类似金刚烷类骨架结构，有极强的机械强度；C组份为密胺树脂砂，具有无毒无味，耐磕碰，耐腐蚀，结构紧密，有极强的硬度，很强的耐用性，色彩鲜艳，非常漂亮，而且抗划伤性能优异。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (9)
1.一种环氧树脂基地坪涂料，包括A组份、B组份和C组份，其特征在于，所述A组份、B组份和C组份的重量比为4：1：2.5，所述A组份包括环氧树脂、活性稀释剂、助剂、颜料和填料，所述A组份的重量百分比如下：环氧树脂38％～50％、活性稀释剂2％～9％、助剂0.5％～1％、颜料0.5％～1％、填料40％～60％，所述B组份选用改性脂环胺环氧固化剂，所述C组份选用彩色有机骨料。
2.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述助剂包括消泡剂0.3～0.5％，润湿剂0.1～0.2％，流平剂0.2～0.4％和分散剂0.1～0.4％。
3.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述环氧树脂选用双酚A型环氧树脂，其环氧值为0.48-0.54。
4.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述活性稀释剂选用丁基缩水甘油醚、C12-14烷基缩水甘油醚、苯基缩水甘油醚、苄基缩水甘油醚或烯丙基缩水甘油醚中的一种或几种。
5.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述填料选用石英粉、重质碳酸钙或重晶石粉中的一种或几种，所述石英粉的大小为325目至600目之间。
6.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述颜料选用钛白粉、酞菁绿、中铬黄、柠檬黄、碳黑、酞菁蓝、永固红和钼铬红中的一种或几种。
7.根据权利要求1所述的一种环氧树脂基地坪涂料，其特征在于，所述改性脂环胺环氧固化剂选用ancamine1618、ancamine2726或ancamine1784中的一种或几种。
8.根据权利要求1或2所述的一种环氧树脂基地坪涂料，其特征在于，所述彩色有机骨料选用彩色密胺树脂砂，所述彩色密胺树脂砂的大小为40目至100目，所述分散剂选用EFKA4015与BYK163中的一种，所述润湿剂的型号为EFKA5065，所述消泡剂的型号为DEFOM6800，所述流平剂选用BYK361N与TEGO1484中的一种。
9.一种采用权利要求1至8任一项所述一种环氧树脂基地坪涂料的制备方法，其特征在于，包括如下步骤:
1)拌合，先将涂料A组份与B组份混合好，用搅拌机搅拌均匀，然后再加入C组份，再用搅拌机搅拌均匀；
2)镘涂，将拌好的涂料铺在做好的中涂层上面，用5毫米的镘刀镘涂施工；
3)消泡，用消泡辊筒在镘涂好的涂料表面来回拉动，让彩色有机骨料在涂层中分布均匀；
4)水磨，待上述涂层在25℃下，经历48小时完全干燥后，用2000目的树脂磨片水磨，待水份完全干燥后即得到美观耐用的地坪成品。